KR960004209A - 무정형 알루미노실리케이트 및 그 제조방법 - Google Patents

무정형 알루미노실리케이트 및 그 제조방법 Download PDF

Info

Publication number
KR960004209A
KR960004209A KR1019940034831A KR19940034831A KR960004209A KR 960004209 A KR960004209 A KR 960004209A KR 1019940034831 A KR1019940034831 A KR 1019940034831A KR 19940034831 A KR19940034831 A KR 19940034831A KR 960004209 A KR960004209 A KR 960004209A
Authority
KR
South Korea
Prior art keywords
angstroms
reaction product
pores
amorphous aluminosilicate
temperature
Prior art date
Application number
KR1019940034831A
Other languages
English (en)
Other versions
KR100304837B1 (ko
Inventor
아츠시 하사다
하지메 후나코시
다케시 오자와
Original Assignee
다시로 마도카
도소 가부시키가이샤
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP26266494A external-priority patent/JPH08119622A/ja
Priority claimed from JP26344994A external-priority patent/JPH0873211A/ja
Application filed by 다시로 마도카, 도소 가부시키가이샤 filed Critical 다시로 마도카
Publication of KR960004209A publication Critical patent/KR960004209A/ko
Application granted granted Critical
Publication of KR100304837B1 publication Critical patent/KR100304837B1/ko

Abstract

본 발명은 수은침투법에 의해 측정할 때 103옹스트롬 내지 105옹스트롬의 직경을 가지는 세공의 전부피가 수은침투법에 의해 검출된 모든 세공의 전부피의 적어도 60%를 차지하고, 질소흡착법에 의해 측정할때 20옹스트롬 내지 120옹스트롬의 직경을 가지는 세공의 전부피가 0.01cc/g이상인 무정형 알루미노실리케이트, 및 이 무정형 알루미노실리케이트의 제조방법에 관한 것이다.

Description

무정형 알루미노실리케이트 및 그 제조방법
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 실시예 1에서 얻어진 무정형 알루미노실리케이트에 대한 수은침투법에 의한 세공(pore)분포 측정결과를 나타내고,
제2도는 비교예 1에서 얻어진 무정형 알루미노실리케이트에 대한 수은침투법에 의한 세공분포 측정결과를 나타낸다.

Claims (7)

  1. 수은침투법에 의해 측정할때 103옹스트롬 내지 105옹스트롬의 직경을 가지는 세공의 전부피가 수은침투법에 의해 검출된 모든 세공의 전부피의 적어도 60%를 차지하고, 질소흡착법에 측정할때 20옹스트롬 내지 120옹스트롬의 직경을 가지는 세공의 전부피가 0.01cc/g이상인 것을 특징으로 하는 무정형 알리미노실리케이트.
  2. 제1항에 있어서, 30옹스트롬 내지 50옹스트롬의 반경을 가지는 세공에 기인하는 비표면적이 10㎡/g이상인 것을 특징으로 하는 무정형 알리미노실리케이트.
  3. 제1항 또는 2항에 있어서, 900℃에서 적어도 1시간 가열할때 가열전의 그 중량을 기준으로 15중량% 내지 35중량%의 중량감소되며, 기준으로서 알루미나를 사용하는 시차열분석에서 110℃ 내지 160℃ 범위내의 흡열피크를 보이며, Na-MASNMR 분석에 의해 얻어지는 20ppm의 화학적 이동치 부근에 존재하는 피크를 피크형태에 의해 가파른 피크와 넓은 피크로 분류할 때, 넓은 피크면적의 비율이 40%이하인 것을 특징으로 하는 무정형 알리미노실리케이트.
  4. 40℃이하로 유지된 알루민산 알칼리금속 수용액을 40℃이하로 유지된 물에 첨가하여 이 혼합물을 교반하고, 거기에 교반하면서 40℃이하로 유지된 규산알칼리금속 수용액을 첨가하여 40℃이하의 온도에서 성분들을 반응시키고, 결과생성한 슬러리를 여과하고, 그 다음 결과생성한 생성물을 100℃미만의 온도에서 건조시키는 것으로 이루어지는 것을 특징으로 하는 특허청구의 범위 제3항에 규정된 무정형 알루미노실리케이트의 제조방법.
  5. 규산알칼리금속 수용액을 알루민산 알칼리금속 수용액에 첨가하여 성분을 반응시키고 반응생성물을 건조시키는 것으로 이루어지며, 상기 반응은 50℃이하의 온도에서 행하고, 상기 규산알칼리금속 수용액의 첨가는 합성된 반응생서물의 수율을 100%로 간주하는 것을 조건으로, 이 첨가속도가 반응계에 존재하는 A1원자에 대한 Si원자의 비율변화의 관점에서 분당 0.10 내지 1.50이고, 최종적으로 반응계의 si원자/A1원자 비율이 0.25 내지 6.00이고 모액내 수산화이온농도가 0.4mol/kg 내지 1.5mol/kg이며, 결과 생성한 슬러리의 농도가 20중량% 이하인 방식으로 행하고, 상기 반응생성물의 건조는 반응생성물의 온도 관점에서 90℃이하에서 행하는 것을 특징으로 하는 특허청구의 범위 제3항에 규정된 무정형 알루미노실리케이트의 제조방법.
  6. 제4항에 있어서, 반응생성물을 반응생성물의 온도 관점에서 60℃이하에서 건조시키는 것을 특징으로 하는 무정형 알리미노실리케이트.
  7. 제5항에 있어서, 반응생성물을 반응생성물의 온도 관점에서 60℃이하에서 건조시키는 것을 특징으로 하는 무정형 알리미노실리케이트의 제조방법.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019940034831A 1994-07-08 1994-12-17 무정형알루미노실리케이트및그제조방법 KR100304837B1 (ko)