KR930700382A - 건식 내화 조성물 - Google Patents
건식 내화 조성물Info
- Publication number
- KR930700382A KR930700382A KR1019920702829A KR920702829A KR930700382A KR 930700382 A KR930700382 A KR 930700382A KR 1019920702829 A KR1019920702829 A KR 1019920702829A KR 920702829 A KR920702829 A KR 920702829A KR 930700382 A KR930700382 A KR 930700382A
- Authority
- KR
- South Korea
- Prior art keywords
- refractory
- weight percent
- composition
- weight
- temperature
- Prior art date
Abstract
내용 없음.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (12)
- 마그네시아, 알루미나, 칼시아, 실리카, 지르코니아 및 이들의 배합물로 이루어지는 그룹 중에서 선택된 내화 응결체 물질을 기본으로 재료로하는 건식 내화물용 내화 조성물에 있어서, 페놀성 수지 저온 결합제 약 1.0 내지 약 5.0중량% 및 나트륨 함량이 약 40.0 중량% 미만인 인산염-함유 화합물 및 알칼리 금속 규산염과 금속 분말의 혼합물로 이루어지는 그룹중에서 선택된 하나 이상의 중간 온도 결합제 약 0.5 내지 약 10.0 중량%(여기서, 조성물 중에는 인산염-함유 화합물 및 규산염-함유 화합물중 하나 이상이 존재하며 중간 온도 결합제는 조성물 중에 10.0 중량%를 초과하는 양으로 존재하기 않고, 내화 응결체 물질은 총 100 중량%인 조성물의 나머지를 차지한다)를 포함함을 특징으로 하는 내화 조성물.
- 제1항에 있어서, 페놀성 수지가 페놀 포름알데히드 중합체인 내화 조성물.
- 제1항에 있어서, 인산염-함유 화합물이 인산 일나트륨, 헥사메타인산 나트륨 및 인산 일암모늄으로 이루어지는 그룹 중에서 선택되고, 알칼리 금속 규산염이 무수 규산 나트륨 및 수화된 규산 나트륨으로 이루어지는 그룹 중에서 선택되며, 금속 분말이 페로규소 합금, 알루미늄/규소 합금 및 마그네슘/알루미늄 합금으로 이루어지는 그룹에서 선택된 내화 조성물.
- 제1항에 있어서, 알칼리 금속 규산염 및 금속 분말이 이들의 혼합물 중에 동량으로 존재하고, 금속 분말의 입자 크기 범위가 약 1μ 내지 약 500μ임을 특징으로 하는 내화 조성물.
- 제2항에 있어서, 페놀 프름알데히드 중합체가 헥사민 약 1.0 내지 약 10.0 중량%를 함유하고 평균 분자량이 약 4000 내지 약 10,000a, m, u(원자 질량 단위)임을 추가의 특징으로 하는 내화 조성물.
- 제3항에 있어서, 페로규소 합금이 철 약 20.0 내지 약 30.0 중량%를 함유하고 규소 약 80.0 내지 약 70.0 중량%를 함유하며, 알루미늄/규소 합금 금속 분말이 알루미늄 약 70.0 내지 약 90.0 중량%를 함유하고 규소 약 30.0 내지 약 10.0 중량%를 함유하며, 마그네슘/알루미늄 금속 분말이 마그네슘 약 40.0 지 약 60.0 중량%를 함유하고 알루미늄 약 60.0 내지 약 40.0 중량%를 함유하는 내화 조성물.
- 제1항에 있어서, 보올 클레이, 고령토, 벤토나이트 및 이들의 혼합물로 이루어지는 그룹중에서 선택된 점토 0.0 내지 약 5.0 중량%를 함유함을 추가의 특징으로 하는 내화 조성물.
- 제1항에 있어서, 저온 결합제가 약 300℉ 내지 약 1000℉의 온도 범위에서 내화재의 입자 사이의 입자간 결합 형성을 개시시키며, 중간 온도 결합제가 약 1000℉ 내지 약 2500℉의 온도 범위에서 내화 물질의 입자 사이의 입자간 결합 형성을 개시시키는 내화 조성물.
- 제1항에 있어서, 진동가능물임을 추가의 특징으로 하는 내화 조성물.
- 페놀 포름알데히드 약 2.5 내지 약 3.5 중량%, 인산일나트륨 약 2.5 내지 약 3.5 중량%, 무수 규산 나트륨과 페로규소 합금 금속 분말의 50/50중량% 혼합물 약 2.5 내지 약 3.5 중량% 및 점토 0.0 내지 약 5.0 중량%를 포함하는 건식 내화물용 내화 조성물.
- a)건식 내화 조성물을 성형시키기 위한 주물-성형 장치를 용기와 주물-성형 장치 사이에 간극이 생기도록 용기내에 넣고, b)간극에 용기의 내부 표면을 피복시키기에 충분한 양의 내화 조성물(여기서, 내화 조성물은 저온 결합제 약 1.0 내지 약 5.0 중량%, 하나 이상의 주간 온도 결합제 0.5 내지 약 10.0중량% 및 점토 0.0 내지 약 5.0중량%외에 나머지 내화 응결체 물질을 합하여 총 100 중량%를 함유한다)을 붓고, c)용기내의 온도를 약 300℉ 내지 약 1000℉로 상승시켜 내화 조성물을 경화시켜 저온 결합제에 의해 내화 응결체의 입자 사이에 입자간 결합이 이루어지도록 하고, d)주물-성형 장치를 제거하여 용기의 내부 표면에 내화재의 일체 주물이 남도록 한 다음, e)용기 내의 온도를 약 1000℉ 내지 약 2500℉로 상승시켜 내화 조성물을 예열함으로써 중간 온도 결합제에 의해 내화 응결체의 입자 사이에 입자간 결합이 형성되도록 하는 단계를 특징으로 하는, 고온 수행법으로 턴디시와 같은 용기의 내부 표면에 일체 내화 라이닝을 건식 도포시키는 방법.
- ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.