KR930013189A - 저항복비 고강도 열연강판 및 그의 제조방법 - Google Patents
저항복비 고강도 열연강판 및 그의 제조방법 Download PDFInfo
- Publication number
- KR930013189A KR930013189A KR1019920025640A KR920025640A KR930013189A KR 930013189 A KR930013189 A KR 930013189A KR 1019920025640 A KR1019920025640 A KR 1019920025640A KR 920025640 A KR920025640 A KR 920025640A KR 930013189 A KR930013189 A KR 930013189A
- Authority
- KR
- South Korea
- Prior art keywords
- high strength
- steel sheet
- less
- martensite
- ferrite
- Prior art date
Abstract
(목적) 종래의 석출 강화 강과 조직 강화 강이 지나는 각각의 특징을 함께 구비하는 한편에서, 각각의 강의 결점이 없는 고강도 강을 얻는 것.
(구성) 종래의 고강도 강의 성분 조성에 대하여 C의 상한을 0.18wt%로 하는 한편, 그의 하한을 Ti,Nb와의 관계에서 C≥0.05+Ti/4+Nb/8을 만족하도록 함유시키는 동시에 Si를 0.5~2.5wt%의 적정 범위내에서 함유하고, 그리고 Ti및/또는 Nb의 탄화물이 석출된 페라이트와 마르텐사이트 및 잔류 오오스테나이트로 이루어지는 조직을 갖는 저항복비 고강도 압연강판 및 그것의 열간압연에 특징이 있는 제조방법.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 인장 특성치와 Si함유량의 관계를 나타내는 그래프,
제2도는 사이드 벤딩 시험 방법을 나타낸 모식도,
제3도는 확장 시험 방법을 나타낸 모식도.
Claims (3)
- C:0.18wt%이하, Si:0.5~2.5wt%, Mn:0.5~2.5wt%, P:0.05wt%이하, S:0.02wt%, Al:0.01~0.1wt%를 함유하고, 그리고, Ti:0.02~0.5wt% 및 Nb:0.03~1.0wt%중의 어느 1종 또는 2종을 함유하는 동시에, 이들 Ti및 Nb는 C와의 관계에서 하기 식을 만족하도록 함유하며, 잔부과 Fe 및 불가피한 불순물로 이루어지는 조성물을 가지며, 그 조직이 Ti 및/도는 Nb의 탄화물이 석출된 페라이트와 마르텐사이트, 또는 상기 탄화물이 석출된 페라이트와 마르텐사이트 및 잔류 오스테나 이트로 이루어지는 저항복비 고강도 열연강판.C wt% ≥ 0.05+Ti wt% / 4 + Nb wt% / 8
- C:0.18wt%이하, Si:0.5~2.5wt%, Mn:0.5~2.5wt%, P:0.05wt%이하, S:0.02wt%, Al:0.01~0.1wt%및 Cr:0.3~1.5wt%를 함유하고, 그리고 Ti:0.02~0.5wt 및 Nb:0.03~1.0wt%중의 어느 1종 또는 2종을 함유하는 동시에, 이것들 Ti 및 Nb는 C와의 관계에서 하기식을 만족하도록 함유하며, 잔부가 Fe및 불가피한 불순물로 이루어지는 조성을 가지며, 또한 그 조직이 Ti 및/또는 Nb의 탄화물이 석출된 페라이트와 마르텐사이트, 또는 상기 탄화물이 석출된 페라이트와 마르텐사이트 및 잔류 오오스테나이트로 이루어지는 저항복비 고강도 열연강판.C wt% ≥ 0.05+Ti wt% / 4 + Nb wt% / 8
- 제1항 또는 2항에 기재된 조성으로 이루어지는 강승랩을 소재로 하고, 이 강슬랩의 열간압연에 있어서는 820℃이상의 온도에서 압연을 종료하고, 이어서 820~720℃의 온도영역에 10초 이상 체류시키고, 그후 10℃/sec이상의 냉각속도로 냉각하여, 500℃이하의 온도에서 감는 것을 특징으로 하는 저항복비 고강도 열연강판의 제조 방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.