KR930007995A - 비대칭 방사상 중합체의 제조 방법 - Google Patents

비대칭 방사상 중합체의 제조 방법 Download PDF

Info

Publication number
KR930007995A
KR930007995A KR1019920019658A KR920019658A KR930007995A KR 930007995 A KR930007995 A KR 930007995A KR 1019920019658 A KR1019920019658 A KR 1019920019658A KR 920019658 A KR920019658 A KR 920019658A KR 930007995 A KR930007995 A KR 930007995A
Authority
KR
South Korea
Prior art keywords
polymer
block
coupling agent
conjugated diolefin
asymmetric radial
Prior art date
Application number
KR1019920019658A
Other languages
English (en)
Other versions
KR100255553B1 (ko
Inventor
치엔-차오 치앙 레이먼드
로빈슨 비인 아아서
제임즈 혹스마이어 로널드
에머슨 애트웃드 하아비
웨인 리치 게리
Original Assignee
알베르투스 빌헬무스
셀 인터나쵸 나아레 레사아치 마아츠샤피 째스트라텐
요아네스 째스트라텐
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 알베르투스 빌헬무스, 셀 인터나쵸 나아레 레사아치 마아츠샤피 째스트라텐, 요아네스 째스트라텐 filed Critical 알베르투스 빌헬무스
Publication of KR930007995A publication Critical patent/KR930007995A/ko
Application granted granted Critical
Publication of KR100255553B1 publication Critical patent/KR100255553B1/ko

Abstract

서로다른 중합체 아암을 비중합성 커플링제와 순차적으로 접촉시키는 비대칭 방사상 중합체의 제조방법, 종종 방법의 두번째 단계이나 반드시 항상 그렇지는 않은 방법의 최종 단계 접촉은 중합동안에 공역 디올레핀 중합체내 비닐 함량을 증가시키는데 적당한 극성 화합물 존재하에서 수행될 것이다. 사용된 방법은 제조된 몇몇 비대칭 방사상 중합체의 상대적 아암 분포를 좁히고 원하는 비율의 중합체 아암을 갖는 전체의 생성물 양을 유의하게 증가시키고, 비교적 짧은 반응시간내에 이 목적을 달성한다. 비대칭 방사상 중합체의 제조에서 유용한 종래 기술에서 알려진 임의의 비중합성 커플링제가 본 발명의 방법에서 사용될 수 있으나 3 내지 약 12개 관능기를 갖는 비중합성 커플링제가 가장 효과적이고 2 또는 3개 관능기를 갖는 비중합성 커플링제가 가장 적절하다. 유용한 극성 화합물은, 일반적으로, 에테르, 삼차아민, 피리딘 및 피롤리딘 화합물로 구성되는 군으로부터 선택된다.

Description

비대칭 방사상 중합체의 제조 방법
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음

Claims (11)

  1. 하기 단계(a)-(c)로 구성되는 비대칭 방사상중합체의 제조방법 : (a) 첫번째 중합체 및 하나의 반응성 말단기를 갖는 마지막 중합체를 제외한 임의의 후속 중합체를 반응성 말단기와 반응할 다수의 관능기를 가진 비중합성 커플링재와 접촉시켜 상기 중합체와 비중합성 커플링제 간의 반응이 실질적으로 완결되게 진행하도록하고, 상기 임의의 후속 중합체는 상기 첫번째 중합체와 다른 단계; (b) 반응성 말단기를 갖는, 상기 첫번째 및 임의의 후속 중합체와 다른 마지막 중합체 및 공역 디올레핀의 중합동안에 비닐기의 양을 조절할 수 있는 극성 화합물을, 상기 마지막 중합체와 커플링제 상기 남아있는 반응기 간의 반응이 실질적으로 완결되게 진행하도록 하는 조건하에서, 단계(a)로부터의 반응생성물과 접촉시키는 단계; 및 (c) 비대칭 방사상 중합체를 회수하는 단계.
  2. 제1항에 있어서, 커플링제는 3 내지 12개 관능기를 포함하는 방법.
  3. 제2항에 있어서, 상기 첫번째 중합체는 평균적으로, 비대칭 방사상 중합체에서 보다 큰 수의 아암을 형성하도록 하는 중합체인 방법.
  4. 제3항에 있어서, 상기 커플링제는 3 또는 6개 관능기를 갖는 방법.
  5. 제2항에 있어서, 상기 극성화합물은 에테르, 삼차아민, 피리딘 및 피롤리딘 화합물로 구성되는 군으로부터 선택되는 방법.
  6. 제2항에 있어서, 아암을 형성하기위해 사용되는 중합체는 유일하게 중합된 공역 디올레핀을 가진 중합체, 및 적어도 하나의 모노알케닐 방향족 탄화수소 중합체 블록 및 적어도 하나의 공역 디올레핀 중합체 블록으로 구성되는 블록 공중합체인 방법.
  7. 제6항에 있어서, 상기 공역 디올레핀 아암은 부타디엔 및 이소프렌으로 구성되는 군으로부터 선택되는 공역 디올레핀의 단독 중합체이고, 상기 모노알케닐 방향족 탄화수소는 스티렌이고, 공역 디올레핀 중합체 블록은 부타디엔 및 이소프렌으로 구성되는 군으로 부터 선택되는 공역 디올레핀의 단독중합체인 방법.
  8. 제7항에 있어서, 상기 첫번째 중합체는 리빙폴리부타디엔이고, 상기 두번째 중합체는 적어도 하나의 폴리스티렌블록 및 적어도 하나의 폴리부타디엔블록으로 구성되는 리빙 블록 공중합체인 방법.
  9. 제7항에 있어서, 단계(a)에서 사용되는 상기 첫번째 중합체는 이소프렌 단독중합체이고 단계(b)에서 사용되는 중합체는 적어도 하나의 폴리스티렌블록과 적어도 하나의 폴리이소프렌블록으로 구성되는 블록 공중합체인 방법.
  10. 제5항에 있어서, 다관능성 에테르가 사용되는 방법.
  11. 제5항에 있어서, 상기 극성화합물은 디- 및 폴리-에테르의 경우 10 내지 1000ppm, 및 모노에테르의 경우 0.1 내지 20 중량% 범위내의 농도로 사용되는 방법.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019920019658A 1991-10-28 1992-10-24 비대칭 방사상 중합체의 제조 방법 KR100255553B1 (ko)