KR920700081A - 야금용 용기를 정련 층으로 피복하는 방법, 피복용 조성물 및 제조된 보호 피막 - Google Patents
야금용 용기를 정련 층으로 피복하는 방법, 피복용 조성물 및 제조된 보호 피막Info
- Publication number
- KR920700081A KR920700081A KR1019900702594A KR900702594A KR920700081A KR 920700081 A KR920700081 A KR 920700081A KR 1019900702594 A KR1019900702594 A KR 1019900702594A KR 900702594 A KR900702594 A KR 900702594A KR 920700081 A KR920700081 A KR 920700081A
- Authority
- KR
- South Korea
- Prior art keywords
- composition
- alkaline earth
- earth metal
- weight
- composition according
- Prior art date
Abstract
내용 없음
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (21)
- 소정비의 과립형 내화재가 첨가된 단체 또는 혼합물 형태의 알칼리 토금속 탄산염을 1종 이상 함유하는 조성물을 야금용 용기의 내벽에 도포하는 단계와, 상기 도포된 라이닝을 가열하여 CO2및 결합수 및(또는) 결정수를 제거하고, 다공성 구조를 갖는 알칼리 토금속 산화물(들)의 층을 얻는 단계로 이루어지고, 상기 내화재가 용기에 주입되는 용융 금속에 대한 충분한 내식성을 상기 라이닝에 부여하기에 충분한 비율로 첨가되는 것을 특징으로 하는, 알칼리 토금속 산화물 기재의 정련용 라이닝을 야금용 용기의 내벽에 도포하는 방법.
- 제 1 항에 있어서, 조성물을 수성 슬러리(slurry) 형태로 분무시키는 것이 특징인 방법.
- 제 1 항에 있어서, 조성물을 용기의 내부 표면 및 주형을 성형하는 벽 사이에 주입하는 것이 특징인 방법.
- 제 1 항 내지 3 항중 어느 한 항에 있어서, 라이닝을 900℃ 근방의 온도까지 가열하는 것이 특징인 방법.
- 제 1 내지 4 항중 어느 한 항에 있어서, 안정한 내화성 산화물을 기재로 하고, 당해 온도에서 적어도 부분적으로 소결될수 있는 재화재의 적어도 제 1 층을 정련용 라이닝의 도포 전에 도포하는 것이 특징인 방법.
- 상기 알칼리 토금속 탄산염이 원석 상태의 백운선과 방해석 및 이들의 혼합물로부터 선택되는 것이 특징인, 제 1 항의 방법에 사용하기 위한 조성물.
- 제 6 항에 있어서, 사용된 조성물이 무기 결합제, 유기 결합제, 수경 결합제 및 이들의 혼합물로부터 선택된 결합제를 추가로 함유하는 것이 특징인 조성물.
- 제 6 또는 7 항에 있어서, 내화재가 하소된 백운석, 석회석, 마그네시아, 크롬마그네시아, 산화크롬, 규산 지르코늄, 실리카, 알루미노실리케이트 및 이들의 혼합물로부터 선택되는 것이 특징인 조성물.
- 제 6 내지 제 8항중 어느 한 항에 있어서, 알칼리 토금속 탄산염 30-95중량%, 내화재 70-5중량% 및 결합제 0-15중량%를 함유하는 것이 특징인 조성물.
- 제 9 항에 있어서, 백운석 원석 60-80중량%, 내화재 10-40중량% 및 결합제 1-5 중량%를 함유하는 것이 특징인 조성물.
- 제 6 내지 10 항중 어느 한 항에 있어서, 내화재의 입도가 알칼리 토금속 타산염의 입도보다 더 큰 것이 특징인 조성물.
- 제 6 내지 11 항중 어느 한 항에 있어서, 20중량%까지의 유기 및(또는) 무기 섬유를 추가로 함유하는 것이 특징인 조성물.
- 제 6 내지 12 항중 어느 한 항에 있어서, 5중량% 까지의 계면 활성제를 추가로 함유하는 것이 특징인 조성물.
- 제 6 내지 13 항중 어느 한 항에 있어서, 조성물의 습윤시에 수화될 수 있는 알칼리 토금속 수산화물 및(또는) 알칼리 토금속 산화물 및(또는)알칼리 토금속 황산염을 특정 비율로 추가로 함유하는 것이 특징인 조성물.
- 제 6 내지 14 항중 어느 한 항에 있어서, 0-10중량%의 플럭스(flux)를 추가로 함유하는 것이 특징인 조성물.
- 제 15 항에 있어서, 플럭스가 감람석, 회붕광, 붕화 방해석(붕산 칼슘), 산화철, 불화물, 붕산 및 그의 염(보락스) 및 그들의 혼합물로부터 선택되는 것이 특징인 조성물.
- 제 15 또는 16 항에 있어서, 용이하게 용해될 수 있는 플럭스를 함유하는 것이 특징인 조성물.
- 제 6 내지 17 항중 어느 한 항에 있어서, 백운석 및(또는) 방해석 및(또는)수산화물 및(또는) 황산염 30-90중량%, 내화성 입자 70-5중량%, 결합제 0-15중량%, 탄소 0-5중량% 및 플럭스 0-10중량%를 함유하는 것이 특징인 조성물.
- 제 6 내지 18 항중 어느 한 항에 있어서, 주성분인 알칼리 토금속 탄산염, 알칼리 토금속 수산화물, 알칼리 토금속 산화물 및 알칼리 토금속 황산염이, 3mm미만, 바람직하게는 1mm미만의 입도를 갖고, 내화성 입자가 5mm미만, 바람직하게는 2mm미만의 입도를 갖는 것이 특징인 조성물.
- 제 6 내지 19 항중 어느 한 항에 있어서, 이종 성분들의 개개 입도가 정련용 라이닝에 최대 조밀도를 제공할 수 있도록 선택되는 것이 특징인 조성물.
- 용융 금속과 접촉하도록 되어 있고, 제 6 내지 20 항중 어느 한 항에 의한 조성물에 의해서 형성되는 내부 정련용 층과, 당해 온도에서 소결되거나 적어도 부분적으로 소결될 수 있고, 안정한 내화성 산화물을 기재로 하는 1개 이상의 외부층을 연속적으로 갖는 것이 특징인 제 5 항에 따른 방법에 의해서 제조되는 야금용 용기의 내벽 보호용 라이닝.※ 참고사항 : 최초 출원 내용에 의하여 공개하는 것임.