KR920016382A - 근청석(cordierite)몸체 및 이의 제조방법 - Google Patents

근청석(cordierite)몸체 및 이의 제조방법 Download PDF

Info

Publication number
KR920016382A
KR920016382A KR1019920001970A KR920001970A KR920016382A KR 920016382 A KR920016382 A KR 920016382A KR 1019920001970 A KR1019920001970 A KR 1019920001970A KR 920001970 A KR920001970 A KR 920001970A KR 920016382 A KR920016382 A KR 920016382A
Authority
KR
South Korea
Prior art keywords
cordierite
coefficient
thermal expansion
aluminum
aluminum oxide
Prior art date
Application number
KR1019920001970A
Other languages
English (en)
Other versions
KR100192747B1 (ko
Inventor
문로 빌 더글라스
맥기 델리소 에브린
로이드 길레 도날드
조셉 무르타그 마틴
Original Assignee
알프레드 엘.미첼슨
코닝 인코오포레이티드
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 알프레드 엘.미첼슨, 코닝 인코오포레이티드 filed Critical 알프레드 엘.미첼슨
Publication of KR920016382A publication Critical patent/KR920016382A/ko
Application granted granted Critical
Publication of KR100192747B1 publication Critical patent/KR100192747B1/ko

Abstract

내용 없음

Description

근청석(CORDIERITE)몸체 및 이의 제조방법
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 본 발명의 원료 조성물의 영역을 나타내는 SiO2-Al2O3-MgO 의 삼상평형도이다.

Claims (20)

  1. (a) 직경이 약 15㎛보다 크지 않는 입자 크기의 성분을 생산하는 산화마그네슘에 의해 제공된 약12~16중량%의 산화마그네슘, 직경이 약8㎛보다 크지 않는 평균 입자 크기의 성분을 생산하는 산화알루미늄에 의해 제공된 약35~41중량%의 산화알루미늄 및 약43~53중량%의 실리카로 구성되고 그 이후의 연소 단계에서 근청석을 제조할 수 있는 조성물을 제조하기 위하여 점토 및 활석이 없는 원료를 선택하는 단계 (b) 소성 형성능력 및 그린 강도를 상기 원료에 부여하기 위하여 효과적인 양의 전색제 및 형성 보조물을 상기 원료와 친밀하게 혼합하여 가소성 혼합물을 제조하는 단계. (c)상기 원료로 그린 몸체를 제조하는 단계, (d) 상기 그린 몸체를 건조시키는 단계, 및 (e) 그린 몸체를 약 1000~1200°C의 첫번째 온도로 가열한 후에 약100/°C시간 보다 낮은 속도로 가열하여 근청석을 형성하기에 충분한 두번째 온도로 높이고, 약10㎛보다 작은 평균 기공 크기를 함유하고 약25~1000˚에서 약0.9 X 10-7/°C보다 크지 않는 열팽창 계수를 함유한 적어도 약90중량% 근청석의 근청석 몸체를 제조하기 위하여 충분한 시간 동안 상기 두번째 온도로 유지시켜 상기 그린 몸체를 연소하는 단계로 구성됨을 특징으로 하는 근청석 몸체의 제조방법.
  2. 제1항에 있어서, 상기 산화 마그네슘은 산화 마그네슘, 수산화 마그네슘, 탄산 마그네슘, 질산 마그네슘 및 그들의 화합물을 구성된 군에서 선택됨을 특징으로 하는 근청석 몸체의 제조방법.
  3. 제1항에 있어서, 상기 산화 알루미늄 성분은 산화알루미늄, 수산화 알루미늄, 탄산알루미늄, 질산 알루미늄 및 그들의 화합물을 구성된 군에서 선택됨을 특징으로 하는 근청석 몸체의 제조방법.
  4. 제3항에 있어서, 상기 산화 알루미늄 성분은 직경이 약 2.0㎛보다 크지 않은 평균 입자 크기를 함유한 산화 알루미늄인 것을 특징으로 하는 근청석 몸체의 제조방법.
  5. 제4항에 있어서, 상기 산화 알루미늄은 직경이 약 1.0㎛보다 크지 않은 평균 입자 크기를 함유함을 특징으로 하는 근청석 몸체의 제조방법.
  6. 제4항에 있어서, 상기 열팽창 계수는 약 25~1000°C에서 약 6.0 X 10-7/°C보다 크지 않는 것을 특징으로 하는 근청석 몸체의 제조방법.
  7. 제5항에 있어서, 상기 열팽창 계수는 약 25~1000°C에서 약 4.0 X 10-7/°C보다 크지 않는 것을 특징으로 하는 근청석 몸체의 제조방법.
  8. 제3항에 있어서, 상기 산화 알루미늄 성분은 직경이 약 6.0㎛보다 크지 않은 평균 입자 크기를 함유한 수소화 알루미늄인 것을 특징으로 하는 근청석 몸체의 제조방법.
  9. 제8항에 있어서, 상기 열팽창 계수는 약 25~1000°C에서 약 6.0 X 10-7/°C보다 크지 않는 것을 특징으로 하는 근청석 몸체의 제조방법.
  10. 제1항에 있어서, 상기 가열 속도는 약 75°C/시간보다 크지 않은 것을 특징으로 하는 근청석 몸체의 제조방법.
  11. 제10항에 있어서, 상기 가열 속도는 약 50°C/시간보다 크지 않은 것을 특징으로 하는 근청석 몸체의 제조방법.
  12. 제11항에 있어서, 상기 가열 속도는 약 25°C/시간보다 크지 않은 것을 특징으로 하는 근청석 몸체의 제조방법.
  13. 제1항에 있어서, 상기 제조단계는 상기 원료를 상기 그린 몸체로 제조하는 단계로 구성됨을 특징으로 하는 근청석 몸체의 제조방법.
  14. 제1항에 있어서, 상기 근청석 뭄체는 벌집구조인 것을 특징으로 하는 근청석 몸체의 제조방법
  15. 제14항에 있어서, 상기 근청석 몸체의 가로의 I비는 약 0.69보다 크고 축의 I비는 0.61보다 작은 것을 특징으로 하는 근청석 몸체의 제조방법.
  16. 약 25~1000˚C에서 약 16 X 10-7/°C보다 작은 열팽창 계수를 함유한 적어도 약 90중량%근청석의 상기 제1항에 의해 제조된 근청석 몸체.
  17. 제16항에 있어서, 상기 열팽창 계수는 약 25~1000°C에서 약 6.0 X 10-7/°C보다 크지 않는 것을 특징으로 하는 근청석 몸체의 제조방법.
  18. 제17항에 있어서, 상기 열팽창 계수는 약 25~1000°C에서 약 4.0 X 10-7/°C보다 크지 않는 것을 특징으로 하는 근청석 몸체의 제조방법.
  19. 제16항에 있어서, 벌집구조인 것을 특징으로 하는 근청석 몸체.
  20. 제19항에 있어서, 가로의 I비는 약 0.69보다 크고 축의 I비는 0.61보다 작은 것을 특징으로 하는 근청석 몸체.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019920001970A 1991-02-13 1992-02-11 근청석몸체 및 이의 제조방법 KR100192747B1 (ko)