KR910009861A - 수분산성 결합제 조성물, 연소 충진제의 제조방법 및 이로부터 제조한 피복물 - Google Patents

수분산성 결합제 조성물, 연소 충진제의 제조방법 및 이로부터 제조한 피복물 Download PDF

Info

Publication number
KR910009861A
KR910009861A KR1019900017522A KR900017522A KR910009861A KR 910009861 A KR910009861 A KR 910009861A KR 1019900017522 A KR1019900017522 A KR 1019900017522A KR 900017522 A KR900017522 A KR 900017522A KR 910009861 A KR910009861 A KR 910009861A
Authority
KR
South Korea
Prior art keywords
weight
molecular weight
acid
binder composition
resin
Prior art date
Application number
KR1019900017522A
Other languages
English (en)
Other versions
KR100190781B1 (ko
Inventor
블룸 하랄트
마이크너 위르겐
페다인 요제프
부르그되르퍼 한스-헤리베르트
Original Assignee
귄터 슈마허, 클라우스 댄너
바이엘 아크티엔게젤샤프트
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 귄터 슈마허, 클라우스 댄너, 바이엘 아크티엔게젤샤프트 filed Critical 귄터 슈마허, 클라우스 댄너
Publication of KR910009861A publication Critical patent/KR910009861A/ko
Application granted granted Critical
Publication of KR100190781B1 publication Critical patent/KR100190781B1/ko

Abstract

내용 없음

Description

수분산성 결합제 조성물, 연소 충진제의 제조방법 및 이로부터 제조한 피복물
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음

Claims (17)

  1. a) 하이드록실 그룹을 함유하고 산가가 15 내지 36이며 하이드록실가가 적어도 40이고 분자량이 5,000 내지 50,000이며, a1) 하이드록실가가 130 내지 200이고 산가가 1 내지 5인 폴리에스테르 폴리올 72 내지 80중량% 및 a2) 2,2-비스-(하이드록시메틸)-알칸 카복실산 4 내지 7중량% 또는 당해 산의 3급 아민염의 산의 양에 상응하는 양과 a3) 분자량이 166 내지 294인 적어도 하나의 지환족 디이소시아네이트 15 내지 24중량%의 반응 생성물을 포함하고 우레탄에 의해 개질된 폴리에스테르 수지 65 내지 95중량%, b) 가교결합제 수지 5 내지 35중량% 및 c) 유화제 0 내지 2중량%[여기서, a),b) 및 c)의 퍼센트는 a) 내지 c)의 전체 중량을 기준으로 함]를 포함함을 특징으로 하는, 수성 상으로부터 수득되는 연소 충진제를 제조하기에 적합한 수분산성 결합제 조성물.
  2. 제1항에 있어서, 카복실 그룹이 암모니아 또는 유기 아민에 의해 적어도 부분적으로 중화되는 수분산성 결합제 조성물.
  3. 제1항에 있어서, 폴리에스테르 폴리올 a1.1) 분자량이 122 내지 340인 적어도 하나의 지방족 모노카복실산 2 내지 11중량%, a1.2) 분자량이 116 내지 600인 적어도 하나의 지방족 디카복실산 17 내지 27중량%, a1.3) 분자량이 166 내지 172인 적어도 하나의 방향족 또는 지환족 디카복실산 및/또는 적어도 하나의 이의 무수물 20 내지 30중량%, a1.4) 분자량이 62 내지 400인 적어도 하나의 지방족 또는 지환족 디올[단, 당해 성분의 적어도 50중량%는 탄소원자수가 5 내지 8인 디1급 디올을 기준으로 함] 27 내지 41중량%[여기서, 퍼센트는 성분 a1.1) 내지 a1.5)의 전체 중량을 기준으로 함] 및 a1.5) 분자량이 92 내지 300인 적어도 하나의 3가 또는 4가 알콜의 반응 생성물을 포함하는 결합제 조성물.
  4. 제1항에 있어서, 가교결합제 수지 b)가 적어도 하나의 아미노 수지 및/또는 적어도 하나의 블럭 폴리이소시아네이트를 포함하는 결합제 조성물.
  5. 제3항에 있어서, 가교결합제 수지 b)가 적어도 하나의 아미노 수지 및/또는 적어도 하나의 블럭 폴리이소시아네이트를 포함하는 결합제 조성물.
  6. 제1항에 있어서, 유화제 c)가 분자당 적어도 10개의 에틸렌 옥사이드 단위를 함유하는 적어도 하나의 에톡시화된 C8-18알킬페놀을 포함하는 결합제 조성물.
  7. a) 카보닐 그룹을 함유하고 산가가 20 내지 29.9이며 하이드록실가가 적어도 40이고 분자량(Mw)이 7,500 내지 30,000이며 a1) 하이드록실가가 145 내지 180이고 산가가 1 내지 3.5인 폴리에스테르 폴리올 73 내지 77중량% 및 a2) 2,2-비스-(하이드록시메틸)-알칸 카복실산 5 내지 6.5중량% 또는 당해 산의 3급 아민염의 산의 양에 상응하는 양과 a3) 분자량이 222 내지 294인 적어도 하나의 지환족 디이소시아네이트 17 내지 22중량%[여기서, a1), a2) 및 a3)의 퍼센트는 a1) 내지 a3)의 전체 중량을 기준으로 함]의 반응 생성물을 포함하고 우레탄에 의해 개질된 폴리에스테르 수지 75 내지 90중량%, b) 가교결합제 수지 10 내지 25중량% 및 c) 유화제 0 내지 1중량%[여기서, a), b) 및 c)의 퍼센트는 a 내지 c의 전체 중량을 기준으로 함]를 포함함을 특징으로 하는, 수성상으로 수득되는 연소 충진제를 제조하기에 적합한 수분산성 결합제 조성물.
  8. 제7항에 있어서, 카복실 그룹이 암모니아 또는 유기 아민에 의해 적어도 부분적으로 중화되는 결합제 조성물.
  9. 제7항에 있어서, 폴리에스테르 폴리올 a1)이 a1.1) 분자량이 122 내지 340인 적어도 하나의 지방족 모노카복실산 2 내지 11중량%, a1.2) 분자량이 116 내지 600인 적어도 하나의 지방족 디카복실산 17 내지 27중량%, a1.3) 분자량의 범위가 166 내지 172인 적어도 하나의 방향족 또는 지환족 디카복실산 및/또는 적어도 하나의 이의 무수물 20 내지 30중량%, a1.4) 분자량이 62 내지 400인 적어도 하나의 지방족 또는 지환족 디올[단, 당해성분의 적어도 50중량%는 탄소원자수가 5 내지 8인 디1급 디올을 기준으로함] 및 a1.5) 분자량이 92 내지 300인 적어도 하나의 3가 또는 4가 알콜 13 내지 21중량%[여기서, 퍼센트는 a1.1) 내지 a1.5)의 전체 중량을 기준으로함]의 반응 생성물을 포함하는 결합제 조성물.
  10. 제7항에 있어서, 가교결합제 수지 b)가 적어도 하나의 아미노 수지 및/또는 적어도 하나의 블럭 폴리이소시아네이트를 포함하는 결합제 조성물.
  11. 제9항에 있어서, 가교결합제 수지 b)가 적어도 하나의 아미노 수지 및/또는 적어도 하나의 블럭 폴리이소시아네이트인 결합제 조성물.
  12. 제7항에 있어서, 유화제 c)가 분자당 적어도 10개의 에틸렌 옥사이드 단위를 함유하는 적어도 하나의 에톡시화된 C8-18알킬페놀을 포함하는 결합제 조성물.
  13. Ⅰ)a1.1) 분자량이 122 내지 340인 적어도 하나의 지방족 디카복실산 2 내지 11중량%, a1.2) 분자량이 116 내지 600인 적어도 하나의 지방족 디카복실산 17 내지 27중량%, a1.3) 분자량 범위가 166 내지 172인 적어도 하나의 방향족 또는 지환족 디카복실산 및/또는 적어도 하나의 이의 무수물 20 내지 30중량%, a1.4) 분자량이 62 내지 400인 적어도 하나의 지방족 또는 지환족 디올[단, 당해 성분의 적어도 50중량%는 탄소원자수가 5 내지 8인 디1급 디올을 기준으로함] 및 a1.5) 분자량이 92 내지 300인 적어도 하나의 3가 또는 4가 알콜 13 내지 21중량%[여기서, 퍼센트는 a1.1) 내지 a1.5)의 전체 중량을 기준으로함]를 반응시킴으로써 하이드록실가가 130 내지 200이고 산가가 1 내지 5인 폴리에스테르 폴리올을 제조하고, Ⅱ)a1)폴리에스테르 a1)72 내지 80중량% 및 a2) 2,2-비스-(하이드록시메틸)-알칸 카복실산 4 내지 7중량% 또는 당해 산의 3급 아민염의 산의 양에 상응하는 양과 a3) 분자량이 166 내지 294인 지환족 디이소시아네이트 15 내지 24 중량%[여기서, 퍼센트는 성분 a1) 내지 a3)의 전체 중량을 기준으로 함]를 불활성 용매의 존재하에 50 내지 140℃에서 반응시킴으로써 분자량(Mw)이 5,000 내지50,000이고 산가가 15 내지 36이며 하이드록실가가 적어도 40이고 우레탄에 의해 개질된 폴리에스테르 수지 a)를 제조하고, Ⅲ)유화제 c)에 대한 우레탄 개질된 폴리에스테르의 중량비가 65:2 내지 95:0으로 되기에 충분한 양의 유화제 c)를 가하고, Ⅳ)단계 Ⅲ)의 생성물과 가교결합제 수지[여기서, 가교결합제 수지는 성분 b)에 대한 성분 a)의 중량비가 65:35 내지 95:5로 되기에 충분한 양으로 존재한다]를 가함을 포함함을 특징으로 하여 내칩성 피복물을 생성하기에 적합한 수성 연소 충진제를 제조하는 방법.
  14. 제13항에 있어서, 성분 a)속에 존재하는 특정한 카복실 그룹을 단계 Ⅳ)후에 암모니아 또는 아민과 함께 카복실레이트 그룹으로 적어도 부분적으로 전환시킴을 포함하는 방법.
  15. 제13항에 있어서, 유기 용매를 단계 (Ⅳ)전, 도중 또는 후에 증류시킴으로써 적어도 부분적으로 제거함을 포함하는 방법.
  16. 제1항의 결합제 조성물을 함유하는 연소 충전제로부터 제조된 내칩성 피복물.
  17. 제3항의 결합제 조성물을 함유하는 연소 충전제로 부터 제조된 내칩성 피복물.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019900017522A 1989-11-01 1990-10-31 수 분산성 결합제 조성물, 스토빙 충전제의 제조방법 및 이로부터 제조된 피막 KR100190781B1 (ko)