KR880003849A - 가스저장용 다공성 규소석회질 매스 및 그 제조방법 - Google Patents

가스저장용 다공성 규소석회질 매스 및 그 제조방법 Download PDF

Info

Publication number
KR880003849A
KR880003849A KR870010190A KR870010190A KR880003849A KR 880003849 A KR880003849 A KR 880003849A KR 870010190 A KR870010190 A KR 870010190A KR 870010190 A KR870010190 A KR 870010190A KR 880003849 A KR880003849 A KR 880003849A
Authority
KR
South Korea
Prior art keywords
suspension
suspending agent
vessel
paste
cellulose fibers
Prior art date
Application number
KR870010190A
Other languages
English (en)
Inventor
데끄 필립
드로드 죠르쥬
반냐르 제라르
메오 꼴뛰리 바르뜰로
Original Assignee
원본미기재
레르 리뀌드, 쏘시에떼 아노뉨뿌르 레뛰드에 렉스쁠로와 따시옹 데 프로세드 죠르쥬 끌로드
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 원본미기재, 레르 리뀌드, 쏘시에떼 아노뉨뿌르 레뛰드에 렉스쁠로와 따시옹 데 프로세드 죠르쥬 끌로드 filed Critical 원본미기재
Publication of KR880003849A publication Critical patent/KR880003849A/ko

Abstract

내용 없음

Description

가스저장용 다공성 규소석회질 매스 및 그 제조방법
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음

Claims (11)

  1. 천연실리카와 생석회의 혼합물로된 수성 페이스트를 현탁제로 안정화하고 강화제로 강화하여 다공성 규소 석회질 매스를 제조하는 방법에 있어서, 상기 강화제는 일부의 목질을 기계적으로 제거한 셀룰로오스 섬유, 일부의 목질을 화학적으로 제거한 셀루로오스 섬유 및 일부의 목질을 화학적으로 제거한 다음 기계적으로 정제한 셀룰로오스 섬유로 이루어진 군에서 선택된 셀룰로오스 섬유이고, 상기 강화제의 비율은 고형 성분의 3-30wt%인 것을 특징으로 하는 다공성 규소 석회질 매스의 제조방법.
  2. 제1항에 있어서, 상기 수성 페이스트는 제1무기 현탁제와 제2무기 현탁제로 이루어진 현탁제로 안정화시키고, 제1무기 현탁제는 비표면적 150-300㎡/g의 비정질 미세합성 실리카로서 고형성분의 2-5%를 점유하고, 제2무기 현탁제는 유리섬유로서 고형성분의 약 0.5-58%를 점유하거나 정제 점토로서 고형 성분의 0.1-2%를 점유하는 것을 특징으로 하는 다공성 규소 석회질 매스의 제조방법.
  3. 제2항에 있어서, 상기 수성 페이스트는 무기 현탁제와 유기 현탁제로 안정화시키고, 상기 유기 현탁제는 알킬 히드록시 알킬 셀룰로오스로서 고형 성분의 약 0.5-2%를 점유하는 것을 특징으로 하는 다공성 규소 석회질 매스의 제조방법.
  4. 제2항에 있어서, 상기 수성 페이스트는 현탁 및 농밀화제로서 규산칼슘의 고형 생성물 약 8-20wt%를 함유하고, 합성 실리카는 함유하지 않는 것을 특징으로 하는 다공성 규소 석회질 매스의 제조방법.
  5. 제1항에 있어서, 실리카 총량에 대한 석회의 중량비는 약 0.7 내지 1.1이고, 페이스트를 만들기 위한 물의 사용량은 고형 성분의 적어도 3배 이상인 것을 특징으로 하는 다공성 규소 석회질 매스의 제조방법.
  6. 제5항에 있어서, 고형 성분에 대한 물의 사용량은 중량비로 약 3-4.5인 것을 특징으로 하는 다공성 규소 석회질 매스의 제조방법.
  7. 제1항에 있어서, 석회를 약 40-85℃의 온수로 소화하는 것을 특징으로 하는 다공성 규소 석회질 매스의 제조방법.
  8. (a) 생석회를 약 40-85℃의 온수로 소화하고, (b) 물을 첨가한 다음 저속에서 교반하에 현탁액을 균질화하고, (c) 강화제를 석회현탁액에 분산시키고, (d) 천연실리카와 합성실리카 및 규산칼슘으로 이루어진 군의 성분중 하나와의 혼합물을 교반하에 현탁액에 첨가하고, (e) 제2무기 현탁제를 현탁액에 분산시켜서 페이스트를 제조하고, (f) 페이스트를 부분 감압하에 라이닝할 용기에 장입하고, (g) 용기를 약 1MPa의 포화 증기압하에서 약 20시간 동안 오토클레이브 내에 방치하고, (h) 용기를 건조로 내에서 170℃ 이하의 온도로 7일간 건조시키는 공정으로 이루어진 것을 특징으로 하는 규소 석회질 매스로 용기를 라이닝하는 방법.
  9. (a) 생석회를 약 40-85℃의 온수로 소화하고, (b) 물을 첨가한 다음 지속에서 교반하여 현탁액을 균질화 하고, (c) 강화제를 석회 현탁액에 분산시키고, (d) 천연실리카와 합성실리카 및 규산 칼슘으로 이루어진 군의 성분 중 하나와의 혼합물을 교반하여 현탁액에 첨가하고, (e) 현탁액을 교반하면서 유기 현탁제를 첨가하고, (f) 제2무기 현탁제를 현탁액에 분산시켜서 페이스트를 제로하고, (g) 페이스트를 부분 감압하에 라이닝할 용기에 장입하고, (h) 용기를 약 1MPa의 포화 증기압하에서 약 20시간 동안 오토클레이브 내에 방치하고, (i) 용기를 건조로 내에서 170℃ 이하의 온도로 약 7일간 건조시키는 공정으로 이루어진 것을 특징으로 하는 규소 석회질 매스로 용기를 라이닝하는 방법.
  10. 공극률이 적어도 88% 이상이고 약 3-30%의 셀룰로오스 섬유를 함유하는 규소 석회질의 단일 매스로 충전된 금속제 용기로 구성되고, 상기 셀룰로오스 섬유는 일부의 목질을 기계적으로 제거한 셀룰로오스 섬유, 일부의 목질을 화학적으로 제거한 셀룰로오스 섬유 및 일부의 목질을 화학적으로 제거한 다음 기계적으로 정제한 셀룰로오스 섬유로 이루어진 군에서 선택된 것이고, 상기 금속제 용기는 제8항 및 제9항의 방법으로 제조한 것을 특징으로 하는 가스 저장 용기.
  11. 제10항에 있어서, 아세틸렌 용액을 저장하는 것을 특징으로 하는 가스 저장 용기.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR870010190A 1986-09-18 1987-09-15 가스저장용 다공성 규소석회질 매스 및 그 제조방법 KR880003849A (ko)