KR870010136A - 보리아- 개조 실리카로 피복된 이산화 티탄 안료 - Google Patents

보리아- 개조 실리카로 피복된 이산화 티탄 안료 Download PDF

Info

Publication number
KR870010136A
KR870010136A KR870004150A KR870004150A KR870010136A KR 870010136 A KR870010136 A KR 870010136A KR 870004150 A KR870004150 A KR 870004150A KR 870004150 A KR870004150 A KR 870004150A KR 870010136 A KR870010136 A KR 870010136A
Authority
KR
South Korea
Prior art keywords
pigment
coating
weight
sio
tio
Prior art date
Application number
KR870004150A
Other languages
English (en)
Other versions
KR960004636B1 (ko
Inventor
웨인 제이콥슨 하워드
Original Assignee
도늘드 에이 호우즈
이 아이 듀우판 디 네모아 앤드 캄파니
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 도늘드 에이 호우즈, 이 아이 듀우판 디 네모아 앤드 캄파니 filed Critical 도늘드 에이 호우즈
Publication of KR870010136A publication Critical patent/KR870010136A/ko
Application granted granted Critical
Publication of KR960004636B1 publication Critical patent/KR960004636B1/ko

Abstract

내용 없음

Description

보리아-개조 실리카로 피복된 이산화 티탄 안료
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음

Claims (20)

  1. 필수적으로, SiO2와 B2O3로 이루어진 코우팅을 갖는 루틸 TiO2입자로 이루어진 안료.
  2. 제 1항에 있어서, TiO2입자가 필수적으로 코우팅 중량을 기준으로 SiO260~98중량%와 B2O30.5~30중량%로 이루어진 코우팅을 갖는 안료.
  3. 제 2항에 있어서, TiO2입자가 필수적으로 코우팅 중량을 기준으로 SiO280~90중량%와 B2O32~20중량%로 이루어진 코우팅을 갖는 안료.
  4. 제3항에 있어서, TiO2입자가 총 안료 중량의 2~10%를 구성하는 SiO2/B2O3코우팅을 갖는 안료.
  5. 제4항에 있어서, TiO2입자가 총 안료 중량의 4~8%를 구성하는 SiO2/B2O3코우팅을 갖는 안료.
  6. 제 5항에 있어서, TiO2입자가 총 중량의 0.5~5%를 구성하는 알루미나의 외부 코우팅을 갖는 안료.
  7. 제 6항에 있어서, TiO2입자가 입자 총중량의 1~4%를 구성하는 알루미나의 외부 코우팅을 갖는 안료.
  8. 다음 (a)~(e)로 이루어진 보리아 -개조 실리카의 코우팅을 갖는 TiO2입자의 제조 방법 ;
    (a) 온도 약 65℃ 내지 약 90℃에서 루틸 TiO2의 수성슬러리를 형성하고 ;
    (b) 슬러리의 pH를 7~10.5범위로 조절하고 ;
    (c) 규산염과 보리아 이온을 용액속에 유지시키는 조건하에, Na2SiO3와 B2O3로 이루어진 용액을 미리 결정한 양만큼 첨가하고 ;
    (d) 슬러리의 pH를 산을 첨가하여 약 7.5~8.5로 점차 낮추고, 그것에 의해서 실리카와 보리아의 코우팅을 부착시키고 ;
    (e) 결과로서 생성된 피복된 안료를 온도 약 65℃ 내지 약 90℃에서 최소한 15분동안 경화시킨다.
  9. 제 8항에 있어서, 단계 (c)에서 Na2SiO3와 B2O3를 충분히 첨가하여 필수적으로 코우팅 중량을 기준으로 SiO260~98중량%와 B2O30.5~30중량%로 이루어진 코우팅을 제공하는 방법.
  10. 제 9항에 있어서, 단계 (c)에서 Na2SiO3와 B2O3를 충분히 첨가하여 필수적으로 코우팅 중량을 기준으로 SiO280~90중량%와 B2O32~20중량%로 이루어진 코우팅을 제공하는 방법.
  11. 제 10항에 있어서, 단계 (c)에서 Na2SiO3와 B2O3를 충분히 첨가하여 총안료 중량의0.5~10%를 구성하는 SiO2/B2O3코우팅을 제공하는 방법.
  12. 제 11항에 있어서, 단계 (c)에서 Na2SiO3와 B2O3를 충분히 첨가하여 총안료 중량의4~8%를 구성하는 SiO2/B2O3코우팅을 제공하는 방법.
  13. 제12항에 있어서, 다음 단계(f)가 포함되어 있는 방법.
    (f) 슬러리의 pH를 6~9로 유지시키기 위해서 무기산을 첨가하면서 은도 약 50°~90℃에서 NaAlO2를 슬러리에 충분히 첨가하여, TiO2의 중량당 약 2~8중량%의 농도를 제공한다.
  14. 제 1항에 따른 안료, 필름-형성 물질 및 액체담체로 이루어진 코우팅 조성물.
  15. 제 2항에 따른 안료, 필름-형성 물질 및 액체담체로 이루어진 코우팅 조성물.
  16. 제 3항에 따른 안료, 필름-형성물질 및 액체담체로 이루어진 코우팅 조성물.
  17. 제 4항에 따른 안료, 필름-형성물질 및 액체담체로 이루어진 코우팅 조성물.
  18. 제 5항에 따른 안료, 필름-형성 물질 및 액체담체로 이루어진 코우팅 조성물.
  19. 제 6항에 따른 안료, 필름-형성물질 및 액체담체로 이루어진 코우팅 조성물.
  20. 제 7항에 따른 안료, 필름-형성물질 및 액체담체로 이루어진 코우팅 조성물.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019870004150A 1986-04-30 1987-04-29 보리아-개조 실리카로 피복된 이산화 티탄 안료 KR960004636B1 (ko)