KR850007806A - 상부 취련전로를 이용한 제강법 - Google Patents
상부 취련전로를 이용한 제강법 Download PDFInfo
- Publication number
- KR850007806A KR850007806A KR1019850000676A KR850000676A KR850007806A KR 850007806 A KR850007806 A KR 850007806A KR 1019850000676 A KR1019850000676 A KR 1019850000676A KR 850000676 A KR850000676 A KR 850000676A KR 850007806 A KR850007806 A KR 850007806A
- Authority
- KR
- South Korea
- Prior art keywords
- inert gas
- oxygen
- hot water
- blowing
- steelmaking method
- Prior art date
Abstract
내용 없음
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (16)
- 탕을 형성하는 고온의 용융물이 있는 상부 취련식의 용융금속 전로에서 제강함에 있어서, 랜스로부터 탕표면으로 또는 탕표면 밑으로 제련용 기체를 상부 취입하고, 탕중에서의 탄소가 약 1%과잉일 때는 제련용 기체를 거의 산소로 사용하고, 탕중에서의 탄소가 약1% 이하일때는 산소와 불활성 기체의 혼잡물을 사용하며 상부 취련도중 탕표면 밑으로부터 탕속으로 불활성 기체를 느린 유속으로 도입하고, 상부취련이 시작될 때에는 탕속으로 도입되는 산소대 불활성 기체의 전체비율을 1/1 이상으로 설정하며, 상부취련도중 탄소함량이 감소되면 상부에서 취입되는 불활성 기체량을 증가시키면서 상부에서 취입되는 산소량을 감소시켜 주어 산소대 불활성 기체의 전체비율을 점진적으로 감소시켜주고, 소요의 탄소함량에 도달하여 산소대 불활성 기체의 비율이 1/1 이하인 때는 상부 취련을 중단하는 제강법.
- 제1항에 있어서, 상부 취련도중 상부에서 취입되는 기체 혼합물 중에서의 점진적으로 감소하는 산소대 불활성 기체의 비에 대하여 상대적으로 탕표면 밑에서부터 도입되는 불활성 기체를 거의 일정한 속도로 유지하는 제강법.
- 제2항에 있어서, 탕표면 밑으로부터 도입되는 불활성 기체를 0.5-20ft3/min/ton의 범위내에서 거의 일정한 속도로 유지하는 제강법.
- 제1항에 있어서, 상부 취련도중 산소대 불활성 기체의 전체비율을 약 20/1 이상에서부터 1/3이하로 점차로 감소시키는 제강법.
- 제4항에 있어서, 상부 취련도중 탕중에서의 탄소함량이 약 1%로 감될될 때 까지는 산소대 불활성 기체의 비율을 약 20/1 이상으로 유지하고, 탕중에서의 탄소함량이 약 0.5%로 감소될 때 까지는 약 3/1로 유지하며, 탕중에서의 탄소함량이 약 0.08%로 감소될 때 까지는 약 1/1로 유지하고, 상부 취련이 끝나고 소요의 탄소함량이 도달할 때 까지는 약 1/3 이하로 유지하는 제강법.
- 제1항에 있어서, 소요의 탄소함량을 약 0.03% 이하로 하는 제강법.
- 제1항에 있어서, 탕속으로 도입되는 불활성 기체로는 아르곤, 질소, 크세논, 네온, 이산화탄소 및 이들의 혼합물로 구성되는 것중에서 선택한 불활성 기체를 사용하는 제강법.
- 제1항에 있어서, 취련 종료시의 탕온도를 3300°F 이하로 하는 제강법.
- 제1항에 있어서, 산소와 불활성 기체의 조성을 변화시키면서 제련용 기체의 상부 취입량을 상부 취련동안 거의 동일한 총유속으로 유지하는 제강법.
- 제1항에 있어서, 탕표면 밑에서 도입되는 불활성 기체의 유속에 대한 상부에서 취입되는 기체의 유속의 상대적인 비율을 취련공정 단계에서 거의 동일하게 하는 제강법.
- 제1항에 있어서, 탕표면 밑에서 불활성 기체를 도입한 후 상부 취련을 시작하는 제강법
- 제1항에 있어서, 탕중에서의 탄소함량이 약2% 과잉일때는 제련용 기체로서 모두 산소만을 사용하고, 탄소함량이 약 2%이하일 때는 산소와 불활성 기체의 혼합물을 사용하는 제강법.
- 제1항에 있어서, 최종적인 탄소함량이 0.03% 이하일때는 최종 취련단계에서 상부에서 취련되는 제련용 기체로서 모두 불활성 기체만을 사용하는 제강법.
- 제1항에 있어서, 상부에서 취입되는 제련용 기체인 산소-불활성 기체 혼합물중의 전부 또는 일부를 건조공기를 하여 공급하는 제강법.
- 제1항에 있어서, 탕중에 고온의 고탄소 금소과 냉각된 재료를 충전시키는 제강법.
- 탕을 형성하는 고온의 고탄소 금속과 크롬함유 합금이 들어있는 상부 취턴식 용융금속 전로에서의 제강법에 의하여 탕표면으로 또는 탕표면 밑에서 랜스를 통하여 산소 및 또는 산소와 불활성기체 혼합물의 제련용 기체를 상부 취입하여 용융탕을 소요의 탄소함량이 되게 탈탄 처리하는 제강법에 있어서, 탕중에서의 탄소함량이 약 1% 과잉일때는 거의 산소로 된 제련용 기체를 상부 취입하고, 탕중에서의 탄소함량이 약 1%이하일때는 산소와 불활성 기체의 혼합물을 상부 취입하며, 탕표면 밑에서부터 탕속으로 계속해서 느린 유속으로 불활성 기체를 도입하고, 상부 취련이 시자될때에는 탕속으로 도입되는 산소대 불활성 기체의 전체비율을 1/1 이상으로 설정하며 상부에서 취입되는 체련용 기체를 거의 동일한 총유속으로 유지하면서 상부 취련도중 탄소함량이 감소되면 상부에서 취입되는 불활성 기체량을 증가시키면서 상부에서 취입되는 산소량을 감소시켜 주어 산소대 불활성 기체의 전체비율을 점진적으로 감소시켜 주고 산소대 불활성 기체의 비율이 1/1 이하인때는 상부 취련을 중단하는 개량된 제강법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.