KR20220168309A - 실리콘 하이드로겔 컬러 콘택트렌즈의 제조방법 - Google Patents
실리콘 하이드로겔 컬러 콘택트렌즈의 제조방법 Download PDFInfo
- Publication number
- KR20220168309A KR20220168309A KR1020210077876A KR20210077876A KR20220168309A KR 20220168309 A KR20220168309 A KR 20220168309A KR 1020210077876 A KR1020210077876 A KR 1020210077876A KR 20210077876 A KR20210077876 A KR 20210077876A KR 20220168309 A KR20220168309 A KR 20220168309A
- Authority
- KR
- South Korea
- Prior art keywords
- lens
- silicone
- silicone hydrogel
- contact lens
- color
- Prior art date
Abstract
본 발명은 실리콘 하이드로겔 컬러 콘택트렌즈의 제조방법에 관한 것으로서 실리콘 컬러 콘택트렌즈의 컬러층이 이탈하는 것을 방지하고, 안전한 렌즈를 생산하기 위하여 실리콘 컬러 콘택트 렌즈와 안료와의 결합을 위해 결합중합체를 제조하는 단계; 상기 중합체에 안료를 혼합하여 잉크페이스트를 제조하는 단계; 상기 잉크페이스트를 표면에 착색하는 단계; 실리콘 하이드로겔 렌즈를 중합하는 단계; 렌즈를 중합 후 미반응 물질인 단량체를 제거하고, 표면을 개질하는 후처리공정 단계로 이루어진다.
Description
본발명은 실리콘 하이드로겔 컬러 콘택트렌즈의 제조방법에 관한 것으로, 보다 상세하게는 산소투과성과 습윤성이 뛰어난 실리콘 하이드로겔에 미용효과를 줄 수 있는 칼라 착색제를 실리콘 결합중합체를 이용하여 컬러층이 이탈되지 않고 안전한 결합이 되게 하여 불량이 없고 품질이 향상되며 제조경비가 낮아지는 실리콘 하이드로겔 컬러 콘택트렌즈의 제조방법에 관한 것이다.
실리콘 하이드로겔 렌즈의 경우 기존 하이드로겔 렌즈와 달리 실리콘이 함유되어 있어 뛰어난 산소투과성과 습윤성을 가진다. 또한 칼라콘택트 렌즈를 제조하는 데 사용되는 잉크의 구성은 안료와 렌즈 표면에 결합을 할 수 있는 중합체 및 용매, 다양한 첨가제로 이용하여 제조되어 왔다.
그리고 종래특허기술의 일례로서, 공개특허공보 공개번호 10-2019-0066563호에는 실록산계 거대단량체의 주사슬, 곁사슬 또는 이들에 1 내지 10개의 글리세릴 반복단위가 도입된 실록산계 거대 단량체를 포함하는 중합 조성물로 제조된 실리콘 하이드로겔 렌즈로서, 상기 실리콘 하이드로겔 렌즈는 80 barrer 이상의 산소투과도 및 40°이하의 포착 기포법으로 측정된 표면접촉각을 만족하는 것인, 실리콘 하이드로겔 렌즈가 공개되어 있다.
또한, 등록특허공보 등록번호 10-1918645호에는 분자 구조 중에 적어도 하나의 수산기 또는 폴리에틸렌글리콜기를 가지는 실리콘 모노머 중 적어도 1종 이상과 글리세롤모노(메타)아크릴레이트를 포함하는 혼합액을 양면 캐스트 몰드 안에서 경화시킴으로써 얻어지는 실리콘 하이드로겔 소프트 콘택트 렌즈로서, 중합 후의 렌즈 형상 재료에 표면의 젖음성을 양호화시키기 위한 후처리를 하지 않아도 습윤성 표면을 가지는 실리콘 하이드로겔 소프트 콘택트 렌즈가 공개되어 있다.
하지만 실리콘 하이드로겔 렌즈에 함유하고 있는 실리콘 재질의 경우 칼라 착색제와 안전한 결합이 어려워 컬러층이 결합하는데 방해를 하여 품질이 저하되는 단점이 있었다.
따라서 본발명은 상기와 같은 문제점을 해결하고자 안출된 것으로, 산소투과성과 습윤성이 뛰어난 실리콘 하이드로겔에 미용효과를 줄 수 있는 칼라 착색제를 실리콘 결합중합체를 이용하여 컬러층이 이탈되지 않고 안전한 결합이 되게 하여 불량이 없고 품질이 향상되며 제조경비가 낮아지는 실리콘 하이드로겔 컬러 콘택트렌즈의 제조방법을 제공하고자 하는 것이다.
본발명은 실리콘 하이드로겔 컬러 콘택트렌즈의 제조방법에 관한 것으로, 실리콘 컬러 전용 결합중합체를 제조하는 결합중합체 제조 단계;
상기 결합중합체를 혼합하여 제조되는 잉크페이스트를 제조하는 단계;
콘택트렌즈 몰드 표면에 패드인쇄기로 인쇄하여 착색하는 단계;
상기 콘택트렌즈 몰드를 이용하여 실리콘 하이드로겔 컬러 콘택트렌즈를 중합하여 렌즈를 형성하는 단계;를 포함하는 것을 특징으로 한다.
또한, 상기 패드인쇄기로 잉크페이스트를 인쇄하는 몰드는 상부몰드인 것을 특징으로 한다.
따라서 본발명은 산소투과성과 습윤성이 뛰어난 실리콘 하이드로겔에 미용효과를 줄 수 있는 칼라 착색제를 실리콘 결합중합체를 이용하여 컬러층이 이탈되지 않고 안전한 결합이 되게 하여 불량이 없고 품질이 향상되며 제조경비가 낮아지는 현저한 효과가 있다.
도 1은 본발명의 안료의 구성물질인 산화타이타늄의 말단을 3-Aminopropyltriethoxysilane으로 표면을 처리하여 가교처리를 한 상태도
도 2는 본발명의 실리콘 하이드로겔 컬러 콘택트렌즈의 컬러층이 렌즈에 결합된 이미지 예시도
도 3은 본발명의 실리콘 결합중합체 적용한 렌즈 사진
도 4는 본발명의 실리콘 결함중합체를 적용하지 않은 렌즈 사진
도 2는 본발명의 실리콘 하이드로겔 컬러 콘택트렌즈의 컬러층이 렌즈에 결합된 이미지 예시도
도 3은 본발명의 실리콘 결합중합체 적용한 렌즈 사진
도 4는 본발명의 실리콘 결함중합체를 적용하지 않은 렌즈 사진
본발명은 실리콘 하이드로겔 컬러 콘택트렌즈의 제조방법에 관한 것으로, 실리콘 컬러 전용 결합중합체를 제조하는 결합중합체 제조 단계;
상기 결합중합체를 혼합하여 제조되는 잉크페이스트를 제조하는 단계;
콘택트렌즈 몰드 표면에 패드인쇄기로 인쇄하여 착색하는 단계;
상기 콘택트렌즈 몰드를 이용하여 실리콘 하이드로겔 컬러 콘택트렌즈를 중합하여 렌즈를 형성하는 단계;를 포함하는 것을 특징으로 한다.
또한, 상기 결합중합체를 제조하는 단계는 ,
단량체 2-하이드록시에틸메타크릴레이트 , 메타크릴산 , 메틸메타크릴레이트 , 또는 글리세릴메타크릴레이트;
실리콘 단량체;
중합 개시제;
용매;
점도유지제를; 혼합하여 교반하여 제조하는 것을 특징으로 한다.
또한, 상기 패드인쇄기로 잉크페이스트를 인쇄하는 몰드는 상부몰드인 것을 특징으로 한다.
본발명을 첨부도면에 의해 상세히 설명하면 다음과 같다.
도 1은 본발명의 안료의 구성물질인 산화타이타늄의 말단을 3-Aminopropyltriethoxysilane으로 표면을 처리하여 가교처리를 한 상태도, 도 2는 본발명의 실리콘 하이드로겔 컬러 콘택트렌즈의 컬러층이 렌즈에 결합된 이미지 예시도, 도 3은 본발명의 실리콘 결합중합체 적용한 렌즈 사진, 도 4는 본발명의 실리콘 결함중합체를 적용하지 않은 렌즈사진이다.
본 발명은 산소투과성과 습윤성이 뛰어난 실리콘 하이드로겔에 미용효과를 줄 수 있는 칼라 착색제가 포함된 실리콘 하이드로겔 칼라 콘택트렌즈로 그 제조방법에 관한 것이다.
곧, 칼라착색제에 실리콘 결합중합체를 이용하여 컨텍트렌즈를 제조하는 것이다.
안료의 물질의 구성물질인 산화타이타늄의 말단을
3-Aminopropyltriethoxysilane으로 표면을 처리하여 안료 물질에 가교 처리 후 결합중합체인 작용그룹 -COOH, -OH, -NH가진 결합 중합체를 혼합 믹스하여 콘텍트렌즈의 표면에 가교시켜 안료가 탈색되거나, 이탈하는 것을 막아주는 역할을 하여 실리콘 미용 칼라 콘택트렌즈를 제조 후 칼라 안료층이 유지되는 것이다.
본발명의 제조공정 실시례는 다음과 같다. 실리콘 컬러 전용 결합중합체를 제조하는 단계는 단량체 2-하이드록시에틸메타크릴레이트 10~40중량부, 실리콘 단량체 5~20부, 메타크릴산 0.1~2중량부, 메틸메타크릴레이트 0.1~2중량부, 글리세릴메타크릴레이트 0.5~5중량부, 여기에 중합 개시제인 디페닐 2-에틸헥실 포스페이트 0.5~~5중량부, 용매인 에틸 셀로솔브 30~60중량부, 부틸 셀로솔브 10~40중량부, 점도유지제인 폴리에틸렌글리콜을 0.5~10중량부를 혼합하여 60~65℃의 항온조에 넣고 질소를 15ml/min으로 투입하면서 300rpm의 속도로 2~3시간 교반하며 결합중합체를 제조한다.
상기 잉크페이스트를 제조하는 단계는 30~40℃ 온도에서 원하는 색상의 분산된 안료와 결합중합체의 혼합물을 75~85중량부, 경화제 0.1~1중량부를 페이스트 믹서에 분산 혼합시켜 잉크페이스트를 제조한 후 콘택트렌즈 상형 몰드 표면에 패드인쇄기로 인쇄한다.
실리콘 하이드로겔 컬러 콘택트렌즈를 중합하여 렌즈를 형성하는 단계로 2-하이드록시에틸메타크릴레이트 10~40중량부, 실리콘 단량체 25~50중량부, 친수성 단량체 10~40중량부, 10~40중량부, 가교결합제로 트리(에틸렌 글리콜)디메타크릴레이트 0.1~0.7중량부, 에틸렌 글리콜 디메타크릴레이트 0.1~0.7중량부, 개시제인 아조비스 2,4-디메틸발레로니트릴 0.5~2중량부를 첨가 및 교반하여 110~120℃에서 1시간 열중합한다.
친수성 단량체는 NVP. MPC, 또는 DMA이다.
그리고 마지막으로 렌즈를 중합 후 미반응 물질인 단량체를 제거하고, 표면을 개질하는 후처리공정 단계로 유기 용매 혼합물로 미반응 물질을 제거함. 유기 용매 혼합물로 프로판올, 부탄올, 펜탄올, 헥산올, 렙탄올, 옥탄올, 나노올, t-아민 알콜, 이소프로판올로 처리가 가능함. 유기용매 또는 1종 이상의 유기 용매의 혼합물로 용해시켜 제거한다.
본발명에서 렌즈 표면을 개질하는 방법은 두가지가 있는데,
1. 렌즈를 PAA 담근 후 꺼내어 MPC Polymer, 알지네이트, 히알루론산으로 침지 후 표면을 코팅하는 방법.
2. MBAA(N',N'-Methylenebisacrylamide Solution), APS(Ammonium persulfated), 히알루론산, MPC Polymer, Carbopol을 개량 후 혼합하여 렌즈를 담근 후 45~70℃ 온도에서 1시간동안 표면을 코팅하는 방법이 있다.
따라서 본발명은 실리콘 하이드로겔 렌즈에 함유하고 있는 실리콘 재질의 경우 칼라 착색제와 안전한 결합이 어려워 컬러층이 결합 산소투과성과 습윤성이 뛰어난 실리콘 하이드로겔에 미용효과를 줄 수 있는 칼라 착색제를 실리콘 결합중합체를 이용하여 안전한 결합이 되게 하여 불량이 없고 품질이 향상되며 제조경비가 낮아지는 현저한 효과가 있다.
Claims (3)
- 실리콘 컬러 전용 결합중합체를 제조하는 결합중합체 제조 단계;
상기 결합중합체를 혼합하여 제조되는 잉크페이스트를 제조하는 단계;
콘택트렌즈 몰드 표면에 패드인쇄기로 인쇄하여 착색하는 단계;
상기 콘택트렌즈 몰드를 이용하여 실리콘 하이드로겔 컬러 콘택트렌즈를 중합하여 렌즈를 형성하는 단계;를 포함하는 것을 특징으로 하는 실리콘 하이드로겔 컬러 콘택트렌즈의 제조방법 - 제1항에 있어서, 상기 결합중합체를 제조하는 단계는 ,
단량체 2-하이드록시에틸메타크릴레이트 , 메타크릴산 , 메틸메타크릴레이트 , 또는 글리세릴메타크릴레이트;
실리콘 단량체;
중합 개시제;
용매;
점도유지제를; 혼합하여 교반하여 제조하는 것을 특징으로 하는 실리콘 하이드로겔 컬러 콘택트렌즈의 제조방법 - 제2항에 있어서, 상기 패드인쇄기로 잉크페이스트를 인쇄하는 몰드는 상부몰드인 것을 특징으로 하는 실리콘 하이드로겔 컬러 콘택트렌즈의 제조방법