KR20220014466A - 세라믹 히터를 구비하는 액상 카트리지 - Google Patents
세라믹 히터를 구비하는 액상 카트리지 Download PDFInfo
- Publication number
- KR20220014466A KR20220014466A KR1020200093931A KR20200093931A KR20220014466A KR 20220014466 A KR20220014466 A KR 20220014466A KR 1020200093931 A KR1020200093931 A KR 1020200093931A KR 20200093931 A KR20200093931 A KR 20200093931A KR 20220014466 A KR20220014466 A KR 20220014466A
- Authority
- KR
- South Korea
- Prior art keywords
- liquid cartridge
- ceramic heater
- porous ceramic
- ceramic
- heating wire
- Prior art date
Abstract
본 발명은 세라믹 히터를 구비하는 액상 카트리지에 관한 것이다.
본 발명은 액상을 저장하며, 액상이 기화되어 발생하는 미세 입자를 흡입할 수 있는 유로가 형성된 케이스; 케이스 내에 결합되며, 액상을 흡수하여 담지하는 다공성 세라믹; 다공성 세라믹에 결합되며, 전류가 인가되면 발열하는 열선; 다공성 세라믹의 외표면에 위치하며, 열선의 양 단부와 연결되는 한 쌍의 패드; 및 케이스에 설치되며 일단은 패드와 접촉하며 타단은 외부 전원과 접촉하는 단자;를 포함하며, 열선의 발열에 의해 다공성 세라믹이 담지하고 있는 액상이 기화되는 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지를 제공한다.
본 발명은 액상을 저장하며, 액상이 기화되어 발생하는 미세 입자를 흡입할 수 있는 유로가 형성된 케이스; 케이스 내에 결합되며, 액상을 흡수하여 담지하는 다공성 세라믹; 다공성 세라믹에 결합되며, 전류가 인가되면 발열하는 열선; 다공성 세라믹의 외표면에 위치하며, 열선의 양 단부와 연결되는 한 쌍의 패드; 및 케이스에 설치되며 일단은 패드와 접촉하며 타단은 외부 전원과 접촉하는 단자;를 포함하며, 열선의 발열에 의해 다공성 세라믹이 담지하고 있는 액상이 기화되는 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지를 제공한다.
Description
본 발명은 세라믹 히터를 구비하는 액상 카트리지에 관한 것이다.
도 1는 종래 기술에 따른 미세입자 발생장치의 기화부를 상부에서 바라본 도면, 도 2는 종래 기술에 따른 미세입자 발생장치의 기화부를 하부에서 바라본 도면이다.
미세입자 발생장치의 기화부는, 액상을 흡수하여 담지하는 다공성 세라믹(12)과 다공성 세라믹(12)의 하면에 부착되어 액상을 가열하여 기화시키는 발열체(12a)을 포함한다. 다공성 세라믹(12a)의 표면에 부착된 발열체(12a)에는 발열체(12a)로 전류를 인가하는 전원선(12b)이 연결될 수 있다.
다공성 세라믹(12)은 중앙에 액상이 담길 수 있는 저수조 역할을 하는 요홈(12c)을 포함하고 있다. 액상이 담길 수 있는 저수조를 구비함으로써, 다공성 세라믹(12)의 기공 내로 좀 더 안정적으로 액상을 지속적으로 공급할 수 있다는 장점이 있다.
그런데, 종래의 다공성 세라믹 히터는 장치의 단자와 접촉을 위해 전원선(12b)을 구비하고 있었다. 전원선(12b)에 주로 사용되는 금속인 니켈은 유해물질을 발생시키기도 하고, 전원선(12b)을 단자와 접촉시키기 위해서는 추가적으로 공정이 필요했다. 또한 전원선(12b)이 단자와 납땜 등에 의해 전기적, 물리적으로 연결되어야 했기 때문에 교체형 카트리지의 구성 부품으로 다공성 세라믹 히터를 구비하는 것이 어렵다는 단점이 있었다.
본 발명은 세라믹 히터에 리드 와이어 대신 접촉 패드를 형성하여, 조립 시 패드와 단자가 바로 접촉하여 동작하게 함으로써, 불필요한 공정을 없애고 유해물질 발생을 방지하는 미세입자 발생장치의 세라믹 히터 및 이를 구비하는 액상 카트리지를 제공하는 것을 목적으로 한다.
본 발명은 액상을 저장하며, 액상이 기화되어 발생하는 미세 입자를 흡입할 수 있는 유로가 형성된 케이스; 케이스 내에 결합되며, 액상을 흡수하여 담지하는 다공성 세라믹; 다공성 세라믹에 결합되며, 전류가 인가되면 발열하는 열선; 다공성 세라믹의 외표면에 위치하며, 열선의 양 단부와 연결되는 한 쌍의 패드; 및 케이스에 설치되며 일단은 패드와 접촉하며 타단은 외부 전원과 접촉하는 단자;를 포함하며, 열선의 발열에 의해 다공성 세라믹이 담지하고 있는 액상이 기화되는 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지를 제공한다.
본 발명의 다른 일 예로, 다공성 세라믹의 적어도 한 면은 액상과 접촉하며, 다공성 세라믹에 결합된 열선과 가장 가까운 위치에 위치한 면은 기류 패스와 연결되는 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지를 제공한다.
또한 본 발명의 다른 일 예로, 열선은 한 쌍의 패드 사이에 위치한 부분이 적어도 2회 이상 굴곡된 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지를 제공한다.
또한 본 발명의 다른 일 예로, 열선의 이웃하는 굴곡된 부분은 서로 0.2∼1.0mm 거리를 두고 배치되는 것을특징으로 하는 세라믹 히터를 구비하는 액상 카트리지를 제공한다.
또한 본 발명의 다른 일 예로, 열선과 패드의 면적은, 다공성 세라믹의 열선과 가장 가까운 면의 면적의 30% 이상인 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지를 제공한다.
또한 본 발명의 다른 일 예로, 열선은 패드보다 열전도율이 높은 물질로 이루어진 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지를 제공한다.
또한 본 발명의 다른 일 예로, 열선의 폭은 패드의 폭의 50%이하인 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지를 제공한다.
또한 본 발명의 다른 일 예로, 다공성 세라믹은 WC, ZrC ,AlN, ZrO2, Al2O, TiO2, SiC, SiO2, Si3N4, Cordierite, Mullite, Spodumene 중에서 선택된 어느 하나 이상의 물질로 이루어지는 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지를 제공한다.
또한 본 발명의 다른 일 예로, 열선의 폭은 0.05mm를 넘는 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지를 제공한다.
또한 본 발명의 다른 일 예로, 열선의 저항은 0.5~2.0Ω 범위 내인 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지를 제공한다.
또한 본 발명의 다른 일 예로, 다공성 세라믹의 기공률은 40~70%인 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지를 제공한다.
또한 본 발명의 다른 일 예로, 다공성 세라믹을 구성하는 비드의 사이즈는 5 ~ 100μm인 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지를 제공한다.
또한 본 발명의 다른 일 예로, 다공성 세라믹은 최소 두께를 가지는 부분의 두께가 0.5mm이상인 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지를 제공한다.
또한 본 발명의 다른 일 예로, 다공성 세라믹은 2kgf 이상의 파괴 강도를 가지는 것을 특징으로 하는 미세입자 발생장치의 세라믹 히터를 구비하는 액상 카트리지를 제공한다.
또한 본 발명의 다른 일 예로, 단자는 SUS, 무연황동, 금, 은, 구리, 합금, 텅스텐, 니켈, Al, 크롬, 철과 같은 전기적 저항이 작은 금속 중에서 선택된 하나 이상의 소재로 이루어지는 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지를 제공한다.
또한 본 발명의 다른 일 예로, 단자는 금, 니켈, 주석, 은, 백금, 팔라듐, 아연 중에서 선택된 어느 하나 이상의 물질로 도금되는 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지를 제공한다.
또한 본 발명의 다른 일 예로, 케이스는, 액상 저장공간과 기류 패스를 형성하는 메인 케이스, 메인 케이스 내측 하부에 결합되는 하부 케이스를 포함하며, 단자는 하부 케이스의 사출 성형시 인서트 되는 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지를 제공한다.
또한 본 발명의 다른 일 예로, 하부 케이스는, 다공성 세라믹 측으로 외기를 도입하는 외기 유입로을 구비하는 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지를 제공한다.
또한 본 발명의 다른 일 예로, 열선은 다공성 세라믹의 외면 중 외기 유입로에서 가장 가까운 면이 가장 높은 온도를 가지는 면이 되도록 배치되는 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지를 제공한다.
또한 본 발명의 다른 일 예로, 케이스는 다공성 세라믹의 외면 중 가장 높은 온도를 가지는 면과 수직하며, 외기를 유입하는 외기 유입로를 구비하는 것을 특징으로 하는 액상 카트리지를 제공한다.
또한 본 발명의 다른 일 예로, 다공성 세라믹의 외주를 감싸 액상의 누액을 방지하는 내열성 러버 커버;를 더 포함하는 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지를 제공한다.
본 발명이 제공하는 세라믹 히터를 구비하는 액상 카트리지는, 기존 세라믹 히터를 채용한 액상 카트리지와 달리 리드 와이어 대신 패드와 패드에 접촉하는 단자를 구비함으로써 납땜 공정을 삭제할 수 있다. 또한 리드 와이어에 주로 이용되는 금속인 니켈은 유해 물질을 발생시키나 본 발명은 리드 와이어를 제거함으로써 유해 물질의 발생도 방지할 수 있다.
도 1는 종래 기술에 따른 미세입자 발생장치의 기화부를 상부에서 바라본 도면,
도 2는 종래 기술에 따른 미세입자 발생장치의 기화부를 하부에서 바라본 도면,
도 3은 본 발명의 일 실시예에 따른 세라믹 히터를 구비하는 액상 카트리지의 분해도,
도 4는 본 발명의 일 실시예에 따른 세라믹 히터를 구비하는 액상 카트리지의 단면도,
도 5는 본 발명의 일 실시예에 따른 액상 카트리지가 구비하는 세라믹 히터를 도시한 도면,
도 6은 본 발명의 일 실시예에 따른 세라믹 히터를 구비하는 액상 카트리지의 작동과 기류의 흐름을 보여주는 도면.
도 2는 종래 기술에 따른 미세입자 발생장치의 기화부를 하부에서 바라본 도면,
도 3은 본 발명의 일 실시예에 따른 세라믹 히터를 구비하는 액상 카트리지의 분해도,
도 4는 본 발명의 일 실시예에 따른 세라믹 히터를 구비하는 액상 카트리지의 단면도,
도 5는 본 발명의 일 실시예에 따른 액상 카트리지가 구비하는 세라믹 히터를 도시한 도면,
도 6은 본 발명의 일 실시예에 따른 세라믹 히터를 구비하는 액상 카트리지의 작동과 기류의 흐름을 보여주는 도면.
이하, 도면을 참조하여 본 발명을 더욱 상세하게 설명한다.
도 3은 본 발명의 일 실시예에 따른 세라믹 히터를 구비하는 액상 카트리지의 분해도, 도 4는 본 발명의 일 실시예에 따른 세라믹 히터를 구비하는 액상 카트리지의 단면도, 도 5는 본 발명의 일 실시예에 따른 액상 카트리지가 구비하는 세라믹 히터를 도시한 도면, 도 5는 본 발명의 일 실시예에 따른 액상 카트리지가 구비하는 세라믹 히터를 도시한 도면이다.
본 발명의 일 실시예에 따른 세라믹 히터를 구비하는 액상 카트리지는 액상을 저장하며, 액상이 기화되어 발생하는 미세 입자를 흡입할 수 있는 유로(114)가 형성된 케이스(110, 120, 130)를 구비한다.
케이스(110, 120, 130)는, 액상 저장공간(112)과 유로(114)를 구비하는 메인 케이스(110)와, 메인 케이스(110) 내측 하부에 결합되는 하부 케이스(120)와, 메인 케이스(110)의 외측 상부에 결합되는 상부 케이스(130)를 포함한다.
메인 케이스(110)는 액상 저장공간(112)과 유로(114)가 나란히 배치되고, 그 하부에 하부 케이스(120)가 결합되는 벽체(116)가 구비된다. 벽체(116) 내에 하부 케이스(120)가 삽입되어 결합된다. 하부 케이스(120)는 상부에 후술할 세라믹 히터가 수용되는 공간을 형성하는 벽체(122)를 구비하며, 벽체(122) 내에서 세라믹 히터에 의해 미세입자가 발생한다. 벽체(122)는 관통홀(126)이 형성되며, 관통홀(126)은 메인 케이스(110)의 유로(114)와 벽체(122) 내부의 공간을 연통시켜준다.
이때, 하부 케이스(120)의 외주에는 액상의 누출을 방지하기 위해, 하부케이스(120)의 외주에 탄성 재질의 O-ring(500)이 설치될 수 있다. O-ring(500)은 하부 케이스(120)와 메인 케이스(110) 사이의 기밀성을 유지시켜준다.
한편 하부 케이스(120)의 하부에는 자석(600)이 설치될 수 있다. 자석(600)은 액상 카트리지가 결합되는 상대물인 미세입자 발생장치(미도시) 설치된 자석 또는 철판과 사이에 인력이 작용하여 액상 카트리지의 결합을 유지해주는데 도움이 된다.
세라믹 히터는, 메인 케이스(110)와 하부 케이스(120)에 고정되는 다공성 세라믹(200)과 다공성 세라믹(200)에 결합된 열선(310)과 패드(320)로 이루어진다. 다공성 세라믹(200)은 메인 케이스(110)의 액상 저장공간(112) 하측에 결합되며, 상부는 액상을 저장할 수 있는 오목부(202)가 형성되어 있다. 이때, 다공성 세라믹(200)과 메인 케이스(110), 하부 케이스(120)의 결합부에서 누액이 발생하는 것을 방지하기 위해, 다공성 세라믹(200)의 외주를 감싸는 내열성 러버 커버(210)를 더 구비하는 것이 바람직하다. 상부 케이스(130)는 메인 케이스(110)의 상부에 결합되며, 메인 케이스(110)의 유로(114)를 통해 전달된 미세입자를 흡입할 수 있는 흡입홀(132)을 구비한다. 이때, 유로(114)를 거치며 액상이 냉각되어 발생할 수 있는 액적을 흡입하는 것을 방지할 수 있도록, 상부 케이스(130)와 메인 케이스(110) 사이에는 흡습재(135)나, 실링막(137)이 제공될 수 있다.
다공성 세라믹(200)은 WC, ZrC ,AlN, ZrO₂, Al₂O₃, TiO₂, SiC, SiO₂, Si₃N₄, Cordierite, Mullite, Spodumene 중에서 선택된 어느 하나 이상의 물질을 소결하여 제조할 수 있다. 이때, 액상의 원활한 공급을 위해 다공성 세라믹(200)의 기공률은 40~70%인 것이 바람직하다. 다공성 세라믹(200)의 제조 시, WC, ZrC ,AlN, ZrO₂, Al₂O₃, TiO₂, SiC, SiO₂, Si₃N₄, Cordierite, Mullite, Spodumene 비드 사이즈는 5 ~ 100μm인 것이 바람직하다. 제조된 다공성 세라믹(200)은 두께가 두꺼운 부분도 있고, 오목부(202)의 외주부처럼 두께가 얇은 부분도 있다. 파손을 방지하기 위해 다공성 세라믹(200)의 최소 두께를 가지는 부분의 두께는 0.5mm이상인 것이 바람직하다. 또한, 다공성 세라믹(200)은 2kgf 이상의 파괴 강도를 가지는 것이 바람직하다.
다공성 세라믹(200)에는 매립되거나, 다공성 세라믹(200)의 표면 부근에 위치하여 적어도 일부가 노출되는 열선(310)이 결합된다. 열선(310)의 양 단에는 후술할 단자와 접촉하기 위한 한 쌍의 패드(320)가 형성된다. 열선(310)과 패드(320)는 다공성 세라믹(200)의 형성 시에 일체로 결합될 수도 있고, 다공성 세라믹(200)의 제조 후에 별도의 공정을 거쳐 결합될 수도 있다.
이때, 열선(310)은 다공성 세라믹(200)과 결합된 길이를 최대한 길게 하여 발열량을 늘리기 위해, 적어도 2회 이상 굴곡되게 형성할 수 있다. 이때, 열선(310)의 이웃하는 굴곡된 부분 간의 간격(a)은 0.2∼1.0mm 인 것이 바람직하다. 반면 패드(320)의 형상에는 별다른 제약이 없으며, 원형, 사각형 또는 다각형으로 다양한 형상으로 실시 가능하다. 이때, 열선(310)과 패드(320)의 면적은, 다공성 세라믹(200)의 외면 중 열선(310)과 가장 가까운 면의 면적의 30% 이상인 것이 바람직하다. 도 3 내지 5에 도시된 다공성 세라믹(200)은 대략 육면체에 가까우며, 상면에 오목부(202)가 형성된 바스형이다. 그리고 열선(310)과 패드(320)는 다공성 세라믹(200)의 하면에 배치되어 있다. 따라서 도 3 내지 5에 도시된 본 발명의 일 실시예에 따른 액상 카트리지는, 열선(310)과 패드(320)의 면적 합이 다공성 세라믹(200)의 하면의 면적의 30% 이상이어야 한다.
이때, 다공성 세라믹(200)은 원기둥 형태이거나, 오목부가 없는 육면체 형태, 필요에 따라 불규칙한 외면을 가지는 형태일 수 있으나, 다공성 세라믹(200)의 외면 중 열선(310)과 가장 가까운 외면은 결정할 수 있으며, 이때, 열선(310)과 패드(320)의 면적은 열선(310)과 가장 가까운 외면의 면적의 30%이상이어야 한다.
이때, 패드(320)는 발열하지 않고, 열선(310)에서만 발열이 일어나는 것이 바람직하다. 따라서 열선(310)은 패드보다 열전도율이 높은 물질로 이루어지는 것이 바람직하다. 또한, 열선(310)의 폭은 패드(320)의 폭의 50%이하인 것이 바람직하다. 그러나 충분한 발열량을 확보하기 위해 열선(310)의 폭은 0.05mm를 넘는 것이 바람직하다. 이때, 열선(310)의 저항은 0.5~2.0Ω 범위 내인 것이 바람직하다.
한편, 외부 전원을 패드(320)를 통해 열선(310)으로 전달할 수 있도록, 패드(320)에 접촉하는 단자(400)를 포함한다. 단자(400)는, 사출물로 제조되는 하부 케이스(120)의 사출 형성 시에 인서트 되어 일체로 제조될 수 있다. 단자(400)의 형상은, 하부 케이스(120)로부터 쉽게 이탈하지 않도록 하부 케이스(120) 내에 결합된 부분이 원기둥에서 외주로 연장된 플랜지부가 형성된 아령형태이다. 상부에 위치한 플랜지부에서 상부로 돌출한 기둥을 더 구비하며, 상부로 돌출한 기둥은 패드(320)에 접촉한다. 또한 하부에 위치한 플랜지부가 외부 전원, 즉 액상 카트리지가 결합되는 미세입자 발생장치의 터미널과 접촉하게 된다.
그러나, 단자(400)의 형상에는 별다른 제약이 없으며, 하부 케이스(120)와의 결합상태를 유지하면서, 패드(320)와 미세입자 발생장치의 터미널 사이를 전기적으로 연결해줄 수 있는 형상이라면 어떠한 형상으로도 실시 가능하다. 예를 들어, 단자(400)는 벤댕된 판재이며, 적어도 일부가 하부 케이스(120)에 인서트 사출된 형태일 수 있다.
단자(400)는 SUS, 무연황동, 금, 은, 구리, 합금, 텅스텐, 니켈, Al, 크롬, 철과 같은 전기적 저항이 작은 금속 중에서 선택된 하나 이상의 소재로 이루어질 수 있다. 이때, 단자(400)에는 금, 니켈, 주석, 은, 백금, 팔라듐, 아연 중에서 선택된 어느 하나 이상의 물질로 도금이 행해질 수 있다.
단자(400)를 통해 전기가 공급되어 열선(310)이 발열하면, 다공성 세라믹(200)에 담지되어 있던 액상이 기화하면서 미세입자가 발생하게 된다.
이때, 하부 케이스(120)에는 사용자의 원활한 흡입을 위해 외기를 도입할 수 있는 외기 유입로(124)가 형성된다. 외기 유입로(124)는 다공성 세라믹(200)의 외면 중 가장 높은 온도를 가지는 면과 수직하게 형성된다. 본 발명의 일 실시예에서는 앞서 설명한 바와 같이, 다공성 세라믹(200)의 하면이 열선(310)과 가장 가까운 면이며, 그에 따라 다공성 세라믹(200)의 하면이 외면 중 가장 높은 온도를 가진다. 따라서 하부 케이스(120)에 형성되는 외기 유입로(124)는 다공성 세라믹(200)의 하면에 수직하게 배치된다.
도 6은 본 발명의 일 실시예에 따른 세라믹 히터를 구비하는 액상 카트리지의 작동과 기류의 이동을 보여주는 도면이다.
앞서 설명한 바와 같이 열선(310)과 패드(320)가 형성된 다공성 세라믹(200)에 러버 커버(210)가 씌워져 메인 케이스(110)와 하부 케이스(120)에 설치된다. 하부 케이스(120) 내에서 다공성 세라믹(200)의 하면의 아래로 빈 공간이 형성된다. 하부 케이스(120)의 하측에 설치된 단자(400)를 통해 다공성 세라믹(200)에 형성된 패드(320)로 전원이 인가되면, 열선(310)이 발열하며 다공성 세라믹(200)에 담지되어 있던 액상을 기화시키며, 세라믹(200)의 하면의 아래로 빈 공간에 기화된 미세입자가 머무르게 된다. 이후, 사용자가 상부 케이스(130; 도 4 참조)의 흡입홀(132)을 통해 음압을 형성하면 하부 케이스(120)의 외기 유입로(124)를 통해 외기가 유입되어 기화된 미세입자와 함께 하부 케이스(120)의 벽체(122)의 관통홀(126)을 통해 메인 케이스(110)의 유로(114)로 이동하고, 흡입홀(132)을 통해 사용자가 흡입할 수 있게 된다.
메인 케이스(110)는 액상 저장공간(112)과 유로(114)가 나란히 배치되고, 그 하부에 하부 케이스(120)가 결합되는 벽체(116)가 구비된다. 벽체(116) 내에 하부 케이스(120)가 삽입되어 결합된다. 하부 케이스(120)는 상부에 후술할 세라믹 히터가 수용되는 공간을 형성하는 벽체(122)를 구비하며, 벽체(122) 내에서 세라믹 히터에 의해 미세입자가 발생한다. 벽체(122)는 관통홀(126)이 형성되며, 관통홀(126)은 메인 케이스(110)의 유로(114)와 벽체(122) 내부의 공간을 연통시켜준다.
다공성 세라믹의 적어도 한 면은 액상과 접촉하며, 다공성 세라믹에 결합된 열선과 가장 가까운 위치에 위치한 면은 기류 패스와 연결되는 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지.
Claims (21)
- 액상을 저장하며, 액상이 기화되어 발생하는 미세 입자를 흡입할 수 있는 유로가 형성된 케이스;
케이스 내에 결합되며, 액상을 흡수하여 담지하는 다공성 세라믹;
다공성 세라믹에 결합되며, 전류가 인가되면 발열하는 열선;
다공성 세라믹의 외표면에 위치하며, 열선의 양 단부와 연결되는 한 쌍의 패드; 및
케이스에 설치되며 일단은 패드와 접촉하며 타단은 외부 전원과 접촉하는 단자;를 포함하며,
열선의 발열에 의해 다공성 세라믹이 담지하고 있는 액상이 기화되는 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지. - 제1항에 있어서,
다공성 세라믹의 적어도 한 면은 액상과 접촉하며, 다공성 세라믹에 결합된 열선과 가장 가까운 위치에 위치한 면은 기류 패스와 연결되는 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지. - 제1항에 있어서,
열선은 한 쌍의 패드 사이에 위치한 부분이 적어도 2회 이상 굴곡된 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지. - 제2항에 있어서,
열선의 이웃하는 굴곡된 부분은 서로 0.2∼1.0mm 거리를 두고 배치되는 것을특징으로 하는 세라믹 히터를 구비하는 액상 카트리지. - 제1항에 있어서,
열선과 패드의 면적은, 다공성 세라믹의 열선과 가장 가까운 면의 면적의 30% 이상인 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지. - 제1항에 있어서,
열선은 패드보다 열전도율이 높은 물질로 이루어진 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지. - 제1항에 있어서,
열선의 폭은 패드의 폭의 50%이하인 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지. - 제1항에 있어서,
다공성 세라믹은 WC, ZrC ,AlN, ZrO₂, Al₂O₃, TiO₂, SiC, SiO₂, Si₃N₄, Cordierite, Mullite, Spodumene 중에서 선택된 어느 하나 이상의 물질로 이루어지는 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지. - 제1항에 있어서,
열선의 폭은 0.05mm를 넘는 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지. - 제1항에 있어서,
열선의 저항은 0.5~2.0Ω 범위 내인 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지. - 제1항에 있어서,
다공성 세라믹의 기공률은 40~70%인 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지. - 제1항에 있어서,
다공성 세라믹을 구성하는 비드의 사이즈는 5 ~ 100μm인 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지. - 제1항에 있어서,
다공성 세라믹은 최소 두께를 가지는 부분의 두께가 0.5mm이상인 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지. - 제1항에 있어서,
다공성 세라믹은 2kgf 이상의 파괴 강도를 가지는 것을 특징으로 하는 미세입자 발생장치의 세라믹 히터를 구비하는 액상 카트리지. - 제1항에 있어서,
단자는 SUS, 무연황동, 금, 은, 구리, 합금, 텅스텐, 니켈, Al, 크롬, 철과 같은 전기적 저항이 작은 금속 중에서 선택된 하나 이상의 소재로 이루어지는 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지. - 제1항에 있어서,
단자는 금, 니켈, 주석, 은, 백금, 팔라듐, 아연 중에서 선택된 어느 하나 이상의 물질로 도금되는 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지. - 제1항에 있어서,
케이스는, 액상 저장공간과 유로를 구비하는 메인 케이스, 메인 케이스 내측 하부에 결합되는 하부 케이스를 포함하며,
단자는 하부 케이스의 사출 성형시 인서트 되는 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지. - 제17항에 있어서,
하부 케이스는, 다공성 세라믹 측으로 외기를 도입하는 외기 유입로를 구비하는 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지. - 제18항에 있어서,
열선은 다공성 세라믹의 외면 중 외기 유입로에서 가장 가까운 면이 가장 높은 온도를 가지는 면이 되도록 배치되는 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지. - 제1항에 있어서,
케이스는, 다공성 세라믹의 외면 중 가장 높은 온도를 가지는 면과 수직하며, 외기를 유입하는 외기 유입로를 구비하는 것을 특징으로 하는 액상 카트리지. - 제1항에 있어서,
다공성 세라믹의 외주를 감싸 액상의 누액을 방지하는 내열성 러버 커버;를 더 포함하는 것을 특징으로 하는 세라믹 히터를 구비하는 액상 카트리지.