KR20180101542A - 편지 및 섬유 제품 - Google Patents
편지 및 섬유 제품 Download PDFInfo
- Publication number
- KR20180101542A KR20180101542A KR1020187023453A KR20187023453A KR20180101542A KR 20180101542 A KR20180101542 A KR 20180101542A KR 1020187023453 A KR1020187023453 A KR 1020187023453A KR 20187023453 A KR20187023453 A KR 20187023453A KR 20180101542 A KR20180101542 A KR 20180101542A
- Authority
- KR
- South Korea
- Prior art keywords
- letter
- torque
- yarn
- crimped
- fibers
- Prior art date
Abstract
본 발명의 과제는, 흡수성, 속건성 및 방투성이 우수한 편지 및 섬유 제품을 제공하는 것이며, 해결 수단은, 30T/m 이하의 토크를 갖는 권축 섬유를 사용하여, 편지의 밀도가 60코스/2.54cm 이상 또한 45웨일/2.54cm이상, 또한 편지의 두께가 0.45mm 이하인 편지를 얻는 것이다.
Description
본 발명은, 흡수성, 속건성 및 방투성이 우수한 편지(knitted fabric, 編地) 및 섬유 제품에 관한 것이다.
종래, 스포츠 의료 등을 중심으로 흡수성이 우수한 포백(cloth)이 제안되어 있다(예를 들어, 특허문헌 1, 특허문헌 2). 또한 한편, 스포츠 의료 등에서는 흡수성 뿐만 아니라 땀을 흘린 후, 바로 건조되는 속건성도 요구된다. 나아가, 방투성도 요구된다.
그러나, 흡수성과 속건성은 서로 상반된 성질이다. 예를 들어, 흡수성을 높이기 위해 천연 섬유를 사용하거나 포백의 단위 면적당 중량을 크게 하면 흡수성은 높아지지만, 속건성이 저하되는 경향이 있다. 반대로, 속건성을 높이기 위해 포백에 발수 가공을 실시하면 흡수성이 저하되는 경향이 있다.
또한, 속건성과 방투성은 서로 상반된 성질이다. 예를 들어, 속건성을 높이기 위해 포백의 단위 면적당 중량을 작게 하면, 방투성이 저하되는 경향이 있다.
본 발명은 상기한 배경을 감안하여 이루어진 것이며, 그의 목적은 흡수성, 속건성 및 방투성이 우수한 편지 및 섬유 제품을 제공하는 데 있다.
본 발명자는 상기한 과제를 달성하기 위해 예의 검토한 결과, 저토크의 권축 섬유를 사용하고, 또한 밀도나 두께를 독창적으로 연구함으로써, 흡수성, 속건성 및 방투성이 우수한 편지가 얻어진다는 것을 알아내어, 더욱 예의 검토를 거듭함으로써 본 발명을 완성하기에 이르렀다.
이와 같이 하여, 본 발명에 따르면 「30T/m 이하의 토크를 갖는 권축 섬유를 포함하는 편지이며, 편지의 밀도가 60코스/2.54cm 이상 또한 45웨일/2.54cm 이상이고, 또한 편지의 두께가 0.45mm 이하인 것을 특징으로 하는 편지」가 제공된다.
그 때, 상기 권축 섬유가 S 방향의 토크를 갖는 가연 권축 가공사(false-twist crimped yarn)와 Z 방향의 토크를 갖는 가연 권축 가공사를 포함하는 복합사인 것이 바람직하다. 또한, 상기 권축 섬유가 인터레이스 가공이 실시된 교락사인 것이 바람직하다. 또한, 상기 권축 섬유의 토크가 논토크인 것이 바람직하다. 또한, 상기 권축 섬유에서, 단섬유 섬도가 0.3 내지 1.3dtex의 범위 내인 것이 바람직하다. 또한, 상기 권축 섬유에서, 총 섬도가 40 내지 80dtex의 범위 내인 것이 바람직하다. 또한, 상기 권축 섬유가 폴리에스테르 섬유 또는 나일론 섬유를 포함하는 것이 바람직하다.
본 발명에 있어서, 편지의 단위 면적당 중량이 130g/m2 이하인 것이 바람직하다. 또한, 편지의 두께가 0.30 내지 0.45mm의 범위 내인 것이 바람직하다. 또한, 편지에 친수화제가 부여되어 있는 것이 바람직하다. 또한, 편지의 표리 적어도 어느 한쪽 표면에서, JIS L1907-1998 5.1.2 바이렉법에 의해 측정한 흡수성이 7cm 이상인 것이 바람직하다. 또한, JIS L0217-1998, 103법에 의해 3회의 세탁을 행한 후의 편지의 표리 적어도 어느 한쪽 표면에서, JIS L1907-1998 5.1.2 바이렉법에 의해 측정한 흡수성이 8cm 이상인 것이 바람직하다. 또한, AATCC 시험법(TEST METHOD) 201-2014에 의해 측정한 건조성이 10분 이하인 것이 바람직하다. 또한, JIS L0217-1998, 103법에 의해 5회의 세탁을 행한 후에 있어서, AATCC 시험법 201-2014에 의해 측정한 건조성이 12분 이하인 것이 바람직하다.
또한, 본 발명에 따르면, 상기한 편지를 사용하여 이루어지는 의료, 안감(lining fabric), 심지, 양말, 복대, 모자, 장갑, 잠옷, 이불잇(futon's outer fabric), 이불 커버, 카시트 표피재의 군으로부터 선택되는 어느 하나의 섬유 제품이 제공된다.
본 발명에 따르면, 흡수성, 속건성 및 방투성이 우수한 편지 및 섬유 제품이 얻어진다.
도 1은, 본 발명에 있어서 채용할 수 있는 편조직도의 일례(평짜기)이다.
도 2는, 본 발명에 있어서 채용할 수 있는 편조직도의 일례(니트 미스)이다.
도 2는, 본 발명에 있어서 채용할 수 있는 편조직도의 일례(니트 미스)이다.
이하, 본 발명의 실시 형태에 대하여 상세하게 설명한다. 우선, 본 발명에 있어서, 30T/m 이하의 토크를 갖는 권축 섬유(이하, 간단히 「권축 섬유」라 하는 경우도 있음)가 포함된다. 이러한 권축 섬유가 편지에 포함됨으로써 단섬유간에 미세한 공극이 형성될 뿐만 아니라, 편지 표면이 플랫해져 물과의 접촉 면적이 커져 흡수성이 향상된다. 또한, 방투성도 향상된다.
여기서, 상기 권축 섬유가 제조 조건 또는 섬도에 있어서 서로 상이한 2종 이상의 가연 권축 가공사를 포함하는 복합사인 것이 바람직하다. 이러한 복합사에는 다른 사조가 포함되어 있어도 되지만, 제조 조건 또는 섬도에 있어서 서로 상이한 2종의 가연 권축 가공사만으로 복합사를 구성하고 있는 것이 바람직하다.
가연 권축 가공사에는 제1 히터 영역에서 가연을 세팅한, 소위 원 히터 가연 권축 가공사와, 해당 실을 나아가 제2 히터 영역에 도입하여 이완 열 처리함으로써 토크를 저감시킨, 소위 세컨드 히터 가연 권축 가공사가 있다. 또한, 시연(施撚: twisting)의 방향에 따라, S 방향의 토크를 갖는 가연 권축 가공사와 Z 방향의 토크를 갖는 가연 권축 가공사가 있다. 본 발명에 있어서 이들 가연 권축 가공사를 사용할 수 있다. 특히, S 방향의 토크를 갖는 가연 권축 가공사와 Z 방향의 토크를 갖는 가연 권축 가공사로 복합사를 구성하면, 저토크의 복합사가 얻어져 바람직하다.
이러한 복합사는 예를 들어 이하의 방법에 의해 제조할 수 있다. 즉, 사조를 제1 롤러, 세팅 온도 90 내지 220℃(보다 바람직하게는 100 내지 190℃)의 열 처리 히터를 경유하여 꼬기 장치에 의해 시연함으로써 원 히터 가연 권축 가공사를 얻어도 되고, 필요에 따라 나아가 제2 히터 영역에 도입하여 이완 열 처리함으로써 세컨드 히터 가연 권축 가공사를 얻어도 된다. 가연 권축 가공시의 연신 배율은, 0.8 내지 1.5의 범위가 바람직하다. 가연수는, 가연수(T/m)=(32500/(D)1/2)×α의 식에 있어서, α가 0.5 내지 1.5(보다 바람직하게는 0.8 내지 1.2)의 범위 내인 것이 바람직하다. 단, D는 사조의 총 섬도(dtex)이다. 사용하는 꼬기 장치로서는, 디스크식 혹은 벨트식의 마찰식 꼬기 장치가 실을 걸기 쉽고, 실 끊어짐도 적어 적당하지만, 핀 방식의 꼬기 장치여도 된다. 또한, 시연의 방향에 의해, 가연 권축 가공사가 갖는 토크를 S 방향인지 Z 방향인지 선택할 수 있다. 이어서, 2종 이상의 가연 권축 가공사를 합사함으로써 상기 복합사가 얻어진다.
상기 권축 섬유에는, 인터레이스 가공에 의해 교락이 부여되어 있는 것이 바람직하다. 교락(인터레이스)의 개수는, 부드러운 감촉이나 스트레치성을 손상시키지 않기 위해 30 내지 90개/m의 범위 내인 것이 바람직하다. 해당 개수가 90개/m보다도 크면 부드러운 감촉이나 스트레치성이 손상될 우려가 있다. 반대로, 해당 개수가 30개/m보다도 작으면 복합사의 집속성이 불충분해져, 편직 제조성이 손상될 우려가 있다. 또한, 교락 처리(인터레이스 가공)는 통상의 인터레이스 노즐을 사용하여 처리한 것이어도 된다.
이와 같이 하여 얻어진 복합사의 토크로서는, 30T/m 이하(바람직하게는 18T/m 이하, 보다 바람직하게는 10T/m 이하, 특히 바람직하게는 논토크(0T/m))인 것이 중요하다. 토크는 작을수록 바람직하고 논토크(0T/m)가 가장 바람직하다. 이와 같이 논토크로 하기 위해서는, S 방향의 토크를 갖는 가연 권축 가공사와 Z 방향의 가연 권축 가공사를 합사할 때, 토크의 방향이 상이한 것 이외는 동일한 토크를 갖는 2종의 가연 권축 가공사를 사용하면 된다.
또한, 상기 권축 섬유에서, 권축률이 2% 이상(보다 바람직하게는 10 내지 30%)인 것이 바람직하다. 해당 권축률이 2% 미만이면, 흡수성이나 방투성이 저하될 우려가 있다.
상기 권축 섬유에서, 나노파이버라 불리는 단섬유 직경이 1000nm 이하인 것이어도 되지만, 단섬유 섬도가 0.3 내지 1.3dtex(보다 바람직하게는 0.4 내지 1.0dtex)의 범위 내인 것이 바람직하다. 해당 단섬유 섬도가 1.3dtex보다도 크면 흡수성이나 방투성이 저하될 우려가 있다. 반대로 해당 단섬유 섬도가 0.3dtex보다도 작으면 속건성이 저하될 우려가 있다.
또한, 상기 권축 섬유에서, 총 섬도(단섬유 섬도와 필라멘트수의 곱)로서는 40 내지 80dtex(보다 바람직하게는 45 내지 70dtex)의 범위 내인 것이 바람직하다. 해당 총 섬도가 80dtex보다도 크면 속건성이 손상될 우려가 있다. 반대로 해당 총 섬도가 40dtex보다도 작으면 흡수성이나 방투성이 손상될 우려가 있다.
또한, 상기 권축 섬유의 단섬유 단면 형상으로서는, 통상의 환 단면이어도 되지만, 환 단면 이외의 이형 단면 형상이어도 된다. 이러한 이형 단면 형상으로서는, 삼각, 사각, 십자, 편평, 잘록한 편평, H형, W형 등이 예시된다. 이 때, 편평한 단면 형상의 길이 중심선 방향의 길이 B의 이 길이 중심선 방향으로 직각을 이루어 교차하는 방향에 있어서의 최대폭 C1에 대한 비 B/C1에 의해 표시되는 단면 편평도가 2 내지 6(보다 바람직하게는 3.1 내지 5.0)의 범위 내인 것이 포백의 소프트성의 면에서 바람직하다. 또한, 그 폭의 최댓값 C1의 최솟값 C2에 대한 비 C1/C2가 1.05 내지 4.00(보다 바람직하게는 1.1 내지 1.5)의 범위 내인 것이 포백의 흡수성 면에서 바람직하다.
상기 권축 섬유를 구성하는 섬유로서는 특별히 제한되지 않으며, 폴리에스테르 섬유, 아크릴 섬유, 나일론 섬유, 레이온 섬유, 아세테이트 섬유, 나아가 면, 울, 비단 등의 천연 섬유나 이들을 복합한 것을 사용 가능하다. 특히 폴리에스테르 섬유 또는 나일론 섬유가 바람직하다. 이러한 폴리에스테르 섬유는, 적어도 폴리에스테르 성분을 포함하는 복합 섬유를 포함한다. 이러한 복합 섬유로서는, 사이드 바이 사이드형 복합 섬유, 편심 코어 시스형 복합 섬유, 코어 시스형 복합 섬유, 해도형 복합 섬유 등이 예시된다. 또한, 나일론 섬유는, 나일론 6 섬유나 나일론 66 섬유를 포함한다.
상기 폴리에스테르로서는 테레프탈산을 주된 산 성분으로 하고, 탄소수 2 내지 6의 알킬렌글리콜, 즉 에틸렌글리콜, 트리메틸렌글리콜, 테트라메틸렌글리콜, 펜타메틸렌글리콜, 헥사메틸렌글리콜로 이루어지는 군으로부터 선택된 적어도 1종을 주된 글리콜 성분으로 하는 폴리에스테르가 바람직하다. 그 중에서도, 에틸렌글리콜을 주된 글리콜 성분으로 하는 폴리에스테르(폴리에틸렌테레프탈레이트) 또는 트리메틸렌글리콜을 주된 글리콜 성분으로 하는 폴리에스테르(폴리트리메틸렌 테레프탈레이트)가 특히 바람직하다.
이러한 폴리에스테르에는, 필요에 따라 소량(통상 30몰% 이하)의 공중합 성분을 갖고 있어도 된다. 이 때, 사용되는 테레프탈산 이외의 2관능성 카르복실산으로서는, 예를 들어 이소프탈산, 나프탈렌디카르복실산, 디페닐디카르복실산, 디페녹시에탄디카르복실산, β-히드록시에톡시벤조산, P-옥시벤조산, 5-나트륨술포이소프탈산, 아디프산, 세바스산, 1,4-시클로헥산디카르복실산과 같은 방향족, 지방족, 지환족의 2관능성 카르복실산을 들 수 있다. 또한, 상기 글리콜 이외의 디올 화합물로서는, 예를 들어 시클로헥산-1,4-디메탄올, 네오펜틸글리콜, 비스페놀 A, 비스페놀 S와 같은 지방족, 지환족, 방향족의 디올 화합물 및 폴리옥시알킬렌글리콜 등을 들 수 있다.
상기 폴리에스테르는 임의의 방법에 의해 합성한 것이어도 된다. 예를 들어 폴리에틸렌테레프탈레이트의 경우에 대하여 설명하면, 테레프탈산과 에틸렌글리콜을 직접 에스테르화 반응시키거나, 테레프탈산디메틸과 같은 테레프탈산의 저급 알킬에스테르와 에틸렌글리콜을 에스테르 교환 반응시키거나 또는 테레프탈산과 에틸렌옥사이드를 반응시키거나 하여 테레프탈산의 글리콜에스테르 및/또는 그의 저중합체를 생성시키는 제1 단계의 반응과, 제1 단계의 반응 생성물을 감압하에 가열하여 원하는 중합도가 될 때까지 중축합 반응시키는 제2 단계의 반응에 의해 제조된 것이어도 된다. 또한, 상기 폴리에스테르는, 머티리얼 리사이클 또는 케미컬 리사이클된 폴리에스테르, 또는 일본 특허 공개 제2004-270097호 공보나 일본 특허 공개 제2004-211268호 공보에 기재되어 있는 바와 같은 특정한 인 화합물 및 티타늄 화합물을 포함하는 촉매를 사용하여 얻어진 폴리에스테르여도 된다. 나아가, 폴리락트산이나 스테레오 컴플렉스 폴리락트산 등의 생분해성을 갖는 폴리에스테르여도 된다.
또한, 상기 폴리에스테르에 자외선 흡수제가 폴리에스테르 중량 대비 0.1중량% 이상(바람직하게는 0.1 내지 5.0중량%) 포함되어 있으면, 포백에 자외선 차폐성이 부가되어 바람직하다. 이러한 자외선 흡수제로서는, 벤조옥사진계 유기 자외선 흡수제, 벤조페논계 유기 자외선 흡수제, 벤조트리아졸계 유기 자외선 흡수제, 살리실산계 유기 자외선 흡수제 등이 예시된다. 그 중에서도, 방사의 단계에서 분해되지 않는다는 점에서 벤조옥사진계 유기 자외선 흡수제가 특히 바람직하다.
이러한 벤조옥사진계 유기 자외선 흡수제로서는, 일본 특허 공개 소62-11744호 공보에 개시된 것이 적합하게 예시된다. 즉, 2-메틸-3,1-벤조옥사진-4-온, 2-부틸-3,1-벤조옥사진-4-온, 2-페닐-3,1-벤조옥사진-4-온, 2,2'-에틸렌비스(3,1-벤조옥사진-4-온), 2,2'- 테트라메틸렌비스(3,1-벤조옥사진-4-온), 2,2'-p-페닐렌비스(3,1-벤조옥사진-4-온), 1,3,5-트리(3,1-벤조옥사진-4-온-2-일)벤젠, 1,3,5-트리(3,1-벤조옥사진-4-온-2-일)나프탈렌 등이다.
또한, 상기 폴리에스테르에 소광제(delusterant)(이산화티타늄)가 폴리에스테르 중량 대비 0.1중량% 이상(바람직하게는 0.2 내지 4.0중량%) 포함되어 있으면, 포백의 방투성이 향상되어 바람직하다.
또한, 상기 폴리에스테르에는, 필요에 따라 미세 구멍 형성제(유기 술폰산 금속염), 착색 방지제, 열 안정제, 난연제(삼산화이안티몬), 형광 증백제, 착색 안료, 대전 방지제(술폰산 금속염), 흡습제(폴리옥시알킬렌글리콜), 항균제, 기타 무기 입자 중 1종 이상이 포함되어 있어도 된다.
본 발명의 편지는, 상기 권축 섬유를 포함한다. 이 때, 상기 권축 섬유가 편지 중량 대비 50중량% 이상 포함되어 있는 것이 바람직하다.
본 발명의 편지에 있어서, 편지의 밀도가 60코스/2.54cm 이상(바람직하게는 60 내지 130코스/2.54cm, 보다 바람직하게는 60 내지 110코스/2.54cm) 또한 45웨일/2.54cm 이상(바람직하게는 45 내지 90웨일/2.54cm, 보다 바람직하게는 45 내지 70웨일/2.54cm)인 것이 중요하다. 편지의 밀도가 해당 범위보다도 작으면 흡수성이나 방투성이 저하될 우려가 있다.
본 발명의 편지에 있어서, 편지의 단위 면적당 중량이 130g/m2 이하(보다 바람직하게는 80 내지 120g/m2)인 것이 바람직하다. 해당 단위 면적당 중량이 130g/m2보다도 크면 속건성이 저하될 우려가 있다. 반대로, 단위 면적당 중량이 80g/m2보다도 작으면 흡수성이나 방투성이 저하될 우려가 있다.
또한, 본 발명의 편지에 있어서, 편지의 두께가 0.45mm 이하(바람직하게는 0.30 내지 0.45mm)인 것이 중요하다. 편지의 두께가 0.45mm보다도 크면 속건성이 저하될 우려가 있다. 반대로, 편지의 두께가 0.30mm보다도 작으면 흡수성이나 방투성이 저하될 우려가 있다.
본 발명의 편지에 있어서 편조직은 특별히 한정되지 않으며, 경편(warp knitting), 환편(위편) 중 어느 것이어도 된다. 층수도 단층이어도 되고, 2층 이상의 다층이어도 된다. 예를 들어, 평짜기, 니트 미스, 스무스(인터로크 스티치), 프라이스(리브 스티치), 카노코(피케 스티치), 첨사편(플레이트 스티치), 덴비, 하프 등이 적합하게 예시되지만, 이들로 한정되는 것은 아니다.
본 발명의 편지는, 상기 권축 섬유를 사용하여(필요에 따라 다른 섬유도 사용하여) 통상의 방법에 의해 제편함으로써 얻어진다.
이어서, 염색 가공을 실시하는 것이 바람직하다. 이 때, 상기 염색 가공의 온도로서는 100 내지 140℃(보다 바람직하게는 110 내지 135℃), 시간으로서는 톱 온도의 유지 시간이 5 내지 40분의 범위 내인 것이 바람직하다. 염색 가공이 실시된 편지에는, 건열 파이널 세팅을 실시하는 것이 바람직하다. 이 때, 건열 파이널 세팅의 온도로서는 120 내지 200℃(보다 바람직하게는 140 내지 180℃), 시간으로서는 1 내지 3분의 범위 내인 것이 바람직하다.
또한, 본 발명의 편지에는 흡수 가공이 실시되어 있는 것이 바람직하다. 편지에 흡수 가공을 실시함으로써, 흡수성이 향상된다. 이러한 흡수 가공으로서는, 예를 들어 폴리에틸렌글리콜디아크릴레이트나 그의 유도체, 또는 폴리에틸렌테레프탈레이트-폴리에틸렌글리콜 공중합체 등의 친수화제(흡수 가공제)를 편지에, 편지 중량에 대하여 0.25 내지 0.50중량% 부착시키는 것 등이 바람직하게 예시된다. 흡수 가공의 방법으로서는, 예를 들어 염색 가공시에 염색액에 흡수 가공제를 혼합하는 욕중 가공법이나, 건열 파이널 세팅 전에, 포백을 흡수 가공액 중에 디핑하여 맹글로 짜내는 방법, 그라비아 코팅법, 스크린 프린트법과 같은 도포에 의한 가공 방법 등이 예시된다.
나아가, 통상의 방법인 기모 가공, 자외선 차폐 혹은 항균제, 탈취제, 방충제, 축광제, 재귀 반사제(retroreflective agent), 마이너스 이온 발생제, 발수제 등의 기능을 부여하는 각종 가공을 부가 적용해도 된다.
이와 같이 하여 얻어진 편지는 상기한 권축 섬유를 포함하며, 또한 상기한 밀도 및 두께를 갖기 때문에, 흡수성, 속건성 및 방투성도 우수하다.
여기서, 편지의 표리 적어도 어느 한쪽 표면에서, JIS L1907-1998 5.1.2 바이렉법에 의해 측정한 흡수성이 7cm 이상(보다 바람직하게는 7 내지 15cm)인 것이 바람직하다.
또한, JIS L0217-1998, 103법에 의해 3회의 세탁을 행한 후의 편지의 표리 적어도 어느 한쪽 표면에서, JIS L1907-1998 5.1.2 바이렉법에 의해 측정한 흡수성이 8cm 이상(보다 바람직하게는 8 내지 16cm)인 것이 바람직하다.
또한, AATCC 시험법 201-2014에 의해 측정한 건조성(건조 속도)이 10분 이하(보다 바람직하게는 1 내지 5분)인 것이 바람직하다. 또한, JIS L0217-1998, 103법에 의해 5회의 세탁을 행한 후에 있어서, AATCC 시험법 201-2014에 의해 측정한 건조성이 12분 이하(보다 바람직하게는 1 내지 5분)인 것이 바람직하다.
또한, 방투성의 지표로서, 자외선 보호 계수 UPF가 23 이상(보다 바람직하게는 25 내지 50)인 것이 바람직하다.
또한, 본 발명에 따르면, 상기한 편지를 사용하여 이루어지는 의료, 안감, 심지, 양말, 복대, 모자, 장갑, 잠옷, 이불잇, 이불 커버, 카시트 표피재의 군으로부터 선택되는 어느 하나의 섬유 제품이 제공된다. 이러한 섬유 제품은 상기한 편지를 사용하고 있기 때문에, 흡수성, 속건성 및 방투성이 우수하다.
실시예
이하, 실시예를 들어 본 발명을 상세하게 설명하지만, 본 발명은 이들에 의해 전혀 한정되는 것은 아니다. 또한, 실시예 중의 각 물성은 하기의 방법에 의해 측정한 것이다.
(1) 토크
시료(권축사) 약 70cm를 옆으로 펴고, 중앙부에 0.18mN×표시 텍스(2mg/de)의 초하중을 매달은 후, 양끝을 한데 뭉친다. 실은 잔류 토크에 의해 회전하기 시작하지만 초하중이 정지할 때까지 그대로의 상태로 연사(撚絲)를 얻는다. 이와 같이 하여 얻은 연사를 17.64mN×표시 텍스(0.2g/de)의 하중하에 25cm 길이의 연수(撚數)를 검연기로 측정한다. 얻어진 연수(T/25cm)를 4배로 하여 토크(T/m)로 한다.
(2) 인터레이스도
교락사를 8.82mN×표시 텍스(0.1g/de)의 하중하에 1m의 길이를 취하고, 하중 제거 후, 실온에서 24시 방치 후의 결절점의 수를 판독하여, 개/m로 표시한다.
(3) 권축률
공시 사조를 둘레 길이가 1.125m인 검척기의 주위에 권취하여, 건섬도(乾纖度)가 3333dtex인 실패를 제조하였다. 상기 실패를 스케일판의 걸이못에 현수하여, 그의 하부분에 6g의 초하중을 부가하고, 600g의 하중을 더 부가했을 때의 실패의 길이 L0을 측정한다. 그 후, 즉시 상기 실패로부터 하중을 제거하고, 스케일판의 걸이못으로부터 떼어내고, 이 실패를 끓는 물 중에 30분간 침지하여, 권축을 발현시킨다. 끓는 물 처리 후의 실패를 끓는 물로부터 취출하고, 실패에 포함되는 수분을 여과지에 의해 흡수 제거하여, 실온에서 24시간 풍건한다. 이 풍건된 실패를 스케일판의 걸이못에 현수하고, 그의 하부분에 600g의 하중을 가하여 1분 후에 실패의 길이 L1a를 측정하고, 그 후 실패로부터 하중을 제거하여 1분 후에 실패의 길이 L2a를 측정한다. 공시 필라멘트 사조의 권축률(CP)을 하기 식에 의해 산출한다.
CP(%)=((L1a-L2a)/L0)×100
(4) 세탁과 건조
JIS L0217-1998, 103법에 의해 세탁을 행한 후, JIS L1096-2010, 8.24.1, A1법-2.3 텀블러에 의해 건조한다. 또한, 세탁을 3회(5회) 행할 때에는 세탁을 3회(5회) 행한 후, 건조한다.
(5) 흡수성
JIS L1907-1998 5.1.2 바이렉법에 의해 측정한다.
(6) 건조성(건조 속도)
AATCC 시험법 201-2014에 의해 측정한다.
(7) 단위 면적당 중량
JISL1018-19986.4에 의해 측정한다.
(8) 두께
JISL1018-19986.5에 의해 측정한다.
(9) 자외선 보호 계수 UPF
오스트레일리아 뉴질랜드 규격(AS/NZS;4399:1996)에 따라, 분광 광도계를 사용하여 280 내지 400nm의 자외선 투과율을 측정하고, 이것에 소정의 대미지 계수를 고려하여 산출한다.
(10) 방투성
시험자의 육안 판정에 의해 4급: 방투성이 특히 우수함, 3급: 방투성이 우수함, 2급: 보통, 1급: 방투성이 떨어짐의 4단계로 평가한다.
[실시예 1]
폴리에틸렌테레프탈레이트(소광제의 함유율 0.3중량%)를 사용하여 통상의 방사 장치로부터 280℃에서 용융 방사하고, 2800m/분의 속도로 인취하고, 연신하지 않고 권취하여, 반연신된 폴리에스테르 사조(단사 섬유의 단면 형상: 환 단면)를 얻었다.
이어서, 해당 폴리에스테르 사조를 사용하여, 연신 배율 1.6배, 가연수 2500T/m(S 방향), 히터 온도 180℃, 사속(絲速) 350m/분의 조건으로 동시 연신 가연 권축 가공을 행하였다.
또한, 상기 폴리에스테르 사조를 사용하여 연신 배율 1.6배, 가연수 2500T/m(Z 방향), 히터 온도 180℃, 사속 350m/분의 조건으로 동시 연신 가연 권축 가공을 행하였다.
이어서, 이들 S 방향의 토크를 갖는 가연 권축 가공사와 Z 방향의 토크를 갖는 가연 권축 가공사를 합사하여 공기 교락 처리를 행하여, 복합사(총 섬도 66dtex/72fil, 권축률 28%, 토크 0T/m)를 얻어 실 종류 1(권축 섬유)로 하였다. 이 때, 공기 교락 처리는, 인터레이스 노즐을 사용한 인터레이스 가공이며, 오버 피드율 1.0%, 압공압 0.3MPa(3kgf/cm2)로 50개/m의 교락을 부여하였다.
이어서, 36게이지의 환편기를 사용하여, 실 종류 1을 사용하여 도 1에 도시하는 평짜기 조직의 환편지를 편성하였다.
그리고, 해당 편지를 온도 130℃, 유지 시간 15분으로 염색 가공하였다. 이 때, 친수화제(폴리에틸렌테레프탈레이트-폴리에틸렌글리콜 공중합체)를 염색액에 대하여 2ml/l의 비율로 염색 가공시에 동욕 처리를 행함으로써, 편지에 친수화제를 부여하였다. 이어서, 해당 환편물에 온도 160℃, 시간 1분으로 건열 파이널 세팅을 실시하였다.
얻어진 편지는 흡수성이 우수하고, 또한 속건성이 우수한 것이었다. 밀도, 단위 면적당 중량, 두께 및 평가 결과를 표 1에 나타낸다. 또한, 「C」는 코스/2.54cm이고, 「W」는 웨일/2.54cm이다.
또한, 이러한 편지를 사용하여 의료를 얻어 착용한 바 흡수성이 우수하고, 또한 속건성이 우수한 것이었다.
[실시예 2]
실시예 1에 있어서, 실 종류 1의 단사수를 변경하여 마찬가지로 실 종류 1(총 섬도 66dtex/144fil, 권축률 9.5%, 토크 0T/m)을 얻었다. 또한, 사용하는 환편기의 게이지수, 실 종류 1, 밀도, 단위 면적당 중량, 두께를 표 1과 같이 변경하였다. 평가 결과를 표 1에 나타낸다.
[실시예 3]
실시예 2에 있어서 실 종류 1 뿐만 아니라, 실 종류 2로서 폴리에틸렌테레프탈레이트를 포함하는 가연 권축 가공사(총 섬도 56dtex/72fil, 권축률 26%, 토크 20T/m)도 사용하여 밀도, 단위 면적당 중량, 두께를 표 1과 같이 변경하였다. 이 때, 편조직을 도 2에 도시하는 니트 미스 조직으로 하였다. 평가 결과를 표 1에 나타낸다. 또한, 실 종류 1의 중량 비율은 55중량%였다.
[실시예 4]
실시예 3에 있어서, 실 종류 1로서 실시예 1과 동일한 것을 사용하여, 밀도, 단위 면적당 중량, 두께를 표 1과 같이 변경하였다. 평가 결과를 표 1에 나타낸다. 또한, 실 종류 1의 중량 비율은 53중량%였다.
[비교예 1]
표 1에 나타낸 바와 같이, 폴리에틸렌테레프탈레이트를 포함하는 가연 권축 가공사(총 섬도 84dtex/72fil, 권축률 18%, 토크 25T/m, 소광제의 함유율 0.3중량%)를 사용하여 편지를 얻었다. 평가 결과를 표 1에 나타낸다.
[비교예 2]
표 1에 나타낸 바와 같이, 폴리에틸렌테레프탈레이트를 포함하는 가연 권축 가공사(총 섬도 56dtex/72fil, 권축률 26%, 토크 20T/m, 소광제의 함유율 0.3중량%)를 사용하여 편지를 얻었다. 평가 결과를 표 1에 나타낸다.
[비교예 3]
표 1에 나타낸 바와 같이, 폴리에틸렌테레프탈레이트를 포함하는 가연 권축 가공사(총 섬도 84dtex/72fil, 권축률 18%, 토크 25T/m, 소광제의 함유율 0.3중량%)와 폴리에틸렌테레프탈레이트를 포함하는 가연 권축 가공사(총 섬도 56dtex/72fil, 권축률 26%, 토크 20T/m, 소광제의 함유율 0.3중량%)를 사용하여 편지를 얻었다. 평가 결과를 표 1에 나타낸다.
본 발명에 따르면, 흡수성, 속건성 및 방투성이 우수한 편지 및 섬유 제품이 제공되며, 그의 공업적 가치는 매우 크다.
Claims (15)
- 30T/m 이하의 토크를 갖는 권축 섬유를 포함하는 편지이며, 편지의 밀도가 60코스/2.54cm 이상 또한 45웨일/2.54cm 이상이고, 또한 편지의 두께가 0.45mm 이하인 것을 특징으로 하는 편지.
- 제1항에 있어서, 상기 권축 섬유가 S 방향의 토크를 갖는 가연 권축 가공사와 Z 방향의 토크를 갖는 가연 권축 가공사를 포함하는 복합사인 편지.
- 제1항 또는 제2항에 있어서, 상기 권축 섬유가 인터레이스 가공이 실시된 교락사인 편지.
- 제1항 내지 제3항 중 어느 한 항에 있어서, 상기 권축 섬유의 토크가 논토크인 편지.
- 제1항 내지 제4항 중 어느 한 항에 있어서, 상기 권축 섬유에서 단섬유 섬도가 0.3 내지 1.3dtex의 범위 내인 편지.
- 제1항 내지 제5항 중 어느 한 항에 있어서, 상기 권축 섬유에서 총 섬도가 40 내지 80dtex의 범위 내인 편지.
- 제1항 내지 제6항 중 어느 한 항에 있어서, 상기 권축 섬유가 폴리에스테르 섬유 또는 나일론 섬유를 포함하는 편지.
- 제1항 내지 제7항 중 어느 한 항에 있어서, 편지의 단위 면적당 중량이 130g/m2 이하인 편지.
- 제1항 내지 제8항 중 어느 한 항에 있어서, 편지의 두께가 0.30 내지 0.45mm의 범위 내인 편지.
- 제1항 내지 제9항 중 어느 한 항에 있어서, 편지에 친수화제가 부여되어 있는 편지.
- 제1항 내지 제10항 중 어느 한 항에 있어서, 편지의 표리 적어도 어느 한쪽 표면에서, JIS L1907-1998 5.1.2 바이렉법에 의해 측정한 흡수성이 7cm 이상인 편지.
- 제1항 내지 제11항 중 어느 한 항에 있어서, JIS L0217-1998, 103법에 의해 3회의 세탁을 행한 후의 편지의 표리 적어도 어느 한쪽 표면에서, JIS L1907-1998 5.1.2 바이렉법에 의해 측정한 흡수성이 8cm 이상인 편지.
- 제1항 내지 제12항 중 어느 한 항에 있어서, AATCC 시험법 201-2014로 측정한 건조성이 10분 이하인 편지.
- 제1항 내지 제12항 중 어느 한 항에 있어서, JIS L0217-1998, 103법에 의해 5회의 세탁을 행한 후에, AATCC 시험법 201-2014로 측정한 건조성이 12분 이하인 편지.
- 제1항 내지 제14항 중 어느 한 항에 기재된 편지를 사용하여 이루어지는 의료, 안감, 심지, 양말, 복대, 모자, 장갑, 잠옷, 이불잇, 이불 커버, 카시트 표피재의 군으로부터 선택되는 어느 하나의 섬유 제품.