KR20180047290A - 직편물의 안티클링 가공방법 및 그에 의해 제조된 직편물 - Google Patents
직편물의 안티클링 가공방법 및 그에 의해 제조된 직편물 Download PDFInfo
- Publication number
- KR20180047290A KR20180047290A KR1020160143244A KR20160143244A KR20180047290A KR 20180047290 A KR20180047290 A KR 20180047290A KR 1020160143244 A KR1020160143244 A KR 1020160143244A KR 20160143244 A KR20160143244 A KR 20160143244A KR 20180047290 A KR20180047290 A KR 20180047290A
- Authority
- KR
- South Korea
- Prior art keywords
- agent
- knitted fabric
- scouring
- water
- remainder
- Prior art date
Abstract
본 발명은 직편물의 안티클링 가공방법 및 그에 의해 제조된 직편물에 관한 것으로서 본 발명에 의해 소수성 조제의 프린팅 부분을 제외한 미세부분으로는 땀이 흡수되고, 땀이 직물표면으로 확산 증발함으로써 속건의 효과를 부여할 수 있으며, 소수성 조제가 프린트된 피부 접촉면인 이면으로는 물이 침투되기가 어려워 쾌적성을 유지할 수 있어 면제품을 사용하는 근무복이나 작업복, Golf casual wear 등의 용도로의 활용을 할 수 있다.
Description
본 발명은 직편물의 안티클링 가공방법 및 그에 의해 제조된 직편물에 관한 것이다.
최근 쾌적성과 위생관념이 강조되는 생활패턴의 변화에 따라 섬유의 고기능화 및 복합기능화를 추구하는 추세가 강화되고 있다. 흡한 속건 소재를 사용한 스포츠웨어, 항균방취의 이너웨어, 원적외선, 음이온이 방출되는 침구류, 친환경 바이오 섬유 등 최근 소비자들의 건강에 대한 관심과 의류 업체의 헬스 마케팅이 활성화되면서 건강기능 섬유시장도 확장되고 있다.
이러한 건강 섬유의 대표적 소재인 면섬유 소재는 최근 로하스 및 웰빙, 스포츠 캐주얼을 즐기는 트렌드에 편승하여 지속적인 성장을 하고 있다. 이러한 면섬유는 환경적인 장점뿐 아니라 면섬유 자체로서 다른 어떤 섬유제품과 비교해서도 피부에 닿는 감촉이 매우 부드럽고, 흡습성이 우수하며 땀의 발산이 빠르며, 중공 구조로 보온성이 우수하며, 물에 젖었을 때 오히려 강도가 높아져 세탁성이 우수하고, 알칼리와 열에 강해 세탁 및 다림질이 쉬우며, 마찰에 의한 정전기 발생이 거의 없어 피부에 불쾌감을 주지 않으며, 열전도가 타 섬유에 비해 높아 무더위에도 피부에 시원한 느낌을 주며, 섬유의 표면이 마이크로피브릴로 되어 있어 표면 감촉이 상쾌하고 드라이하며, 보습성이 뛰어나 건성피부와 같은 민감한 피부에 적합한 장점을 갖고 있다.
그러나 이러한 면섬유의 뛰어난 장점에도 불구하고 육체적 활동 후 땀을 많이 흘린 경우에는 면섬유에 흡수된 땀으로 인하여 오히려 옷이 몸에 끈적끈적 달라붙고 또한 체온을 떨어뜨리는 불편함이 있다. 면섬유의 이러한 끈적이는 성질은 "Cling"으로도 불리며, 섬유업계에서는 직편물과 피부사이의 끈적임을 의미한다. 이러한 끈적임은 의복으로 인한 불쾌감을 주는 요인 중 한가지로서 이를 해결하기 위한 방법으로 흡한 속건 제품들의 개발이 이루어 졌으며 대부분은 합성섬유를 가공하여 효과를 얻고 있는데 그치고 있으며, 면섬유에 대한 가공방법은 개발이 되지 못하는 실정이다.
그러므로 본 발명에 의하면, 면소재 직편물의 특성인 친수성에 소수성 미세가공을 통해 흡수성은 유지하면서도 육체적인 활동 후 면섬유에 흡수된 땀으로 인하여 옷이 몸에 끈적끈적 달라붙고 끈적이는 것을 방지하며 체온 유지가 가능한 쾌적성이 높고 촉감을 유지하는 면직편물을 제공하는 것을 기술적과제로 한다.
그러므로 본 발명에 의하면, 면섬유를 함유하는 직편물을 전처리 한 후,
흡습제 1~3중량%의 잔부로 물을 함유한 흡습가공액에 패딩하고 큐어링한 후,
발수제 5~10중량%, 증점제 1~3중량% 및 잔부로서 물을 함유한 소수성 조제를 사용하여 상기 직편물의 표면 또는 이면에 일정패턴으로 프린트한 후 170~180℃로 큐어링하는 것을 특징으로 하는 직편물의 안티클링 가공방법이 제공된다.
이하 본 발명을 보다 상세히 설명하기로 한다.
본 발명의 직편물의 안티클링 가공방법은 면섬유를 함유하는 직편물을 전처리한 후, 흡습가공액에 패딩하고 큐어링한 후, 일정 조성의 소수성 조제를 사용하여 상기 직편물의 표면 또는 이면에 일정패턴으로 프린트한 후 큐어링하여 천연섬유의 장점을 최대한 살리면서 육체적인 활동 후 면섬유에 흡수된 땀으로 인하여 옷이 몸에 끈적끈적 달라붙고 끈적이는 것을 방지하며 체온 유지가 가능하도록 하는 가공방법이다.
본 발명의 가공방법을 상세히 설명하자면, 우선, 면섬유를 함유하는 직편물을 전처리하는데, 가공의 대상인 면섬유를 함유하는 직편물은 면섬유만으로 구성된 직편물이어도 좋고, 면섬유와 합성섬유의 교직물 내지 혼방직편물도 무방하다.
전처리공정은 직편물을 통상의방법으로 모소(singing)한 후, 호발제 10~15g/l, 정련침투제 5~10g/l, 정련유화제 2~3g/l 및 잔부로서 물을 함유하는 디사이징제로 처리하여 디사이징한 후, 수산화나트륨 60~80g/l, 정련제 10~15g/l, 정련유화제 10~15g/l 및 잔부로서 물을 함유하는 정련제로 처리하여 정련한 후, 과산화수소 12~15g/l, 수산화나트륨 10~20g/l, 금속이온봉쇄제 5~10g/l, 정련제10~20g/l 및 잔부로서 물을 함유하는 표백제로 처리하여 표백한 후, 머서라이징 작업을 한 후, 열 셋팅하는 것으로 이루어진다. 경우에 따라서는 상기 전처리공정 중에 염색을 할 수도 있다.
이렇게 전처리를 함으로써 면섬유에 함유되어 있는 1차 협잡물 및 호제, 유제, 오염등의 2차 협잡물을 제거를 통해 염색/프린팅 성능향상과 흡수제 가공액 처리를 효율적으로 행하기 위한 준비를 하게 된다.
상기 전처리 후 흡습가공액으로 처리하고 큐어링하는데, 흡습가공액은 흡습제 1~3중량% 잔부로서 물을 함유한 흡습가공액을 사용한다.
상기 흡습가공액의 처리에 의해 면섬유에 낙하 흡수도를 개선할 수 있으며, 하기의 소수성 조제 가공 후, 빠른 땀 흡수로 보다 나은 안티클링성을 제공하기 위한 준비를 하게 된다.
상기 흡습가공 후 소수성 조제를 사용하여 상기 직편물의 표면 또는 이면에 일정패턴으로 프린트한 후 170~180℃로 큐어링하여 소수성 가공제 고착을 통한 모세관현상으로 안티클링성 작용을 부여하는데, 상기 소수성 조제는 발수제 10~15중량%, 증점제 1~3중량% 및 잔부로서 물을 함유한 소수성 조제를 사용한다. 상기 소수성 조제는 통상적인 발수제를 사용할 수 있으며, 특히 불소계발수제를 사용하는 것이 바람직하다. 상기 발수제 10중량%미만에서는 가공 후 발수제 효과가 떨어져 안티클링성 효능이 떨어지는 문제점이 발생하며, 15중량%초과시에는 흡수성이 떨어지는 문제점이 발생 할 수 있다. 상기 증점제는 통상적인 날염용 증점제를 사용할 수 있으며, 특히 아크릴계를 사용하는 것이 바람직하다. 상기 증점제 1중량%미만에서는 점도가 낮아 면섬유의 소수성 조제의 침투도가 높아짐으로 Sharpness성이 떨어져 Cling성이 떨어지며, 3중량% 초과 시에는 현장의 작업성에 문제점이 발생할 수 있다.
상기 소수성 조제의 프린팅시 상기 직편물의 표면 또는 이면에 일정패턴으로 프린팅하게 되는데, 다수의 점, 직선, 곡선, 물결무늬 등의 여러 가지 패턴으로 프린팅하여 프린트된 부분은 소수성을 갖게 하면서 프린트 되지 않은 부분은 흡습가공에 의한 흡습성이 남아 있게 하는 것이다. 직편물의 안쪽 면 즉, 피부에 닿는 면에만 프린트를 하기 때문에, 수분 또는 땀은 소수성 조제가 프린트된 부분에서는 묻지 않게 되고, 프린트 되지 않은 부분을 통해서 직편물 안쪽 면에서 흡수된 수분이 바깥쪽으로 이동되어 직편물의 표면(원단 바깥쪽)에서 땀이 증발되는 것이다. 직편물에 상기와 같이 소수성 프린트를 함으로써 직편물의 함수 능력은 현저하게 감소하고 수분이 직편물 안쪽에서 바깥쪽으로 이동함으로써 직편물의 건조 시간은 크게 단축될 수 있다. 또한, 피부에 닿는 부분에 소수성 프린트가 되어 있어 원단이 피부에 달라붙거나 끈적거릴 가능성을 줄여주어 Anti-Cling작용을 발현할 수 있다. 특히 패턴은 모세관 현상을 극대화 할 수 있는 패턴으로 하는 것이 바람직하다.
상기 패턴은 프린트후 큐어링은 170~180℃로 40~60초 동안 하는 것이 좋은데, 큐어링이 제대로 되지 못하면 세탁 시에 날염된 소수성 조제가 탈착이 많이 될 가능성이 있다.
본 발명에서는 상기 안티클링 가공방법에 의해 제조된 직편물이 제공되는데, 낙하흡수성 및 클링성이 우수하여 면제품을 사용하는 근무복이나 작업복, Golf casual wear 등의 용도로의 사용에 바람직하다.
그러므로 본 발명에 의하면, 소수성 조제의 프린팅 부분을 제외한 미세부분으로는 땀이 흡수되고, 땀이 직물표면으로 확산 증발함으로써 속건의 효과를 부여할 수 있으며, 소수성 조제가 프린트된 피부 접촉면인 이면으로는 물이 침투되기가 어려워 쾌적성을 유지할 수 있어 면제품을 사용하는 근무복이나 작업복, Golf casual wear 등의 용도로의 활용을 할 수 있다.
도 1은 본 발명의 안티클링 가공을 한 면섬유의 시험결과사진이며,
도 2는 본 발명의 안티클링 가공을 하지 않은 면섬유의 시험결과사진이다.
도 3은 본 발명의 시험장치사진이다.
도 2는 본 발명의 안티클링 가공을 하지 않은 면섬유의 시험결과사진이다.
도 3은 본 발명의 시험장치사진이다.
다음의 실시예에서는 본 발명의 안티클링 가공방법의 비한정적인 예시를 하고 있다.
[실시예 1]
면/폴리에스테르 교직물원단을 하기 표 1의 조건에 따라 전처리 한 후, 흡습제 1중량% 잔부로서 물을 함유한 흡습가공액으로 패딩 후 160℃, 60초간 큐어링한 후, 소수성 조제 10중량%, 증점제 1중량% 및 잔부로서 물을 함유한 소수성조제를 사용하여 상기 직편물의 표면에 일정패턴으로 프린트한 후 180℃로 큐어링하여 본 발명의 안티클링 가공을 완료하였다. 가공이 완료된 제품의 Cling성 Test와 낙하 흡수도 Test를 진행하여 표2 및 표 3에 나타내었다.
| Gas Singeing | 조건 | |||
| 모소방법 | 모소세기 | 이면불꽃높이 | 표면불꽃높이 | 속도 |
| 양면 | 강 | 10cm | 10cm | 80m/min |
| Desizing | ||||
| 조제 | 사용량 | During Time | During Temperature | |
| 호발제 | 10g/l | 6Hr | 75℃ | |
| 정련침투제 | 5g/l | |||
| 정련유화제 | 3g/l | |||
| Scouring | ||||
| 조제 | 사용량 | 속도 | Steamer | |
| 수산화나트륨 | 60g/l | 80m/min | 85℃ | |
| 정련제 | 10g/l | |||
| 정련유화제 | 10g/l | |||
| Bleaching | ||||
| 조제 | 사용량 | 속도 | Steamer | |
| 과산화수소 | 15g/l | 80m/min | 10℃ | |
| 수산화나트륨 | 10g/l | |||
| 금속이온봉쇄제 | 7g/l | |||
| 정련제 | 10g/l | |||
| Mercerizing | ||||
| 수산화나트륨 | 온도 | 속도 | ||
| 27Be' | 25℃ | 60m/min | ||
| Setting | ||||
| 온도 | 속도 | |||
| 210℃ | 30m/min | |||
| 구분 | 세탁 | Cling성(gf) | |||
| 좌 | 중 | 우 | 평균 | ||
| 실시예 1 | 전 | 34.25 | 38.80 | 36.33 | 36.46 |
| 5회 후 | 42.15 | 44.38 | 41.48 | 42.67 | |
| 구분 | 세탁 | 낙하흡수도 |
| sec | ||
| 실시예 1 | 전 | 2.53 |
| 5회 후 | 1.29 |
Claims (3)
- 면섬유를 함유하는 직편물을 전처리한 후,
흡습제 1~3중량%, 잔부로서 물을 함유한 흡습가공액에 패딩하고 큐어링한 후, 소수성 조제 10~15중량%, 증점제 1~3중량% 및 잔부로서 물을 함유한 소수성 조제를 사용하여 상기 직편물의 표면 또는 이면에 일정패턴으로 프린트한 후 170~180℃로 큐어링하는 것을 특징으로 하는 직편물의 안티클링 가공방법. - 제 1항에 있어서,
상기 전처리는 직편물을 모소(singing)한 후, 호발제 10~15g/l, 정련침투제 5~10g/l, 정련유화제 2~3g/l 및 잔부로서 물을 함유하는 디사이징제로 처리하여 디사이징한 후, 수산화나트륨 60~80g/l, 정련제 10~15g/l, 정련유화제 10~15g/l 및 잔부로서 물을 함유하는 정련제로 처리하여 정련한 후, 과산화수소 12~15g/l, 수산화나트륨 10~20g/l, 금속이온봉쇄제 5~10g/l, 정련제 10~20g/l 및 잔부로서 물을 함유하는 표백제로 처리하여 표백한 후, 머서라이징 작업을 한 후, 열셋팅하는 것을 특징으로 하는 직편물의 안티클링 가공방법. - 제 1항 또는 제 2항의 안티클링 가공방법에 의해 제조된 직편물.