KR20150036475A - 스위치가능한 전기적 복합 판유리 어레이 - Google Patents

스위치가능한 전기적 복합 판유리 어레이 Download PDF

Info

Publication number
KR20150036475A
KR20150036475A KR20157003411A KR20157003411A KR20150036475A KR 20150036475 A KR20150036475 A KR 20150036475A KR 20157003411 A KR20157003411 A KR 20157003411A KR 20157003411 A KR20157003411 A KR 20157003411A KR 20150036475 A KR20150036475 A KR 20150036475A
Authority
KR
South Korea
Prior art keywords
film
thermoplastic polymer
polymer film
composite sheet
spd
Prior art date
Application number
KR20157003411A
Other languages
English (en)
Other versions
KR101795192B1 (ko
Inventor
데르 바이덴 잉고 본
안드레아스 스즈네르스키
프란츠 펜네르스
줄리우스 멘니그
Original Assignee
쌩-고벵 글래스 프랑스
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 쌩-고벵 글래스 프랑스 filed Critical 쌩-고벵 글래스 프랑스
Publication of KR20150036475A publication Critical patent/KR20150036475A/ko
Application granted granted Critical
Publication of KR101795192B1 publication Critical patent/KR101795192B1/ko

Abstract

본 발명은 적어도 a. 제1 판유리(1); b. 제2 판유리(2); 및 c. 그 사이에 배열되며, 적어도 하나의 제1 열가소성 중합체 필름(3a) 및 적어도 하나의 제2 열가소성 중합체 필름(3c)와 그 사이에 배열된 SPD 필름(3b)을 갖는 중간층(3); 및 d. 중간층(3)의 외측 가장자리 영역(5)에 배열되며, 폴리이미드(PI) 및/또는 폴리이소부틸렌(PIB)을 함유하는 가장자리 밀봉부(4)를 포함하는, 스위치가능한 복합 판유리 어레이에 관한 것이다.

Description

스위치가능한 전기적 복합 판유리 어레이 {SWITCHABLE ELECTRICAL COMPOSITE PANE ARRAY}
본 발명은 전기적으로 스위치가능한 복합 판유리 배열, 그의 제조 방법, 및 자동차 및 건축 글레이징으로서의 그의 용도에 관한 것이다.
버튼을 누르면 광 투과율을 변화시키고 이렇게 해서 어두운 외관과 투명한 외관 사이에서 바뀔 수 있는 글레이징이 관련 분야에서 널리 퍼져 있다. 특히, 자동차 산업에서는 많은 가능성이 나타난다. 한여름에 및 햇빛이 강할 때, 탑승부는 창 개구를 통해서 매우 크게 가열될 수 있다. 또한, 운전자는 운전 중에 산란된 빛에 의해 눈앞이 안 보일 수 있다. 특히, 자동차의 지붕 글레이징의 경우, 자동차가 여름에 신속하게 및 강하게 가열될 수 있다. 자동차 내부의 이러한 가열은 운전자의 집중 및 반응 능력에 부정적인 영향을 미칠 뿐만 아니라, 자동차의 에너지 및 연료 소비를 상당한 정도로 증가시킨다.
예를 들어, 전기변색 글레이징 또는 액정 디스플레이(LCD)에서 판유리의 광 투과율을 조절하는데 있어서 다양한 가능성이 존재한다.
US 6,277,523 B1은 전기변색 코팅의 제작 및 작용을 기술한다. 상이한 파장의 빛에 대한 투명도가 전기 부하 적용에 의해 제어되고 조절될 수 있다.
JP 2008-025229 A1은 이중 파사드에서 광 투과율을 변화시키는 시스템을 개시한다. 이것은 건물에서 입사광의 양 및 따라서, 열의 양의 조절을 가능하게 한다. 투과율 제어는 핵생성 방법, 즉, 중간층에서의 기체 소적 형성에 의해 제어된다.
US 2004257649 A1은 전기적으로 스위치가능한 SPD 필름을 갖는 다중부분 건축 글레이징을 개시한다.
US 2005/0227061 A1은 SPD 필름(부유 입자 디바이스)를 제조하고 적층하는 방법을 개시한다. 실제 SPD 필름은 열 및 진공의 작용 하에서 접착 필름들 사이에 적층된다.
EP 2 010 385 B1은 다층 중간층을 갖는 복합 글레이징을 개시한다. 중간층은 적어도 3개의 접착 필름, 적외선 반사 기능을 갖는 층, 및 전기 디바이스를 함유한다. 이것은 액정층을 갖는 디바이스 또는 SPD 필름을 포함한다. 전기 디바이스는 접착 필름 내에 절결부 내부에 배열된다.
EP 2 013 013 B1은 적어도 3겹 중간층을 갖는 복합 글레이징을 개시한다. 가운데 중간층이 SPD 필름의 틀을 형성하고, 하부 중간층 및 상부 중간층과 함께 적층된다. 중요한 조건으로서, 중간층 물질을 가소제를 함유하지 않는다.
적층된 글레이징의 경우에 빈번한 문제는 중간 필름의 조기 노화이다. 특히, 햇빛의 UV 방사선과 함께, 수분 및 산소를 침투시키는 것은 접착 필름의 적어도 표재성 열화를 초래할 수 있다. 따라서, 가장자리 밀봉부의 품질이 전체 글레이징의 품질 및 장기 안정성에 큰 영향을 미친다. 무기 기능성 층, 특히, 금속 기능성 층이 추가로 있는 경우에는, 중간층의 노화가 상당히 더 증가한다.
노화는 글레이징의 전체 시각적 외관에 영향을 미칠 뿐만 아니라, 기능성을 상당히 저하시킬 수 있다. 특히, 글레이징의 외측 가장자리 영역에서, 글레이징의 기능성이 상당히 저하될 수 있다. SPD 필름을 갖는 글레이징의 영역에서, 이것은 가장자리 영역에서 변색이 지연되거나 또는 심지어 완전히 없을 수 있다는 것을 의미한다. 특히, 전압이 적용되지 않을 때, 글레이징은 가장자리 영역에서 점점 더 밝게 나타난다. 이 밝아짐 효과는 시간이 지남에 따라 글레이징의 전체 영역에 퍼질 수 있다.
본 발명의 목적은 기능성 층의 오래 지속되는 높은 노화 안정성을 갖는 SPD 필름을 갖는 전기적으로 스위치가능한 글레이징을 제공하는 것에 있다.
본 발명의 목적은 독립항인 청구항 1에 따라서 달성된다. 바람직한 실시양태는 종속항으로부터 드러난다.
SPD 필름을 갖는 전기적으로 스위치가능한 글레이징을 제조하는 본 발명에 따른 두 가지 방법 및 그의 용도가 추가의 독립항으로부터 드러난다.
본 발명에 따른 스위치가능한 복합 판유리 배열은 적어도 하나의 제1 판유리, 제2 판유리 및 그 사이에 배열된 중간층을 포함한다. 판유리는 바람직하게는 평평한 유리, 플로트 유리, 석영 유리, 보로실리케이트 유리, 소다석회 유리, 및/또는 그의 혼합물을 함유한다. 별법으로, 판유리는 또한 중합체, 예컨대 폴리카르보네이트 또는 폴리메틸 메타크릴레이트(플렉시글라스(Plexiglas))를 포함할 수 있다. 중간층은 적어도 하나의 제1 열가소성 중합체 필름 및 적어도 하나의 제2 열가소성 중합체 필름과 그 사이에 배열된 전기적으로 스위치가능한 투과율 가변 SPD 필름을 함유한다. SPD(부유 입자 디바이스) 필름 및 호일은 1 ㎛ 미만의 바람직한 크기 범위의 콜로이드 입자를 함유한다. 입자는 용액에, 또는 바람직하게는 중합체 매트릭스에 부유된다. 전기장 부재 하에서는, 콜로이드 입자가 매질에 랜덤하게 배열되고 배향된다. 이 상태에서는, 입사광이 흡수되거나 또는 반사되고; SPD 필름이 어둡고 불투명하게 나타난다. 전기장 적용시에는, 콜로이드 입자가 정렬된다. 입사광 빔이 통과할 수 있고, SPD 필름이 투명하게 나타난다. 전압 변동을 통해, 심지어 SPD 필름의 광 투과율의 점진적 변화도 가능하다. SPD 필름에 대한 상세한 설명은 예를 들어 US 2005/0227061 A1에서 특히 문단 [0004] 내지 [0015]에서 발견되고, 판유리와 SPD 필름의 적층 방법은 문단 [0016]에서 발견된다. 열가소성 중합체 필름은 바람직하게는 PVB(폴리비닐 부티랄) 또는 EVA(폴리에틸 비닐 아세테이트)를 함유한다. 임의로, 또한 폴리부틸렌 테레프탈레이트(PBT), 폴리카르보네이트(PC), 폴리에틸렌 테레프탈레이트(PET), 및 폴리에틸렌 나프탈레이트(PEN), 폴리비닐 클로라이드(PVC), 폴리비닐 플루오라이드(PVF), 가소제 없는 폴리비닐 부티랄(PVB), 및/또는 그의 공중합체, 특히 바람직하게는, 폴리에틸렌 테레프탈레이트(PET)도 함유될 수 있다. 전기적으로 스위치가능한 투과율 가변 SPD 필름의 외측 가장자리 영역, 바람직하게는 전체 외측 가장자리 영역에 가장자리 밀봉부가 배열된다. 바람직하게는 절연 필름으로서의 가장자리 밀봉부가 폴리이미드(PI) 및/또는 폴리이소부틸렌(PIB)을 함유한다.
본 발명과 관련해서, SPD 필름이라는 용어는 실제 활성 SPD 필름이 적어도 하나의 제1 캐리어 필름과 적어도 하나의 제2 캐리어 필름 사이에서 합치되게 배열된 다층 필름을 의미한다. SPD 필름의 이점은 스위치가능한 복합 판유리 배열의 간단한 제조에 있다. SPD 필름은 판유리 배열의 제조 전에 상대적으로 다량으로 제조될 수 있고, 제조 동안에 복합체에 간단히 삽입될 수 있고, 그 다음, 이것이 통상적인 방법에 의해 적층되어 복합 판유리를 형성한다.
캐리어 필름은 바람직하게는 적어도 하나의 열가소성 중합체, 특히 바람직하게는 폴리에틸렌 테레프탈레이트(PET)를 함유한다. 각 캐리어 필름의 두께는 바람직하게는 0.1 ㎜ 내지 1 ㎜, 특히 바람직하게는 0.1 ㎜ 내지 0.2 ㎜이다.
가장자리 밀봉부는 바람직하게는 전기적으로 스위치가능한 투과율 가변 SPD 필름의 외측 가장자리 영역에서부터 SPD 필름의 내부 표면 방향으로 적어도 1 ㎜ 연장된다. 가장자리 밀봉부는 바람직하게는 폴리이미드 호일 또는 필름을 포함한다. 본 발명과 관련해서, "외측 가장자리 영역"이라는 용어는 수평의 평평한 필름의 절결된 가장자리를 의미한다. 가장자리 밀봉부를 이용한 덮음은 중간층의 노화를 상당히 및 측정가능하게 저하시킨다. 놀랍게도, 가장자리 밀봉부의 폴리이미드 함유 조성물이 예를 들어 상업적으로 입수가능한 접착 테이프("테사필름(Tesafilm)®"[셀로판 테이프])보다 더 좋은 노화 보호를 나타낸다.
한 대안적 실시양태에서는, 가장자리 밀봉부가 중간층의 영역에서 적어도 1 ㎜ 깊이 노치로서 실시된다. 노치는 적어도 SPD 필름까지 연장되고, 폴리이소부틸렌(PIB) 및/또는 폴리우레탄(PU)으로 충전된다. 이 가장자리 밀봉부는 SPD 필름을 노화로부터 효과적으로 보호하고, 스위치가능한 판유리 배열의 유효 수명을 연장한다.
열가소성 중합체 필름은 바람직하게는 PVB(폴리비닐 부티랄) 및/또는 EVA(폴리에틸 비닐 아세테이트)를 함유한다. 놀랍게도, 폴리이미드(PI) 및/또는 폴리이소부틸렌을 함유하는 본 발명에 따른 가장자리 밀봉부와 병용된, EVA로 제조된 중합체 필름이 노화로부터 가장 높은 보호를 나타낸다. 이는 글레이징 적층 동안의 본 발명에 따른 가장자리 밀봉부 및 EVA(폴리에틸렌 비닐 아세테이트)의 매우 강한 결합에 기인한 것일 수 있다.
스위치가능한 복합 판유리 배열은 바람직하게는 제1 판유리와 제2 열가소성 중합체 필름 사이에 제3 열가소성 중합체 필름을 포함한다. 이 제3 열가소성 중합체 필름은 기계적 성질, 예를 들어 내파괴성의 개선에 기여할 수 있다. 별법으로, 제3 열가소성 필름은 또한 다른 기능, 예를 들어 태양으로부터의 보호를 위한 캐리어로서 역할을 할 수 있다.
스위치가능한 복합 판유리 배열은 바람직하게는 제3 열가소성 중합체 필름과 제2 열가소성 중합체 필름 사이에 IR(적외선) 방사선 반사 코팅을 포함한다.
IR-방사선 반사 코팅은 바람직하게는 니오븀, 탄탈럼, 몰리브데넘, 지르코늄, 은, 금, 알루미늄, 니켈, 크로뮴, 구리, 및/또는 그의 혼합물 또는 합금을 함유한다.
전기적으로 스위치가능한 투과율 가변 SPD 필름은 바람직하게는 제1 열가소성 중합체 필름 및 제2 열가소성 중합체 필름보다 1 ㎜ 내지 4 ㎜ 더 후방에 위치하는 가장자리(절결부)를 갖는다. 이것은 SPD 필름을 둘러싸는 제1 열가소성 필름 및 제2 열가소성 필름이 SPD 필름의 외측 가장자리를 지나서 1 ㎜ 내지 4 ㎜만큼 연장되는 효과를 갖는다. 본 발명에 따른 가장자리 밀봉부와 함께, 이 열가소성 필름 돌출은 SPD 필름 및 전체의 스위치가능한 복합 판유리 배열의 내노화성을 상당히 증가시킨다.
가장자리 밀봉부는 바람직하게는 폴리우레탄으로 제조된 외피를 포함하고, 이것은 내노화성을 추가로 증가시킨다.
전기적으로 스위치가능한 투과율 가변 SPD 필름은 바람직하게는 100 ㎛ 내지 500 ㎛, 바람직하게는 150 ㎛ 내지 400 ㎛의 두께를 갖는다.
전기적으로 스위치가능한 투과율 가변 SPD 필름은 바람직하게는 전기 접촉부를 포함한다. 전기 접촉부는 전압원 및 제어 요소에 연결되고, 이렇게 해서 이것은 스위치가능한 복합 판유리 배열의 투과율의 변화, 바람직하게는 심지어 점진적 변화를 가능하게 한다.
바람직하게는, 가장자리 밀봉부는 폴리아크릴 접착제를 갖는다. 바람직한 실시양태에서, 가장자리 밀봉부는 절연 필름으로서 실시되고, 폴리아크릴 접착제가 전기적으로 스위치가능한 SPD 필름 상에 절연 필름을 고정시킨다.
추가로, 본 발명은 스위치가능한 복합 판유리 배열의 제조 방법을 포함한다. 제1 단계에서는, 전기적으로 스위치가능한 투과율 가변 SPD 필름을 그의 가장자리 영역에서 폴리이미드(PI)를 함유하는 가장자리 밀봉부(4)로 피복한다. 가장자리 밀봉부는 바람직하게는 폴리아크릴 접착제를 갖는 폴리이미드 필름을 포함하는 절연 필름으로서 실시된다. 피복된 전기적으로 스위치가능한 투과율 가변 SPD 필름은 필름을 형성한다.
다음 단계에서는, 이 필름을 제1 열가소성 중합체 필름과 제2 열가소성 중합체 필름 사이에 배열하여 중간층을 형성한다. 제1 열가소성 중합체 필름 및 제2 열가소성 중합체 필름은 열가소성 중합체 필름들이 전기적으로 스위치가능한 투과율 가변 SPD 필름보다 적어도 2 ㎜ 더 큰 외측 가장자리 돌출부를 갖도록 배열된다. 바람직하게는, 전기적으로 스위치가능한 투과율 가변 SPD 필름에는 또한 전기 접촉부가 제공된다.
다음 단계에서는, 제1 판유리와 제2 판유리 사이에 중간층을 적층한다. 추가의 단계에서는, 또한, 결과적으로 얻은 복합 글레이징에 전기 제어 디바이스를 제공할 수 있다.
추가로, 본 발명은 스위치가능한 복합 판유리 배열을 제조하는 대안적 방법을 포함한다. 전기적으로 스위치가능한 투과율 가변 SPD 필름을 제1 열가소성 중합체 필름과 제2 열가소성 중합체 필름 사이에 배열하여 중간층을 형성한다.
이어서, 중간층을 제1 판유리와 제2 판유리 사이에 적층한다.
다음 단계에서는, 전기적으로 스위치가능한 투과율 가변 SPD 필름의 영역에 1 ㎜ 내지 5 ㎜ 깊이 노치를 밀링한다. 다음 단계에서는, 노치에 폴리이소부틸렌(PIB)을 충전한 다음 폴리우레탄(PU)을 충전한다.
추가로, 본 발명은 본 발명에 따른 스위치가능한 복합 판유리 배열의 자동차 글레이징, 선박 글레이징, 열차 글레이징, 항공기 글레이징 및/또는 건축 글레이징으로서의 용도를 포함한다.
본 발명을 다음에서 도면과 관련해서 설명한다. 도면은 순전히 개략적으로 나타낸 것이고, 비율에 충실하지 않는다. 그것은 결코 본 발명을 제한하지 않는다.
도 1은 선행 기술에 따른 전기적으로 스위치가능한 복합 판유리 배열의 단면도이다.
도 2는 본 발명에 따른 전기적으로 스위치가능한 복합 판유리 배열의 단면도이다.
도 3은 본 발명에 따른 바람직한 전기적으로 스위치가능한 복합 판유리 배열의 단면도이다.
도 4는 본 발명에 따른 또 다른 바람직한 전기적으로 스위치가능한 복합 판유리 배열의 단면도이다.
도 5는 본 발명에 따른 전기적으로 스위치가능한 복합 판유리 배열 제조의 흐름도이다.
도 6은 본 발명에 따른 전기적으로 스위치가능한 복합 판유리 배열의 또 다른 제조의 흐름도이다.
도 1은 선행 기술에 따른 전기적으로 스위치가능한 복합 판유리 배열의 단면도를 묘사한다. 열가소성 중간층(3)이 제1 판유리(1)와 제2 판유리(2) 사이에 배열된다. 열가소성 중간층(3)은 하나의 제1 열가소성 중합체 필름(3a) 및 하나의 제2 열가소성 중합체 필름(3c)과 그 사이에 배열된 전기적으로 스위치가능한 투과율 가변 SPD 필름(3b)을 포함한다. 전기적으로 스위치가능한 투과율 가변 SPD 필름(3b)에 전기 접촉부(나타내지 않음)에 의해 전압원이 연결된다.
도 2는 본 발명에 따른 전기적으로 스위치가능한 복합 판유리 배열의 단면도를 묘사한다. 열가소성 중간층(3)이 제1 판유리(1)와 제2 판유리(2) 사이에 배열된다. 열가소성 중간층(3)은 하나의 제1 열가소성 중합체 필름(3a) 및 하나의 제2 열가소성 중합체 필름(3c)과 그 사이에 배열된 전기적으로 스위치가능한 투과율 가변 SPD 필름(3b)을 포함한다. 전기적으로 스위치가능한 투과율 가변 SPD 필름(3b)의 외측 가장자리 영역(5)에 가장자리 밀봉부(4)가 배열된다. 가장자리 밀봉부는 폴리이미드(PI)를 함유하고, 가장자리 밀봉부(4)는 외측 가장자리 영역(5)에서부터 연장되고, 제1 열가소성 중합체 필름(3a)과 제2 열가소성 중합체 필름(3c) 사이에서, SPD 필름(3b)의 (I) 위로 및 (II) 아래로 1 ㎜ 이상의 길이(L)를 갖는다. 가장자리 밀봉부(4)는 바람직하게는 폴리이미드 필름으로서 실시된다.
도 3은 본 발명에 따른 바람직한 전기적으로 스위치가능한 복합 판유리 배열의 단면도를 묘사한다. 기본 구조는 도 2에 묘사된 것에 상응한다. 추가로, 제3 열가소성 중합체 필름(3d)이 제1 판유리(1)와 중간층(3) 사이에 배열된다. 게다가, IR 방사선 반사 코팅(6), 예를 들어 은이 제3 열가소성 중합체 필름(3d)과 중간층(3) 사이에 배열된다.
도 4는 본 발명에 따른 대안적인 바람직한 전기적으로 스위치가능한 복합 판유리 배열의 단면도를 묘사한다. 기본 구조는 가장자리 밀봉부(4)를 제외하고는 도 2에 묘사된 것에 상응한다. 폴리이소부틸렌 및 폴리우레탄으로 제조된 가장자리 밀봉부(4)로 충전된 노치(7)가 중간층(3)의 가장자리 영역에 위치한다.
도 5는 본 발명에 따른 전기적으로 스위치가능한 복합 판유리 배열 제조의 흐름도를 나타낸다. 제1 단계에서는, 전기적으로 스위치가능한 투과율 가변 SPD 필름(3b)을 그의 외측 가장자리 영역에서 폴리이미드(PI)를 함유하는 가장자리 밀봉부(4)로 피복한다. 가장자리 밀봉부(4)는 바람직하게는 폴리아크릴 접착제와 함께 폴리이미드 필름을 포함하는 절연 필름으로서 실시된다. 피복된 전기적으로 스위치가능한 투과율 가변 SPD 필름(3b)은 필름을 형성한다. 다음 단계에서는, 상기 필름보다 열가소성 중합체 필름(3a, 3c)이 적어도 2 ㎜ 더 큰 가장자리 돌출부를 갖도록 상기 필름이 제1 열가소성 중합체 필름과 제2 열가소성 중합체 필름 사이에 배열된다. 마지막 단계(묘사되지 않음)에서는, 전기적으로 스위치가능한 투과율 가변 SPD 필름(3b)에 또한 전기 접촉부 및 전기 제어기를 제공한다.
도 6은 본 발명에 따른 전기적으로 스위치가능한 복합 판유리 배열의 대안적 제조의 흐름도를 묘사한다. 전기적으로 스위치가능한 투과율 가변 SPD 필름(3b)을 제1 열가소성 중합체 필름(3a)과 제2 열가소성 중합체 필름(3c) 사이에 배열하여 중간층(3)을 형성한다. 이어서, 결과적으로 얻은 중간층(3)을 제1 판유리(1)와 제2 판유리(2) 사이에 적층한다. 다음 단계에서는, 전기적으로 스위치가능한 투과율 가변 SPD 필름(3b)의 영역에서 중간층(3) 내로 적어도 1 ㎜의 노치(7)를 밀링한다. 다음 단계에서는, 노치(7)에 폴리이소부틸렌(PIB)을 충전한다. 폴리이소부틸렌 경화 후, 그 다음, 노치(7)를 폴리우레탄 (PU)으로 밀봉한다.
다음에서 본 발명을 2개의 실시예 및 1개의 비교 실시예와 관련해서 상세히 설명한다. 실시예들은 결코 본 발명을 제한하지 않는다.
1. 실시예(본 발명에 따름)
유리 복합 판유리(20 ㎝ x 20 ㎝)를 하기 구조(두께를 표시함): 제1 판유리(1) (2.1 ㎜), 제1 열가소성 중합체 필름(3a)(EVA, 0.38 ㎜), SPD 필름(3b)(0.35 ㎜), 제2 열가소성 중합체 필름(3c)(EVA, 0.38 ㎜), 은 코팅을 갖는 PET (6)(0.05 ㎜), 제3 열가소성 중합체 필름(3c)(EVA, 0.38 ㎜), 제2 판유리(2)(2.1 ㎜)를 포함시켜 제조하였다. 도 2 및 3에 묘사된 바와 같이 SPD 필름(3b)을 가장자리 영역에서 폴리이미드 필름으로 제조된 가장자리 밀봉부(4)로 피복하였다. EVA로 제조된 열가소성 필름(3a, 3c)은 SPD 필름(3b)에 비해 대략 2 ㎜의 돌출부를 가졌다. 유리 복합 판유리를 90℃에서 28 일 동안 가열 상태에서 저장하고, 90℃에서 1000 시간 동안 WOM 시험(내후성 시험기 시험)을 수행하고, 1250 W/h*㎡의 에너지로 크세논 램프(PV3929)로 조사하였다.
2. 실시예(본 발명에 따름)
유리 복합 판유리(20 ㎝ x 20 ㎝)를 하기 구조(두께를 표시함): 제1 판유리(1) (2.1 ㎜), 제1 열가소성 중합체 필름(3a)(EVA, 0.38 ㎜), SPD 필름(3b)(0.35 ㎜), 제2 열가소성 중합체 필름(3c)(EVA, 0.38 ㎜), 은 코팅을 갖는 PET (6)(0.05 ㎜), 제3 열가소성 중합체 필름(3c)(EVA, 0.38 ㎜), 제2 판유리(2)(2.1 ㎜)를 포함시켜 제조하였다. 도 4에 묘사된 바와 같이 SPD 필름(3b)을 가장자리 영역에서 폴리이소부틸렌 및 폴리우레탄으로 제조된 가장자리 밀봉부(4)로 피복하였다. 유리 복합 판유리를, 실시예 1에서와 같이, 90℃에서 28 일 동안 가열 상태에서 저장하고, 90℃에서 1000 시간 동안 WOM 시험(내후성 시험기 시험)을 수행하고, 1250 W/h*㎡의 에너지로 크세논 램프(PV3929)로 조사하였다.
3. 비교 실시예(선행 기술)
실시예 1 및 2의 것에 상응하되 SPD 필름(3b)의 밀봉부는 없는 유리 복합 판유리를 제조하였다. 유리 복합 판유리를 실시예 1 및 2에서처럼 90℃에서 28 일 동안 가열 상태에서 저장하고, 90℃에서 1000 시간 동안 WOM 시험을 수행하고, 1250 W/h*㎡의 에너지로 크세논 램프(PV3929)로 조사하였다.
실시예의 시험의 결과를 표 1에 제시하였다. 실시예에서, "가열 상태에서 저장" 및 "WOM 시험"을 수행한 후 SPD 필름의 가장자리 영역에서 변성을 측정하였다. SPD 필름의 변성은 전원이 끊긴 상태에서 SPD 필름의 밝아짐에 의해 입증된다. 표 1은 전원이 끊긴 상태에서 밝게 나타나는 SPD 필름의 가장자리 영역의 크기(㎜)를 나타낸다. 이렇게 해서, 이 영역은 더 이상 (완전히) 기능적이지 않다.
Figure pct00001
본 발명에 따른 실시예 1 및 실시예 2는 가열 상태에서 저장 및 또한 WOM 시험 둘 모두에서 SPD 필름의 가장자리에서 아주 최소한의 무시할 수 있는 손상을 나타낼 뿐이다. 즉, 기능을 하는 가장자리 영역의 감소가 시험 조건에 따라 0.5 ㎜와 2 ㎜ 사이에서 달라진다. 비교 실시예 3에서는, SPD 필름의 가장자리 손상(> 5 ㎜)이 본 발명에 따른 실시예에서보다 2.5 내지 10 배 더 높다. 이 결과는 놀라운 것이었고, 관련 분야의 기술자에게 자명한 것이 아니다. 상업적으로 입수가능한 테사필름®을 이용한 SPD 필름의 절연은 비교 실시예 3과 유사한 값을 내놓는다.
1: 제1 판유리
2: 제2 판유리
3: 중간층
3a: 제1 열가소성 중합체 필름
3b: 전기적으로 스위치가능한 투과율 가변 SPD 필름
3c: 제2 열가소성 중합체 필름
3d: 제3 열가소성 중합체 필름
4: 가장자리 밀봉부
5: 외측 가장자리 영역
6: IR-방사선 반사 코팅
7: 노치
L: SPD 필름을 따르는 가장자리 밀봉부의 길이
I: SPD 필름의 위 표면
II: SPD 필름의 아래 표면

Claims (15)

  1. 적어도
    a. 제1 판유리(1),
    b. 제2 판유리(2), 및
    c. 제1 판유리(1)와 제2 판유리(2) 사이에 배열되며, 적어도 하나의 제1 열가소성 중합체 필름(3a) 및 적어도 하나의 제2 열가소성 중합체 필름(3c)과 그 사이에 배열된 적어도 하나의 SPD 필름(3b)을 함유하는 중간층(3), 및
    d. 중간층(3)의 외측 가장자리 영역(5)에 배열되며, 폴리이미드(PI) 및/또는 폴리이소부틸렌(PIB)을 함유하는 가장자리 밀봉부(4)
    를 포함하는 스위치가능한 복합 판유리 배열.
  2. 제1항에 있어서, 가장자리 밀봉부(4)가 SPD 필름(3b)을 외측 가장자리 영역(5)에서 덮고, SPD 필름(3b)의 내부 표면(I, II)의 위로 및 아래로 적어도 1 ㎜의 길이 (L)를 갖는 것인 스위치가능한 복합 판유리 배열.
  3. 제2항에 있어서, 가장자리 밀봉부(4)가 폴리이미드 필름을 포함하는 것인 스위치가능한 복합 판유리 배열.
  4. 제1항에 있어서, 중간층(3)의 영역에서 적어도 1 ㎜ 깊이의 노치(7)가 폴리이소부틸렌(PIB) 및/또는 폴리우레탄(PU)으로 충전된 것인 스위치가능한 복합 판유리 배열.
  5. 제1항 내지 제4항 중 어느 한 항에 있어서, 제1 판유리(1)와 제2 열가소성 중합체 필름(3c) 사이에 제3 열가소성 중합체 필름(3d)이 배열된 것인 스위치가능한 복합 판유리 배열.
  6. 제5항에 있어서, 제3 열가소성 중합체 필름(3d)과 제2 열가소성 중합체 필름(3c) 사이에 IR 방사선 반사 코팅(6)이 배열된 것인 스위치가능한 복합 판유리 배열.
  7. 제6항에 있어서, IR 방사선 반사 코팅(6)이 니오븀, 탄탈럼, 몰리브데넘, 지르코늄, 은, 금, 알루미늄, 니켈, 크로뮴, 구리, 및/또는 그의 혼합물 또는 합금을 함유하는 것인 스위치가능한 복합 판유리 배열.
  8. 제1항 내지 제7항 중 어느 한 항에 있어서, 열가소성 중합체 필름(3a, 3c, 3d)이 PVB(폴리비닐 부티랄) 및/또는 EVA(폴리에틸 비닐 아세테이트), 특히 바람직하게는 EVA(폴리에틸 비닐 아세테이트)를 함유하는 것인 스위치가능한 복합 판유리 배열.
  9. 제1항 내지 제8항 중 어느 한 항에 있어서, SPD 필름(3b)이 제1 열가소성 중합체 필름(3a) 및 제2 열가소성 중합체 필름(3c)에 비해 1 ㎜ 내지 4 ㎜만큼 후방에 위치하는 외부 가장자리(절결부)를 갖는 것인 스위치가능한 복합 판유리 배열.
  10. 제1항 내지 제9항 중 어느 한 항에 있어서, SPD 필름(3b)이 100 ㎛ 내지 500 ㎛, 바람직하게는 150 ㎛ 내지 400 ㎛의 두께를 갖는 것인 스위치가능한 복합 판유리 배열.
  11. 제1항 내지 제10항 중 어느 한 항에 있어서, SPD 필름(3b)이 전기 접촉부를 포함하는 것인 스위치가능한 복합 판유리 배열.
  12. 제1항 내지 제11항 중 어느 한 항에 있어서, 가장자리 밀봉부(4)가 폴리아크릴 접착제를 포함하는 것인 스위치가능한 복합 판유리 배열.
  13. a. SPD 필름(3b)을 그의 외측 가장자리 영역에서, 폴리이미드(PI)를 함유하는 가장자리 밀봉부(4)로 피복하여 필름을 얻고,
    b. 이 필름을 제1 열가소성 중합체 필름(3a)과 제2 열가소성 중합체 필름(3c) 사이에 배열하여 중간층(3)을 형성하고, 여기서 제1 열가소성 중합체 필름(3a) 및 제2 열가소성 중합체 필름(3c)은 기능성 필름(7)보다 적어도 2 ㎜만큼 더 큰 외측 가장자리 돌출부를 가지며,
    c. 중간층(3) 및 필름을 제1 판유리(1)와 제2 판유리(2) 사이에 적층하는 것인,
    스위치가능한 복합 판유리 배열의 제조 방법.
  14. a. SPD 필름(3b)을 제1 열가소성 중합체 필름(3a)과 제2 열가소성 중합체 필름(3c) 사이에 배열하여 중간층(3)을 얻고,
    b. 중간층(3)을 제1 판유리(1)와 제2 판유리 사이에서 적층하고,
    c. SPD 필름(3b)의 영역에 적어도 1 ㎜ 깊이의 노치(7)를 밀링하거나 또는 스크래칭하고,
    d. 노치를 폴리이소부틸렌(PIB) 및 이어서 폴리우레탄(PU)으로 충전하는 것인,
    스위치가능한 복합 판유리 배열의 제조 방법.
  15. 자동차 글레이징, 선박 글레이징, 열차 글레이징, 항공기 글레이징 및/또는 건축 글레이징으로서의, 제1항 내지 제12항 중 어느 한 항에 따른 스위치가능한 복합 판유리 배열의 용도.
KR1020157003411A 2012-08-09 2013-06-28 스위치가능한 전기적 복합 판유리 어레이 KR101795192B1 (ko)