KR20130040722A - 개선된 안료 분산성을 갖는 광기전력 모듈용 후면 필름 - Google Patents
개선된 안료 분산성을 갖는 광기전력 모듈용 후면 필름 Download PDFInfo
- Publication number
- KR20130040722A KR20130040722A KR20120113293A KR20120113293A KR20130040722A KR 20130040722 A KR20130040722 A KR 20130040722A KR 20120113293 A KR20120113293 A KR 20120113293A KR 20120113293 A KR20120113293 A KR 20120113293A KR 20130040722 A KR20130040722 A KR 20130040722A
- Authority
- KR
- South Korea
- Prior art keywords
- layer
- layer according
- weight
- polyamide
- molding composition
- Prior art date
Abstract
a) I. 35 중량% 이상의 폴리아미드 함량 및
II. 1 내지 65 중량%의 광-반사 충전제 함량
을 포함하는 성형 조성물의 제1 외부층, 및
c) I. 35 중량% 이상의 폴리아미드 함량 및
II. 1 내지 65 중량%의 충전제 함량
을 갖는 성형 조성물의 제2 외부층
을 포함하며, 여기서 상기 백분율은 각각 전체 성형 조성물을 기준으로 한 것인 필름에서,
a)에 따른 층의 성형 조성물 및/또는 c)에 따른 층의 성형 조성물에서 폴리아미드 성분으로서 폴리에테르에스테르아미드 및 폴리에테르아미드로부터 선택되는 폴리아미드 엘라스토머는, a)에 따른 층의 성형 조성물 및/또는 c)에 따른 층의 성형 조성물이 1 내지 25 중량%의 폴리아미드 엘라스토머를 함유하도록 사용된다. 이러한 필름은 태양전지가 포매된 밀봉층에 a)에 따른 층을 결합시키는 것에 의해, 광기전력 모듈의 후면 커버로 사용된다.
II. 1 내지 65 중량%의 광-반사 충전제 함량
을 포함하는 성형 조성물의 제1 외부층, 및
c) I. 35 중량% 이상의 폴리아미드 함량 및
II. 1 내지 65 중량%의 충전제 함량
을 갖는 성형 조성물의 제2 외부층
을 포함하며, 여기서 상기 백분율은 각각 전체 성형 조성물을 기준으로 한 것인 필름에서,
a)에 따른 층의 성형 조성물 및/또는 c)에 따른 층의 성형 조성물에서 폴리아미드 성분으로서 폴리에테르에스테르아미드 및 폴리에테르아미드로부터 선택되는 폴리아미드 엘라스토머는, a)에 따른 층의 성형 조성물 및/또는 c)에 따른 층의 성형 조성물이 1 내지 25 중량%의 폴리아미드 엘라스토머를 함유하도록 사용된다. 이러한 필름은 태양전지가 포매된 밀봉층에 a)에 따른 층을 결합시키는 것에 의해, 광기전력 모듈의 후면 커버로 사용된다.
Description
본 발명은 개선된 안료 및 충전제 분산성을 갖는 폴리아미드-함유 태양광 모듈용 후면 커버로서의 다층 필름에 관한 것이다.
흔히 광기전력 모듈이라고도 지칭되는 태양광 모듈은, 태양광으로부터 전력을 발생시키는 역할을 하고, 태양전지 시스템을 코어층으로서 포함하는 라미네이트로 이루어진다. 이러한 코어층은 기계적 영향 및 기후-관련 영향으로부터 보호하는 역할을 하는 캡슐화 물질로 감싸진다.
여기서 활성 태양전지는 전면 커버와 후면 커버 사이에 존재한다. 전면 커버는 투명하며 일반적으로 유리로 이루어져 있고, 흔히 에틸렌-비닐 아세테이트 공중합체로 이루어진 접착촉진제 층에 의해, 태양전지를 포함하는 층에 결합된다. 후면 커버는 전기적 차단을 보장하고, 자외선광과 같은 기후 영향으로부터 보호하는 역할 및 수분 장벽으로서의 역할을 한다.
후면 커버의 경우, 현재 플루오로중합체 필름 및 폴리에스테르로 구성된 필름 복합체가 표준으로 사용되고 있다. 외부의 플루오로중합체 필름은 내후성을 보장하고, 폴리에스테르 필름은 기계적 안정성 및 목적한 전기적 절연성을 보장한다. 내부의 추가 플루오로중합체 필름은 태양전지 시스템의 밀봉층에 부착되는 역할을 한다. 그러나, 이러한 플루오로중합체 필름은 태양전지 자체를 위한 포매(embedding) 물질로서 사용되는 밀봉층에 대해 단지 낮은 접착력을 가진다. 또한, 플루오로중합체 필름은 단지 미미한 정도로만 전기적 절연에 기여하고, 이로 인해 비교적 두꺼운 폴리에스테르 필름을 사용할 필요가 있게 된다.
따라서, WO 2008138022는 이러한 복합체 내의 두 플루오로중합체 필름을 나일론-12 (PA12)의 필름으로 대체할 것을 제안한다. 그의 개발에 있어서, WO 2011066595는 태양전지 대향 열가소성 층은 이산화티타늄과 같은 광-반사 충전제를 포함하고, 태양전지로부터 멀리 있는 열가소성 층은 유리 섬유, 규회석 또는 운모와 같은 제2 충전제를 포함으로써 상기 층의 보다 높은 열전도도를 야기하는 것을 제안한다. 예시적인 열가소성 물질은 폴리아미드, 폴리에스테르 또는 폴리아미드와 폴리올레핀의 블렌드의 군으로부터 비롯된다. PA11, PA12 및 PA1010, 및 이들과 폴리올레핀의 블렌드가 명시적으로 언급된다.
이러한 광기전력 모듈에서, 광-반사 충전제의 분포는 특히 중요하다. 따라서, 태양전지의 반사 수준 및 그에 따른 출력은 분산성의 증가에 따라 증가한다. 또한, 분포의 양호한 정도는 동시에 후면 필름의 표면 질에 영향을 준다. 이는 실제의 태양전지에 대향해 있고 외부에서 눈에 보이는, 후면 커버의 일반적으로 순수한 폴리아미드-기재 층에서 각별히 중요한데, 안료 집괴는 얇은 층 두께로 인해 여기서 특히 분명해지기 때문이다.
따라서, 본 발명의 목적은 광기전력 모듈 후면 필름의 2개 외부층에서 개선된 안료 및 충전제 분산성을 달성하는 것이다.
놀랍게도, 폴리에테르에스테르아미드 또는 폴리에테르아미드 유형의 폴리아미드 엘라스토머를 사용함으로써 상기 목적을 달성할 수 있음을 발견하였다.
그러므로, 본 발명은
a) I. 35 중량% 이상, 바람직하게는 40 중량% 이상, 더 바람직하게는 45 중량% 이상, 특히 바람직하게는 50 중량% 이상, 가장 바람직하게는 55 중량% 이상의 폴리아미드 함량, 및
II. 1 내지 65 중량%, 바람직하게는 2 내지 60 중량%, 더 바람직하게는 3 내지 55 중량%, 특히 바람직하게는 4 내지 50 중량%, 가장 바람직하게는 5 내지 45 중량%의 광-반사 충전제 함량
을 포함하는 성형 조성물의 제1 외부층,
b) 임의로 열가소성 성형 조성물의 중간층, 및
c) I. 35 중량% 이상, 바람직하게는 40 중량% 이상, 더 바람직하게는 45 중량% 이상, 특히 바람직하게는 50 중량% 이상, 가장 바람직하게는 55 중량% 이상의 폴리아미드 함량, 및
II. 1 내지 65 중량%, 바람직하게는 2 내지 60 중량%, 더 바람직하게는 3 내지 55 중량%, 특히 바람직하게는 4 내지 50 중량%, 가장 바람직하게는 5 내지 45 중량%의 충전제 함량
을 갖는 성형 조성물의 제2 외부층
을 포함하는 필름이며, 여기서 상기 백분율은 각각 전체 성형 조성물을 기준으로 한 것이고, 필름 복합체가 a)에 따른 층의 성형 조성물 및/또는 c)에 따른 층의 성형 조성물에서 폴리아미드 성분으로서 폴리에테르에스테르아미드 및 폴리에테르아미드로부터 선택되는 폴리아미드 엘라스토머를, a)에 따른 층의 성형 조성물 및/또는 c)에 따른 층의 성형 조성물이 1 내지 25 중량%, 바람직하게는 2 내지 20 중량%, 더 바람직하게는 4 내지 20 중량%의 폴리아미드 엘라스토머를 함유하도록 사용하는 것에 의해 변형되는 것인 필름을 제공한다.
이 경우, a), b) 및 c)에 따른 층들은 바람직하게는 서로 직접적으로 이어져 있다. 또한, a)에 따른 층 및 c)에 따른 층이 둘 다 폴리아미드 엘라스토머를 포함하는 것이 바람직하다. 일부 경우에는, a)에 따른 층과 b)에 따른 층 사이 및/또는 b)에 따른 층과 c)에 따른 층 사이의 층 접착력을 접착촉진제의 삽입에 의해서 개선시킬 수 있다.
폴리아미드는 부분 결정질 폴리아미드, 예를 들어 PA6, PA66, PA610, PA612, PA10, PA810, PA106, PA1010, PA11, PA1011, PA1012, PA1210, PA1212, PA814, PA1014, PA618, PA512, PA613, PA813, PA914, PA1015, PA11, PA12, 또는 폴리프탈아미드 (PPA)라고 불리는 반-방향족 폴리아미드일 수 있다. (폴리아미드의 명명법은 국제 표준에 상응하며, 첫 번째 숫자(들)는 출발 디아민의 탄소 원자의 개수를 나타내고, 마지막 숫자(들)는 디카르복실산의 탄소 원자의 개수를 나타낸다. 단 하나의 숫자가 언급되는 경우에는, 출발 물질이 α,ω-아미노카르복실산 또는 이로부터 유도된 락탐임을 의미하고; 나머지에 대해서는, 문헌 [H. Domininghaus, Die Kunststoffe und ihre Eigenschaften [The polymers and their properties], pages 272 ff., VDI-Verlag, 1976]을 참고하도록 한다.) 적합한 PPA는 예를 들어 PA66/6T, PA6/6T, PA6T/MPMDT (MPMD는 2-메틸펜타메틸렌디아민을 나타냄), PA9T, PA10T, PA11T, PA12T, PA14T, 및 이들 후자의 유형과 지방족 디아민 및 지방족 디카르복실산 또는 ω-아미노카르복실산 또는 락탐과의 공중축합물(copolycondensate)이다. 부분 결정질 폴리아미드는, 제2 가열 단계 및 용융 피크의 적분에서 ISO 11357에 따른 DSC 방법에 의해 측정된, 25 J/g 초과의 융합 엔탈피를 갖는다.
폴리아미드는 반결정질 폴리아미드일 수도 있다. 반결정질 폴리아미드는, 제2 가열 단계 및 용융 피크의 적분에서 ISO 11357에 따른 DSC 방법에 의해 측정된, 4 내지 25 J/g의 융합 엔탈피를 갖는다. 적합한 반결정질 폴리아미드의 예는
- 35 내지 65%의 트랜스,트랜스 이성질체 함량을 갖는 4,4'-디아미노디시클로헥실메탄으로부터 기인하는, 4,4'-디아미노디시클로헥실메탄과 1,10-데칸이산 또는 1,12-도데칸이산의 폴리아미드 (PA PACM10 및 PA PACM12);
- 상기에서 언급된 부분 결정질 폴리아미드를 기재로 하는 공중합체; 및
- 상기에서 언급된 부분 결정질 폴리아미드와 상용성 무정형 폴리아미드의 블렌드이다.
폴리아미드는 무정형 폴리아미드일 수도 있다. 무정형 폴리아미드는, 제2 가열 단계 및 용융 피크의 적분에서 ISO 11357에 따른 DSC 방법에 의해 측정된, 4 J/g 미만의 융합 엔탈피를 갖는다. 무정형 폴리아미드의 예는
- 테레프탈산 및/또는 이소프탈산과, 2,2,4- 및 2,4,4-트리메틸헥사메틸렌디아민의 이성질체 혼합물의 폴리아미드,
- 이소프탈산과 1,6-헥사메틸렌디아민의 폴리아미드,
- 테레프탈산/이소프탈산 혼합물과, 임의로는 4,4'-디아미노디시클로헥실메탄과의 혼합물로서의 1,6-헥사메틸렌디아민의 코폴리아미드,
- 테레프탈산 및/또는 이소프탈산과 3,3'-디메틸-4,4'-디아미노디시클로헥실메탄과 라우로락탐 또는 카프로락탐의 코폴리아미드,
- 1,12-도데칸이산 또는 세박산과 3,3'-디메틸-4,4'-디아미노디시클로헥실메탄과, 임의로 라우로락탐 또는 카프로락탐의 (코)폴리아미드,
- 이소프탈산과 4,4'-디아미노디시클로헥실메탄과 라우로락탐 또는 카프로락탐의 코폴리아미드,
- 1,12-도데칸이산과 4,4'-디아미노디시클로헥실메탄 (낮은 트랜스,트랜스 이성질체 함량의 경우)의 폴리아미드,
- 테레프탈산 및/또는 이소프탈산과, 임의로는 헥사메틸렌디아민과의 혼합물로서의 알킬-치환된 비스(4-아미노시클로헥실)메탄 동족체의 (코)폴리아미드,
- 비스(4-아미노-3-메틸-5-에틸-시클로헥실)메탄 및 임의로 추가의 디아민과, 이소프탈산 및 임의로 추가의 디카르복실산의 코폴리아미드,
- m-자일릴렌디아민 및 추가의 디아민, 예를 들어 헥사메틸렌디아민의 혼합물과, 이소프탈산 및 임의로 추가의 디카르복실산, 예를 들어 테레프탈산 및/또는 2,6-나프탈렌디카르복실산의 코폴리아미드,
- 비스(4-아미노시클로헥실)메탄 및 비스(4-아미노-3-메틸시클로헥실)메탄의 혼합물과, 8 내지 14개의 탄소 원자를 갖는 지방족 디카르복실산의 코폴리아미드, 및
- 1,14-테트라데칸이산을 포함하는 혼합물과 방향족, 아릴지방족 또는 지환족 디아민의 폴리아미드 또는 코폴리아미드이다.
이러한 예는 추가 성분 (예를 들어 카프로락탐, 라우로락탐 또는 디아민/디카르복실산 조합)의 첨가 또는 기타 성분에 의한 출발 성분의 부분 또는 완전 교체에 의해 매우 실질적인 정도까지 변경될 수 있다.
폴리에테르에스테르아미드는, 예를 들어 DE-A-25 23 991 및 DE-A-27 12 987로부터 공지되어 있고; 이것은 폴리에테르디올을 공단량체로서 함유한다. 폴리에테르아미드는, 예를 들어 DE-A-30 06 961로부터 공지되어 있고; 이것은 폴리에테르디아민을 공단량체로서 함유한다.
폴리에테르디올 또는 폴리에테르디아민에서, 폴리에테르 단위는, 예를 들어 1,2-에탄디올, 1,2-프로판디올, 1,3-프로판디올, 1,4-부탄디올 또는 1,3-부탄디올을 기재로 할 수 있다. 폴리에테르 단위는 또한, 예를 들어 디올로부터 유래된 단위의 랜덤 또는 블록 방식 분포를 갖는 혼합 구조를 가질 수도 있다. 폴리에테르디올 또는 폴리에테르디아민의 중량-평균 몰질량은 200 내지 5000 g/mol, 바람직하게는 400 내지 3000 g/mol이고; 폴리에테르에스테르아미드 또는 폴리에테르아미드에서의 그의 비율은 바람직하게는 4 내지 60 중량%, 더욱 바람직하게는 10 내지 50 중량%이다. 적합한 폴리에테르디아민은, 상응하는 폴리에테르디올의 환원적 아민화 또는 아크릴로니트릴과의 커플링 및 후속 수소화에 의한 전환에 의해 수득될 수 있다. 이것은 예를 들어 헌츠만 코포레이션(Huntsman Corp.)으로부터의 제파민(JEFFAMIN)? D 또는 ED 유형 또는 엘라스타민(ELASTAMINE)? 유형의 형태로, 또는 바스프 에스이(BASF SE)로부터의 폴리에테르아민 D 시리즈의 형태로서 상업적으로 입수가능하다. 분지화된 폴리에테르아미드를 사용할 경우에는, 보다 적은 양의 폴리에테르트리아민, 예를 들어 제파민? T 유형을 또한 사용하는 것도 가능하다. 에테르 산소 원자 당 쇄 내에 평균 2.3개 이상의 탄소 원자를 함유하는 폴리에테르디아민 또는 폴리에테르트리아민을 사용하는 것이 바람직하다. 본 발명에 따르면, 폴리에테르아미드가 더 양호한 가수분해 안정성을 갖기 때문에 바람직하다.
a)에 따른 층의 성형 조성물은 전술한 폴리아미드 중 하나 또는 그 중 둘 이상을 혼합물로서 함유할 수 있다. 또한, 성형 조성물의 전체 중합체 함량을 기준으로 40 중량%까지 다른 열가소성 물질, 예를 들면 충격-개질 고무가 존재할 수 있다. 존재하는 임의의 고무는 바람직하게는, 선행기술에 따르면, 폴리아미드 매트릭스와의 상용성이 얻어지는 작용기를 함유한다. 또한, 폴리아미드에 대한 통상적인 보조제 및 첨가제, 특히 광 및/또는 열 안정화제가 존재할 수 있다. 광-반사 충전제는 a)에 따른 층의 열가소성 성분의 반사 용량보다 높은 반사 용량을 갖는 임의의 충전제일 수 있고, 이것은 구체적으로는 이산화티타늄이다 (WO 2011066595).
b)에 따른 층의 성형 조성물은, 열가소성 물질로서, 예를 들면 폴리아미드, 폴리올레핀 및/또는 폴리에스테르를 포함할 수 있다. 또한, 통상적인 보조제 및 첨가제, 특히 광 및/또는 열 안정화제, 광-반사 충전제, 예를 들면 이산화티타늄, 및 강화 충전제, 예를 들면 유리 섬유, 규회석 또는 운모가 존재할 수 있다.
c)에 따른 층의 성형 조성물에 대해서는, a)에 따른 층의 성형 조성물에 대한 것과 동일한 것이 적용되고, 또한 충전제와 관련해서는, b)에 따른 층의 성형 조성물에 대한 것과 동일한 것이 적용된다. 또한, c)에 따른 층의 성형 조성물은 착색되고/거나 소광제를 포함할 수 있다.
3층 실시양태에서, 개별적인 필름층은 일반적으로 다음과 같은 두께를 갖는다:
ㆍ a) 및 c)에 따른 층: 15 내지 100 ㎛, 바람직하게는 25 내지 50 ㎛;
ㆍ b)에 따른 층: 100 내지 500 ㎛, 바람직하게는 150 내지 400 ㎛.
2층 실시양태에서, 층 두께는 일반적으로 다음과 같다:
ㆍ a)에 따른 층: 15 내지 100 ㎛, 바람직하게는 25 내지 50 ㎛;
ㆍ c)에 따른 층: 100 내지 500 ㎛, 바람직하게는 150 내지 400 ㎛.
a)에 따른 층과 b)에 따른 층 사이 및/또는 b)에 따른 층과 c)에 따른 층 사이에 존재하는 임의의 접착촉진제 층은 일반적으로 3 내지 40 ㎛, 바람직하게는 5 내지 25 ㎛ 두께이다.
본 발명에 따라 사용되는 다층 필름은 모든 종래 기술 방법, 예를 들면 공압출 또는 적층에 의해 제조될 수 있다.
본 발명은 또한 특허청구범위에 따른 필름의, 광기전력 모듈의 후면 커버로서의 용도를 제공한다. 이러한 목적을 위해, a)에 따른 층을, 예를 들면 적층 또는 접착에 의해, 태양전지가 포매된 밀봉층에 결합시킨다. a)에 따른 층에서의 폴리아미드 또는 폴리아미드 엘라스토머 비율로 인해서, 적층은 밀봉층에 대한 양호한 접착을 제공한다. 사용되는 밀봉층은 종래 기술에 따라 통상적으로 사용되는 임의의 물질일 수 있다.
본 발명은 추가로, 태양전지가 포매된 밀봉층에 a)에 따른 층을 결합시키는 것에 의해, 특허청구범위에 따른 다층 필름을 후면 커버로서 포함하는 광기전력 모듈을 제공한다.
본 발명은 이후의 실시예에 의해 예시된다. 이러한 목적을 위해, 하기 성형 조성물을 제조하였고, "부"는 항상 중량부이다.
외부층을 위한 화합물 1:
79.25 부의 베스타미드(VESTAMID)? L1901 nf (PA12), 0.5 부의 이르가녹스(IRGANOX)? 1098 (입체장애 페놀 산화방지제), 0.2 부의 티누빈(TINUVIN)? 312 (자외선 흡수제) 및 20 부의 이산화티타늄 작트레벤(Sachtleben) R 420을, 이축 압출기 (코페리온 베르너 운트 플라이더러(Coperion Werner & Pfleiderer) ZSK 25 WLE, 36 L/D)를 사용하여, 220℃의 배럴 온도에서 혼합하였다. 압출물을 수욕을 사용하여 냉각시키고 잘게 썰고; 이어서 펠릿을 80℃에서 12시간 동안 강제 공기 오븐에서 건조시켰다.
외부층을 위한 화합물 2:
71.75 부의 베스타미드? L1901 nf, 7.5 부의 폴리에테르에스테르아미드 (63.796 중량%의 라우로락탐, 6.645 중량%의 도데칸이산, 29.492 중량%의 PTHF 1000 및 0.067 중량%의 50% 차아인산으로부터 제조됨), 0.5 부의 이르가녹스? 1098, 0.2 부의 티누빈? 312 및 20 부의 이산화티타늄 작트레벤 R 420을, 이축 압출기 (코페리온 베르너 운트 플라이더러 ZSK 25 WLE, 36 L/D)를 사용하여, 220℃의 배럴 온도에서 혼합하였다. 압출물을 수욕을 사용하여 냉각시키고 잘게 썰고; 이어서 펠릿을 80℃에서 12시간 동안 강제 공기 오븐에서 건조시켰다.
외부층을 위한 화합물 3:
64.25 부의 베스타미드? L1901 nf, 15 부의 화합물 2에서와 동일한 폴리에테르에스테르아미드, 0.5 부의 이르가녹스? 1098, 0.2 부의 티누빈? 312 및 20 부의 이산화티타늄 작트레벤 R 420을, 이축 압출기 (코페리온 베르너 운트 플라이더러 ZSK 25 WLE, 36 L/D)를 사용하여, 220℃의 배럴 온도에서 혼합하였다. 압출물을 수욕을 사용하여 냉각시키고 잘게 썰고; 이어서 펠릿을 80℃에서 12시간 동안 강제 공기 오븐에서 건조시켰다.
중간층을 위한 화합물 4:
50.6 부의 베스타미드? L1901, 26 부의 모플렌(MOPLEN) HP552L (호모폴리프로필렌, 압출 유형), 20 부의 TEC 110 카올린, 3 부의 크레이튼(KRATON)? FG1901 (말레산 무수물-개질 스티렌-에틸렌/부틸렌 블록 공중합체) 및 0.4 부의 이르가녹스? 1098을, 이축 압출기 (코페리온 베르너 운트 플라이더러 ZSK 25 WLE, 36 L/D)를 사용하여, 200℃의 배럴 온도에서 혼합하였다. 압출물을 수욕을 사용하여 냉각시키고 잘게 썰고; 이어서 펠릿을 80℃에서 12시간 동안 강제 공기 오븐에서 건조시켰다.
3층 필름의 압출:
콜린(Collin)으로부터의 다층 필름 시스템 (300 mm 슬롯 다이, 0-6 mm 갭, 3층 또는 5층 필름에 대한 공-압출 공급 블록)을 사용하여 대략 230℃의 가공 온도에서 3층 필름을 제조하였다. 중간층은 250 ㎛로 설정하고, 외부층은 각각 50 ㎛로 설정하였다. 결과를 표 1에 나타냈다.
표 1: 실시예
개선된 안료 분산성은 본 발명에 따른 반사도에서의 개선으로부터 분명하다.
Claims (12)
- a) I. 35 중량% 이상의 폴리아미드 함량 및
II. 1 내지 65 중량%의 광-반사 충전제 함량
을 포함하는 성형 조성물의 제1 외부층, 및
c) I. 35 중량% 이상의 폴리아미드 함량 및
II. 1 내지 65 중량%의 충전제 함량
을 갖는 성형 조성물의 제2 외부층
을 포함하는 필름이며, 여기서 상기 백분율은 각각 전체 성형 조성물을 기준으로 한 것이고,
a)에 따른 층의 성형 조성물 및/또는 c)에 따른 층의 성형 조성물에서 폴리아미드 성분으로서 폴리에테르에스테르아미드 및 폴리에테르아미드로부터 선택되는 폴리아미드 엘라스토머가, a)에 따른 층의 성형 조성물 및/또는 c)에 따른 층의 성형 조성물이 1 내지 25 중량%의 폴리아미드 엘라스토머를 함유하도록 사용되는 것을 특징으로 하는 필름. - 제1항에 있어서, a)에 따른 층의 성형 조성물 및/또는 c)에 따른 층의 성형 조성물이 2 내지 20 중량%의 폴리아미드 엘라스토머를 함유하는 것을 특징으로 하는 필름.
- 제1항 또는 제2항에 있어서, 폴리아미드 엘라스토머가 폴리에테르아미드인 것을 특징으로 하는 필름.
- 제1항 내지 제3항 중 어느 한 항에 있어서, a)에 따른 층과 c)에 따른 층 사이에 b) 열가소성 성형 조성물의 중간층이 존재하는 것을 특징으로 하는 필름.
- 제4항에 있어서, a)에 따른 층과 b)에 따른 층 사이 및/또는 b)에 따른 층과 c)에 따른 층 사이에 접착촉진제 층이 존재하는 것을 특징으로 하는 필름.
- 제1항 내지 제3항 중 어느 한 항에 있어서, a)에 따른 층 및 c)에 따른 층이 직접적으로 연속하여 존재하는 것을 특징으로 하는 필름.
- 제4항 또는 제5항에 있어서, a)에 따른 층 및 c)에 따른 층이 15 내지 100 ㎛의 두께를 갖고, b)에 따른 층이 100 내지 500 ㎛의 두께를 갖는 것을 특징으로 하는 필름.
- 제5항 또는 제7항에 있어서, 접착촉진제 층/접착촉진제 층들이 각각 3 내지 40 ㎛ 두께인 것을 특징으로 하는 필름.
- 제6항에 있어서, a)에 따른 층이 15 내지 100 ㎛의 두께를 갖고, c)에 따른 층이 100 내지 500 ㎛의 두께를 갖는 것을 특징으로 하는 필름.
- 제1항 내지 제9항 중 어느 한 항에 있어서, 광-반사 충전제가 이산화티타늄인 것을 특징으로 하는 필름.
- 태양전지가 포매된 밀봉층에 a)에 따른 층을 결합시키는 것에 의한, 제1항 내지 제10항 중 어느 한 항에 따른 필름의 광기전력 모듈의 후면 커버로서의 용도.
- 태양전지가 포매된 밀봉층에 a)에 따른 층을 결합시키는 것에 의해, 제1항 내지 제10항 중 어느 한 항에 따른 필름을 후면 커버로서 포함하는 광기전력 모듈.