KR20060001767A - 접착제의 조성물 및 그의 제조방법 - Google Patents

접착제의 조성물 및 그의 제조방법 Download PDF

Info

Publication number
KR20060001767A
KR20060001767A KR1020040051752A KR20040051752A KR20060001767A KR 20060001767 A KR20060001767 A KR 20060001767A KR 1020040051752 A KR1020040051752 A KR 1020040051752A KR 20040051752 A KR20040051752 A KR 20040051752A KR 20060001767 A KR20060001767 A KR 20060001767A
Authority
KR
South Korea
Prior art keywords
weight
concentration
adhesive
composition
added
Prior art date
Application number
KR1020040051752A
Other languages
English (en)
Other versions
KR100612590B1 (ko
Inventor
전창호
Original Assignee
전창호
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 전창호 filed Critical 전창호
Priority to KR1020040051752A priority Critical patent/KR100612590B1/ko
Publication of KR20060001767A publication Critical patent/KR20060001767A/ko
Application granted granted Critical
Publication of KR100612590B1 publication Critical patent/KR100612590B1/ko

Abstract

본 발명은 접착제의 조성물 및 그의 제조방법에 관한 것으로서, 주거생활 실내의 벽지, 바닥제등 각종의 화학접착제로 인한 인체의 피부질환, 두통, 호흡기장애등의 문제점을 근본적으로 해결코자 환경친화적이고, 인체친화적인, 접착제의 조성물 및 그의 제조방법에 목적이 있다.
이의 조성물로서, 교반기의 계속적인 교반 중에 고형분 40%농도의 점액질 액상의 규산소다(sodium silicate) 60중량%에, 뜨거운 물중에 10%농도로 용해시킨 폴리비닐알콜(polyvinyl alcohol)를 5중량%첨가하고, 상온의 물중에 50%농도로 용해시킨 아라비아고무(gum arabic)를 3중량%첨가, 섭씨80-90℃의 온도의 물중에 50%농도로 용해한 젤라틴(gelatin)을 5중량%첨가, 탄산칼슘(calcium carbonate)을 6중량%첨가 , 수산화마그네슘(Mg(OH)₂) 3중량%첨가, 수산화알루미늄(Al(OH)₃) 3중량%첨가, 챠콜파우다(charcoal powder) 5중량%첨가, 황토(clay) 7중량%첨가, 펄프분말 3중량%첨가하여 격열하게 교반하여 점액질상으로 완성된 것에 그 특징이 있는 접착제의 조성물 및 그의 제조방법.
규산소다(sodium silicate), 폴리비닐알콜(polyvinyl alcohol), 아라비아고무(gum arabic), 젤라틴(gelatin), 탄산칼슘(calcium carbonate), 수산화마그네슘(Mg(OH)₂), 수산화알루미늄(Al(OH)₃), 챠콜파우다(charcoal powder), 황토(clay), 펄프분말.

Description

접착제의 조성물 및 그의 제조방법{omitted}
본 발명은 접착제의 조성물 및 그의 제조방법에 관한 것으로서, 종래의 대부분의 접착제는 멜라민과 발암물질인 포르마린과 합성 한 것과 방향성 유기용제를 사용하여 냄새 및 포름알데히드의 발생으로 인체에 치명적인 문제점 등이 발생하고 있다. 이러한 문제점을 해결코자 본 발명은 냄새의 발생이 없고, 포름알데히드의 발생이 없는 접착제로서 다음과 같다.
석영모래인 규사(SiO₂) 및 백토를 고온에서 축합하여 만들어진 규산소다(sodium silicate(Na₂O. nSiO₂. nH₂O))와 합성하고자 하는 첨가물이 강알카리인 점액질상의 규산소다(sodium silicate)의 화학적인 반응에 의하여 첨가물에 의하여 겔화한다든지, 접착력, 경화시간, 열 및 습기, 냉각 등 주변 환경변화에 의하여 박리현상의 발생이 없는 첨가물에 의한 합성방법의 기술적인 차이와 종래의 접착제의 조성물과는 완전히 다른 것이다.
본 발명의 기술적인 과제는 포르말린 및 방향성 유기용제를 사용하지 않고서 접착력을 갖는 접착제와 본 발명의 접착제를 만들기 위한 조성물의 첨가제에 의하 여 화학적인 반응에 의하여 겔화, 접착력저하, 접착제의 경화 시간 등의 문제점등의 기술적 해결을 위한 조성물의 조성방법은 다음과 같다.
점액질상의 불휘발분 40%농도의 규산소다(sodium silicate) 에 , 폴리비닐알콜(polyvinyl alcohol)원료를 뜨거운 물중에 10%의 농도로 분산 용해하여 5 중량% 첨가 교반 하고, 상온의 물중에 50%농도로 용해시킨 아라비아고무(gum arabic)를 3중량% 첨가, 섭씨 80-90℃의 온도의 물중에 50%농도로 용해한 젤라틴(gelatin)을 5중량%첨가, 탄산칼슘(calcium carbonate)을 6중량% 첨가, 경화촉진제로서 수산화마그네슘(Mg(OH)₂)3중량%첨가, 수산화알루미늄(Al(OH)₃) 3중량%첨가, 펄프분말 3중량% 첨가, 탈취, 원적외선방사, 음이온방사의 기능으로서 챠콜파우다(charcoal powder) 5중량%첨가, 황토(clay)분말 5중량% 첨가 교반하여 포름알데히드 발생 및 냄새의 발생이 전혀 없는 점액질상의 접착제를 만들었다.
본 발명의 구성에 있어서는, (1). 점액질상의 40%농도의 규산소다(sodium silicate), (2). 뜨거운 물중에 10%농도로 용해시킨 폴리비닐알콜(polyvinyl alcohol), (3). 상온의 물중에 50%농도로 용해시킨 아라비아고무(gum arabic), (4). 섭씨 80-90℃의 온도의 물중에 50%농도로 용해한 젤라틴(gelatin), (5). 탄산칼슘(calcium carbonate), (6). 수산화마그네슘(Mg(OH)₂), (7). 수산화알루미늄(Al(OH)₃), (8). 챠콜분말(charcoal powder), (9). 황토분말(clay powder), (10). 펄프분말(cellulose fiber)의 조성물을 실시예를 들어서 설명 하면 다음과 같다.
실시예 1
1. 40%농도의 규산소다(sodium silicate) --- 70중량%
2. 수산화마그네슘(Mg(OH)₂) --- 3중량%
3. 수산화알루미늄(Al(OH)₃) --- 3중량%
4. 탄산칼슘(calcium carbonate) --- 4중량%
5. 펄프분말(cellulose fiber) --- 20중량%
실시예 2
1. 40%농도의 규산소다(sodium silicate) --- 60중량%
2. 10%농도의 폴리비닐알콜(polyvinyl alcohol) --- 7중량%
3. 50%농도의 아라비아고무(gum arabic) --- 5중량%
4. 50%농도의 젤라틴(gelatin) --- 7중량%
5. 탄산칼슘(calcium carbonate) --- 10중량%
6. 수산화마그네슘(Mg(OH)₂) --- 3중량%
7. 수산화알루미늄(Al(OH)₃) --- 3중량%
8. 챠콜분말(charcoal powder) --- 5중량%
실시예 3
1. 40%농도의 규산소다(sodium silicate) --- 60중량%
2. 10%농도의 폴리비닐알콜(polyvinyl alcohol) --- 7중량%
3. 50%농도의 아라비아고무(gum arabic) --- 5중량%
4. 50%농도의 젤라틴(gelatin) --- 7중량%
5. 탄산칼슘(calcium carbonate) --- 10중량%
6. 수산화마그네슘(Mg(OH)₂) --- 3중량%
7. 수산화알루미늄(Al(OH)₃) --- 3중량%
8. 황토분말(clay powder) --- 5중량%
실시예 1 에 있어서 접착제의 조성물은 건물내부의 천장부위에 뿜칠(spray)하여 상온에서 자연 경화 건조되어 흡음기능, 화재 발생시 불연제로서의 기능역할을 하는 접착제, 실시예 2의 조성물은 건물 내부의 벽지, 장판, 마루판등 실내 내부의 인테리어 접착제로서 실내의 각종의 냄새를 탈취, 원적외선방사, 음이온의 방사로 쾌적한 실내공기를 정화해주는 역할의 접착제,
실시예 3 의 조성물의 기능은 실예 2의 기능과 유사하면서 황토로 인해서 실내 습도조절 및 공기정화의 기능을 주는 접착제의 특징이 있는 접착제의 조성물 및 그의 제조방법.
본 발명의 접착제는 기존의 접착제인 멜라민과 포르마린으로 축합하여 조성된 접착제의 포름알데히드의 발생 등 의 문제점을 해소하고, 접착력을 강화하면서, 냄새의 발생 및 포름알데히드의 발생이 전혀 없고 실내의 냄새를 탈취, 원적외선의 방사 및 음이온의 발생으로 공기를 정화하여주면서, 화재발생시 불연재로서 그 기능이 있고 벽지, 장판지, 마루판의 접착제로서 종이, 콘크리트, 나무, 금속, 합성수지등의 다양한 접착력을 갖는 것에 그 효과가 있는 접착제의 조성물 및 그의 제조방법.

Claims (4)

  1. (1). 점액질상의 불휘발분 40%농도의 규산소다(sodium silicate)60중량%에, (2). 뜨거운 물중에 10%농도로 용해시킨 폴리비닐알콜(polyvinyl alcohol)5중량% 첨가하여 교반, (3). 상온의 물중에 50%농도로 용해시킨 아라비아고무(gum arabic) 3중량% 첨가하여 교반, (4). 섭씨 80-90℃의 온도의 물중에 50%농도로 용해한 젤라틴(gelatin) 5중량% 첨가하여 교반, (5). 탄산칼슘(calcium carbonate) 6중량% 첨가하여 교반, (6). 경화촉진제로서 수산화마그네슘(Mg(OH)₂) 3중량% 첨가하여 교반, (7). 경화촉진제로서 수산화알루미늄(Al(OH)₃) 3중량% 첨가하여 교반, (8). 탈취기능으로서 챠콜분말(charcoal powder) 5중량% 첨가하여 교반, (9). 펄프분말(cellulose fiber) 5중량% 첨가하여 교반, (10). 황토분말(clay powder) 5중량% 첨가 교반한 접착제의 그 특징이 있는 접착제의 조성물 및 그의 제조방법.
  2. 1항에 있어서, (1). 40%농도의 규산소다(sodium silicate) 70중량%에 , (2). 수산화마그네슘(Mg(OH)₂) 3중량%첨가, (3). 수산화알루미늄(Al(OH)₃) 3중량%첨가, (4). 탄산칼슘(calcium carbonate) 4중량%첨가, (5). 펄프분말(cellulose fiber) 20중량% 첨가 교반하여 완성된 접착제에 그 특징이 있는 접착제의 조성물.
  3. 1항에 있어서, (1). 40%농도 규산소다(sodium silicate) 60중량%에, (2). 10%농도의 폴리비닐알콜(polyvinyl alcohol) 7중량% 첨가, (3). 50%농도의 아라비 아고무(gum arabic) 5중량% 첨가, (4). 50%농도의 젤라틴(gelatin) 7중량% 첨가, (5). 탄산칼슘(calcium carbonate) 10중량% 첨가, (6). 수산화마그네슘(Mg(OH)₂) 3중량% 첨가, (7). 수산화알루미늄(Al(OH)₃) 3중량% 첨가, (8). 챠콜분말(charcoal powder) 5중량% 첨가 교반하여 완성한 접착제에 그 특징이 있는 접착제의 조성물.
  4. 1항에 있어서, (1). 40%농도의 규산소다(sodium silicate) 60중량%에, (2). 10%농도의 폴리비닐알콜(polyvinyl alcohol) 7중량% 첨가, (3). 50%농도의 아라비아고무(gum arabic) 5중량% 첨가, (4). 50%농도의 젤라틴(gelatin) 7중량% 첨가, (5). 탄산칼슘(calcium carbonate) 10중량% 첨가, (6). 수산화마그네슘(Mg(OH)₂) 3중량% 첨가, (7). 수산화알루미늄(Al(OH)₃)3중량% 첨가, (8). 황토분말(clay powder) 5중량% 첨가 교반하여 완성한 접착제에 그 특징이 있는 접착제의 조성물.
KR1020040051752A 2004-06-30 2004-06-30 접착제 조성물 및 그 제조방법 KR100612590B1 (ko)