KR20040046248A - 마그네슘 티타네이트 산화막 임플란트 및 그 제조방법 - Google Patents
마그네슘 티타네이트 산화막 임플란트 및 그 제조방법 Download PDFInfo
- Publication number
- KR20040046248A KR20040046248A KR1020020074091A KR20020074091A KR20040046248A KR 20040046248 A KR20040046248 A KR 20040046248A KR 1020020074091 A KR1020020074091 A KR 1020020074091A KR 20020074091 A KR20020074091 A KR 20020074091A KR 20040046248 A KR20040046248 A KR 20040046248A
- Authority
- KR
- South Korea
- Prior art keywords
- magnesium
- magnesium titanate
- implant
- oxide film
- titanate oxide
- Prior art date
Abstract
Description
참조번호 | 전해질 용액의 성분 | 전해질 용액의 농도(몰/l) | 전류 밀도(mA/㎠) | 전압(V, DC) | 산도(pH) |
1 | 마그네슘 아세테이트+완충제 | 0.01-1.0 | 30-4000 | 50-500 | 7.0 이하 |
2 | 인산 마그네슘+완충제 | 0.01-1.0 | 30-4000 | 50-500 | 7.0 이하 |
3 | 황산 마그네슘+완충제 | 0.01-1.0 | 30-4000 | 50-500 | 7.0 이하 |
4 | 요드산 마그네슘+완충제 | 0.01-1.0 | 120-1000 | 50-500 | 7.0 이하 |
5 | 글루콘산 마그네슘+완충제 | 0.01-1.0 | 60-4000 | 50-500 | 7.0 이하 |
6 | 질산 마그네슘+완충제 | 0.01-1.0 | 10-300 | 23-500 | 7.0 이하 |
7 | 수산화 마그네슘+완충제 | 0.01-1.0 | 30-4000 | 50-500 | 7.0 이하 |
8 | 염화 마그네슘+완충제 | 0.01-1.0 | 30-4000 | 50-500 | 7.0 이하 |
9 | 질산 마그네슘+초산+완충제 | 0.01-1.0 | 30-2000 | 23-500 | 3.5-12.5 |
10 | 인산 마그네슘+말릭산+완충제 | 0.01-1.0 | 20-4000 | 50-500 | 3.5-12.5 |
11 | 마그네슘 아세테이트+ 옥살릭산+완충제 | 0.01-1.0 | 10-1000 | 50-500 | 3.5-12.5 |
12 | 황산 마그네슘+에틸렌 디아만 테트라 아세트산+완충제 | 0.01-1.0 | 30-4000 | 50-500 | 3.5-12.5 |
13 | 글루콘산 마그네슘+수산화나트륨+완충제 | 0.01-1.0 | 30-4000 | 50-500 | 3.5-12.5 |
14 | 수산화 마그네슘+인산+완충제 | 0.01-1.0 | 30-4000 | 50-500 | 3.5-12.5 |
15 | 요드산 마그네슘+초산+완충제 | 0.01-1.0 | 120-2000 | 50-500 | 3.5-12.5 |
16 | 염화 마그네슘+옥살릭산+완충제 | 0.01-1.0 | 50-1000 | 50-500 | 3.5-12.5 |
원소 | 시료 1 | 시료 2 | 시료 3 | 시료 4 | 시료 5 | 시료 6 |
Ti | 18.78 | 26.29 | 5.72 | 6.4 | 6.51 | 7.32 |
O | 55.72 | 56.22 | 69.23 | 67.35 | 56.32 | 50.07 |
Mg | 1.84 | 2.25 | 13.6 | 15.23 | 25.58 | 32.31 |
C | 15.24 | 9.57 | 9.44 | 7.02 | 7.32 | 6.38 |
P | 5.86 | 3.1 | 0 | 1.4 | 0 | 2.4 |
N | 1.4 | 2.02 | 0 | 0 | 0.6 | 1.2 |
S | 0.3 | 0 | 0.5 | 0.5 | 0 | 0 |
Na | 0.5 | 0.5 | 0 | 0 | 2.13 | 0.3 |
K | 0 | 0 | 0 | 0.6 | 0 | 0 |
Ca | 0 | 0 | 0 | 0 | 0.8 | 0 |
Claims (11)
- 티타늄 또는 티타늄 합금을 포함하는 임플란트 본체 및 상기 본체의 표면에 형성된 마그네슘 티타네이트 산화막을 포함하는 것을 특징으로 하는 마그네슘 티타네이트 임플란트.
- 제 1항에 있어서, 상기 마그네슘 티타네이트 산화막은 마그네슘을 포함하는 하나 또는 2 이상의 혼합 용액내에서 저전압 절연파괴 양극산화법에 의하여 제조되는 것을 특징으로 하는 마그네슘 티타네이트 임플란트.
- 제 1항 또는 제 2항에 있어서, 상기 마그네슘 티타네이트 산화막은 주성분으로서 6~26%의 티타늄, 51~71%의 산소 및 1.8~32%의 마그네슘을 포함하는 것을 특징으로 하는 마그네슘 티타네이트 임플란트.
- 제 1항 또는 제 2항에 있어서, 상기 마그네슘 티타네이트 산화막은 이중충 구조로 되어 있으며, 위층은 다공성 구조를 갖고 있으며, 아래층은 배리어층 구조를 갖는 것을 특징으로 하는 마그네슘 티타네이트 임플란트.
- 제 1항 또는 제 2항에 있어서, 상기 마그네슘 티타네이트 산화막의 두께는 300nm 내지 30㎛인 것을 특징으로 하는 마그네슘 티타네이트 임플란트.
- 제 5항에 있어서, 상기 마그네슘 티타네이트 산화막의 두께는 500nm 내지 10㎛인 것을 특징으로 하는 마그네슘 티타네이트 임플란트.
- 티타늄 또는 티타늄 합금으로 구성된 임플란트 본체를 증류슈 속에서 자외선에 2시간 이상 조사하는 단계;상기 자외선에 조사된 임플란트 본체를 마그네슘이 포함된 전해질 용액에 침지하는 단계; 및60 내지 500V의 전압에서 양극 산화법에 의하여 상기 침지된 임플란트 본체에 마그네슘 티타네이트 산화막을 피복시키는 단계를 포함하는 것을 특징으로 하는 마그네슘 티타네이트 산화막 임플란트의 제조방법.
- 제 7항에 있어서, 상기 전해질 용액은 마그네슘을 포함하는 하나의 단독 용액 또는 2 이상의 혼합용액인 것을 특징으로 하는 마그네슘 티타네이트 산화막 임플란트의 제조방법.
- 제 7항 또는 제 8항에 있어서 상기 전해질 용액의 농도는 0.01 내지 1.0M인 것을 특징으로 하는 마그네슘 티타네이트 산화막 임플란트의 제조방법.
- 제 7항 또는 제 8항에 있어서, 상기 전해질 용액의 산도는 3.0 내지 12.5pH인 것을 특징으로 하는 마그네슘 티타네이트 산화막 임플란트의 제조방법.
- 제 7항 또는 제 8항에 있어서, 상기 양극 산화법이 일어나는 전류밀도는 30 내지 4000mA/㎠인 것을 특징으로 하는 마그네슘 티타네이트 산화막 임플란트의 제조방법.