KR20030049612A - 칼슘-알루미늄 합금철을 이용한 고청정 알루미늄-킬드강제조방법 - Google Patents
칼슘-알루미늄 합금철을 이용한 고청정 알루미늄-킬드강제조방법 Download PDFInfo
- Publication number
- KR20030049612A KR20030049612A KR1020010079856A KR20010079856A KR20030049612A KR 20030049612 A KR20030049612 A KR 20030049612A KR 1020010079856 A KR1020010079856 A KR 1020010079856A KR 20010079856 A KR20010079856 A KR 20010079856A KR 20030049612 A KR20030049612 A KR 20030049612A
- Authority
- KR
- South Korea
- Prior art keywords
- steel
- alloy
- molten steel
- less
- killed
- Prior art date
Abstract
Description
Ca-Si 분체 및 Ca-Fe 분체의 조성 | ||||
성분(%)종류 | Ca | Si | Fe | 기타 |
Ca-Si 분체 | 36 | 60 | - | 4 |
Ca-Fe 분체 | 30 | - | 65 | 5 |
Claims (4)
- [C]≤100ppm, [Si]≤0.03% 를 기본조성으로 하는 Al-killed 극저탄소강에 Ca-Al 합금철을 투입하여 고청정강을 제조하는 방법으로서,상온에서 중량비로 Ca을 15%~75%, Al을 25%~85%로 혼합한 후 외부 공기와 차단된 챔버내의 Al2O3도가니에서 두 금속을 완전 용해, 혼합하고, 상기 도가니를 650℃ ~ 1050℃ 온도에서 1시간이상 유지시켜 제조한 Ca-Al 합금철을 용강중에 투입하는 것을 특징으로 하는 Ca-Al 합금철을 이용한 고청정 Al-Killed강 제조 방법.
- 제1항에 있어서, 상기 Ca-Al 합금철을 입도 1mm이하의 분체로 파쇄하여 [C]함량 0.02%이하의 연강재 철피로 제조된 직경 18mm이하의 파이프내에 넣어 제작한 코어드 와이어를 탈탄 및 탈산조업 실시공정인 RH공정에서 처리종료후 래이들내 용강속으로 200~350m/분의 양으로 투입하여, Al2O3를 저융점화하여 제거 및 구형화하는 것을 특징으로 하는 Ca-Al 합금철을 이용한 고청정 Al-Killed강 제조 방법.
- 제2항에 있어서, 상기 Al2O3가 완전히 저융점화하기 위해 용강중 [Ca]/[Al]농도비를 0.010 ~ 0.115가 되도록 Ca-Al 합금철을 투입하는 것을 특징으로 하는 Ca-Al 합금철을 이용한 고청정 Al-Killed강 제조 방법.
- 제2항에 있어서, 상기 Ca-Al 와이어를 투입한 후 래이들의 바닥으로부터 Ar을 1.0~1.2Nm3/분 유량으로 3~5분간 버블링을 실시하여 투입된 [Ca]과 Al2O3의 반응을 촉진시키는 것을 특징으로 하는 Ca-Al 합금철을 이용한 고청정 Al-killed강 제조 방법.