KR20020086381A

KR20020086381A - Antibacterial Bio Ceramic Ball Manufacturing Method

Info

Publication number: KR20020086381A
Application number: KR1020020061096A
Authority: KR
Inventors: 김선익
Original assignee: 김선익
Priority date: 2002-10-07
Filing date: 2002-10-07
Publication date: 2002-11-18

Abstract

PURPOSE: Provided is a manufacturing method of antibiotic bio-ceramic balls composed of natural minerals which substitute for sands as a filter, preventing bacteria of seawater from flowing into a water tank for fish-breeding. CONSTITUTION: The manufacturing method of antibiotic bio-ceramic balls comprises the steps of: preparing natural minerals such as 15wt.% of fine charcoal(>=100mesh), 40-50wt.% of quartz porphyry(>=120mesh), 15-20wt.% of clay(>=200mesh), and 5-10wt.% of limestone(>=200mesh); adding 5-10wt.% of sodium silicate with a specific gravity of 1.5g/cm¬3, and mixing for 15min; compressing under pressure of 150kg/cm¬2; drying compacts at 50-80deg.C over 5hrs; and sintering at 150-200deg.C.

Description

Antimicrobial Bio Ceramic Ball Manufacturing Method

본 발명은 바이오세라믹볼 제조방법에 관한 것으로, 보다 상세하게는 숯,맥반석,생석회등이 가지는 항균성,수질정화의 기능을 이용하여 항균필터 역할을 할 수 있는 볼 형태의 고형물이다.The present invention relates to a method for producing a bioceramic ball, and more specifically, it is a ball-type solid material that can act as an antibacterial filter by using the antibacterial and water purification functions of charcoal, barley stone, and quicklime.

기존에 세사(모래)의 필터 작용 외에는 별다른 기능을 발휘하지 못하는 실정이나, 본 발명은 세사가 가지는 기능을 추가하는 작용이 있다.Existing situation that does not exhibit any function other than the filter action of sesa (sand), the present invention has the effect of adding the function of the sesa.

본 발명은 숯,맥반석,생석회등이 가지는 항균성,수질정화의 기능을 효과적으로 증대하고,세사를 대체하는 기능을 가지며, 경제성있는 고형물을 만드는데 있다. 이에 물의 압력을 견디는 강도와 기능을 효과적으로 높일수 있는 적절한 배합과 소모성인 필터의 특수성으로 인한 저렴한 생산성으로 경제적 가치를 창출하는데 본 발명의 기술적 과제이다.The present invention is to effectively increase the function of antimicrobial, water purification of charcoal, elvan, quicklime, etc., has the function of replacing the fine sand, and to produce economical solids. Accordingly, the technical problem of the present invention is to create an economic value due to the low productivity due to the special combination of the appropriate mixing and consumable filter that can effectively increase the strength and function to withstand the pressure of water.

상기한 목적을 달성하기 위한 구체적인 수단으로는;Specific means for achieving the above object;

탄소 함량 90%이상, 회분3%이상의 백탄을 사용하고, 이를 100메쉬(mesh)이상의 백탄 분말 15중량%,120메쉬(mesh)이상의 맥반석 분말 40～5중량%, 200메쉬(mesh)이상의 점토분말 15～20중량%, 200메쉬(mesh)이상의 생석회분말 5～10중량%을 분쇄하는 단계와; 상기 준비된 원료를 비중 1.5g/㎤규산나트륨(NaSi)5～10중량%를 비율로 교반기에 15분 이상 혼합하는 단계와; 상기 혼합물을 소정의 금형에 넣어 150kg/㎠내외의 압축 성형기에 넣어 압축하는 단계와; 압축 성형물을 섭시 50～80℃의 전기 건조대에서 5시간 이상 건조 단계와; 상기 건조 상태의 고형물을 150℃～200℃로 소성하여 제조토록 한 것이다.More than 90% of carbon content, 3% ash or more of charcoal is used, 15% by weight of 100% of mesh powder or more, 120% or more of mesh rock powder 40 ~ 5% by weight, clay powder of more than 200 mesh Grinding 15 to 20% by weight, 5 to 10% by weight of quicklime powder of 200 mesh or more; Mixing the prepared raw material with a specific gravity of 1.5 g / cm 3 sodium silicate (NaSi) 5 to 10% by weight in a stirrer for at least 15 minutes; Putting the mixture into a predetermined mold and compressing the mixture into a compression molding machine of about 150 kg / cm 2; Drying the press-molded product at an electric drying stand of 50 ° C. to 80 ° C. for at least 5 hours; The dried solid is calcined at 150 ° C to 200 ° C to be manufactured.

본 발명은 숯, 맥반석, 생석회등이 가지는 항균성, 수질정화의 기능을 효과적으로 사용하기 위해 볼형태의 고형물로 생산하며, 점차 확대되는 해양오염에 따른 양어장용 해수의 병원균을 억제하기 위한 샌드필터용 세사(모래)를 대체하고 알카리성 세라믹 조형물이다. 또한 조형물의 정화작용으로 활성화된 해수를 공급하므로 물고기의 저항력과 신진대사의 활성화로 양어 성장 효과를 기대하고 있다.The present invention is produced in the form of a ball-shaped solid to effectively use the functions of antibacterial, water purification, charcoal, ganban stone, quicklime, etc., sand filter for sand filter for suppressing the pathogens of the seawater for fish farms according to the gradually expanding marine pollution It replaces (sand) and is an alkaline ceramic molding. In addition, it supplies seawater activated by the purification of the sculptures, and expects the growth effect of fish farming by activating the fish's resistance and metabolism.

Claims

More than 90% of carbon content, 3% ash or more of charcoal is used, and it is 15% by weight of 100% of mesh powder or more, 100% of mesh powder of gannetite powder of more than 120 mesh, clay powder of more than 200 mesh. Grinding 15 to 20% by weight, 5 to 10% by weight of quicklime powder of 200 mesh or more; Mixing the prepared raw material with a specific gravity of 1.5 g / cm 3 sodium silicate (NaSi) 5 to 10% by weight in a stirrer for at least 15 minutes; Putting the mixture into a predetermined mold and compressing the mixture into a compression molding machine of about 150 kg / cm 2; The compression molded product was dried at an electric drying stand of 50 to 80 ° C. for at least 5 hours. The dried solid was calcined at 150 ° C. to 200 ° C. to prepare. The present invention has been developed to be suitable for the water purification and antibacterial action of fish farms, and also an antimicrobial bio-ceramic ball manufacturing method consisting of steps that can be applied to aquariums, ponds, etc.