KR20020071139A - 응력제거소둔후 철손이 개선된 무방향성 전기강판 및 그제조방법 - Google Patents
응력제거소둔후 철손이 개선된 무방향성 전기강판 및 그제조방법 Download PDFInfo
- Publication number
- KR20020071139A KR20020071139A KR1020010011087A KR20010011087A KR20020071139A KR 20020071139 A KR20020071139 A KR 20020071139A KR 1020010011087 A KR1020010011087 A KR 1020010011087A KR 20010011087 A KR20010011087 A KR 20010011087A KR 20020071139 A KR20020071139 A KR 20020071139A
- Authority
- KR
- South Korea
- Prior art keywords
- stress relief
- steel sheet
- annealing
- oriented electrical
- relief annealing
- Prior art date
Abstract
Description
강종 | 성분(중량%) | |||||||||
C | Si | Al | Mn | P | S | N | S+N | Misch Metal(M) | M/(S+N) | |
발명강A | 0.003 | 1.5 | 0.5 | 0.25 | 0.015 | 0.010 | 0.003 | 0.013 | 0.010 | 0.77 |
발명강B | 0.005 | 1.5 | 0.5 | 0.25 | 0.014 | 0.003 | 0.010 | 0.013 | 0.020 | 1.54 |
발명강C | 0.003 | 1.5 | 0.5 | 0.24 | 0.014 | 0.003 | 0.003 | 0.006 | 0.003 | 0.5 |
발명강D | 0.002 | 1.5 | 0.5 | 0.25 | 0.015 | 0.003 | 0.002 | 0.005 | 0.005 | 1.0 |
발명강E | 0.003 | 1.5 | 0.5 | 0.25 | 0.015 | 0.002 | 0.003 | 0.005 | 0.010 | 2.0 |
비교강A | 0.003 | 1.5 | 0.5 | 0.25 | 0.015 | 0.015 | 0.003 | 0.018 | 0.020 | 1.11 |
비교강B | 0.005 | 1.5 | 0.5 | 0.20 | 0.015 | 0.003 | 0.012 | 0.015 | 0.020 | 1.33 |
비교강C | 0.003 | 1.5 | 0.5 | 0.25 | 0.015 | 0.003 | 0.003 | 0.006 | 0.002 | 0.33 |
비교강D | 0.002 | 1.5 | 0.5 | 0.25 | 0.015 | 0.006 | 0.005 | 0.011 | 0.025 | 2.27 |
구분 | 자기특성 | 응력제거소둔후 철손개선율(%) | 강종 | |||
최종소둔후 | 응력제거소둔후 | |||||
자속밀도,B50(T) | 철손,W15/50(W/kg) | 자속밀도,B50(T) | 철손,W15/50(W/kg) | |||
발명재1 | 1.74 | 5.25 | 1.73 | 3.44 | 34.5 | 발명강A |
발명재2 | 1.73 | 5.36 | 1.72 | 3.42 | 36.2 | 발명강B |
발명재3 | 1.74 | 5.35 | 1.73 | 3.40 | 36.4 | 발명강C |
발명재4 | 1.73 | 5.38 | 1.72 | 3.37 | 37.4 | 발명강D |
발명재5 | 1.74 | 5.42 | 1.73 | 3.36 | 38.0 | 발명강E |
비교재1 | 1.74 | 6.60 | 1.72 | 5.39 | 18.4 | 비교강A |
비교재2 | 1.74 | 6.65 | 1.73 | 5.31 | 20.1 | 비교강B |
비교재3 | 1.73 | 5.34 | 1.72 | 4.03 | 24.6 | 비교강C |
비교재4 | 1.74 | 6.03 | 1.73 | 4.67 | 22.5 | 비교강D |
Claims (4)
- 중량%로, C≤0.005%, Si≤2.0%, Al≤1.0%, Mn≤1.5%, P≤0.15%, S≤0.010%, N≤0.010%을 함유하고, 미쉬메탈(Misch Metal)의 함량과 S+N함량의 비{M/(S+N), M은 미쉬메탈}가 0.5~2.0이며, 나머지 Fe 및 기타 불가피한 불순물로 조성되는 응력제거소둔후 철손이 개선된 무방향성 전기강판
- 제 1항에 있어서, 상기 무방향성 전기강판의 응력제거소둔후 철손이 최종소둔후의 철손 보다 30% 이상 개선된 것을 특징으로 하는 응력제거소둔후 철손이 개선된 무방향성 전기강판
- 중량%로, C≤0.005%, Si≤2.0%, Al≤1.0%, Mn≤1.5%, P≤0.15%, S≤0.010%, N≤0.010%을 함유하고, 미쉬메탈(Misch Metal)의 함량과 S+N함량의 비가 0.5~2.0이며, 나머지 Fe 및 기타 불가피한 불순물로 조성되는 강 슬라브를 1100~1300℃로 재가열한 다음 열간압연하고, 800℃이하의 온도로 권취한 다음 산세하고, 70% 이상의 압하율로 냉간압연한 후 650~850℃의 온도에서 최종소둔하는 것을 포함하여 이루어지는 응력제거소둔후 철손이 개선된 무방향성 전기강판의 제조방법
- 제 3항에 있어서, 상기 최종소둔후에는 응력제거소둔이 추가로 실시되고, 상기 응력제거소둔은 700~850℃의 온도에서 30분 이상 실시하는 것을 특징으로 하는응력제거소둔후 철손이 개선된 무방향성 전기강판의 제조방법