KR102618634B1 - 흑색 감광성 수지 조성물, 이를 이용하여 제조된 감광성 수지막 및 표시장치 - Google Patents
흑색 감광성 수지 조성물, 이를 이용하여 제조된 감광성 수지막 및 표시장치 Download PDFInfo
- Publication number
- KR102618634B1 KR102618634B1 KR1020200088631A KR20200088631A KR102618634B1 KR 102618634 B1 KR102618634 B1 KR 102618634B1 KR 1020200088631 A KR1020200088631 A KR 1020200088631A KR 20200088631 A KR20200088631 A KR 20200088631A KR 102618634 B1 KR102618634 B1 KR 102618634B1
- Authority
- KR
- South Korea
- Prior art keywords
- photosensitive resin
- black
- resin composition
- binder resin
- weight
- Prior art date
Abstract
(A) 아크릴계 바인더 수지 및 카도계 바인더 수지를 포함하는 바인더 수지, (B) 광중합성 단량체, (C) 광중합 개시제, (D) 흑색 착색제, (E) 50nm 이하의 평균입경을 가지는 다공성 나노졸 및 (F) 용매를 포함하는 흑색 감광성 수지 조성물, 이를 이용하여 제조된 감광성 수지막 및 상기 감광성 수지막을 포함하는 표시장치가 제공된다.
Description
본 기재는 흑색 감광성 수지 조성물, 이를 이용하여 제조된 감광성 수지막 및 상기 감광성 수지막을 포함하는 표시장치에 관한 것이다.
흑색 감광성 수지 조성물은 컬러필터, 액정표시재료, 유기발광소자(EL), 디스플레이 패널 재료 등의 표시 소자의 제조에 필수적인 재료이다. 예를 들어, 컬러 액정 디스플레이 등의 컬러필터에는 표시 콘트라스트나 발색 효과를 높이기 위해, 레드(red), 그린(green), 블루(blue) 등의 착색층 간의 경계 부분에 블랙 매트릭스나 차광용 격벽이 필요하고, 이는 주로 흑색 감광성 수지 조성물로 형성되는 것이다.
특히, 최근의 액정 표시 디스플레이의 개발 방향은 고휘도 및 고색재현율에 맞춰져 있다. 즉, 야외에서 들어오는 빛의 반사율을 저감시켜 고휘도 및 고색재현율을 달성하려는 시도가 있으며, 따라서 블랙 매트릭스나 차광용 격벽의 반사율을 낮추려는 노력이 계속되고 있다. 또한 해상도(8k)가 높아지면서 미세 블랙 매트릭스 패턴의 구현 요구도 높아지고 있다.
디스플레이의 반사율 저하를 위해서 주로 개발하고 있는 방법은 편광필름의 반사방지 필름인 AR(Anti Reflective) 필름과 AG(Anti Glare) 필름을 적용하는 방법이다.
그러나, 이와 같은 방법은 이제 한계에 봉착하여, 다른 방법으로 반사율을 저감시키려는 노력이 계속되고 있다.
일 구현예는 차광 특성과 저반사 특성을 동시에 구현하면서, 해상도 또한 우수한 흑색 감광성 수지 조성물을 제공하기 위한 것이다.
다른 일 구현예는 상기 감광성 수지 조성물을 이용하여 제조된 감광성 수지막을 제공하기 위한 것이다.
또 다른 일 구현예는 상기 감광성 수지막을 포함하는 표시장치를 제공하기 위한 것이다.
일 구현예는 (A) 아크릴계 바인더 수지 및 카도계 바인더 수지를 포함하는 바인더 수지; (B) 광중합성 단량체; (C) 광중합 개시제; (D) 흑색 착색제; (E) 50nm 이하의 평균입경을 가지는 다공성 나노졸; 및 (F) 용매를 포함하는 흑색 감광성 수지 조성물을 제공한다.
상기 다공성 나노졸은 10nm 내지 50nm의 평균입경을 가질 수 있다.
상기 다공성 나노졸은 카본나노튜브, 중공 실리카 또는 이들의 조합을 포함할 수 있다.
상기 다공성 나노졸은 상기 흑색 감광성 수지 조성물 총량에 대해 1 중량% 내지 10 중량%로 포함될 수 있다.
상기 흑색 착색제는 카본블랙을 포함할 수 있다.
상기 카본블랙은 30nm 내지 100nm의 1차 입경을 가질 수 있다.
상기 카본블랙은 45ml/100g 내지 90ml/100g의 오일 흡유량을 가질 수 있다.
상기 카도계 바인더 수지는 상기 아크릴계 바인더 수지보다 많은 함량으로 포함될 수 있다.
상기 아크릴계 바인더 수지 및 카도계 바인더 수지는 각각 독립적으로 1,000 g/mol 내지 50,000 g/mol의 중량평균분자량을 가질 수 있다.
상기 감광성 수지 조성물은, 상기 감광성 수지 조성물 총량에 대해, 상기 (A) 바인더 수지 0.5 중량% 내지 20 중량%; 상기 (B) 광중합성 단량체 1 중량% 내지 10 중량%; 상기 (C) 광중합 개시제 0.1 중량% 내지 10 중량%; 상기 (D) 흑색 착색제 1 중량% 내지 20 중량%; 상기 (E) 다공성 나노졸 1 중량% 내지 10 중량%; 및 상기 (F) 용매 잔부량을 포함할 수 있다.
상기 감광성 수지 조성물은 말론산, 3-아미노-1,2-프로판디올, 실란계 커플링제, 레벨링제, 계면활성제 또는 이들의 조합을 더 포함할 수 있다.
다른 일 구현예는 상기 흑색 감광성 수지 조성물을 이용하여 제조된 감광성 수지막을 제공한다.
상기 감광성 수지막은 블랙 매트릭스 또는 차광용 격벽일 수 있다.
또 다른 일 구현예는 상기 감광성 수지막을 포함하는 표시장치를 제공한다.
상기 표시장치는 액정 디스플레이 소자(LCD)를 포함할 수 있다.
기타 본 발명의 측면들의 구체적인 사항은 이하의 상세한 설명에 포함되어 있다.
일 구현예에 따른 감광성 수지 조성물은 차광성과 저반사 특성을 동시에 구현할 수 있으며, 나아가 해상도 또한 우수하게 유지할 수 있다.
이하, 본 발명의 구현예를 상세히 설명하기로 한다. 다만, 이는 예시로서 제시되는 것으로, 이에 의해 본 발명이 제한되지는 않으며 본 발명은 후술할 청구범위의 범주에 의해 정의될 뿐이다.
본 명세서에서 특별한 언급이 없는 한, "알킬기"란 C1 내지 C20 알킬기를 의미하고, "알케닐기"란 C2 내지 C20 알케닐기를 의미하고, "사이클로알케닐기"란 C3 내지 C20 사이클로알케닐기를 의미하고, "헤테로사이클로알케닐기"란 C3 내지 C20 헤테로사이클로알케닐기를 의미하고, "아릴기"란 C6 내지 C20 아릴기를 의미하고, "아릴알킬기"란 C6 내지 C20 아릴알킬기를 의미하며, "알킬렌기"란 C1 내지 C20 알킬렌기를 의미하고, "아릴렌기"란 C6 내지 C20 아릴렌기를 의미하고, "알킬아릴렌기"란 C6 내지 C20 알킬아릴렌기를 의미하고, "헤테로아릴렌기"란 C3 내지 C20 헤테로아릴렌기를 의미하고, "알콕실렌기"란 C1 내지 C20 알콕실렌기를 의미한다.
본 명세서에서 특별한 언급이 없는 한, "치환"이란 적어도 하나의 수소 원자가 할로겐원자(F, Cl, Br, I), 히드록시기, C1 내지 C20 알콕시기, 니트로기, 시아노기, 아민기, 이미노기, 아지도기, 아미디노기, 히드라지노기, 히드라조노기, 카르보닐기, 카르바밀기, 티올기, 에스테르기, 에테르기, 카르복실기 또는 그것의 염, 술폰산기 또는 그것의 염, 인산이나 그것의 염, C1 내지 C20 알킬기, C2 내지 C20 알케닐기, C2 내지 C20 알키닐기, C6 내지 C20 아릴기, C3 내지 C20 사이클로알킬기, C3 내지 C20 사이클로알케닐기, C3 내지 C20 사이클로알키닐기, C2 내지 C20 헤테로사이클로알킬기, C2 내지 C20 헤테로사이클로알케닐기, C2 내지 C20 헤테로사이클로알키닐기, C3 내지 C20 헤테로아릴기 또는 이들의 조합의 치환기로 치환된 것을 의미한다.
또한 본 명세서에서 특별한 언급이 없는 한, "헤테로"란, 화학식 내에 N, O, S 및 P 중 적어도 하나의 헤테로 원자가 적어도 하나 포함된 것을 의미한다.
또한 본 명세서에서 특별한 언급이 없는 한, "(메타)아크릴레이트"는 "아크릴레이트"와 "메타크릴레이트" 둘 다 가능함을 의미하며, "(메타)아크릴산"은 "아크릴산"과 "메타크릴산" 둘 다 가능함을 의미한다.
본 명세서에서 별도의 정의가 없는 한, "조합"이란 혼합 또는 공중합을 의미한다. 또한 "공중합"이란 블록 공중합 내지 랜덤 공중합을 의미하고, "공중합체"란 블록 공중합체 내지 랜덤 공중합체를 의미한다.
본 명세서 내 화학식에서 별도의 정의가 없는 한, 화학 결합이 그려져야 하는 위치에 화학결합이 그려져 있지 않은 경우는 상기 위치에 수소 원자가 결합되어 있음을 의미한다.
본 명세서에서 카도계 수지란, 하기 화학식 1-1 내지 화학식 1-11로 이루어진 군에서 선택된 하나 이상의 관능기가 수지 내 주골격(backbone)에 포함되는 수지를 의미한다.
본 명세서에서 별도의 정의가 없는 한, "*"는 동일하거나 상이한 원자(수소원자 포함) 또는 화학식과 연결되는 부분을 의미한다.
본 명세서에서 별도의 정의가 없는 한, 굴절율이란 550nm 파장에서의 굴절율을 의미한다.
일 구현예에 따른 흑색 감광성 수지 조성물은 (A) 아크릴계 바인더 수지 및 카도계 바인더 수지를 포함하는 바인더 수지; (B) 광중합성 단량체; (C) 광중합 개시제; (D) 흑색 착색제; (E) 50nm 이하의 평균입경을 가지는 다공성 나노졸; 및 (F) 용매를 포함하기 때문에, 일 구현예에 따른 흑색 감광성 수지 조성물을 이용하여 제조된 감광성 수지막, 예컨대 블랙 매트릭스나 차광용 격벽은 종래 블랙 매트릭스나 차광용 격벽과 비교하여 차광성과 저반사 특성을 모두 구현할 수 있으며, 해상도 또한 우수하다.
구체적으로, 일 구현예에 따른 흑색 감광성 수지 조성물은 컬러필터 내 Red, Green, Blue 색간 구별을 위한 블랙 매트릭스나 차광용 격벽에 적용되는데, 종래에는 블랙 매트릭스나 차광용 격벽용 조성물은 효과적인 차광 특성을 구현하기 위해 카본블랙을 주성분으로 하는 조성물이 대부분이었다. 카본블랙을 주성분으로 할 경우 광학밀도가 높아 차광 특성 구현에는 적합하나, 시인성 개선이 이루어지지 않는다는 문제점이 있다. 본 발명자들은 시인성 개선을 위해 패널의 반사율을 낮추는 방향으로 개발을 진행하였으며, 여러 번의 시행착오 끝에 아크릴계 바인더 수지와 카도계 바인더 수지를 혼용하면서 다공성 나노졸의 크기를 제어함으로써 카본블랙의 차광성을 저해하지 않으면서도 저반사 특성을 구현할 수 있으며, 나아가 해상도도 보다 개선시킬 수 있음을 확인하고, 본 발명을 완성하기에 이르렀다. 실제로 반사율 개선을 위한 필름(예컨대, 저반사 편광 필름 등)을 부착하는 방식이 시도된 적이 있으나, 편광 필름의 가격이 비싸고, 해당기술로 구현 가능한 반사율이 이미 하한치에 다다랐기 때문에 한계가 왔다고 평가되고 있어, 다른 방향으로 반사율을 낮출 수 있는 블랙 매트릭스 제조용 조성물의 개발이 이루어지고 있다. 특히 8K 고해상도 모델의 TV의 경우 블랙 매트릭스의 표면적이 4K 대비 약 2배 증가하기 때문에, 차광성뿐만 아니라 반사율이 낮을수록 시인성 개선 효과는 더욱 커질 수 있다.
이하에서 각 성분에 대하여 구체적으로 설명한다.
(E) 다공성 나노졸
일 구현예에 따른 흑색 감광성 수지 조성물은 i) 50nm 이하의 평균입경을 가지는 다공성 나노졸을 후술하는 ii) 흑색 착색제 및 iii) 2종의 바인더 수지와 함께 포함하기에, 저반사 특성과 차광 특성을 동시에 구현할 수 있으며, 해상도도 개선시킬 수 있다. 상기 다공성 나노졸의 평균입경이 50nm 초과인 경우에는 후술하는 용매에 대한 상용성이 떨어져 저반사 특성 구현이 어렵다. 또한, 상기 흑색 착색제를 함께 사용하지 않을 경우 차광 특성을 구현할 수 없고, 무엇보다 2종의 바인더 수지, 즉 아크릴계 바인더 수지와 카도계 바인더 수지를 혼용해서 사용하지 않을 경우, 50nm 이하의 평균입경을 가지는 다공성 나노졸을 사용하더라도 반사율을 낮추는 데 한계가 있으며, 해상도 개선 측면에서도 바람직하지 않다.
예컨대, 상기 다공성 나노졸은 10nm 내지 50nm의 평균입경을 가질 수 있다. 상기 다공성 나노졸이 상기 범위의 평균입경을 가질 경우 차광 특성과 저반사 특성을 동시에 구현하면서, 해상도도 개선시키기에 유리할 수 있다.
상기 다공성 나노졸은 그 종류가 다양한데, 예컨대 카본나노튜브, 중공 실리카 또는 이들의 조합을 포함할 수 있으나, 반드시 이에 한정되는 것은 아니다. 예컨대, 상기 다공성 나노졸은 카본나노튜브일 수 있다. 상기 카본나노튜브는 그 입경, 보다 구체적으로 직경을 50nm 이하로 제어함으로써 저반사 특성을 구현할 수 있으며, 또한 일 구현예에 따른 흑색 감광성 수지 조성물의 저항을 낮추어 주어 빛샘 현상을 효과적으로 방지할 수 있기에, 차광 특성도 용이하게 구현할 수 있다. 상기 카본나노튜브는 그 직경을 상기와 같이 제어해야 하나, 길이도 함께 제어해야만 하는 것은 아니다. 예컨대, 상기 카본나노튜브는 1㎛ 내지 500㎛의 길이를 가질 수 있으나, 반드시 이에 한정되는 것은 아니다. 상기 카본나노튜브는 일반적으로 사용되는 단일벽(single wall), 이중벽(duble wall), 다중 (multi wall)의 구조 및 다발형 구조로 이루어진 군으로부터 선택되는 적어도 하나를 사용할 수 있으며, 반드시 이에 한정되는 것은 아니다. 상기 카본나노튜브는 표면안정화를 위해 산처리하여 사용할 수 있으며, 상기 산으로는 질산(HNO3), 염산(HCl), 인산(H3PO4), 불화붕소산(HBF4), 불산(HF), 황산(H2SO4) 및 디노닐나프탈렌술폴산으로 이루어진 군으로부터 선택된 하나 이상 또는 그 수용액을 사용할 수 있다. 상기 산 수용액인 경우, 산 수용액의 농도는 5 중량% 내지 99 중량%일 수 있다. 상기 산처리는 6초 내지 120분 동안 실시할 수 있다.
상기 다공성 나노졸로 중공 실리카를 사용할 수도 있는데, 중공 실리카는 상기 카본나노튜브와 달리 흑색 감광성 수지 조성물의 저항을 낮추어 주어 빛샘 현상을 방지하는 기능을 수행하지 못하기에 차광 특성 구현 측면에서는 불리할 수 있다.
상기 다공성 나노졸은 상기 흑색 감광성 수지 조성물 총량에 대해 1 중량% 내지 10 중량%, 예컨대5중량% 내지 10 중량%로 포함될 수 있다. 상기 다공성 나노졸이 상기 함량범위로 포함되는 것이, 흑색 착색제와의 상용성이 우수하여 저반사 특성 및 우수한 패턴성을 유지하면서, 동시에 차광성도 확보할 수 있다.
(A) 바인더 수지
상기 바인더 수지는 카도계 바인더 수지 및 아크릴계 바인더 수지를 포함한다. 상기 바인더 수지는 반드시 상기 2종의 바인더 수지를 모두 포함하며, 예컨대 상기 바인더 수지로 카도계 바인더 수지만을 단독으로 사용할 경우 저반사 특성을 구현하기가 어려우며, 상기 바인더 수지로 아크릴계 바인더 수지만을 단독으로 사용할 경우 저반사 특성 구현이 어려우면서 해상도 또한 개선시키기 어렵다.
예컨대, 상기 카도계 바인더 수지는 상기 아크릴계 바인더 수지보다 많은 함량으로 포함될 수 있다. 상기 카도계 바인더 수지가 상기 아크릴계 바인더 수지보다 많은 함량으로 포함될 경우 차광 특성, 저반사 특성 및 우수한 해상도를 동시에 구현하는데 보다 유리할 수 있다. 또한, 현상성 및 공정마진 향상에도 유리할 수 있다.
상기 바인더 수지는 상기 카도계 바인더 수지 및 아크릴계 바인더 수지 외에, 폴리이미드계 바인더 수지, 폴리우레탄계 바인더 수지 또는 이들의 조합의 수지를 더 포함할 수 있다.
상기 카도계 바인더 수지의 중량평균분자량은 1,000 g/mol 내지 50,000 g/mol일 수 있고, 구체적으로는 3,000 g/mol 내지 35,000 g/mol일 수 있다. 상기 카도계 바인더 수지의 중량평균분자량이 상기 범위 내일 경우 블랙 매트릭스나 차광용 격벽 제조 시 우수한 패턴성 및 현상성을 얻을 수 있다.
상기 카도계 바인더 수지는 하기 화학식 1로 표시되는 반복단위를 포함하는 화합물일 수 있다.
[화학식 1]
상기 화학식 1에서,
R24 내지 R27은 각각 독립적으로 수소 원자, 할로겐 원자, 또는 치환 또는 비치환된 C1 내지 C20 알킬기일 수 있고,
R28 및 R29는 각각 독립적으로 수소 원자, 또는 CH2ORa(Ra는 비닐기, 아크릴기 또는 메타크릴기)일 수 있고,
R30은 수소 원자, 치환 또는 비치환된 C1 내지 C20 알킬기, 치환 또는 비치환된 C2 내지 C20 알케닐기, 아크릴기, 또는 메타크릴기일 수 있고,
Z1은 단일결합, O, CO, SO2, CRbRc, SiRdRe(여기서, Rb 내지 Re는 서로 동일하거나 상이하며, 수소 원자, 또는 치환 또는 비치환된 C1 내지 C20 알킬기임), 또는 하기 화학식 2 내지 화학식 12로 표시되는 화합물로 이루어진 군에서 선택되는 어느 하나일 수 있고,
Z2는 산무수물 잔기 또는 산이무수물 잔기일 수 있다.
[화학식 2]
[화학식 3]
[화학식 4]
[화학식 5]
[화학식 6]
상기 화학식 6에서,
Rf는 수소 원자, 에틸기, C2H4Cl, C2H4OH, CH2CH=CH2, 또는 페닐기이다.
[화학식 7]
[화학식 8]
[화학식 9]
[화학식 10]
[화학식 11]
[화학식 12]
상기 카도계 바인더 수지는 구체적으로 하기 화학식 13으로 표시되는 화합물을 테트라카르복실산 이무수물과 반응시켜 얻을 수 있다.
[화학식 13]
상기 테트라카르복시산 이무수물은 방향족 테트라카르복시산 이무수물일 수 있다. 상기 방향족 테트라카르복시산 이무수물의 예로는, 피로멜릭산 이무수물, 3,3',4,4'-비페닐테트라카르복시산 이무수물, 2,3,3',4-비페닐테트라카르복시산 이무수물, 2,2',3,3'-비페닐테트라카르복시산 이무수물, 3,3',4,4'-벤조페논테트라카르복시산 이무수물, 3,3',4,4'-비페닐에테르테트라카르복시산 이무수물, 3,3',4,4'-디페닐술폰테트라카르복시산 이무수물, 1,2,3,4-사이클로펜탄테트라카르복시산 이무수물, 1,2,5,6-나프탈렌테트라카르복시산 이무수물, 2,3,6,7-나프탈렌테트라카르복시산 이무수물, 1,4,5,8-나프탈렌테트라카르복시산 이무수물, 2,3,5,6-피리딘테트라카르복시산 이무수물, 3,4,9,10-페릴렌테트라카르복시산 이무수물, 2,2-비스(3,4-디카르복시페닐)헥사플루오로프로판 이무수물 등을 들 수 있으나, 이에 한정되는 것은 아니다.
상기 아크릴계 바인더 수지는 제1 에틸렌성 불포화 단량체 및 이와 공중합 가능한 제2 에틸렌성 불포화 단량체의 공중합체로, 하나 이상의 아크릴계 반복단위를 포함하는 수지이다.
상기 제1 에틸렌성 불포화 단량체는 하나 이상의 카르복시기를 함유하는 에틸렌성 불포화 단량체이며, 이의 구체적인 예로는 아크릴산, 메타크릴산, 말레산, 이타콘산, 푸마르산 또는 이들의 조합을 들 수 있다.
상기 제1 에틸렌성 불포화 단량체는 상기 아크릴계 바인더 수지 총량에 대하여 5 내지 50 중량%로 포함될 수 있고, 구체적으로는 10 내지 40 중량%로 포함될 수 있다.
상기 제2 에틸렌성 불포화 단량체는 스티렌, α-메틸스티렌, 비닐톨루엔, 비닐벤질메틸에테르 등의 방향족 비닐 화합물; 메틸(메타)아크릴레이트, 에틸(메타)아크릴레이트, 부틸(메타)아크릴레이트, 2-히드록시에틸(메타)아크릴레이트, 2-히드록시 부틸(메타)아크릴레이트, 벤질(메타)아크릴레이트, 사이클로헥실(메타)아크릴레이트, 페닐(메타)아크릴레이트 등의 불포화 카르복시산 에스테르 화합물; 2-아미노에틸(메타)아크릴레이트, 2-디메틸아미노에틸(메타)아크릴레이트 등의 불포화 카르복시산 아미노 알킬 에스테르 화합물; 초산비닐, 안식향산 비닐 등의 카르복시산 비닐 에스테르 화합물; 글리시딜(메타)아크릴레이트 등의 불포화 카르복시산 글리시딜 에스테르 화합물; (메타)아크릴로니트릴 등의 시안화 비닐 화합물; (메타)아크릴아미드 등의 불포화 아미드 화합물; 등을 들 수 있으며, 이들을 단독으로 또는 둘 이상 혼합하여 사용할 수 있다.
상기 아크릴계 바인더 수지의 구체적인 예로는 메타크릴산/벤질메타크릴레이트 공중합체, 메타크릴산/벤질메타크릴레이트/스티렌 공중합체, 메타크릴산/벤질메타크릴레이트/2-히드록시에틸메타크릴레이트 공중합체, 메타크릴산/벤질메타크릴레이트/스티렌/2-히드록시에틸메타크릴레이트 공중합체 등을 들 수 있으나, 이에 한정되는 것은 아니며, 이들을 단독 또는 2종 이상을 배합하여 사용할 수도 있다.
상기 아크릴계 바인더 수지의 중량평균분자량은 1,000 g/mol 내지 50,000 g/mol일 수 있고, 구체적으로는 5,000 g/mol 내지 50,000 g/mol일 수 있고, 더욱 구체적으로는 20,000 g/mol 내지 30,000 g/mol일 수 있다. 상기 아크릴계 바인더 수지의 중량평균분자량이 상기 범위 내일 경우, 상기 흑색 감광성 수지 조성물의 물리적 및 화학적 물성이 우수하고 점도가 적절하며, 차광층 제조시 기판과의 밀착성이 우수하다.
상기 아크릴계 바인더 수지의 산가는 15 mgKOH/g 내지 60 mgKOH/g일 수 있고, 구체적으로는 20 mgKOH/g 내지 50 mgKOH/g일 수 있다. 상기 아크릴계 바인더 수지의 산가가 상기 범위 내일 경우 픽셀 패턴의 해상도가 우수하다.
상기 바인더 수지는 상기 감광성 수지 조성물 총량에 대하여 0.5 중량% 내지 20 중량%, 예컨대 1 중량% 내지 10 중량%로 포함될 수 있다. 상기 바인더 수지가 상기 범위 내로 포함될 경우, 점도가 적절히 유지되어 블랙 매트릭스나 차광용 격벽 제조 시 패턴성, 공정성 및 현상성이 우수하다.
(B) 광중합성 단량체
상기 광중합성 단량체는 적어도 1개의 에틸렌성 불포화 이중결합을 가지는 (메타)아크릴산의 일관능 또는 다관능 에스테르가 사용될 수 있다.
상기 아크릴계 광중합성 단량체는 상기 에틸렌성 불포화 이중결합을 가짐으로써, 패턴 형성 공정에서 노광 시 충분한 중합을 일으킴으로써 내열성, 내광성 및 내화학성이 우수한 패턴을 형성할 수 있다.
상기 광중합성 단량체의 구체적인 예로는, 에틸렌 글리콜 디(메타)아크릴레이트, 디에틸렌 글리콜 디(메타)아크릴레이트, 트리에틸렌 글리콜 디(메타)아크릴레이트, 프로필렌 글리콜 디(메타)아크릴레이트, 네오펜틸 글리콜 디(메타)아크릴레이트, 1,4-부탄디올 디(메타)아크릴레이트, 1,6-헥산디올 디(메타)아크릴레이트, 비스페놀A 디(메타)아크릴레이트, 펜타에리트리톨 디(메타)아크릴레이트, 펜타에리트리톨 트리(메타)아크릴레이트, 펜타에리트리톨 테트라(메타)아크릴레이트, 펜타에리트리톨 헥사(메타)아크릴레이트, 디펜타에리트리톨 디(메타)아크릴레이트, 디펜타에리트리톨 트리(메타)아크릴레이트, 디펜타에리트리톨 펜타(메타)아크릴레이트, 디펜타에리트리톨 헥사(메타)아크릴레이트, 비스페놀A 에폭시(메타)아크릴레이트, 에틸렌 글리콜 모노메틸에테르 (메타)아크릴레이트, 트리메틸올 프로판 트리(메타)아크릴레이트, 트리스(메타)아크릴로일옥시에틸 포스페이트, 노볼락에폭시 (메타)아크릴레이트 등을 들 수 있다.
상기 광중합성 단량체의 시판되는 제품을 예로 들면 다음과 같다. 상기 (메타)아크릴산의 일관능 에스테르의 예로는, 도아 고세이 화학공업(주)社의 아로닉스 M-101®, 아로닉스 M-111®, 아로닉스 M-114® 등; 일본화학(주)社의 KAYARAD TC-110S®, KAYARAD TC-120S® 등; 오사카 유끼 화학공업(주)社의 V-158®, V-2311® 등을 들 수 있다. 상기 (메타)아크릴산의 이관능 에스테르의 예로는, 도아 고세이 화학공업(주)社의 아로닉스 M-210®, 아로닉스 M-240®, 아로닉스 M-6200® 등; 일본화학(주)社의 KAYARAD HDDA®, KAYARAD HX-220®, KAYARAD R-604® 등; 오사카 유끼 화학공업(주)社의 V-260®, V-312®, V-335 HP® 등을 들 수 있다. 상기 (메타)아크릴산의 삼관능 에스테르의 예로는, 도아 고세이 화학공업(주)社의 아로닉스 M-309®, 아로닉스 M-400®, 아로닉스 M-405®, 아로닉스 M-450®, 아로닉스 M-710®, 아로닉스 M-8030®, 아로닉스 M-8060® 등; 일본화학(주)社의 KAYARAD TMPTA®, KAYARAD DPCA-20®, KAYARAD-30®, KAYARAD-60®, KAYARAD-120® 등; 오사카 유끼 화학공업(주)社의 V-295®, V-300®, V-360®, V-GPT®, V-3PA®, V-400® 등을 들 수 있다. 상기 제품을 단독 사용 또는 2종 이상 함께 사용할 수 있다.
상기 광중합성 단량체는 보다 우수한 현상성을 부여하기 위하여 산무수물로 처리하여 사용할 수도 있다.
상기 광중합성 단량체는 상기 감광성 수지 조성물 총량 대비 1 중량% 내지 10 중량%, 예컨대 5 중량% 내지 10 중량%로 포함될 수 있다. 상기 광중합성 단량체가 상기 범위 내로 포함될 경우, 패턴 형성 공정에서 노광시 경화가 충분히 일어나 신뢰성이 우수하며, 알칼리 현상액에의 현상성이 우수하다.
(C) 광중합 개시제
상기 광중합 개시제는 아세토페논계 화합물, 벤조페논계 화합물, 티오크산톤계 화합물, 벤조인계 화합물, 트리아진계 화합물, 옥심계 화합물 또는 이들의 조합 등을 사용할 수 있다.
상기 아세토페논계 화합물의 예로는, 2,2'-디에톡시 아세토페논, 2,2'-디부톡시 아세토페논, 2-히드록시-2-메틸프로피오페논, p-t-부틸트리클로로 아세토페논, p-t-부틸디클로로 아세토페논, 4-클로로 아세토페논, 2,2'-디클로로-4-페녹시 아세토페논, 2-메틸-1-(4-(메틸티오)페닐)-2-모폴리노프로판-1-온, 2-벤질-2-디메틸아미노-1-(4-모폴리노페닐)-부탄-1-온 등을 들 수 있다.
상기 벤조페논계 화합물의 예로는, 벤조페논, 벤조일 안식향산, 벤조일 안식향산 메틸, 4-페닐 벤조페논, 히드록시 벤조페논, 아크릴화 벤조페논, 4,4'-비스(디메틸 아미노)벤조페논, 4,4'-비스(디에틸아미노)벤조페논, 4,4'-디메틸아미노벤조페논,4,4'-디클로로벤조페논, 3,3'-디메틸-2-메톡시벤조페논 등을 들 수 있다.
상기 티오크산톤계 화합물의 예로는, 티오크산톤, 2-클로로티오크산톤, 2-메틸티오크산톤, 이소프로필 티오크산톤, 2,4-디에틸 티오크산톤, 2,4-디이소프로필 티오크산톤 등을 들 수 있다.
상기 벤조인계 화합물의 예로는, 벤조인, 벤조인 메틸 에테르, 벤조인 에틸 에테르, 벤조인 이소프로필 에테르, 벤조인 이소부틸 에테르, 벤질디메틸케탈 등을 들 수 있다.
상기 트리아진계 화합물의 예로는, 2,4,6-트리클로로-s-트리아진, 2-페닐 4,6-비스(트리클로로메틸)-s-트리아진, 2-(3',4'-디메톡시스티릴)-4,6-비스(트리클로로메틸)-s-트리아진, 2-(4'-메톡시나프틸)-4,6-비스(트리클로로메틸)-s-트리아진, 2-(p-메톡시페닐)-4,6-비스(트리클로로메틸)-s-트리아진, 2-(p-톨릴)-4,6-비스(트리클로로 메틸)-s-트리아진, 2-비페닐 4,6-비스(트리클로로 메틸)-s-트리아진, 비스(트리클로로메틸)-6-스티릴-s-트리아진, 2-(나프토1-일)-4,6-비스(트리클로로메틸)-s-트리아진, 2-(4-메톡시나프토1-일)-4,6-비스(트리클로로메틸)-s-트리아진, 2-4-비스(트리클로로메틸)-6-피페로닐-s-트리아진, 2-4-비스(트리클로로메틸)-6-(4-메톡시스티릴)-s-트리아진등을 들 수 있다.
상기 옥심계 화합물의 예로는 O-아실옥심계화합물, 2-(O-벤조일옥심)-1-[4-(페닐티오)페닐]-1,2-옥탄디온, 1-(O-아세틸옥심)-1-[9-에틸-6-(2-메틸벤조일)-9H-카르바졸-3-일]에탄온, O-에톡시카르보닐-α-옥시아미노-1-페닐프로판-1-온, 1-(3-사이클로펜틸-1-(9-에틸-6-(2-메틸벤조일)-9H-카바졸-3-일)프로필리덴아미노옥시)에탄온, 2-(벤조일옥시이미노)-3-사이클로펜틸-1-(4-(페닐티오)페닐)프로판-1-온 등을 사용할 수 있다. 상기 O-아실옥심계 화합물의 구체적인 예로는, 1,2-옥탄디온, 2-디메틸아미노-2-(4-메틸벤질)-1-(4-모르폴린-4-일-페닐)-부탄-1-온, 1-(4-페닐술파닐페닐)-부탄-1,2-디온-2-옥심-O-벤조에이트, 1-(4-페닐술파닐페닐)-옥탄-1,2-디온-2-옥심-O-벤조에이트, 1-(4-페닐술파닐페닐)-옥탄-1-온옥심-O-아세테이트 및 1-(4-페닐술파닐페닐)-부탄-1-온옥심-O-아세테이트 등을 사용할 수 있다.
상기 광중합 개시제는 상기 화합물 이외에도 카바졸계 화합물, 디케톤류 화합물, 술포늄 보레이트계 화합물, 디아조계 화합물, 이미다졸계 화합물, 비이미다졸계 화합물, 플루오렌계 화합물 등을 사용할 수 있다.
상기 광중합 개시제는 상기 감광성 수지 조성물 총량 대비 0.1 중량% 내지 10 중량%, 예컨대 0.1 중량% 내지 5 중량%로 포함될 수 있다. 상기 광중합 개시제가 상기 범위 내로 포함될 경우, 패턴 형성 공정에서 노광 시 광중합이 충분히 일어나게 되어, 제조된 블랙 매트릭스나 차광용 격벽의 감도가 우수해지게 된다.
(D) 흑색 착색제
전술한 다공성 나노졸과의 상용성을 고려하되, 차광성을 높여 흑색을 용이하게 구현하기 위해, 상기 흑색 착색제는 카본블랙, 티탄블랙 등의 무기흑색안료를 포함할 수 있다. 무기흑색안료는 유기흑색안료에 비해 차광성이 매우 우수하며, 전술한 무기입자와의 상용성 또한 우수해, 일 구현예에 따른 감광성 수지 조성물 내 흑색 착색제로 사용되기에 적합할 수 있다.
예컨대, 상기 무기흑색안료, 구체적으로 카본블랙은 30nm 내지 100nm의 1차 입경을 가질 수 있다.
여기서, 카본블랙의 '1차 입경'이란, 투과 전자 현미경(TEM) 또는 X선 회절장치(XRD) 등을 이용하여 측정한 카본블랙 입자의 지름을 의미하고, 카본블랙의 '2차 입경'은 1차 입자들이 사슬(chain)처럼 다방향으로 연결된 2차 입자의 크기로써, 이는 후술하는 오일 흡유량으로도 표시될 수 있다.
예컨대, 상기 무기흑색안료, 구체적으로 카본블랙은 45ml/100g 내지 90ml/100g의 오일 흡유량을 가질 수 있다. 여기서, “오일 흡유량”이란, 카본블랙에 오일을 첨가하여 일정한 유동도가 있는 반죽상태로 만드는데 필요한 오일의 양을 의미한다. 보통 안료 100g에 대한 기름의 ml로써 표시한다.
1차 입경이 30nm 내지 100nm 이면서 오일흡유량이 45ml/100g 내지 90ml/100g인 카본블랙을 흑색 착색제로 사용할 경우, 전술한 다공성 나노졸과의 상용성이 우수해져 저반사 특성 구현에 유리해지며, 또한 미세 패턴의 형성이 가능하고, 테이퍼 앵글을 조절하여 원하는 모양과 수치로 상기 미세 패턴을 디자인할 수 있는 바, 밀착력이 우수한 흑색 감광성 수지막을 얻을 수 있다.
상기 흑색 착색제는 이를 구성하는 단독 또는 각각의 안료를 분산시키기 위해 분산제를 함께 사용할 수 있다. 구체적으로는, 상기 단독 또는 각각의 안료를 분산제로 미리 표면처리하여 사용하거나, 조성물 제조 시 안료와 함께 분산제를 첨가하여 사용할 수 있다.
상기 분산제로는 비이온성 분산제, 음이온성 분산제, 양이온성 분산제 등을 사용할 수 있다. 상기 분산제의 구체적인 예로는, 폴리 알킬렌 글리콜 및 이의 에스테르, 폴리 옥시 알킬렌, 다가 알코올 에스테르 알킬렌 옥사이드 부가물, 알코올 알킬렌 옥사이드 부가물, 술폰산에스테르, 술폰산염, 카르복실산 에스테르, 카르복실산염, 알킬 아미드 알킬렌 옥사이드 부가물, 알킬 아민 등을 들 수 있으며, 이들을 단독으로 또는 둘 이상 혼합하여 사용할 수 있다.
상기 분산제의 시판되는 제품을 예로 들면, BYK社의 DISPERBYK-101, DISPERBYK-130, DISPERBYK-140, DISPERBYK-160, DISPERBYK-161, DISPERBYK-162, DISPERBYK-163, DISPERBYK-164, DISPERBYK-165, DISPERBYK-166, DISPERBYK-170, DISPERBYK-171, DISPERBYK-182, DISPERBYK-2000, DISPERBYK-2001 등; EFKA 케미칼社의 EFKA-47, EFKA-47EA, EFKA-48, EFKA-49, EFKA-100, EFKA-400, EFKA-450 등; Zeneka社의 Solsperse 5000, Solsperse 12000, Solsperse 13240, Solsperse 13940, Solsperse 17000, Solsperse 20000, Solsperse 24000GR, Solsperse 27000, Solsperse 28000 등; 또는 Ajinomoto社의 PB711, PB821 등이 있다.
상기 분산제는 상기 감광성 수지 조성물 총량 대비 0.1 중량% 내지 15 중량%로 포함될 수 있다. 분산제가 상기 범위 내로 포함될 경우, 조성물의 분산성이 우수함에 따라 차광용 격벽 제조 시 안정성, 현상성 및 패턴성이 우수하다.
상기 안료는 수용성 무기염 및 습윤제를 이용하여 전처리하여 사용할 수도 있다. 안료를 상기 전처리하여 사용할 경우 안료의 평균입경을 미세화할 수 있다.
상기 전처리는 상기 안료를 수용성 무기염 및 습윤제와 함께 니딩(kneading)하는 단계, 그리고 상기 니딩단계에서 얻어진 안료를 여과 및 수세하는 단계를 거쳐 수행될 수 있다.
상기 니딩은 40℃내지 100℃의 온도에서 수행될 수 있고, 상기 여과 및 수세는 물 등을 사용하여 무기염을 수세한 후 여과하여 수행될 수 있다.
상기 수용성 무기염의 예로는 염화나트륨, 염화칼륨 등을 들 수 있으나, 이에 한정되는 것은 아니다. 상기 습윤제는 상기 안료 및 상기 수용성 무기염이 균일하게 섞여 안료가 용이하게 분쇄될 수 있는 매개체 역할을 하며, 그 예로는 에틸렌 글리콜 모노에틸에테르, 프로필렌 글리콜 모노메틸에테르, 디에틸렌 글리콜 모노메틸에테르 등과 같은 알킬렌 글리콜 모노알킬에테르; 에탄올, 이소프로판올, 부탄올, 헥산올, 시클로헥산올, 에틸렌글리콜, 디에틸렌글리콜, 폴리에틸렌글리콜, 글리세린폴리에틸렌글리콜 등과 같은 알코올 등을 들 수 있으며, 이들을 단독 또는 둘 이상 혼합하여 사용할 수 있다.
상기 니딩 단계를 거친 안료는 5 nm 내지 200 nm, 예컨대 5 nm 내지 150 nm의 평균 입경을 가질 수 있다. 안료의 평균 입경이 상기 범위 내인 경우, 안료 분산액에서의 안정성이 우수하고, 픽셀의 해상성 저하의 우려가 없다.
구체적으로, 상기 무기흑색안료는 상기 분산제 및 PGMEA 등의 용매를 포함하는 안료분산액의 형태로 사용될 수 있고, 상기 안료분산액은 고형분의 안료, 분산제 및 용매를 포함할 수 있다. 상기 고형분의 안료는 상기 안료분산액 총량에 대해 15 중량% 내지 40 중량%, 예컨대 20 중량% 내지 30 중량%로 포함될 수 있다.
상기 흑색 착색제는 상기 감광성 수지 조성물 총량 대비 1 중량% 내지 20 중량%, 예컨대 1 중량% 내지 15 중량%로 포함될 수 있다. 상기 흑색 착색제가 상기 범위 내로 포함될 경우, 흑색 구현 효과 및 현상 성능이 우수해지게 된다.
(F) 용매
상기 용매는 상기 다공성 나노졸, 바인더 수지, 광중합성 단량체, 광중합 개시제, 흑색 착색제 및 후술하는 기타 첨가제 등과의 상용성을 가지되 반응하지 않는 물질들이 사용될 수 있다.
상기 용매의 예로는, 메탄올, 에탄올 등의 알코올류; 디클로로에틸에테르, n-부틸에테르, 디이소아밀에테르, 메틸페닐에테르, 테트라히드로퓨란 등의 에테르류; 에틸렌글리콜모노메틸에테르, 에틸렌글리콜모노에틸에테르, 에틸렌글리콜디메틸에테르 등의 글리콜에테르류; 메틸셀로솔브아세테이트, 에틸셀로솔브아세테이트, 디에틸셀로솔브아세테이트 등의 셀로솔브아세테이트류; 메틸에틸카르비톨, 디에틸카르비톨, 디에틸렌글리콜모노메틸에테르, 디에틸렌글리콜모노에틸에테르, 디에틸렌글리콜디메틸에테르, 디에틸렌글리콜에틸메틸에테르, 디에틸렌글리콜디에틸에테르 등의 카르비톨류; 프로필렌글리콜메틸에테르아세테이트, 프로필렌글리콜프로필에테르아세테이트 등의 프로필렌글리콜알킬에테르아세테이트류; 톨루엔, 크실렌 등의 방향족탄화수소류; 메틸에틸케톤, 사이클로헥사논, 4-히드록시-4-메틸-2-펜타논, 메틸-n-프로필케톤, 메틸-n-부틸케톤, 메틸-n-아밀케톤, 2-헵타논 등의 케톤류; 초산에틸, 초산-n-부틸, 초산이소부틸 등의 포화 지방족 모노카르복실산알킬에스테르류; 젖산메틸, 젖산에틸 등의 젖산에스테르류; 옥시초산메틸, 옥시초산에틸, 옥시초산부틸 등의 옥시초산알킬에스테르류; 메톡시초산메틸, 메톡시초산에틸, 메톡시초산부틸, 에톡시초산메틸, 에톡시초산에틸 등의 알콕시초산알킬에스테르류; 3-옥시프로피온산메틸, 3-옥시프로피온산에틸 등의 3-옥시프로피온산알킬에스테르류; 3-메톡시프로피온산메틸, 3-메톡시프로피온산에틸, 3-에톡시프로피온산에틸, 3-에톡시프로피온산메틸 등의 3-알콕시프로피온산알킬에스테르류; 2-옥시프로피온산메틸, 2-옥시프로피온산에틸, 2-옥시프로피온산프로필 등의 2-옥시프로피온산알킬에스테르류; 2-메톡시프로피온산메틸, 2-메톡시프로피온산에틸, 2-에톡시프로피온산에틸, 2-에톡시프로피온산메틸 등의 2-알콕시프로피온산알킬에스테르류; 2-옥시-2-메틸프로피온산메틸, 2-옥시-2-메틸프로피온산에틸 등의2-옥시-2-메틸프로피온산에스테르류, 2-메톡시-2-메틸프로피온산메틸, 2-에톡시-2-메틸프로피온산에틸 등의 2-알콕시-2-메틸프로피온산알킬류의 모노옥시모노카르복실산알킬에스테르류; 2-히드록시프로피온산에틸, 2-히드록시-2-메틸프로피온산에틸, 히드록시초산에틸, 2-히드록시-3-메틸부탄산메틸 등의 에스테르류; 피루빈산에틸 등의 케톤산에스테르류 등이 있으며, 또한, N-메틸포름아미드, N,N-디메틸포름아미드, N-메틸포름아닐라드, N-메틸아세트아미드, N,N-디메틸아세트아미드, N-메틸피롤리돈, 디메틸술폭시드, 벤질에틸에테르, 디헥실에테르, 아세틸아세톤, 이소포론, 카프론산, 카프릴산, 1-옥탄올, 1-노난올, 벤질알코올, 초산벤질, 안식향산에틸, 옥살산디에틸, 말레인산디에틸, γ부티로락톤, 3-메틸벤조산, 3-메톡시부틸아세테이트, 탄산에틸렌, 탄산프로필렌, 페닐셀로솔브아세테이트 등의 고비점 용매를 들 수 있다.
이들 중 좋게는 상용성 및 반응성을 고려하여, 사이클로헥사논 등의 케톤류; 에틸렌글리콜모노에틸에테르, 에틸렌글리콜디메틸에테르, 에틸렌글리콜디에틸에테르, 디에틸렌글리콜에틸메틸에테르 등의 글리콜에테르류; 에틸셀로솔브아세테이트 등의 에틸렌글리콜알킬에테르아세테이트류; 2-히드록시프로피온산에틸 등의 에스테르류; 디에틸렌글리콜모노메틸에테르 등의 카르비톨류; 프로필렌글리콜모노메틸에테르아세테이트, 프로필렌글리콜프로필에테르아세테이트 등의 프로필렌글리콜알킬에테르아세테이트류, 3-메틸벤조산, 3-메톡시부틸아세테이트 등이 사용될 수 있다.
상기 용매는 상기 감광성 수지 조성물 총량 대비 잔부량, 예컨대 30 중량% 내지 90 중량%, 예컨대 60 중량% 내지 90 중량%, 예컨대 70 중량% 내지 90 중량%로 포함될 수 있다. 상기 용매가 상기 범위 내로 포함될 경우 흑색 감광성 수지 조성물이 적절한 점도를 가짐에 따라 블랙 매트릭스나 차광용 격벽 제조 시 공정성이 우수하다.
(G) 기타 첨가제
한편, 상기 감광성 수지 조성물은 말론산, 3-아미노-1,2-프로판디올, 실란계 커플링제, 레벨링제, 계면활성제 또는 이들의 조합의 첨가제를 더 포함할 수 있다.
상기 실란계 커플링제는 기판과의 밀착성 등을 개선하기 위해 비닐기, 카르복실기, 메타크릴옥시기, 이소시아네이트기, 에폭시기 등의 반응성 치환기를 가질 수 있다.
상기 실란계 커플링제의 예로는, 트리메톡시실릴벤조산, γ메타크릴옥시프로필트리메톡시실란, 비닐트리아세톡시실란, 비닐트리메톡시실란, γ이소시아네이트프로필트리에톡시실란, γ글리시독시프로필트리메톡시실란, β에폭시사이클로헥실)에틸트리메톡시실란 등을 들 수 있으며, 이들을 단독 또는 2종 이상 혼합하여 사용할 수 있다.
상기 실란계 커플링제는 상기 감광성 수지 조성물 총량 대비 0.01 중량부 내지 10 중량부로 포함될 수 있다. 상기 실란계 커플링제가 상기 범위 내로 포함될 경우 밀착성, 저장성 등이 우수하다.
또한 상기 감광성 수지 조성물은 필요에 따라 코팅성 향상 및 결점생성 방지효과를 위해 계면활성제, 예컨대 불소계 계면활성제 및/또는 실리콘계 계면활성제를 더 포함할 수 있다.
상기 불소계 계면활성제로는, BM Chemie社의 BM-1000®, BM-1100®등; 다이닛폰잉키가가꾸고교(주)社의 메카팩 F 142D®, 메카팩 F 172®, 메카팩 F 173®, 메카팩 F 183®, 메카팩 F 554® 등; 스미토모스리엠(주)社의 프로라드 FC-135®, 프로라드 FC-170C®, 프로라드 FC-430®, 프로라드 FC-431® 등; 아사히그라스(주)社의 사프론 S-112®, 사프론 S-113®, 사프론 S-131®, 사프론 S-141®, 사프론 S-145®등; 도레이실리콘(주)社의 SH-28PA®, SH-190®, SH-193®, SZ-6032®, SF-8428® 등의 명칭으로 시판되고 있는 것을 사용할 수 있다.
상기 실리콘계 계면활성제로는 BYK Chem社의 BYK-307, BYK-333, BYK-361N, BYK-051, BYK-052, BYK-053, BYK-067A, BYK-077, BYK-301, BYK-322, BYK-325등의 명칭으로 시판되고 있는 것을 사용할 수 있다.
상기 계면활성제는 상기 감광성 수지 조성물 총량 대비 0.001 중량부 내지 5 중량부로 사용될 수 있다. 상기 계면활성제가 상기 범위 내로 포함될 경우 코팅 균일성이 확보되고, 얼룩이 발생하지 않으며, IZO 기판 또는 유리기판에 대한 습윤성(wetting)이 우수하다.
또한 상기 감광성 수지 조성물은 물성을 저해하지 않는 범위 내에서 산화방지제, 안정제 등의 기타 첨가제가 일정량 첨가될 수도 있다.
일 구현예에 따른 감광성 수지 조성물은 포지티브형일 수도 있고, 네가티브형일 수도 있으나, 차광성을 가지는 조성물의 노광 및 현상 후 패턴이 노출되는 영역의 잔기(residue)를 보다 완벽하게 제거하기 위해서는 네가티브형인 것이 보다 바람직하다.
다른 일 구현예는 전술한 흑색 감광성 수지 조성물을 노광, 현상 및 경화하여 제조된 (흑색) 감광성 수지막, 예컨대 블랙 매트릭스 또는 차광용 격벽을 제공한다.
상기 감광성 수지막 제조방법은 다음과 같다.
(1) 도포 및 도막 형성 단계
흑색 감광성 수지 조성물을 소정의 전처리를 한 유리 기판 또는 ITO 기판 등의 기판 상에 스핀 또는 슬릿 코트법, 롤 코트법, 스크린 인쇄법, 어플리케이터법 등의 방법을 사용하여 원하는 두께로 도포한 후, 70℃내지 110℃에서 1분 내지 10분 동안 가열(프리베이킹)하여 용제를 제거함으로써 도막을 형성한다.
(2) 노광 단계
상기 얻어진 도막에 필요한 패턴 형성을 위해 마스크를 개재한 뒤, 200 nm 내지 500 nm의 활성선을 조사하여 노광을 진행한다. 조사에 사용되는 광원으로는 저압 수은등, 고압 수은등, 초고압 수은등, 금속 할로겐화물 램프, 아르곤 가스 레이저 등을 사용할 수 있으며, 경우에 따라 X선, 전자선 등도 이용할 수 있다.
노광량은 조성물 각 성분의 종류, 배합량 및 건조 막 두께에 따라 다르지만, 고압 수은등을 사용하는 경우에는 500 mJ/cm2(365 nm 센서에 의함) 이하이다.
(3) 현상 단계
알칼리성 수용액을 현상액으로 이용하여 불필요한 부분을 용해, 제거함으로써 노광 부분만을 잔존시켜 패턴을 형성시킨다.
(4) 후처리 단계
현상에 의해 수득된 화상 패턴을 내열성, 밀착성, 내화학성 등의 측면에서 우수한 패턴을 얻기 위한 후가열 공정이 있다. 예컨대, 현상 후 250℃의 컨벡션 오븐에 현상에 의해 수득된 화상 패턴을 넣은 후 1시간 동안 가열(포스트베이킹)할 수 있다.
또 다른 일 구현예는 상기 감광성 수지막을 포함하는 표시장치를 제공한다.
예컨대, 상기 표시장치는 액정 디스플레이 소자(LCD)를 포함할 수 있다.
이하, 본 발명의 바람직한 실시예를 기재한다. 다만, 하기의 실시예는 본 발명의 바람직한 일실시예일 뿐, 본 발명이 하기 실시예에 의해 한정되는 것은 아니다.
(흑색 감광성 수지 조성물 제조)
하기 언급된 구성성분들을 하기 표 1 및 표 2에 나타낸 조성으로 혼합 후, 6시간 동안 교반하여, 실시예 1 내지 실시예 11 및 비교예 1 내지 비교예 10에 따른 흑색 감광성 수지 조성물을 제조하였다. 구체적으로 광중합 개시제 함량을 정확히 측정한 뒤, 용제를 투입한 후 개시제가 다 녹을 때까지 충분히 교반하였다. 이 후, 바인더 수지와 광중합성 단량체를 순차적으로 첨가한 뒤, 다시 1시간 가량 교반하였다. 이 후, 다공성 나노졸 및 기타 첨가제를 투입하고, 흑색 착색제(안료 분산액)을 넣은 후, 최종적으로 조성물 전체를 2시간 이상 교반하여, 감광성 수지 조성물을 제조하였다.
실시예 1 | 실시예 2 | 실시예 3 | 실시예 4 | 실시예 5 | 실시예 6 | 실시예 7 | 실시예 8 | 실시예 9 | 실시예 10 | 실시예 11 | ||
(A) 바인더 수지 | (A-1) | 3.63 | 3.63 | 3.63 | 3.63 | 1.55 | 2.59 | 3.63 | 3.63 | 3.63 | 3.63 | 3.63 |
(A-2) | 1.55 | 1.55 | 1.55 | 1.55 | 3.63 | 2.59 | 1.55 | 1.55 | 1.55 | 1.55 | 1.55 | |
(B) 광중합성 단량체 | 5.18 | 5.18 | 5.18 | 5.18 | 5.18 | 5.18 | 5.18 | 5.18 | 5.18 | 5.18 | 5.18 | |
(C) 광중합 개시제 | 0.19 | 0.19 | 0.19 | 0.19 | 0.19 | 0.19 | 0.19 | 0.19 | 0.19 | 0.19 | 0.19 | |
(D) 흑색 착색제 | (D-1) | 4.56 | 4.56 | 4.56 | 4.56 | 4.56 | 4.56 | |||||
(D-2) | 4.56 | |||||||||||
(D-3) | 4.56 | |||||||||||
(D-4) | 4.56 | |||||||||||
(D-5) | 4.56 | |||||||||||
(D-6) | 4.56 | |||||||||||
(E) 다공성 나노졸 | (E-1) | 10 | 10 | 10 | 10 | 10 | 10 | 10 | 10 | |||
(E-2) | 10 | |||||||||||
(E-3) | 10 | |||||||||||
(E-4) | ||||||||||||
(E-5) | 10 | |||||||||||
(F) 용매 | (F-1) | 58.34 | 58.34 | 58.34 | 58.34 | 58.34 | 58.34 | 58.34 | 58.34 | 58.34 | 58.34 | 58.34 |
(F-2) | 16.2 | 16.2 | 16.2 | 16.2 | 16.2 | 16.2 | 16.2 | 16.2 | 16.2 | 16.2 | 16.2 | |
(G) 기타 첨가제 | 0.35 | 0.35 | 0.35 | 0.35 | 0.35 | 0.35 | 0.35 | 0.35 | 0.35 | 0.35 | 0.35 |
교 비교예 2 | 비교예 3 | 비교예 4 | 비교예 5 | 비교예 6 | 비교예 7 | 비교예 8 | 비교예 9 | 비교예 10 | |||||||||||||||||
수101 | 6.13 | 5.18 | 3.63 | 5.18 | 5.18 | ||||||||||||||||||||
10.18 | 4.05 | 5.18 | 1.55 | 5.18 | 5.18 | ||||||||||||||||||||
0110.18 | 10.18 | 5.18 | 5.18 | 5.18 | 5.18 | 5.18 | 5.18 | 5.18 | |||||||||||||||||
광개010.19 | 0.19 | 0.19 | 0.19 | 0.19 | 0.19 | 0.19 | 0.19 | 0.19 | |||||||||||||||||
흑색(D-1) | |||||||||||||||||||||||||
E다성나졸(E-1) | (E-2) | ||||||||||||||||||||||||
(E-3) | (E-4) | ||||||||||||||||||||||||
(E-5) | () 매(F-1) | ||||||||||||||||||||||||
0.35 | 0.35 | 0.35 | 0.35 | 0.35 | 0.35 | 0.35 | 0.35 | 0.35 |
(A) 바인더 수지
(A-1) 카도계 바인더 수지 (KBR-101, 경인社)
(A-2) 아크릴계 바인더 수지 (RY-25, Showa Denko社)
(B) 광중합성 단량체
디펜타에리트리톨 헥사(메타)아크릴레이트 (DPHA, 일본화약社)
(C) 광중합 개시제
NCI831E (ADEKA社)
(D) 흑색 착색제
(D-1) 1차 입경이 30nm이고, 오일 흡유량이 45ml/100g인 카본블랙 안료 분산액 (SAKATA社)
(D-2) 1차 입경이 50nm이고, 오일 흡유량이 90ml/100g인 카본블랙 안료 분산액 (SAKATA社)
(D-3) 1차 입경이 100nm이고, 오일 흡유량이 80ml/100g인 카본블랙 안료 분산액 (SAKATA社)
(D-4) 1차 입경이 30nm이고, 오일 흡유량이 35ml/100g인 카본블랙 안료 분산액 (SAKATA社)
(D-5) 1차 입경이 28nm이고, 오일 흡유량이 60ml/100g인 카본블랙 안료 분산액 (SAKATA社)
(D-6) 1차 입경이 120nm이고, 오일 흡유량이 200ml/100g인 카본블랙 안료 분산액 (SAKATA社)
(E) 다공성 나노졸
(E-1) 카본나노튜브 (Dito technology, 평균직경: 10nm)
(E-2) 카본나노튜브 (Sanyo, 평균직경: 50nm)
(E-3) 카본나노튜브 (Sanyo, 평균직경: 1nm)
(E-4) 카본나노튜브 (Sanyo, 평균직경: 60nm)
(E-5) 중공 실리카 (나노신소재, 평균입경: 50nm)
(F) 용매
(F-1) 프로필렌 글리콜 모노메틸에테르 아세테이트 (PGMEA, Sigma-Aldrich)
(F-2) 디에틸렌글리콜메틸에틸에테르 (EDM, Sigma-Aldrich)
(G) 기타 첨가제
γ-글리시독시 프로필 트리메톡시실란 (S-510, Chisso)
(평가)
광학밀도 및 반사율
상기 실시예 1 내지 실시예 11 및 비교예 1 내지 비교예 10에서 제조된 흑색 감광성 수지 조성물을 각각 유리기판 상에 스핀 코팅하고, 약 100℃에서 90초 동안 pre-bake하여 약 1.2㎛의 두께로 도포하였다. 그 다음 실온에서 60초 동안 냉각한 후, 초고압 수은 램프로 30mJ/㎠의 자외선을 전면 조사하여 감광 부분의 광경화 반응을 유도하였다. 상기 노광된 기판을 실온에서 0.043% KOH 수용액에서 스프레이 방식으로 현상한 후, 순수 용매로 60초 동안 세정하였다. 그 후 실온에서 건조한 후 230℃의 컨벡션 오븐에서 30분간 post-bake하여 전면 시편을 얻었다. 상기 시편 형성 후, 광학밀도를 X-rite 장비를 이용하여 측정하고, 반사율을 CM-3700A(코니카 미놀타) 장비를 이용하여 측정한 후, 그 결과를 하기 표 3에 나타내었다.
해상도
상기 실시예 1 내지 실시예 11 및 비교예 1 내지 비교예 10에서 제조된 흑색 감광성 수지 조성물을 각각 유리기판 상에 스핀 코팅하고, 약 100℃에서 90초 동안 pre-bake하여 약 1.3㎛의 두께로 도포하였다. 그 다음 실온에서 60초 동안 냉각한 후, 초고압 수은 램프로 40mJ/㎠의 자외선을 패턴 사이즈가 split되어 있는 마스크에 조사하여 감광 부분의 광경화 반응을 유도하였다. 상기 노광된 기판을 실온에서 0.043% KOH 수용액에서 스프레이 방식으로 현상한 후, 순수 용매로 60초 동안 세정하였다. 그 후 실온에서 건조한 후 230℃의 컨벡션 오븐에서 30분간 post-bake하여 패턴 시편을 얻었다. 상기 시편 형성 후, BX-51(올림푸스) 장비를 이용하여 해상도를 측정하고, 그 결과를 하기 표 3에 나타내었다.
광학밀도 (/㎛) | 반사율 (%) | 해상도 (㎛) | |
실시예 1 | ◎ | ◎ | ◎ |
실시예 2 | ◎ | ◎ | ◎ |
실시예 3 | ◎ | ○ | ○ |
실시예 4 | ◎ | ○ | ○ |
실시예 5 | ○ | ◎ | ○ |
실시예 6 | ◎ | ◎ | ○ |
실시예 7 | ◎ | ◎ | ◎ |
실시예 8 | ◎ | ◎ | ◎ |
실시예 9 | ◎ | ○ | ◎ |
실시예 10 | ◎ | ○ | ◎ |
실시예 11 | ◎ | ○ | ◎ |
비교예 1 | ◎ | △ | ◎ |
비교예 2 | ◎ | △ | ◎ |
비교예 3 | ◎ | △ | ◎ |
비교예 4 | △ | ○ | ◎ |
비교예 5 | △ | ◎ | △ |
비교예 6 | ◎ | △ | ◎ |
비교예 7 | ◎ | △ | ◎ |
비교예 8 | ◎ | △ | ◎ |
비교예 9 | ◎ | ○ | △ |
비교예 10 | ◎ | ○ | △ |
광학밀도, 반사율 및 해상도 평가기준
- 광학밀도: ◎ (>4.5) / ○(4.5≥x>4.2) / △(≤4.2)
- 반사율 : ◎(<5.5), ○(5.9>x≥5.5), △(≥5.9)
- 해상도(Resolution) : ◎(<7), ○(10>x≥7), △(≥10)
상기 표 3으로부터, 일 구현예에 따른 흑색 감광성 수지 조성물은 차광 특성과 저반사 특성을 동시에구현하면서 해상도 또한 우수한 것을 확인할 수 있다.
본 발명은 상기 실시예들에 한정되는 것이 아니라 서로 다른 다양한 형태로 제조될 수 있으며, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자는 본 발명의 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예들은 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해해야만 한다.
Claims (15)
- (A) 아크릴계 바인더 수지 및 카도계 바인더 수지를 포함하는 바인더 수지;
(B) 광중합성 단량체;
(C) 광중합 개시제;
(D) 흑색 착색제;
(E) 50nm 이하의 평균입경을 가지는 카본나노튜브; 및
(F) 용매
를 포함하는 흑색 감광성 수지 조성물.
- 제1항에 있어서,
상기 카본나노튜브는 10nm 내지 50nm의 평균입경을 가지는 흑색 감광성 수지 조성물.
- 삭제
- 제1항에 있어서,
상기 카본나노튜브는 상기 흑색 감광성 수지 조성물 총량에 대해 1 중량% 내지 10 중량%로 포함되는 흑색 감광성 수지 조성물.
- 제1항에 있어서,
상기 흑색 착색제는 카본블랙을 포함하는 흑색 감광성 수지 조성물.
- 제5항에 있어서,
상기 카본블랙은 30nm 내지 100nm의 1차 입경을 가지는 흑색 감광성 수지 조성물.
- 제5항에 있어서,
상기 카본블랙은 45ml/100g 내지 90ml/100g의 오일 흡유량을 가지는 흑색 감광성 수지 조성물.
- 제1항에 있어서,
상기 카도계 바인더 수지는 상기 아크릴계 바인더 수지보다 많은 함량으로 포함되는 흑색 감광성 수지 조성물.
- 제1항에 있어서,
상기 아크릴계 바인더 수지 및 카도계 바인더 수지는 각각 독립적으로 1,000 g/mol 내지 50,000 g/mol의 중량평균분자량을 가지는 흑색 감광성 수지 조성물.
- 제1항에 있어서,
상기 흑색 감광성 수지 조성물은, 상기 흑색 감광성 수지 조성물 총량에 대해,
상기 (A) 바인더 수지 0.5 중량% 내지 20 중량%;
상기 (B) 광중합성 단량체 1 중량% 내지 10 중량%;
상기 (C) 광중합 개시제 0.1 중량% 내지 10 중량%;
상기 (D) 흑색 착색제 1 중량% 내지 20 중량%;
상기 (E) 카본나노튜브 1 중량% 내지 10 중량%; 및
상기 (F) 용매 잔부량
을 포함하는 흑색 감광성 수지 조성물.
- 제1항에 있어서,
상기 흑색 감광성 수지 조성물은 말론산, 3-아미노-1,2-프로판디올, 실란계 커플링제, 레벨링제, 계면활성제 또는 이들의 조합을 더 포함하는 흑색 감광성 수지 조성물.
- 제1항, 제2항 및 제4항 내지 제11항 중 어느 한 항의 흑색 감광성 수지 조성물을 이용하여 제조된 감광성 수지막.
- 제12항에 있어서,
상기 감광성 수지막은 블랙 매트릭스 또는 차광용 격벽인 감광성 수지막.
- 제12항의 감광성 수지막을 포함하는 표시장치.
- 제14항에 있어서,
상기 표시장치는 액정 디스플레이 소자(LCD)를 포함하는 표시장치.