KR101955326B1 - Buoy and its manufacturing method - Google Patents
Buoy and its manufacturing method Download PDFInfo
- Publication number
- KR101955326B1 KR101955326B1 KR1020170030498A KR20170030498A KR101955326B1 KR 101955326 B1 KR101955326 B1 KR 101955326B1 KR 1020170030498 A KR1020170030498 A KR 1020170030498A KR 20170030498 A KR20170030498 A KR 20170030498A KR 101955326 B1 KR101955326 B1 KR 101955326B1
- Authority
- KR
- South Korea
- Prior art keywords
- foam
- coating layer
- buoy
- protective layer
- forming
- Prior art date
Abstract
본 발명은, 발포체의 내·외부 및 보호층이 코팅된 부표를 형성하여 햇빛 및 온도변화에 따른 발포체와 코팅층의 분리현상을 방지하므로 부표 본래의 기능을 유지함과 아울러 외부의 충격으로부터 발포체를 보호할 수 있으므로 제품의 수명을 연장하면서 안정감있게 사용할 수 있는 코팅층 및 보호층을 구비한 친환경 부표 및 이의 제조방법에 관한 것이다.The present invention forms a buoy coated with the inside and outside of the foam and the protective layer to prevent separation of the foam and the coating layer due to the change of the sunlight and the temperature so as to maintain the original function of the buoy and to protect the foam from external impact Friendly buoy having a coating layer and a protective layer which can be used with stability while extending the life of the product, and a method for producing the buoy.
Description
본 발명은 부표에 관한 것으로, 보다 상세하게는, 발포체의 내·외부 및 보호층이 코팅된 부표를 형성하여 햇빛 및 온도변화에 따른 발포체와 코팅층의 분리현상을 방지하는 코팅층 및 보호층을 구비한 친환경 부표 및 이의 제조방법에 관한 것이다.The present invention relates to a buoy, and more particularly, to a buoy having a coating layer and a protective layer for preventing the separation of the foam layer and the coating layer due to sunlight and temperature change by forming buoys coated with the inside and outside of the foam and the protective layer Friendly buoy and its manufacturing method.
일반적으로 부표는 부력을 이용하여 각종 수산물 양식에 필요한 시설이나 부교 등의 부상 시설물을 물 위에 띄우기 위해 사용되는 도구이며, 통상 스티로폼으로 성형한 원통형의 스티로폼의 외주면에 마대를 감아 끈으로 연결하여 사용하였다.In general, buoy is a tool used to float float facilities such as facilities and bridge for water aquaculture using buoyancy, and is usually connected to a circumference of a cylindrical styrofoam formed by styrofoam, .
그러나 스티로폼으로 제작되는 부표는 재질이 연약하고 표면이 매끄럽지 않아 조류나 파도, 작업선 등의 외부 충격이 그대로 전달되어 쉽게 부스러지고, 강한 자외선에 의해 조직이 손상되어 사용 수명이 짧아 자주 교체하여야 할 뿐만 아니라 그에 따른 경제적 손실이 증가하며, 파손된 스티로폼이 수면 위로 부유하여 심각한 오염을 일으키는 문제점이 있었다.However, buoys made of styrofoam are weak in material and smooth on the surface, so they are easily damaged by the external impacts such as algae, waves and work lines, and are damaged by strong ultraviolet rays. However, there is a problem in that the economic loss is increased, and the damaged styrofoam floats on the surface of water and causes serious pollution.
또한, 스티로폼 재질의 밀도가 낮고 표면이 거칠어서 각종 해조류 및 패류 등의 이물질이 부착되기 쉽고 스티로폼 내부에 수분이 침투되어 시간이 갈수록 부력이 급격히 저하되어 사용이 어려운 문제점이 있었다.Also, since the density of the styrofoam material is low and the surface is rough, various seaweeds and shellfish are easily adhered to the styrofoam, and the water is infiltrated into the styrofoam.
상기의 문제점을 해결하기 위한 방법으로 등록된 대한민국 등록특허 제10-1599258호는 부표에 보호층을 형성하여 종래의 문제점을 해결할 수 있었으나, 햇빛 및 온도변화에 따라 내열온도가 낮은 스티로폼이 변형되면서 보호층과 스티로폼의 분리현상이 발생하고 보호층을 별도로 구매하여야 하므로 제조원가가 상승하는 문제점이 있었다.Korean Registered Patent No. 10-1599258, which is registered as a method for solving the above problems, has solved the conventional problems by forming a protective layer on the buoys. However, when the styrofoam having a low heat- The separation of the layer and styrofoam occurs, and the protective layer needs to be separately purchased, which raises the manufacturing cost.
본 발명은 상기와 같은 문제점을 해결하기 위해 안출된 것으로서, 발포체의 내·외부 및 보호층이 코팅된 부표를 형성하여 햇빛 및 온도변화에 따른 발포체와 코팅층의 분리현상을 방지하는 데 그 목적이 있다.SUMMARY OF THE INVENTION The present invention has been made to solve the above-mentioned problems, and it is an object of the present invention to prevent foaming and coating layer separation due to sunlight and temperature change by forming buoys coated with inner and outer surfaces of a foam and a protective layer .
본 발명 코팅층 및 보호층을 구비한 친환경 부표는,The eco-friendly buoy having the coating layer and the protective layer of the present invention,
발포 폴리프로필렌(expanded polyproptlene) 또는 발포 폴리에틸렌(expanded polythylene)으로 내부에 수용공간이 형성되는 발포체가 구비되고, 상기 발포체 내주면에 형성되어 발포체를 보호하는 내부 코팅층이 구비되며, 상기 발포체 외주면에 형성되어 외부의 충격으로부터 발포체를 보호하는 외부 코팅층이 구비된 제1몸체와;An internal coating layer is formed on an inner circumferential surface of the foam to protect the foam, and is formed on the outer circumferential surface of the foam, and is formed on the outer surface of the foam, A first body having an outer coating layer for protecting the foam from impacts of the first body;
발포 폴리프로필렌(expanded polyproptlene) 또는 발포 폴리에틸렌(expanded polythylene)으로 내부에 수용공간이 형성되는 발포체가 구비되고, 상기 발포체 내주면에 형성되어 발포체를 보호하는 내부 코팅층이 구비되며, 상기 발포체 외주면에 형성되어 외부의 충격으로부터 발포체를 보호하는 외부 코팅층이 구비된 제2몸체와;An internal coating layer is formed on an inner circumferential surface of the foam to protect the foam, and is formed on the outer circumferential surface of the foam, and is formed on the outer surface of the foam, A second body having an outer coating layer for protecting the foam from the impact of the first body;
상기 제1·2몸체의 수용공간이 대응되도록 제1·2몸체를 대향하게 밀착시킨 후, 밀착된 연결부위를 열융착으로 고정하고, 제1·2몸체의 외부코팅층에 외부의 충격으로부터 발포체를 이중으로 보호하는 보호층을 포함하는 것을 특징으로 한다.The first and second bodies are brought into close contact with each other so as to correspond to the accommodation spaces of the first and second bodies, and then the tightly connected portions are fixed by thermal fusion, and the outer coat layer of the first and second bodies is foamed And a protective layer for protecting the protective layer.
상기 발포체에 자외선 차단제를 포함한다.The foam contains an ultraviolet screening agent.
상기 보호층에 자외선 차단제를 포함한다.The protective layer contains an ultraviolet blocking agent.
본 발명 코팅층 및 보호층을 구비한 친환경 부표의 제조방법은,A method of manufacturing an eco-friendly buoy having a coating layer and a protective layer according to the present invention,
금형 내부로 발포 폴리프로필렌(expanded polyproptlene) 또는 발포 폴리에틸렌(expanded polythylene)을 공급하는 원료 공급단계와;A supply step of supplying expanded polypropylene or expanded polythylene into the mold;
상기 원료가 공급된 금형을 가열부의 열로 가열하여 반원형의 발포체를 형성하는 발포체 형성단계와;A foam forming step of heating a mold supplied with the raw material with heat of a heating part to form a semicircular foam;
상기 발포체의 내부면을 가열부의 열로 녹여 내부 코팅층을 형성하고, 상기 발포체의 외부면을 가열부의 열로 녹여 외부 코팅층을 형성하는 코팅층 형성단계와;A coating layer forming step of forming an inner coating layer by melting the inner surface of the foamed body with the heat of the heating part and melting the outer surface of the foamed body with heat of the heating part to form an outer coating layer;
상기 내·외부 코팅층이 형성된 반원형의 발포체를 대향하게 위치시킨 후, 발포체의 연결부위를 열융착으로 고정하여 원통형의 고정몸체를 형성하는 고정몸체형성단계와;A fixed body forming step of placing a semicircular foam having the inner and outer coating layers formed thereon in opposition to each other and then fixing the connecting portion of the foam by thermal fusion to form a cylindrical fixed body;
상기 외부 코팅층에 보호층을 형성하는 보호층 형성단계를 포함하는 것을 특징으로 한다.
또한, 코팅층과 보호층을 구비한 친환경 부표의 제조방법은,
발포 폴리프로필렌(expanded polypropylene) 또는 발포 폴리에틸렌(expanded polyethlene)의 원료를 금형 내부로 공급하는 원료 공급단계;
상기 원료가 공급된 금형을 가열부의 열로 가열하여 반원형의 발포체를 형성하는 발포체 형성단계;
상기 발포체의 내부면과 외부면을 발포체를 형성하는 온도보다 더 높은 온도로 가열 및 용융시켜 발포체의 내부면과 외부면에 내부 및 외부 코팅층을 발포체에 동시에 형성하는 코팅층 형성단계;
상기 내부 및 외부 코팅층이 형성된 발포체를 대향하게 위치시킨 후, 발포체의 연결부위를 열융착으로 고정하여 고정몸체를 형성하는 고정몸체 형성단계; 및
상기 고정몸체의 외부 코팅층에 도료를 도포하여 보호층을 형성하는 단계;를 포함한다.And forming a protective layer on the outer coating layer.
Further, a method of manufacturing an environment friendly buoy having a coating layer and a protective layer,
A raw material supplying step of supplying a raw material of expanded polypropylene or expanded polyethlene into a mold;
A foam forming step of heating a mold supplied with the raw material with heat of a heating part to form a semicircular foam;
A coating layer forming step of heating and melting the inner and outer surfaces of the foam at a temperature higher than the temperature at which the foam is formed to simultaneously form inner and outer coating layers on the inner and outer surfaces of the foam on the foam;
Forming a fixed body by locating the foams on which the inner and outer coating layers are formed, and fixing the connecting portions of the foam by thermal fusion; And
And applying a coating material to the outer coating layer of the fixed body to form a protective layer.
본 발명에 의하면, 발포체의 내·외부 및 보호층이 코팅된 부표를 형성하여 햇빛 및 온도변화에 따른 발포체와 코팅층의 분리현상을 방지하므로 부표 본래의 기능을 유지할 수 있는 효과가 있다.According to the present invention, it is possible to maintain the original function of the buoy by preventing the separation of the foam and the coating layer due to the change of sunlight and temperature by forming the buoys coated with the inside / outside and the protective layer of the foam.
또한, 내·외부 및 보호층이 삼중으로 코팅된 부표는 외부의 충격으로부터 발포체를 보호할 수 있으므로 제품의 수명을 연장하면서 안정감있게 사용할 수 있는 효과가 있다.In addition, buoys coated with inner / outer and protective layers in triplets can protect the foam from external impact, so that the life of the product can be extended and the product can be used in a stable manner.
도 1은 본 발명에 따른 부표의 제조공정도
도 2는 본 발명에 따른 부표의 분리사시도
도 3 내지 도 6은 본 발명에 따른 부표의 제조과정도Fig. 1 is a view showing a process of manufacturing a buoy according to the present invention
2 is an exploded perspective view of a buoy according to the present invention;
FIGS. 3 to 6 show a process of manufacturing the buoy according to the present invention
이하, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 본 발명의 실시예에 대하여 첨부한 도면을 참고로 하여 상세히 설명한다. 그러나 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며 여기에서 설명하는 실시예에 한정되지 않는다. 명세서 전체를 통하여 유사한 부분에 대해서는 동일한 도면 부호를 붙였다.Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings so that those skilled in the art can easily carry out the present invention. The present invention may, however, be embodied in many different forms and should not be construed as limited to the embodiments set forth herein. Like parts are designated with like reference numerals throughout the specification.
도 1은 본 발명에 따른 부표의 제조공정도이고, 도 2는 본 발명에 따른 부표의 분리사시도이다.FIG. 1 is a view showing a manufacturing process of a buoy according to the present invention, and FIG. 2 is an exploded perspective view of a buoy according to the present invention.
도 1 내지 도 2를 참조하면, 본 발명 친환경 부표(100)는, 제1몸체(110), 제2몸체(120) 및 보호층(130)을 포함한다.1 and 2, the
상기 제1몸체(110)는, 비드폼이면서 내충격성 및 내구성이 우수하여 미세분말화의 진행이 안되는 발포 폴리프로필렌(expanded polyproptlene) 또는 발포 폴리에틸렌(expanded polythylene) 등으로 반원형으로 발포체(111)가 제조되는데, 상기 발포체(111)는 반원형으로 한정하는 것은 아니며, 다각형상 등 다양한 형상으로 제조될 수 있다.The
상기 발포체(111) 내부의 수용공간(111a)에는 복수의 리브(111b)를 형성하여 발포체(111)를 보강할 수도 있다.A plurality of
상기 발포체(111) 내·외주면에는 외부의 충격으로부터 발포체(111)를 보호하는 내·외부 코팅층(112)(113)이 형성된다.On the inner and outer peripheral surfaces of the
상기 제2몸체(120)는, 비드폼이면서 내충격성 및 내구성이 우수하여 미세분말화의 진행이 안되는 발포 폴리프로필렌(expanded polyproptlene) 또는 발포 폴리에틸렌(expanded polythylene) 등으로 반원형으로 발포체(111)가 제조되는데, 상기 발포체(121)는 반원형으로 한정하는 것은 아니며, 다각형상 등 다양한 형상으로 제조될 수 있다.The
상기 발포체(121) 내부의 수용공간(121a)에는 복수의 리브(121b)를 형성하여 발포체(121)를 보강할 수도 있다.A plurality of
상기 발포체(121) 내·외주면에는 외부의 충격으로부터 발포체(121)를 보호하는 내·외부 코팅층(122)(123)이 형성된다.On the inner and outer peripheral surfaces of the
또한, 상기 발포체(111)(121)를 형성하는 발포 폴리프로필렌(expanded polyproptlene) 또는 발포 폴리에틸렌(expanded polythylene)에 자외선 차단제를 부가하여 발포체의 강도를 더 높일 수도 있다.In addition, the ultraviolet ray blocking agent may be added to the expanded polypropylene or expanded polythylene forming the
상기 보호층(130)은, 수용공간(111a)(121a)이 대응되는 제1·2몸체(110)(120)의 연결부위를 열융착으로 고정한 후, 제1·2몸체(110)(120)의 외부코팅층(113)(123)을 보호하도록 형성된다.The
또한, 상기 보호층(130)에 자외선 차단제를 부가하여 햇볕으로부터 제1·2몸체(110)(120)로 조사되는 자외선을 차단할 수 있다.In addition, an ultraviolet screening agent may be added to the
다음으로 상기 친환경 부표(100)의 제조과정을 설명한다.Next, a manufacturing process of the
먼저, 도 3을 참조하면, 반원의 형상으로 형성된 제1 하부금형(11) 내부에 폴리프로필렌(expanded polyproptlene) 또는 발포 폴리에틸렌(expanded polythylene)의 원료를 공급하고, 상기 원료가 공급된 제1 하부금형(11)에 제1 상부금형(12)을 결합한 상태에서 제어부의 제어에 따라 상기 금형을 가열부로 가열하여 발포체(111)(121)를 형성하는데, 상기 제1 상부금형(12)의 모양에 따라 발포체(111)(121) 내부에는 수용공간(111a)(121a)이 형성되면서 복수의 리브(111b)(121b)를 형성할 수 있다.3, a raw material of expanded polypropylene or expanded polythylene is fed into a first
상기 발포체(111)(121)를 금형으로부터 분리하여 냉각시키면서 발포체(111)(121)의 형상을 유지하도록 한 후, 도 4를 참조하면, 상기 발포체(111)(121)를 제2 하부금형(21)에 투입하고 제2 하부금형(21)에 제2 상부금형(22)을 결합한 상태에서 상기 금형을 가열부로 가열한다.Referring to FIG. 4, after the
이때, 상기 금형은 발포체(111)(121)를 형성할 때보다 더 높은 온도의 가열부로 가열하여 발포체(111)(121) 내·외주면이 녹으면서 발포체(111)(121) 내·외주면에 내·외부 코팅층(112)(122)(113)(123)이 형성되도록 한 후, 금형으로부터 분리하여 냉각시키면서 반원형의 제1·2몸체(110)(120)를 형성하게 된다.At this time, the mold is heated to a heating part at a temperature higher than that at the time of forming the
또한, 도 5 내지 도 6을 참조하면, 수용공간(111a)(121a)이 대응되도록 제1·2몸체(110)(120)의 발포체(111)(121)를 대향하게 위치시킨 후, 발포체(111)(121)의 연결부위를 열융착으로 융착고정하여 고정몸체를 형성한 후, 상기 고정몸체를 형성한 제1·2몸체(110)(120)의 외부 코팅층(113)(123)에 보호층(130)을 형성하면 부표(100)의 제조가 완료된다.5 to 6, after the
여기서, 상기 보호층(130)은, 어선에 녹이 발생하지 않도록 코팅하는 페인트이면서 자외선 차단제가 부가된 도료이며, 상기 페인트 100 중량부에 자외선 차단제는 20~30 중량부로 포함하여 자외선 차단지수가 20~30 이 되도록 하는 것이 바람직하다.Here, the
상기의 과정으로 제조된 부표(100)는 나무나 합성수지를 이용한 고정부재에 다수 배치되고, 부표(100)와 고정부재를 와이어와 같은 별도의 고정부재로 고정할 수 있는데, 상기 부표(100)는 보호층(130)에 자외선 차단제가 부가되어 발포체(111)(112)로 투입되는 자외선을 차단할 수 있으므로 햇빛 및 온도변화에 따른 발포체와 코팅층의 분리현상을 방지하여 부표 본래의 기능을 유지할 수 있는 것이다.A plurality of
또한, 발포체(111)(112) 내·외주면에 내·외부 코팅층(112)(122)(113)(123)과 리브(111b)(121b) 및 보호층(130)이 형성되도록 삼중으로 코팅하여 부표(100)를 보강하기 때문에 부표(100)의 외부로부터 전달되는 충격에 의한 손상을 방지할 수 있으므로 제품의 수명을 연장하면서 안정감있게 사용할 수 있는 것이다.In addition, the inner and
또한, 부표(100) 내부에 수용공간(111a)(121a)이 형성되어 있어, 물속에 들어가 수압에 의한 변형이 발생되어도 물 위로 나오면 복원되면서 원형을 유지할 수 있으므로 안정감있게 사용할 수 있는 것이다.In addition, since the
이상과 같이 본 발명은 비록 한정된 실시예와 도면에 의해 설명되었으나, 본 발명은 상기의 실시예에 한정되는 것은 아니며, 본 발명이 속하는 분야에서 통상의 지식을 가진 자라면 이러한 기재로부터 다양한 수정 및 변형이 가능하다.While the invention has been shown and described with reference to certain preferred embodiments thereof, it will be understood by those of ordinary skill in the art that various changes in form and details may be made therein without departing from the spirit and scope of the invention as defined by the appended claims. This is possible.
그러므로 본 발명의 범위는 설명된 실시예에 국한되어 정해져서는 아니 되며, 후술하는 특허청구범위뿐 아니라 이 특허청구범위와 균등한 것들에 의해 정해져야 한다.Therefore, the scope of the present invention should not be limited by the described embodiments, but should be determined by the equivalents of the appended claims, as well as the appended claims.
100: 부표 110: 제1몸체
120: 제2몸체 130: 보호층100: Buoy 110: First body
120: second body 130: protective layer
Claims (6)
상기 원료가 공급된 금형을 가열부의 열로 가열하여 반원형의 발포체를 형성하는 발포체 형성단계;
상기 발포체의 내부면과 외부면을 발포체를 형성하는 온도보다 더 높은 온도로 가열 및 용융시켜 발포체의 내부면과 외부면에 내부 및 외부 코팅층을 발포체에 동시에 형성하는 코팅층 형성단계;
상기 내부 및 외부 코팅층이 형성된 발포체를 대향하게 위치시킨 후, 발포체의 연결부위를 열융착으로 고정하여 고정몸체를 형성하는 고정몸체 형성단계; 및
상기 고정몸체의 외부 코팅층에 도료를 도포하여 보호층을 형성하는 단계;를 포함하는 코팅층과 보호층을 구비한 친환경 부표의 제조방법.A raw material supplying step of supplying a raw material of expanded polypropylene or expanded polyethlene into a mold;
A foam forming step of heating a mold supplied with the raw material with heat of a heating part to form a semicircular foam;
The inner and outer surfaces of the foam form a foam Forming a coating layer on the foamed body by heating and melting the foamed body at a temperature higher than the temperature to simultaneously form inner and outer coating layers on the inner and outer surfaces of the foamed body;
Forming a fixed body by locating the foams on which the inner and outer coating layers are formed, and fixing the connecting portions of the foam by thermal fusion; And
And forming a protective layer on the outer coating layer of the fixed body by applying a paint to the outer coating layer of the fixed body.
상기 발포체에 자외선 차단제가 포함되는 코팅층 및 보호층을 구비한 친환경 부표의 제조방법.In claim 4,
And a coating layer and a protective layer that contain the ultraviolet screening agent in the foam.
상기 보호층에 자외선 차단제가 포함되는 코팅층 및 보호층을 구비한 친환경 부표의 제조방법.In claim 4,
Wherein the protective layer comprises a coating layer containing an ultraviolet screening agent.