KR101389869B1 - 외벽 단열 마감재 및 그 제조방법 - Google Patents
외벽 단열 마감재 및 그 제조방법 Download PDFInfo
- Publication number
- KR101389869B1 KR101389869B1 KR1020130108297A KR20130108297A KR101389869B1 KR 101389869 B1 KR101389869 B1 KR 101389869B1 KR 1020130108297 A KR1020130108297 A KR 1020130108297A KR 20130108297 A KR20130108297 A KR 20130108297A KR 101389869 B1 KR101389869 B1 KR 101389869B1
- Authority
- KR
- South Korea
- Prior art keywords
- aging
- exterior wall
- acrylic emulsion
- expanded vermiculite
- present
- Prior art date
Abstract
본 발명은 외벽 단열 마감재 및 그 제조방법에 관한 것으로서, 보다 구체적으로는 건물이나 구조물 외벽에 스프레이 타입으로 도포하는 외벽 단열 마감재에 있어서, 팽창 질석과 아크릴 에멀젼을 교반 혼합하여, 스프레이 하는 외벽 단열 마감재 및 그 제조방법에 관한 것이다.
본 발명은 건물이나 구조물 외벽에 스프레이 타입으로 도포하는 외벽 단열 마감재 제조방법에 있어서, 질석을 가열하여, 팽창질석으로 변환시킨후, 냉각와 숙성단계를 거친 팽창 질석 가루와; 아크릴 에멀젼을 혼합하되, 상기 팽창 질석가루와 아크릴 에멀젼은 중량기준으로 1~3:1로 교반 혼합(T90)하여 제조하는 것을 특징으로 한다.
본 발명의 모든 소재 성분이 무기질 소재로 구성되어, 인체 유해성이 없어 친환경적이며, 단열효과가 뛰어나, 외벽에 2-3mm만 도포하여도 샌드위치 판넬 200mm와 동등한 단열효과를 가지며, 내화성, 불연성 및 내부식성이 강하여, 샌드위치 판넬에 1~2mm 만 도포하여도 1200℃화염에 5분 이상 노출되어도 화염전파가 발생하지 않으며, 본 발명의 아크릴 에멀젼 접착력은 우수하여, 시멘트, 목재, 철재, 흙벽 및 유리소재에도 강한 접착력을 보이며, 외부온도에 구애 없이 외부에 노출된 상태에서 15년 이상 접착력을 유지할 수 있다.
본 발명은 건물이나 구조물 외벽에 스프레이 타입으로 도포하는 외벽 단열 마감재 제조방법에 있어서, 질석을 가열하여, 팽창질석으로 변환시킨후, 냉각와 숙성단계를 거친 팽창 질석 가루와; 아크릴 에멀젼을 혼합하되, 상기 팽창 질석가루와 아크릴 에멀젼은 중량기준으로 1~3:1로 교반 혼합(T90)하여 제조하는 것을 특징으로 한다.
본 발명의 모든 소재 성분이 무기질 소재로 구성되어, 인체 유해성이 없어 친환경적이며, 단열효과가 뛰어나, 외벽에 2-3mm만 도포하여도 샌드위치 판넬 200mm와 동등한 단열효과를 가지며, 내화성, 불연성 및 내부식성이 강하여, 샌드위치 판넬에 1~2mm 만 도포하여도 1200℃화염에 5분 이상 노출되어도 화염전파가 발생하지 않으며, 본 발명의 아크릴 에멀젼 접착력은 우수하여, 시멘트, 목재, 철재, 흙벽 및 유리소재에도 강한 접착력을 보이며, 외부온도에 구애 없이 외부에 노출된 상태에서 15년 이상 접착력을 유지할 수 있다.
Description
본 발명은 외벽 단열 마감재 및 그 제조방법에 관한 것으로서, 보다 구체적으로는 건물이나 구조물 외벽에 스프레이 타입으로 도포하는 외벽 단열 마감재에 있어서, 팽창 질석과 아크릴 에멀젼을 혼합하여, 스프레이 하는 외벽 단열 마감재 및 그 제조방법에 관한 것이다.
종래의 외벽단열 마감재는 유리섬유나 발포합성수지 재질의 단열재를 구비하는 샌드위치 판넬을 많이 사용하였으나, 화재에 취약하다. 상기의 문제점을 해결하고자, 석재 또는 점토 등과 같이 자연 채취되는 무기 광물질을 이용한 외벽 마감재가 개시되고 있지만, 생산원가가 높고, 부피 대비 중량이 무거운 단점이 있다.
질석은 운모계의 광석으로, 1000℃ 정도로 가열하면 층간수가 탈수하고 이때 결정수에서 발생하는 압력 때문에 밑면 방향으로 박리 팽창하여 거머리와 같이 늘어나는 성질이 있으며, 버미큐라이트(VERMICULITE)라고 불린다. 질석은 상온에서는 조직이 치밀하지만 950℃ 정도로 가열할 경우, 조직 사이가 팽창하여 다공질이 되면서 '팽창 질석'으로 변환된다. 상기 팽창 질석은 다공성 조직으로 인해 내화, 단열, 경량, 흡음, 결로방지성 등이 뛰어나 건축, 산업용 소재로 널리 사용된다.
상기 질석 또는 팽창 질석을 이용한 기술은 대부분이 평판 보드 형태로, 성형하여 외벽에 드라이 피트 방식으로 시공하는 것이며, 대표적인 기술로는 대한민국 등록 KR 10-0734237, KR 10-0895213 및 KR 10-1074491 등이 있다. 상기 공지된 기술은 제조원가가 높고, 외벽에 시공 이후 내구성과 내후성이 떨어지고 재시공해야 하는 문제점이 대두되고 있다.
상기 내구성이 떨어지는 문제점과 시공작업을 쉽게 하기 위한 방법으로, 건물 외벽이나 구조물보호용으로 마감재를 스프레이 타입의 마감재가 대안으로 제시되고 있으며, 대한민국 등록특허 KR 10-1004888와 KR 10-1198853 등이 대표적이다.
본 발명은 상기 공지된 기술보다 단열성, 내화성, 결로방지, 탈취, 내부식성및 친환경을 고려함과 아울러 다양한 재질에도 접착력을 장시간(10년 이상) 유지할 수 있는 스프레이 타입의 외벽 단열 마감재 제조방법을 개시하고자 한다.
1. 월간축산컨설팅&시설, '뿌리는 단열재 '노블스톤'', 2013년 6월호 Vol.19.
본 발명은 상기의 문제점을 해결하고자 창안된 것으로서, 건물이나 구조물 외벽에 스프레이 타입으로 도포하며, 팽창 질석과 아크릴 에멀젼을 혼합하여, 스프레이하는 외벽 단열 마감재 및 그 제조방법을 제공하는 것이 본 발명의 목적이다.
또한, 팽창 질석가루와 아크릴 에멀젼의 구성성분이 모두 무기질 소재로 인체유해성이 없으며, 친환경적인 외벽 단열 마감재를 제공하는 것이 본 발명의 또 다른 목적이다.
상기의 목적을 달성하기 위하여, 본 발명은 건물이나 구조물 외벽에 스프레이 타입으로 도포하는 외벽 단열 마감재 제조방법에 있어서, 질석을 가열하여, 팽창질석으로 변환시킨후, 냉각와 숙성단계를 거친 팽창 질석 가루와; 아크릴 에멀젼을 혼합하되, 상기 팽창 질석가루와 아크릴 에멀젼은 중량기준으로 1~3:1로 교반 혼합(T90)하여 제조하는 것을 특징으로 하는 외벽 단열 마감재 제조방법을 제공하고자 한다.
또한, 본 발명의 아크릴 에멀젼의 제조방법은, 물, 유화제, 모노머(monomer)를 원료는 준비하는 단계(A10)와; 상기 준비된 원료를 탱크(30)에 주입하여, 300 내지 500 rpm으로 회전하는 교반기(10)로 강제 유화하는 프리 에멀젼 단계(A20)와; 상기 프리 에멀젼 단계(A20)이후, 히터(40)를 구비한 반응기에 주입하며, 추가적으로 개시제를 주입하여, 60 내지 100℃ 온도상태에서, 50 내지 100 rpm으로 저속회전하는 교반기(10)에 3 내지 5시간 반응시키는 폴리머 에멀젼 단계(A30)와; 상기 폴리먼 에멀젼 단계(A30) 이후, 온도를 유지한 상태에서 숙성하는 1차 숙성 단계(A40)와; 상기 1차 숙성 단계(A40) 이후, 산화제 또는 환원제를 추가 주입하여 공급된 원료가 완전하게 반응하도록 하는 포스터 촉매 첨가단계(A50)와; 상기 포스터 촉매 첨가 단계(A50) 이후, 온도를 유지한 상태에서 원료들이 완전하게 반응하도록 1 내지 2시간 숙성하는 2차 숙성 단계(A60)와; 상기 2차 숙성 단계(A60) 이후, 냉각하는 단계(A70)와; 상기 냉각단계(A70) 이후, ph 조절제, 점도 조절제, 분산제, 소포제, 습윤제, 방부제, 분자량 조절제 중 하나 또는 하나 이상을 구비한 후첨가제를 투입하는 단계(A80)를 포함하는 것을 특징으로 하는 외벽 단열 마감재 제조방법을 제공하고자 한다.
또한, 본 발명의 아크릴 에멀젼의 폴리머는, 메틸 메타크릴레이트(MMA), 시클로헥실메타크릴레이트(CHMA), 비닐 아세트산(VAc), 아크릴로 니트릴(AN), 에틸 아크릴레이트(EA), 부틸 아크릴레이트(BA), 2-에틸헥산아크릴레이트(2EHA), 라우릴 메타크릴레이트(LMA), 비닐 에스테르(VEOVA), 아크릴 산, 메타크릴 산, 말레인 산, 니트론, 이타콘산, 비닐 설포네이트(비닐 술폰산염), 트리 아세틸 셀룰로오스(TAC), 디비닐벤젠(DVB), 아크릴산 에스테르 (AAEMA), 글리콜 메타그릴레이트(GMA) 등의 모노머(Monomer) 중 어느 하나 또는 하나 이상을 구비하는 것을 특징으로 하는 외벽 단열 마감재 제조방법을 제공하고자 한다.
또한, 본 발명은 건물이나 구조물 외벽에 스프레이 타입으로 도포하는 외벽 단열 마감재에 있어서, 상기 제조방법에 따라, 팽창 질석가루와; 아크릴 에멀젼을 혼합하되, 상기 팽창 질석가루와 아크릴 에멀젼은 중량기준으로 1~3:1로 혼합하여 스프레이 방식으로 도포하는 것을 특징으로 하는 외벽 단열 마감재를 제공하고자 한다.
본 발명으로 인해 다음과 같은 효과를 가진다.
첫째, 본 발명의 주요 구성요소인 팽창 질석, 아크릴 에멀젼 및 도료의 소재 성분이 모두 무기질 소재로 구성되어, 인체 유해성이 없으며, 친환경적인 외벽 단열 마감재를 제공한다.
둘째, 단열효과가 뛰어나, 외벽에 2-3mm만 도포하여도 샌드위치 판넬 200mm와 동등한 단열효과를 가지며, 제조원가가 저렴하며, 스프레이 타입으로 시공이 간단하다.
셋째, 본 발명은 내화성, 불연성이 강하여, 샌드위치 판넬에 1~2mm 만 도포하여도 1200℃화염에 5분 이상 노출되어도 화염전파가 발생하지 않는다.
넷째, 본 발명의 아크릴 에멀젼 접착력은 우수하여, 시멘트, 목재, 철재, 흙벽 및 유리소재에도 강한 접착력을 보이며, 외부에 노출된 상태에서 15년 이상 장기간 접착력을 유지할 수 있다.
다섯째, 농가에 적용할 경우, 축산 시설물의 외부 단열재를 제거하지 않은 상태에서 바로 시공이 가능하므로, 종래제품에 비해 시공비는 1/10배 수준이며, 시공시간도 종래기술에 비해 1/10배 수준으로 단축시킬 수 있다.
도 1은 본 발명의 바람직한 일실시예의 제조방법 흐름도.
도 2는 본 발명에 사용되는 아크릴 에멀젼의 모노머(Monomer)
도 3은 프리 에멀젼 단계(A20)와 폴리머 에멀젼 단계(A30)의 개략도
도 4는 개시제의 종류 및 화학식
도 5는 건물 외벽 또는 내벽에 도포된 일 실시예
도 6은 단열 및 불연성을 시험하기 위한 화염 전도 시험.
도 7은 샌드위치 판넬에서의 화염전파 시험직후의 일실시 예
도 2는 본 발명에 사용되는 아크릴 에멀젼의 모노머(Monomer)
도 3은 프리 에멀젼 단계(A20)와 폴리머 에멀젼 단계(A30)의 개략도
도 4는 개시제의 종류 및 화학식
도 5는 건물 외벽 또는 내벽에 도포된 일 실시예
도 6은 단열 및 불연성을 시험하기 위한 화염 전도 시험.
도 7은 샌드위치 판넬에서의 화염전파 시험직후의 일실시 예
본 발명은 상기 공지된 기술보다 단열성, 내화성, 내부식성 및 다양한 재질에 부착되는 접착력 등의 기능을 장시간(10년 이상) 유지할 수 있으며, 친환경 소재로 구성된 스프레이 타입의 외벽 단열 마감개를 개시하고자 한다.
질석은 운모계의 광석으로, 1000℃ 정도로 가열하면 층간수가 탈수하고 이때 결정수에서 발생하는 압력 때문에 밑면 방향으로 박리 팽창하여 거머리와 같이 늘어나는 성질이 있으며, 버미큐라이트(VERMICULITE)라고 불린다.
질석은 상온에서는 조직이 치밀하지만 950℃ 정도로 가열할 경우, 조직사이가 팽창하여 다공질이 되면서 '팽창 질석'으로 변환된다. 상기 팽창 질석은 다공성 조직으로 인해 내화, 단열, 경량, 흡음, 결로방지성 등이 뛰어나 건축, 산업용 소재로 널리 사용된다.
따라서, 본 발명은, 건물이나 구조물 외벽에 스프레이 타입으로 도포하는 외벽 단열 마감재 제조방법에 있어서, 질석을 가열하여, 팽창질석으로 변환시킨후, 냉각와 숙성단계를 거친 팽창 질석 가루와; 아크릴 에멀젼을 혼합하되, 상기 팽창 질석가루와 아크릴 에멀젼은 중량기준으로 1~3:1로 교반 혼합(T90)하여 제조하는 것을 특징으로 하는 외벽 단열 마감재 제조방법을 개시하고자 한다.
도 1은 본 발명의 바람직한 일 실시예의 제조공정 흐름도이다. 도 1에서 도시한 바와 같이, 본 발명은 외벽단열 마감재 및 그 제조방법에 관한 것으로서, 건물이나 구조물 외벽에 스프레이 타입으로 도포하는 외벽 단열 마감재 제조방법에 있어서, 질석을 1000℃ 이상으로 가열하여(P20), 팽창질석으로 변환시킨후, 냉각와 숙성단계(P30)를 거친 팽창 질석 가루와; 아크릴 에멀젼을 혼합하되, 상기 팽창 질석가루와 아크릴 에멀젼은 중량기준으로 1~3:1로 교반 혼합(T90)하여 제조하는 것을 특징으로 한다.
도 1에서 도시한 바와 같이, 본 발명에 있어서 아크릴 에멀젼의 제조방법은, 물, 유화제, 모노머(monomer)를 원료는 준비하는 단계(A10)와; 상기 준비된 원료를 탱크(30)에 주입하여, 300 내지 500 rpm으로 회전하는 교반기(10)로 강제 유화하는 프리 에멀젼 단계(A20)와; 상기 프리 에멀젼 단계(A20)이후, 히터(40)를 구비한 반응기에 주입하며, 추가적으로 개시재를 주입하여, 60 내지 100℃ 온도상태에서, 50 내지 100 rpm으로 저속회전하는 교반기(10)에 3 내지 5시간 반응시키는 폴리머 에멀젼 단계(A30)와; 상기 폴리머 에멀젼 단계(A30) 이후, 온도를 유지한 상태에서 숙성하는 1차 숙성 단계(A40)와; 상기 1차 숙성 단계(A40) 이후, 산화제 또는 환원제를 추가 주입하여 공급된 원료가 완전하게 반응하도록 하는 포스터 촉매 첨가단계(A50)와; 상기 포스터 촉매 첨가 단계(A50) 이후, 온도를 유지한 상태에서 원료들이 완전하게 반응하도록 1 내지 2시간 숙성하는 2차 숙성 단계(A60)와; 상기 2차 숙성 단계(A60) 이후, 냉각하는 단계(A70)와; 상기 냉각단계(A70) 이후, pH 조절제, 점도 조절제, 분산제, 소포제, 습윤제, 방부제, 분자량 조절제 중 하나 또는 하나 이상을 구비한 후첨가제를 투입하는 단계(A80)를 포함하는 것을 특징으로 한다.
상기 1차 숙성 단계(A40)는 60 내지 100℃ 온도를 유지한 상태에서 숙성하는 단계로, 폴리머 에멀젼으로 변환율이 99%에 도달되도록 한다.
상기 1차 숙성 단계(A40) 이후의 포스터 촉매 첨가단계(A50)와 2차 숙성 단계(A60)는, 산화제 또는 환원제를 추가 주입하여 미반응 모노머를 100% 폴리머 에머젼으로 변환시키기 위한 공정이다.
도 2는 본 발명에 사용되는 아크릴 에멀젼의 모노머(Monomer)의 목록이다.
본 발명에 사용된 상기 아크릴 에멀젼의 폴리머는, 메틸 메타크릴레이트(MMA), 시클로헥실메타크릴레이트(CHMA), 비닐 아세트산(VAc), 아크릴로 니트릴(AN), 에틸 아크릴레이트(EA), 부틸 아크릴레이트(BA), 2-에틸헥산아크릴레이트(2EHA), 라우릴 메타크릴레이트(LMA), 비닐 에스테르(VEOVA), 아크릴 산, 메타크릴 산, 말레인 산, 니트론, 이타콘산, 비닐 설포네이트(비닐 술폰산염), 트리 아세틸 셀룰로오스(TAC), 디비닐벤젠(DVB), 아크릴산 에스테르 (AAEMA), 글리콜 메타그릴레이트(GMA) 등의 모노머(Monomer) 중 어느 하나 또는 하나 이상을 구비하는 것을 특징으로 한다.
도 3은 프리 에멀젼 단계(A20)와 폴리머 에멀젼 단계(A30)의 개략도이며, 도 4는 개시제의 종류 및 화학식이다.
상기 프리 에멀젼 단계(A20)는 물, 모노머, 유화제와 아울러 관능성 모노머 또는 기능성 모노머를 탱크(30)에 주입하여, 300 내지 500 rpm으로 회전하는 교반기(10)로 강제 혼합시킨다.
상기 관능성 모노머 또는 기능성 모노머는 입자 결합력을 향상시킨다.
상기 유화제는 크게 음이온성과 비이온성으로 구분된다.
상기 음이온성 유화제는 모노모 중량 대비 1 내지 3 % 사용하며, 가장 효율이 높아 통상적으로 많이 사용된다. 또한, 상기 음이온성 유화제는 중합과정 중에 입자크기와 입자분포를 조절하며, 고분자 입자의 응집과 이물질(grit)을 줄이는 역할을 한다.
반면, 상기 비이온성 유화제는 중합과정 중에 입자의 응집을 방지하여, 입자의 안정성을 유지하며, 동결융해 안전성을 향상시키며, 염 안전성을 향상시키며, 전단 안정성(shear stability)을 향상시킨다. 또한, 상기 비이온성 유화제는 모노모 중량 대비 2 내지 6 % 사용하는 것이 바람직하다.
도 5는 본 발명에 적용되는 대표적인 개시제의 목록표이다.
상기 프리 에멀젼 단계(A20)이후, 혼합된 모노머를 히터(40)를 구비한 반응기에 주입하고, 개시제를 주입하면 폴리머 에멀젼으로 변환하는 반응이 일어난다.
상기 폴리머 에멀젼으로 반응속도를 촉진하기 위하여, 60 내지 100℃ 온도상태에서, 50 내지 100 rpm으로 저속회전하는 교반기(10)를 구비하는 것이 바람직하다.
본 발명에서 사용되는 개시제는 수용성 개시제를 사용하는 것이 바람직하다. 대표적으로는 Persulfates, Peroxides, AZO 화합물등이다.
상기 후 첨가제를 투입 단계(A80)에 있어서, 후 첨가제는 크게 분자량 조절제, pH 조절제, 점도 조절제, 분산제, 소포제, 습윤제, 방부제를 포함하는 것이 바람직하다.
상기 분자량 조절제는 Mercaptane, 황화합물 등이 대표적이며, 폴리머로 변환시키기 위한 분기 또는 이식기능을 가진다.
상기 pH 조절제는 Na2CO3, NaHCO3, (NH4)2CO3, NH4OH, KOH, NaOH, DMEA 등을 사용하는 것이 바람직하다.
상기 점도 조절제는 HEC(hydroxy ethyl cellulose), NVP(N-vinyl pyrrolidone) 등을 사용하는 것이 바람직하다.
도 5는 건물 외벽 또는 내벽에 도포된 일 실시예이다.
본 발명은 도 5에서 도시한 바와 같이, 건물이나 구조물 외벽에 스프레이 타입으로 도포하는 외벽 단열 마감재에 있어서, 상기 제 1항의 제조방법으로, 팽창 질석가루와; 아크릴 에멀젼을 혼합하되, 상기 팽창 질석가루와 아크릴 에멀젼은 중량기준으로 1~3:1로 혼합하여 스프레이 방식으로 도포하는 것을 특징으로 하는 외벽 단열 마감재이다.
또한, 외벽 마감재로서 다양한 색상을 구현하기 위하여, 상기 혼합 교반단계(T90)에 무기 광물질 도료를 더 포함하는 것을 특징으로 한다.
상기 무기 광물질 도료는 황토, 견운모, 맥반석, 자수정, 숯, 옥, 게르마늄 중 어느 하나 또는 하나 이상의 무기질을 더 포함하는 것을 특징으로 한다.
도 6은 단열 및 불연성을 시험하기 위한 화염 전도 시험이며, 도 7은 상기 화염전도 시험직후의 샌드위치 판넬 일실시 예이다.
본 발명의 외벽 단열 마감재는 불연성과 단열성이 높은 것이 특징이다. 본 발명의 팽창 질석 가루는 다공성 조직을 가지고 있어, 단열성이 매우 뛰어나며, 건물 외벽 또는 구조물 외벽에 2-3mm 만 도포하여도 샌드위치 판넬 200mm와 동등한 단열효과를 가진다.
본 발명의 불연성을 표현하기 위하여 샌드위치 판넬 일측면부에 본 발명의 외벽단열 마감재를 2mm 도포한 상태에서, 1200℃이상의 화염에 노출 시킨 직후의 사진을 나타내고 있다.
본 발명의 외벽 단열 마감재를 도포하지 않은 미도포 측면은 1200℃이상의 화염에 노출되는 즉시 연기와 함께 5초 이내에 샌드위치 판넬 내에 있는 스트로폼에서 화염이 발생하였다.
반면, 본 발명의 외벽 단열 마감재를 2mm 도포한 도포 측면에서는, 1200℃이상의 화염에 5분 정도 노출된 이후 사진이며, 도 4에서 도시한 바와 같이 아크릴 에멀젼의 일부에서 소량의 연기가 발생할 뿐 샌드위치 내부로 열이 전달되지 않아, 내부에 위치한 스트로폼이 건재함을 볼 수 있다.
본 발명의 일실시예에 있어서, 본 발명은 건축물, 축사, 양돈장, 물탱크, 기름 저장탱크, 스팀 파이프, 유리, 강철, 전기배선 파이프류, 수도관 외벽, 구조물 외벽, 컨테이너 외벽, 눈길 미끄러움 방지제 등 작업대상 및 작업공간에 따른 제약 없이 시공이 가능하다.
본 발명은 스프레이 도포작업은 도포분사, 건조를 반복하여, 필요로 하는 두께까지 다수 스프레이하여 설정 도막 두께에 도달한다.
본 발명은 상술한 특정의 바람직한 실시 예에 한정되지 아니하며, 청구범위에서 청구하는 본 발명의 요지를 벗어남이 없이 당해 발명이 속하는 기술분야에서 통상의 지식을 가진 자라면 누구든지 다양한 변형실시가 가능한 것은 물론이고, 그와 같은 변경은 청구범위 기재의 범위 내에 있게 된다.
10: 교반기, 20: 모노머, 30: 탱크, 40: 히터, 50: 폴리머
Claims (5)
- 건물이나 구조물 외벽에 스프레이 타입으로 도포하는 외벽 단열 마감재 제조방법에 있어서,
질석을 가열하여, 팽창질석으로 변환시킨후, 냉각와 숙성단계를 거친 팽창 질석 가루와;
상기 팽창 질석가루와 아크릴 에멀젼은 중량기준으로 1~3:1로 교반 혼합(T90)하되,
상기 아크릴 에멀젼은,
물, 유화제, 모노머(monomer,30)를 원료는 준비하는 단계(A10)와;
상기 준비된 원료를 탱크(30)에 주입하여, 300 내지 500 rpm으로 회전하는 교반기(10)로 강제 유화하는 프리 에멀젼 단계(A20)와;
상기 프리 에멀젼 단계(A20)이후, 히터(40)를 구비한 반응기에 주입하며, 추가적으로 개시제를 주입하여, 60 내지 100℃ 온도상태에서, 50 내지 100 rpm으로 저속회전하는 교반기(10)에 3 내지 5시간 반응시키는 폴리머 에멀젼 단계(A30)와;
상기 폴리먼 에멀젼 단계(A30) 이후, 온도를 유지한 상태에서 숙성하는 1차 숙성 단계(A40)와;
상기 1차 숙성 단계(A40) 이후, 산화제 또는 환원제를 추가 주입하여 공급된 원료가 완전하게 반응하도록 하는 포스터 촉매 첨가단계(A50)와;
상기 포스터 촉매 첨가 단계(A50) 이후, 온도를 유지한 상태에서 원료들이 완전하게 반응하도록 1 내지 2시간 숙성하는 2차 숙성 단계(A60)와;
상기 2차 숙성 단계(A60) 이후, 냉각하는 단계(A70)와;
상기 냉각단계(A70) 이후, pH 조절제, 점도 조절제, 분산제, 소포제, 습윤제, 방부제, 분자량 조절제 중 하나 또는 하나 이상을 구비한 후첨가제를 투입하는 단계(A80)를 포함하는 것을 특징으로 하는 외벽 단열 마감재 제조방법.
- 제 1항에 있어서,
상기 아크릴 에멀젼의 폴리머는,
메틸 메타크릴레이트(MMA), 시클로헥실메타크릴레이트(CHMA), 비닐 아세트산(VAc), 아크릴로 니트릴(AN), 에틸 아크릴레이트(EA), 부틸 아크릴레이트(BA), 2-에틸헥산아크릴레이트(2EHA), 라우릴 메타크릴레이트(LMA), 비닐 에스테르(VEOVA), 아크릴 산, 메타크릴 산, 말레인 산, 니트론, 이타콘산, 비닐 설포네이트(비닐 술폰산염), 트리 아세틸 셀룰로오스(TAC), 디비닐벤젠(DVB), 아크릴산 에스테르 (AAEMA), 글리콜 메타그릴레이트(GMA) 등의 모노머(Monomer) 중 어느 하나 또는 하나 이상을 구비하는 것을 특징으로 하는 외벽 단열 마감재 제조방법.
- 제 1항에 있어서,
외벽 마감재로서 다양한 색상을 구현하기 위하여,
상기 혼합 교반단계(T90)에 무기 광물질 도료를 더 포함하는 것을 특징으로 하는 외벽 단열 마감재 제조방법. - 삭제
- 삭제