KR101271877B1 - Fabrics coated by chamaecyparis obtusa extract and manufacturing method thereof - Google Patents

Fabrics coated by chamaecyparis obtusa extract and manufacturing method thereof Download PDF

Info

Publication number
KR101271877B1
KR101271877B1 KR1020110116170A KR20110116170A KR101271877B1 KR 101271877 B1 KR101271877 B1 KR 101271877B1 KR 1020110116170 A KR1020110116170 A KR 1020110116170A KR 20110116170 A KR20110116170 A KR 20110116170A KR 101271877 B1 KR101271877 B1 KR 101271877B1
Authority
KR
South Korea
Prior art keywords
fabric
extract
cypress
wood
coated
Prior art date
Application number
KR1020110116170A
Other languages
Korean (ko)
Other versions
KR20130051048A (en
Inventor
오성환
Original Assignee
(주)한성헬스피아
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)한성헬스피아 filed Critical (주)한성헬스피아
Priority to KR1020110116170A priority Critical patent/KR101271877B1/en
Publication of KR20130051048A publication Critical patent/KR20130051048A/en
Application granted granted Critical
Publication of KR101271877B1 publication Critical patent/KR101271877B1/en

Abstract

본 발명은 나무 추출액이 코팅된 원단 및 그 제조방법에 관한 것으로, 구체적으로 본 발명은 나무 추출액에 함유된 유효성분에 의해 탈취, 항균 및 항바이러스 효과가 있는 나무 추출액이 코팅된 원단 및 그 제조방법에 관한 것이다.
또한, 본 발명은 편백나무, 대나무, 소나무, 향나무, 오동나무 및 전나무로 이루어지는 군에서 선택되는 나무의 원목을 포함하는 원료를 추출용매로 추출하고 이를 여과하여 나무 추출액을 제조하는 S1단계; 상기 나무 추출액을 바인더와 혼합하여 원단 코팅액을 제조하는 S2단계; 상기 원단 코팅액을 원단의 일면에 분무하거나 도포하는 S3단계; 및 상기 S3단계를 거친 원단을 열처리하여 코팅층을 형성하는 S4단계;를 포함하는 것을 특징으로 한다.
The present invention relates to a fabric coated with a wood extract, and a method for manufacturing the same. Specifically, the present invention relates to a fabric coated with a wood extract having a deodorant, antibacterial and antiviral effect by an active ingredient contained in a tree extract, and a method for manufacturing the same. It is about.
In addition, the present invention S1 step of extracting the raw material containing the solid wood of the tree selected from the group consisting of cypress, bamboo, pine, juniper, paulownia and fir with an extraction solvent and filtering the same to prepare a tree extract; S2 step of preparing a fabric coating solution by mixing the wood extract with a binder; S3 step of spraying or applying the fabric coating liquid to one side of the fabric; And S4 step of forming a coating layer by heat-treating the fabric having passed through S3 step.

Description

나무 추출액이 코팅된 원단 및 그 제조방법{FABRICS COATED BY CHAMAECYPARIS OBTUSA EXTRACT AND MANUFACTURING METHOD THEREOF}Fabric coated with wood extract and its manufacturing method {FABRICS COATED BY CHAMAECYPARIS OBTUSA EXTRACT AND MANUFACTURING METHOD THEREOF}
본 발명은 나무 추출액이 코팅된 원단 및 그 제조방법에 관한 것으로, 구체적으로 본 발명은 나무 추출액에 함유된 유효성분에 의해 탈취, 항균 및 항바이러스 효과가 있는 나무 추출액이 코팅된 원단 및 그 제조방법에 관한 것이다.
The present invention relates to a fabric coated with a wood extract, and a method for manufacturing the same. Specifically, the present invention relates to a fabric coated with a wood extract having a deodorant, antibacterial and antiviral effect by an active ingredient contained in a tree extract, and a method for manufacturing the same. It is about.
편백나무(Chamaecyparis obtusa)는 노송나무라고도 하며, 겉씨식물 구과목 측백나무과의 상록교목으로서, 일본이 원산지이지만 개발을 통해 우리나라 남부 지방에서 조림수종(造林樹種)으로 널리 재배되고 있으며, 특히 편백나무 특유의 향으로 인해 탈취제, 항균제 등으로 사용되고 있다.Chamaecyparis obtusa, also known as cypress tree, is an evergreen tree belonging to the gymnospermae of the gymnosperma, and is widely grown as a plantation tree species in southern Korea through development, Deodorant, antimicrobial agent and the like due to the fragrance of the product.
편백나무에서 탈취 또는 항균 효과를 가지는 성분 중에는 대표적으로 피톤치드(phytoncide)가 있는데, 피톤치드는 수목이 미생물과 각종 균으로부터 자신을 방어하기 위해 발산하는 천연의 항균물질로서, 독특한 방향성(芳香性)을 가지며 강력한 공기정화력과 유해물질 중화작용이 있어, 심폐, 혈관, 호흡기 기능강화 및 피부 살균작용 등 여러 가지 효능을 발휘하는 것으로 알려져 있다. 피톤치드의 방출량과 함유된 성분은 수목마다 다르고 침엽수는 활엽수에 비해 두 배 이상의 피톤치드를 발산하는 것으로 알려져 있으며, 특히 편백나무의 피톤치드 방출량은 타 수목에 비하여 월등할 뿐만 아니라 그 효능도 뛰어난 것으로 학계에 보고되고 있다.Among the components that have deodorant or antimicrobial effect in cypress, phytoncide is representative. Phytoncide is a natural antibacterial substance emitted by trees to protect themselves from microorganisms and various bacteria, and has a unique fragrance. It has strong air purifying power and neutralizing harmful substance, and it is known to show various effects such as cardiopulmonary, vascular, respiratory function enhancement and skin sterilization. The amount and content of phytoncide are different from tree to tree, and coniferous tree is known to emit more than twice the amount of phytoncide than hardwood. Especially, phytoncide emission of cypress is not only superior to other trees but also excellent in efficacy It is becoming.
최근에는 이러한 피톤치드를 상품 등에 많이 이용하고 있으며, 특히 편백나무 특유의 향으로 인해 편백나무를 이용한 탈취제, 항균제 등의 상품개발이 이루어지고 있다.In recent years, such phytoncide is used a lot of products, etc. In particular, due to the peculiar aroma of cypress, product development such as deodorant and antibacterial agent using cypress has been made.
이러한 편백나무의 피톤치드를 이용하여 항균 작용을 하는 원단을 제조하는 과정에서 단순히 편백나무잎이나 줄기에서 짜낸 편백정유를 도포하는 경우에는 시간이 흐름에 따라 피톤치드의 양이 급격히 감소하는 문제가 있다.In the process of manufacturing a fabric having an antimicrobial effect using the phytoncide of the cypress, when the application of the cypress essential oil squeezed from the cypress leaves or stems, there is a problem that the amount of phytoncide is drastically reduced with time.
한편, 합성섬유 또는 천연섬유로 이루어진 원단의 경우에는 원단 표면에 합성수지 성분만을 함유하는 코팅층을 형성하기 때문에, 코팅을 한 후 장시간에 걸쳐 합성 수지에 의한 냄새가 잘 빠지지 않는 문제가 있다.On the other hand, in the case of a fabric made of synthetic fibers or natural fibers to form a coating layer containing only a synthetic resin component on the surface of the fabric, there is a problem that the smell by the synthetic resin does not fall well for a long time after coating.
또한, 자주 세탁할 수 없는 침구류 원단의 경우에는 각종 세균이나 진드기가 서식할 수 있는 환경을 제공하여 아토피 또는 피부염 등을 유발하게 된다.In addition, in the case of bedding fabrics that can not be frequently washed to provide an environment in which a variety of bacteria or mites can inhabit atopic or dermatitis.
그러나 종래의 원단 코팅에 의해서는 항균 내지 살균 효과를 기대할 수 없으며, 코팅에 의한 원단의 유연성이 감소한다는 문제가 있었다.
However, the conventional fabric coating can not expect antibacterial to sterilization effect, there was a problem that the flexibility of the fabric by the coating is reduced.
이에 본 발명은 상기와 같은 문제점을 해결하기 위해 안출된 것으로서, 본 발명의 목적은 나무 추출액에 함유된 유효성분에 의해 탈취, 항균 및 항바이러스 효과가 있는 나무 추출액이 코팅된 원단 및 그 제조방법을 제공하는 것이다.Accordingly, the present invention has been made to solve the above problems, an object of the present invention is a fabric and a method of manufacturing the coated wood extract having a deodorant, antibacterial and antiviral effect by the active ingredient contained in the wood extract To provide.
또한, 본 발명의 목적은 기존의 원단 가공장치를 그대로 이용하되, 단지 나무 추출액만을 별도로 제조하여 원단 코팅액에 혼합하여 가공이 간편한 나무 추출액이 코팅된 원단 및 그 제조방법을 제공하는 것이다.In addition, an object of the present invention is to use a conventional fabric processing apparatus as it is, to provide a fabric and a method of manufacturing the coated wood extract is easy to process only by separately preparing the wood extract is mixed with the fabric coating solution.
또한, 본 발명의 목적은 편백나무 원목은 물론, 편백잎, 편백뿌리, 편백열매 등을 모두 이용할 수 있어 자원의 효율적인 이용을 도모하고, 탈취 내지 항균 효과를 더욱 증가시킬 수 있는 나무 추출액이 코팅된 원단 및 그 제조방법을 제공하는 것이다.In addition, it is an object of the present invention can be used not only cypress wood, but also cypress leaves, cypress roots, cypress berries, etc., so that the efficient use of resources, the tree extract is coated that can further increase the deodorant to antibacterial effect It is to provide a fabric and a method of manufacturing the same.
또한, 본 발명의 목적은 접착력이 향상되어 장시간 사용하더라도 코팅층이 쉽게 벗겨지지 않고, 원단의 유연성도 향상된 나무 추출액이 코팅된 원단 및 그 제조방법을 제공하는 것이다.
In addition, it is an object of the present invention to provide a fabric and a method of manufacturing the same, which is coated with a wooden extract solution is improved even if the coating layer is not easily peeled off even when used for a long time, the flexibility of the fabric.
상기와 목적을 달성하기 위하여 본 발명에 따른 나무 추출액이 코팅된 원단의 제조방법은 편백나무, 대나무, 소나무, 향나무, 오동나무 및 전나무로 이루어지는 군에서 선택되는 나무의 원목을 포함하는 원료를 추출용매로 추출하고 이를 여과하여 나무 추출액을 제조하는 S1단계; 상기 나무 추출액을 바인더와 혼합하여 원단 코팅액을 제조하는 S2단계; 상기 원단 코팅액을 원단의 일면에 분무하거나 도포하는 S3단계; 및 상기 S3단계를 거친 원단을 열처리하여 코팅층을 형성하는 S4단계;를 포함하는 것을 특징으로 한다.In order to achieve the above and the object, the method of manufacturing a fabric coated with a tree extract according to the present invention extracts a raw material containing a raw material of wood selected from the group consisting of cypress, bamboo, pine, juniper, paulownia and fir S1 step of extracting and filtering to prepare a tree extract; S2 step of preparing a fabric coating solution by mixing the wood extract with a binder; S3 step of spraying or applying the fabric coating liquid to one side of the fabric; And S4 step of forming a coating layer by heat-treating the fabric having passed through S3 step.
또한, 본 발명에 따른 나무 추출액이 코팅된 원단의 제조방법의 S1단계의 원료는 상기 나무의 잎, 열매, 뿌리 및 줄기로 이루어지는 군에서 선택되는 적어도 하나를 더 포함하여, 상기 원목과 함께 추출되는 것을 특징으로 한다.In addition, the raw material of step S1 of the manufacturing method of the fabric coated with wood extracts according to the present invention further comprises at least one selected from the group consisting of the leaves, berries, roots and stems of the tree, which is extracted with the wood It is characterized by.
또한, 본 발명에 따른 나무 추출액이 코팅된 원단의 제조방법의 S1단계에서 상기 추출용매는 알콜 또는 알콜 수용액이고, 상기 원료와 상기 추출용매는 1:5 ~ 1:10의 중량비로 혼합된 상태에서 5~10 시간 동안 추출이 이루어지는 것을 특징으로 한다.In addition, in the step S1 of the manufacturing method of the fabric coated with wood extracts according to the present invention, the extraction solvent is an alcohol or an aqueous alcohol solution, the raw material and the extraction solvent is mixed in a weight ratio of 1: 5 ~ 1:10. Characterized in that the extraction is made for 5 to 10 hours.
또한, 본 발명에 따른 나무 추출액이 코팅된 원단의 제조방법의 바인더는, 에폭시, 아크릴, 비닐, 폴리에틸렌, 폴리프로필렌, 폴리에스테르, 폴리에테르, 폴리우레탄, 폴리이소시아네이트 및 폴리아미드로 이루어지는 군에서 적어도 하나 선택되는 제1성분; 및 알코올, 케톤, 글리콜 및 에테르로 이루어지는 군에서 적어도 하나 선택되는 제2성분;을 포함하는 것을 특징으로 한다.In addition, the binder of the manufacturing method of the fabric coated with the wood extract according to the present invention, at least one of the group consisting of epoxy, acrylic, vinyl, polyethylene, polypropylene, polyester, polyether, polyurethane, polyisocyanate and polyamide Selected first component; And at least one second component selected from the group consisting of alcohols, ketones, glycols, and ethers.
또한, 본 발명에 따른 나무 추출액이 코팅된 원단의 제조방법의 S4단계의 열처리는 한 쌍의 히팅 롤러에 의해 80~150℃에서 1~5분 동안 이루어지는 것을 특징으로 한다.In addition, the heat treatment of the step S4 of the method of manufacturing a fabric coated with a wood extract according to the present invention is characterized in that it is made for 1 to 5 minutes at 80 ~ 150 ℃ by a pair of heating roller.
또한, 본 발명에 따른 나무 추출액이 코팅된 원단의 제조방법은 상기 나무가 편백나무인 경우, S4단계를 거친 후, 편백정유 성분을 함유하는 편백정유 코팅층을 형성하는 S5단계를 더 포함하는 것을 특징으로 한다.In addition, the method of manufacturing a fabric coated with a tree extract according to the present invention, if the wood is a cypress, after the step S4, further comprising a step S5 to form a cypress essential oil coating layer containing a cypress essential oil component. It is done.
또한, 본 발명에 따른 나무 추출액이 코팅된 원단은 상기한 제조방법에 의해 제조되는 것을 특징으로 한다.
In addition, the fabric coated with the tree extract according to the present invention is characterized in that it is produced by the above-described manufacturing method.
이상과 같은 구성의 본 발명에 따른 나무 추출액이 코팅된 원단 및 그 제조방법에 의하면 나무 추출액에 함유된 유효성분에 의해 탈취, 항균 및 항바이러스 효과가 있다.According to the fabric coated with the wood extract according to the present invention having the configuration described above and a method for producing the same, there is an effect of deodorization, antibacterial and antiviral by the active ingredient contained in the wood extract.
또한, 본 발명에 따른 나무 추출액이 코팅된 원단의 제조방법에 의하면 기존의 원단 가공장치를 그대로 이용하되, 단지 나무 추출액만을 별도로 제조하여 원단 코팅액에 혼합하여 원단의 가공이 간편하다는 효과가 있다.In addition, according to the manufacturing method of the fabric coated with the wood extract according to the present invention, using the existing fabric processing apparatus as it is, there is an effect that the processing of the fabric is easy to prepare by mixing only the wood extract is mixed with the fabric coating solution.
또한, 본 발명에 따른 나무 추출액이 코팅된 원단 및 그 제조방법에 의하면 편백나무 원목은 물론, 편백잎, 편백뿌리, 편백열매 등을 모두 이용할 수 있어 자원의 효율적인 이용을 도모하고, 탈취 내지 항균 효과를 더욱 증가시키는 효과가 있다.In addition, according to the fabric coated with the extract of the tree according to the present invention and a method for manufacturing the same, not only cypress logs, but also cypress leaves, cypress roots, cypress berries, etc. can be used to promote efficient use of resources, deodorizing to antibacterial effect There is an effect to further increase.
또한, 본 발명에 따른 본 발명에 따른 나무 추출액이 코팅된 원단 및 그 제조방법에 의하면 접착력이 향상되어 장시간 사용하더라도 코팅층이 쉽게 벗겨지지 않고, 원단의 유연성도 향상되는 효과가 있다.
In addition, according to the present invention according to the present invention, the coating material and the manufacturing method coated with the wood extract according to the present invention has an effect that the coating layer is not easily peeled off even if used for a long time, the flexibility of the fabric is also improved.
도 1은 본 발명에 나무 추출액이 코팅된 원단의 제조방법의 제1실시예를 도시하는 공정도이다.
도 2는 본 발명에 나무 추출액이 코팅된 원단의 제조방법의 제2실시예를 도시하는 공정도이다.
1 is a process chart showing a first embodiment of the method of manufacturing a fabric coated with a tree extract in the present invention.
Figure 2 is a process diagram showing a second embodiment of the method for producing a fabric coated with a tree extract in the present invention.
이하 본 발명의 바람직한 실시예에 대하여 첨부된 도면을 참조하여 구체적으로 설명한다.Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings.
본 발명의 설명에서 동일 또는 유사한 구성요소는 동일 또는 유사한 도면번호를 부여하고, 그 자세한 설명은 생략하기로 한다.
In the description of the present invention, the same or similar elements are denoted by the same or similar reference numerals, and a detailed description thereof will be omitted.
도 1은 본 발명에 따른 나무 추출액이 코팅된 원단의 제조방법의 제1실시예를 도시하는 공정도이다.1 is a process chart showing a first embodiment of a method for manufacturing a fabric coated with a tree extract according to the present invention.
도 1에 도시된 바와 같이, 본 발명은 편백나무, 대나무, 소나무, 향나무, 오동나무 및 전나무로 이루어지는 군에서 선택되는 나무의 원목을 포함하는 원료를 추출용매로 추출하고 이를 여과하여 나무 추출액을 제조하는 S1단계, 상기 나무 추출액을 바인더와 혼합하여 원단 코팅액을 제조하는 S2단계, 상기 원단 코팅액을 원단의 일면에 분무하거나 도포하는 S3단계 및 상기 S3단계를 거친 원단을 열처리하여 코팅층을 형성하는 S4단계를 포함하는 것이다.
As shown in FIG. 1, the present invention extracts a raw material including a solid wood of a tree selected from the group consisting of cypress, bamboo, pine, juniper, paulownia and fir with an extraction solvent and filters the same to prepare a tree extract. S1 step, S2 step of manufacturing the fabric coating solution by mixing the wood extract with a binder, S3 step of spraying or applying the fabric coating solution to one side of the fabric and S4 step of forming a coating layer by heat-treating the fabric through the S3 step It will include.
본 발명에 따른 S1단계는 편백나무, 대나무, 소나무, 향나무, 오동나무 및 전나무로 이루어지는 군에서 선택되는 나무의 원목을 포함하는 원료를 추출용매로 추출하고 이를 여과하여 나무 추출액을 제조하는 것이다.Step S1 according to the present invention is to extract a raw material containing a solid wood of a tree selected from the group consisting of cypress, bamboo, pine, juniper, paulownia and fir with an extraction solvent and to filter it to produce a tree extract.
본 발명에 따른 원료는 크게 상기 나무의 원목을 단일 성분으로 하는 것과, 상기 나무 원목에 잎, 열매, 뿌리 및 줄기로 이루어지는 군에서 선택되는 적어도 하나의 성분을 더 포함하는 복합 성분으로 하는 것이 있다.The raw material according to the present invention includes a single component of the wood of the tree as a single component, and a composite component of the wood of the tree further comprising at least one component selected from the group consisting of leaves, fruits, roots and stems.
이하에서는 본 발명의 원료가 편백나무 원목을 포함하는 일실시예를 중심으로 본 발명을 설명하도록 한다.Hereinafter, the present invention will be described with reference to an embodiment, in which the raw material of the present invention includes a cypress solid wood.
본 발명에 따른 원료는 크게 상기 편백나무의 원목을 단일 성분으로 하는 것과, 상기 나무 원목에 편백잎, 편백열매, 편백뿌리 및 편백줄기로 이루어지는 군에서 선택되는 적어도 하나의 성분을 더 포함하는 복합 성분으로 하는 것이 있다.The raw material according to the present invention is a composite component that further includes at least one component selected from the group consisting of the solid wood of the cypress as a single component, and the cypress leaves, cypresses, cypress roots and cypress stems in the solid wood. There is something to do.
따라서, 나무 추출액의 제조에 있어서, 편백나무 원목만을 분쇄하여 나무 추출액을 제조하는 방식과, 편백나무 원목을 기본 원료로 하고 여기에 편백잎, 편백열매 및 편백뿌리 및 편백줄기로 이루어지는 군에서 선택되는 적어도 하나를 더 포함하여 나무 추출액을 제조하는 방식으로 구분할 수 있다.Therefore, in the production of wood extract, the method of producing wood extract by pulverizing only the cypress wood, and from the group consisting of cypress wood, cypress leaves, cypress berries and cypress roots and cypress stems. At least one may be further divided into a method of preparing a tree extract.
본 발명의 원료인 편백나무 원목, 편백잎, 편백열매, 편백뿌리 및 편백줄기에는 피톤치드라는 화합물이 다량 함유되어 있고, 피톤치드의 효능은 아래와 같다. The raw wood, cypress leaves, cypress berries, cypress roots and cypress stems, which are the raw materials of the present invention, contain a large amount of a compound called phytoncide, and the efficacy of phytoncide is as follows.
피톤치드(phytoncide)는 그리스어로 "식물"을 의미하는 phyton(식물)과 살균력을 의미하는 cide(살인자)를 합성한 말로서 "식물이 분비하는 살균물"을 의미한다. 모든 식물들은 자신을 방어하기 위한 수단으로서 동물들과 달리 이동할 수 없어 자기 방어를 하는 물질을 만드는데, 이러한 피톤치드는 편백나무, 측백나무 등에서 특히 많이 추출되며 방향성이 있는 항생물질의 총칭을 피톤치드라 하며 테르핀(terpene) 계통의 유기 화합물을 말한다.Phytoncide is a mixture of phyton (plant), which means "plant" in Greek, and cide (killer), which means sterilizing power. As a means to defend oneself, all plants can not move unlike animals and make self-defense material. These phytoncides are extracted especially from cotton trees, bamboo trees, etc., and the generic name of oriental antibiotics is phytoncide, Refers to an organic compound of the terpene system.
최근에 많이 각광받고 있는 산림욕이란 피톤치드가 휘산되어 있는 상태의 대기에 인간이 접하는 것으로서, 피톤치드가 주목받는 이유는 해충, 병균, 곰팡이, 박테리아 등에는 치명적인 제거 역할을 하지만 인간에게는 유익하기 때문이다. 또한, 피톤치드의 효능은 크게 6가지 효능을 갖는데, 스트레스 완화작용, 강한 항균작용, 소취작용 및 유해한 성분의 중화, 진정작용, 알레르기 및 피부 질환 개선 작업, 면역기능 증대 작업 효능을 갖는다.Recently, forest baths, which have been widely spotlighted, are exposed to humans in the atmosphere of phytoncide volatilized, and phytoncide is attracting attention because it acts as a deadly remover for pests, germs, molds and bacteria, but is beneficial to humans. In addition, the efficacy of phytoncide has six effects, stress relief, strong antibacterial action, deodorant action and neutralization of harmful ingredients, sedation, allergy and skin disease improvement work, immune function enhancement work.
피톤치드는 스트레스 호르몬인 코르티솔을 감소시켜 스트레스를 완화하는 작용을 가진다. 그리고 피톤치드는 리스테리아균, 포도상구균, 캔디다균, 레지오넬라균에 대한 미생물 억제능력을 가지고 있어, 항균 및 살균 효과가 우수하다.Phytoncide relieves stress by reducing the stress hormone cortisol. In addition, phytoncide has the ability to inhibit microorganisms against Listeria, Staphylococcus, Candida, and Legionella, and has excellent antibacterial and bactericidal effects.
또한, 피톤치드는 신축건물 입주시 두통, 눈과 목의 따가움, 아토피 피부염 및 비염 등 각종 알러지성 질환을 유발하는 포름알데히드와 톨루엔 등 유기화합물을 중화시키는 효능을 가지고 있다. 그리고 알레르기 및 피부 질환 개선과 관련하여, 피톤치드는 아토피 피부염과 알러지의 원인 중 하나인 집먼지 진드기의 생육을 저해한다.In addition, phytoncide has the effect of neutralizing organic compounds such as formaldehyde and toluene, which cause various allergic diseases such as headache, eye and neck stigma, atopic dermatitis and rhinitis when entering new buildings. And in connection with improving allergies and skin diseases, phytoncide inhibits the growth of house dust mites, one of the causes of atopic dermatitis and allergies.
본 발명에서 편백나무 이외의 대나무, 소나무, 향나무, 오동나무 및 전나무에서 추출한 나무 추출액도 피톤치드를 함유하고 있으며, 각각의 나무에 대하여 이미 공지된 고유의 특성에 대한 자세한 설명은 생략한다.In the present invention, tree extracts extracted from bamboo, pine, juniper, paulownia, and fir other than cypress also contain phytoncide, and detailed descriptions of the inherent known characteristics of each tree are omitted.
한편, 본 발명의 원료가 편백나무 원목과 편백잎, 편백열매, 편백뿌리 및 편백줄기로 이루어지는 군에서 선택되는 적어도 하나의 성분을 더 포함하는 복합 성분으로 이루어지는 경우에는 편백나무 원목과, 적어도 하나의 나머지 성분(편백잎, 편백열매, 편백뿌리 및 편백줄기)은 대략 1:0.5 ~ 1:1의 중량비로 혼합되어 이루어질 수 있다.On the other hand, when the raw material of the present invention consists of a composite component further comprises at least one component selected from the group consisting of solid wood, cypress leaves, cypress berries, cypress roots and cypress stems, the cypress logs and at least one The remaining ingredients (cypress leaf, cypress fruit, cypress root and cypress stem) may be mixed in a weight ratio of approximately 1: 0.5 to 1: 1.
그리고 상기 원료들은 건조한 상태에서 분쇄하여 혼합하는 것이 나무 추출액에서 유효 성분 추출하는 것이 용이하다. 예를 들어, 편백나무 원목, 편백뿌리, 편백줄기 등은 톱 등으로 소정 크기로 절단할 수도 있으나, 톱밥/대패밥과 같이 더 작은 형태로 분쇄하여 사용할 수 있다. 반면 편백잎이나 편백열매는 건조한 상태에서 믹서 등으로 갈은 형태로 사용할 수 있다.
And it is easy to extract the active ingredient from the wood extract to mix the raw materials are ground and mixed in a dry state. For example, solid cypress, cypress roots, cypress stems, etc. may be cut to a predetermined size with a saw or the like, but may be used by grinding into smaller forms such as sawdust / scallop. On the other hand, cypress leaves or cypress berries can be used in a dry form in a mixer.
한편, 본 발명의 원료 중에서 편백열매에는 다른 원료보다도 월등한 양의 피톤치드가 함유되어 있다. 따라서, 원료는 편백나무 원목 40~60중량부, 편백잎 20~30중량부 및 편백열매 5~10중량부로 이루어질 수도 있다.On the other hand, in the raw material of the present invention, the cypress fruit contains an amount of phytoncide superior to other raw materials. Therefore, the raw material may be composed of 40 to 60 parts by weight of solid cypress wood, 20 to 30 parts by weight of cypress leaves and 5 to 10 parts by weight of cypress berries.
왜냐하면, 상기 편백잎, 편백열매 및 편백나무 원목 상호 간의 혼합비율이 상기 범위인 경우에는 편백나무 원목, 편백잎 및 편백열매에 공통적으로 함유된 피톤치드는 물론이고, 각각의 고유한 성분들과의 시너지 작용으로 인해 보다 효과적인 항박테리아 내지 항진균 효과 등을 발휘할 수 있기 때문이다.
Because, if the mixing ratio between the cypress leaves, cypress berries and cypress wood is within the above range, synergy with each of the unique components as well as phytoncides commonly contained in the cypress logs, cypress leaves and cypress berries This is because it can exert more effective antibacterial to antifungal effect due to the action.
본 발명의 원료에서 나무 추출액을 제조하는 방식은 크게 열수추출과 유기 용제에 의한 추출 두 가지 방식이 있다.There are two methods of preparing a tree extract from the raw material of the present invention, hot water extraction and extraction with an organic solvent.
먼저, 열수 추출 방식에 있어서, 추출용매인 열수는 90~100℃의 물이고, 상기 원료는 상기 물에 1:5 ~ 1:10의 중량비로 혼합되어, 5~10 시간 동안 열수추출되는 것이다.First, in the hot water extraction method, hot water as an extraction solvent is water of 90 ~ 100 ℃, the raw material is mixed with the water in a weight ratio of 1: 5 to 1:10, and the hot water is extracted for 5 to 10 hours.
상기 원료와 물의 중량비가 1:5 미만으로 혼합되는 경우에는 유효성분을 충분히 추출할 수 있는 5~10 시간 동안 열수 추출하기에 물(열수)의 양이 부족할 수 있고, 그에 따라 유효성분이 파괴될 우려가 있기 때문이다.When the weight ratio of the raw material and water is mixed less than 1: 5, the amount of water (hot water) may be insufficient to extract hot water for 5 to 10 hours to sufficiently extract the active ingredient, and thus the active ingredient may be destroyed. Because there is.
그리고 원료와 물의 중량비가 1:10을 초과하여 혼합되는 경우에는 5~10 시간 동안 열수 추출되더라도 나무 추출액의 농도가 낮아 항박테리아와 항진균의 효과를 제대로 발휘하지 못할 수 있기 때문이다.
And if the weight ratio of the raw material and water is mixed in excess of 1:10, even if the hot water is extracted for 5 to 10 hours, the concentration of the wood extract is low, it may not be able to properly exhibit the effects of antibacterial and antifungal.
다음으로, 유기 용제에 의한 추출 방식은 알콜 또는 알콜 수용액을 이용하여 나무 추출액을 얻는 것이다. 그리고 알콜은 메탄올, 에탄올, 프로판올, 이소프로판올 또는 부탄올 중에서 적어도 하나 선택될 수 있다.Next, the extraction method by the organic solvent is to obtain a tree extract using an alcohol or an aqueous alcohol solution. And the alcohol may be selected from at least one of methanol, ethanol, propanol, isopropanol or butanol.
예를 들어, 편백잎, 편백열매 및 편백나무 원목을 수세한 다음, 편백잎과 편백나무 원목은 잘게 절단하여 사용하고, 편백열매는 믹서 등을 이용하여 갈아서 원료를 준비한다.For example, after washing with cypress leaves, cypress berries and cypress logs, the cypress leaves and cypress logs are finely cut, and the cypress berries are ground using a mixer to prepare raw materials.
예를 들어, 준비된 원료 100g에 대하여 알콜 또는 50% 상의 알콜 수용액 0.5~1L를 넣고 5~10 시간 동안 마그네틱바 등으로 교반하여 얻은 나무 추출액을 여과지를 이용하여 찌꺼기를 제거하여 추출액을 얻을 수 있다.
For example, 0.5-1 L of alcohol or 50% aqueous alcohol solution is added to 100 g of the prepared raw material, and the wood extract obtained by stirring with a magnetic bar or the like for 5 to 10 hours is removed by using filter paper to obtain an extract.
본 발명에 따른 S2단계는 상기 나무 추출액을 바인더와 혼합하여 원단 코팅액을 제조하는 것이다.Step S2 according to the present invention is to prepare a fabric coating solution by mixing the wood extract with a binder.
본 발명에 따른 원단 코팅액에서, 나무 추출액과 바인더는 1:5 ~ 1:10의 중량비로 혼합되는 것이 바람직하다.In the fabric coating solution according to the present invention, the wood extract and the binder is preferably mixed in a weight ratio of 1: 5 to 1:10.
왜냐하면, 나무 추출액과 바인더가 혼합되는 중량비가 1:5 미만인 경우에는 나무 추출액의 양이 상대적으로 크기 때문에 바인더에 의한 섬유와의 접착력이 약해질 수 있기 때문이다.This is because, when the weight ratio of the wood extract and the binder is mixed less than 1: 5, the amount of the wood extract is relatively large, and thus the adhesive strength with the fiber by the binder may be weakened.
그리고 나무 추출액과 바인더가 1:10 중량비를 초과하는 경우에는 나무 추출액에 의한 항바이러스 내지 항균 효과를 기대하기 어렵기 때문이다.When the wood extract and the binder exceeds 1:10 by weight, it is because it is difficult to expect the antiviral or antimicrobial effect of the wood extract.
본 발명에 따른 바인더는 크게 원단과의 접착력 내지 점착력을 제공하는 제1성분과 분산성과 상기 나무 추출액과 제1성분과의 혼합을 원활하게 해주는 용제 역할의 제2성분을 포함하여 이루어진다.The binder according to the present invention comprises a first component that largely provides adhesion to the fabric and adhesion, and a second component of dispersibility and a solvent that facilitates mixing of the wood extract and the first component.
그리고 제1성분과 제2성분은 1:0.4 ~ 1:0.6의 중량비로 혼합될 수 있다.The first component and the second component may be mixed in a weight ratio of 1: 0.4 to 1: 0.6.
구체적으로 본 발명의 제1성분은 에폭시, 아크릴, 비닐, 폴리에틸렌, 폴리프로필렌, 폴리에스테르, 폴리에테르, 폴리우레탄, 폴리이소시아네이트 및 폴리아미드로 이루어지는 군에서 적어도 하나 선택되는 것이다.Specifically, the first component of the present invention is at least one selected from the group consisting of epoxy, acrylic, vinyl, polyethylene, polypropylene, polyester, polyether, polyurethane, polyisocyanate and polyamide.
그리고 본 발명의 제2성분은 알코올, 케톤, 글리콜 및 에테르로 이루어지는 군에서 적어도 하나 선택되는 것이다.And the second component of the present invention is at least one selected from the group consisting of alcohols, ketones, glycols and ethers.
또한, 바인더에는 실리카 등의 표면효과 개선제, 가소제, 셀룰로오스 아세테이트 부틸레이트 등의 점도조절제, 레벨링제, 접착증진제 등의 첨가제를 더 포함하여 이루어질 수 있다. In addition, the binder may further include additives such as surface effect improvers such as silica, plasticizers, viscosity modifiers such as cellulose acetate butyrate, leveling agents, adhesion promoters, and the like.
이러한 첨가제로 사용되는 개개의 성분을 선택하는 것과 그 첨가량은 원단의 사용 용도 등에 따라 적절히 조정될 수 있다.
The selection of the individual components used as such additives and the amount of their addition can be appropriately adjusted according to the use purpose of the fabric.
본 발명에 따른 S3단계는 상기 원단 코팅액을 원단의 일면에 분무하거나 도포하는 것이 바람직하다.In the step S3 according to the present invention, it is preferable to spray or apply the fabric coating solution on one surface of the fabric.
본 발명에 따른 원단은 합성섬유, 천연섬유 또는 합성섬유와 천연섬유가 혼합된 섬유로 이루어질 수 있다.Fabric according to the present invention may be made of synthetic fibers, natural fibers or fibers mixed with synthetic fibers and natural fibers.
그리고 본 발명은 S2단계에서 제조된 원단 코팅액을 원단의 일면에 브러시로 도포할 수도 있고, 원단의 일면에 스프레이 방식으로 분무할 수도 있다.And the present invention may be applied to the fabric coating solution prepared in step S2 with a brush on one side of the fabric, sprayed on one surface of the fabric in a spray method.
이렇듯 원단의 일면에만 원단 코팅액을 분무 또는 도포하는 이유는, 예를 들어 원단의 일면에 원단 코팅액을 분무하면 원단 자체의 흡수력으로 인해 원단 코팅액의 일부가 자연스럽게 원단의 내부로 스며들기 때문이다.The reason for spraying or applying the fabric coating liquid to only one surface of the fabric as described above is that, for example, spraying the fabric coating liquid on one side of the fabric naturally causes a part of the fabric coating liquid to penetrate into the fabric due to the absorbency of the fabric itself.
본 발명과 달리 원단을 코팅액에 침지시키는 방식을 이용하게 되면, 후술할 원단 코팅액의 열처리에 의해 형성되는 코팅층이 원단보다 더 두껍게 형성되기 때문에 유연성이 급격히 감소하게 되는 문제가 있다. 또한 두껍게 형성된 코팅층은 균열이 생기기 쉽기 때문에 제품의 품질 저하가 되는 요인이 될 수도 있기 때문이다.Unlike the present invention, if a method of immersing the fabric in the coating solution is used, the flexibility of the coating layer formed by the heat treatment of the fabric coating solution to be described later is made thicker than that of the fabric. In addition, since a thick coating layer is likely to cause cracks, the quality of the product may be a factor.
다만, 본 발명의 기술적 범위에서 원단의 양면에 원단 코팅액을 도포하거나 분무하는 것을 배제한다는 의미는 아니므로, 원단의 재질 또는 두께 등에 따라 원단의 양면에 도포하는 방식도 포함할 수 있다.
However, in the technical scope of the present invention does not mean that the coating or spraying the fabric coating solution on both sides of the fabric, it may also include a method of applying to both sides of the fabric according to the material or thickness of the fabric.
본 발명에 따른 S4단계는 거친 원단을 열처리하여 코팅층을 형성하는 것이 바람직하다.In the step S4 according to the present invention, it is preferable to form a coating layer by heat-treating rough fabrics.
또한, 본 발명에 따른 S4단계의 열처리는 한 쌍의 히팅 롤러에 의해 80~150℃에서 1~5분 동안 이루어지는 것이 바람직하다.In addition, the heat treatment of step S4 according to the present invention is preferably made for 1 to 5 minutes at 80 ~ 150 ℃ by a pair of heating roller.
본 발명에 따른 열처리 온도가 80℃ 미만인 경우에는 상기 바인더에 의한 원단과의 접착이 제대로 이루어지지 않기 때문이다.If the heat treatment temperature according to the present invention is less than 80 ℃ is because the adhesion with the fabric by the binder is not made properly.
그리고 열처리 온도가 150℃를 초과하는 경우에는 접착력은 다소 강해질 수 있으나, 열에 의한 섬유의 손상이 있을 수 있을 뿐만 아니라, 나무 추출액에 함유된 유효성분이 변형 내지 손상될 수 있기 때문이다.And when the heat treatment temperature exceeds 150 ℃, the adhesive force may be somewhat stronger, not only because the fiber may be damaged by heat, but also because the active ingredient contained in the wood extract may be deformed or damaged.
열처리에 사용되는 한 쌍의 히팅 롤러가 복수 개 설치되어 원단의 열처리에 의한 코팅층을 형성할 수도 있다.A plurality of pairs of heating rollers used for the heat treatment may be provided to form a coating layer by heat treatment of the fabric.
그리고, 본 발명의 히팅 롤러는 연속작업의 용이성을 고려한 것이므로, 공정 조건에 따라 히팅 롤러가 아닌 예를 들어, 판 형상의 히팅판에 원단 코팅액을 도포한 면을 접촉시키는 방식으로 코팅층을 형성할 수도 있음은 물론이다.
In addition, since the heating roller of the present invention considers the ease of continuous operation, the coating layer may be formed in such a manner that the surface coated with the fabric coating liquid is not contacted with the heating roller, for example, in the shape of a plate rather than the heating roller. Of course.
도 2는 본 발명에 따른 나무 추출액이 코팅된 원단의 제조방법의 제2실시예를 도시하는 공정도이다.Figure 2 is a process diagram showing a second embodiment of the method for producing a fabric coated with a tree extract according to the present invention.
도 2에 도시된 바와 같이, 본 발명의 S5단계는 상기 S4단계를 거친 후, 편백정유 성분을 함유하는 편백정유 코팅층을 형성하는 것이다. 본 발명의 편백정유는 편백나무의 피톤치드를 함유하는 것으로서, 편백잎을 수증기 증류방식에 의해 얻어질 수 있고,이미 시중에서 시판되는 것을 사용할 수 있다.As shown in Figure 2, step S5 of the present invention after the step S4, to form a protein-containing essential oil coating layer containing the protein-containing essential oil component. The cypress essential oil of the present invention contains phytoncide of cypress, the cypress leaves can be obtained by steam distillation, and those already available on the market can be used.
그리고 편백정유 코팅층은 S4단계를 거쳐 코팅층의 온도가 60℃ 이상인 상태에서 편백정유 성분을 함유한 분사액을 분무하는 방식으로 형성되는 것이 바람직하다. 그리고 상기 편백정유 성분을 함유한 분사액에는 바인더 성분이 포함될 수 있다. And the protein white oil coating layer is preferably formed by spraying the injection liquid containing the protein white oil component in a state in which the temperature of the coating layer is 60 ° C or more through the step S4. And the injection liquid containing the cypress essential oil component may include a binder component.
이와 같이, 편백정유 코팅층을 형성함으로써, 보다 우수한 항균 효과를 기대할 수 있다.In this manner, by forming a protein-containing essential oil coating layer, more excellent antibacterial effect can be expected.
만일 바인더 성분을 포함한 분사액을 사용하는 경우에는, 본 발명의 편백정유 코팅층은 S4단계의 코팅층의 두께에 비해 대략 0.05~0.1mm의 두께로 형성되되, S4단계의 코팅층의 전체 표면을 덮지 않을 정도로 도포된 상태에서 압착하여 형성되는 것이 바람직하다.If the injection liquid containing the binder component is used, the cypress essential oil coating layer of the present invention is formed to a thickness of approximately 0.05 ~ 0.1mm compared to the thickness of the coating layer of the step S4, so as not to cover the entire surface of the coating layer of the step S4 It is preferable to form by crimping | bonding in the apply | coated state.
한편, 상기한 바와 같이 제조된 나무 추출액이 코팅된 원단은 의류, 각종 침구류 등에 사용될 수 있고, 특히 자주 세탁하기 어려운 침구류에 본 발명의 원단을 사용하는 경우에는 항바이러스 내지 항균 효과로 인해 각종 세균 등의 번식을 방지할 수 있다.
On the other hand, the fabric coated with the wood extract prepared as described above can be used for clothing, various bedding, and the like, especially when using the fabric of the present invention in bedding difficult to wash frequently, due to the anti-viral to antibacterial effect It can prevent the growth of bacteria and the like.
이하, 본 발명에 따른 나무 추출액이 코팅된 원단의 제조방법에 대한 실시예는 다음과 같다.Hereinafter, an embodiment of a method for manufacturing a fabric coated with a tree extract according to the present invention is as follows.
(1) 편백나무 원목 0.5kg, 편백잎 0.3kg, 편백열매 0.2kg을 수세한 후, 분쇄하여 원료를 준비한다.(1) 0.5 kg of cypress logs, 0.3 kg of cypress leaves and 0.2 kg of cypress berries are washed with water, and then ground to prepare raw materials.
준비된 원료를 90℃ 이상의 물 10kg이 담긴 용기에 넣고 대략 8 시간 동안 열수 추출을 하고, 여과지에 통과시켜 불순물을 제거하여 나무 추출액을 얻었다.(S1단계)The prepared raw materials were placed in a container containing 10 kg of water of 90 ° C. or more, extracted with hot water for about 8 hours, and passed through a filter paper to remove impurities to obtain a tree extract.
(2) 나무 추출액 500g에 대하여 바인더는 2.5kg을 혼합하여 원단 코팅액을 제조한다. 이때 바인더의 제1성분으로 폴리에틸렌 약 1.5kg을, 제2성분으로 에틸렌글리콜을 1.0kg을 사용하였다.(S2단계)(2) For 500 g of wood extract, 2.5 kg of binder is mixed to prepare a fabric coating solution. In this case, about 1.5 kg of polyethylene was used as the first component of the binder and 1.0 kg of ethylene glycol was used as the second component.
(3) 롤 형태의 원단을 자동으로 이송시키는 원단 가공장치에 장착하고, 펼쳐진 원단 상에 원단 코팅액을 스프레이 방식으로 분사한다.(S3단계)(3) It is mounted on the fabric processing apparatus that automatically transfers the roll-shaped fabric, and sprays the fabric coating liquid on the spread fabric by spray method. (S3 step)
(4) 그리고 원단을 140℃로 가열된 히팅 롤러로 이송시켜 열처리하고, 자연 냉각시켜 코팅층을 형성하여, 본 발명의 나무 추출액이 코팅된 원단을 제조한다.(S4단계)
(4) And the fabric is transferred to a heating roller heated to 140 ℃ heat treatment, and naturally cooled to form a coating layer, to prepare a fabric coated with the wood extract of the present invention. (S4 step)
이와 같은 제조방법에 의하여 제조된 나무 추출액이 코팅된 원단은 편백잎, 편백열매, 편백나무 원목에 있는 피톤치드에 의한 항균 작용 등으로 유해한 미생물 또는 집먼지 진드기와 같은 해충이 서식하는 것을 방지할 수 있게 된다.
The fabric coated with the wood extract prepared by such a manufacturing method can prevent harmful microorganisms or pests such as house dust mites from incubating due to antibacterial action by phytoncides in cypress leaves, cypress berries, and cypress logs. .
이상에서 설명된 본 발명은 예시적인 것에 불과하며, 본 발명이 속한 기술분야의 통상의 지식을 가진 자라면 이로부터 다양한 변형 및 균등한 타 실시예가 가능하다는 점을 잘 알 수 있을 것이다. 그러므로 본 발명은 상기의 상세한 설명에서 언급되는 형태로만 한정되는 것은 아님을 잘 이해할 수 있을 것이다. 따라서 본 발명의 진정한 기술적 보호 범위는 첨부된 특허청구범위의 기술적 사상에 의해 정해져야 할 것이다. 또한, 본 발명은 첨부된 청구범위에 의해 정의되는 본 발명의 정신과 그 범위 내에 있는 모든 변형물과 균등물 및 대체물을 포함하는 것으로 이해되어야 한다.
While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is to be understood that the invention is not limited to the disclosed exemplary embodiments, but, on the contrary, is intended to cover various modifications and equivalent arrangements included within the spirit and scope of the invention. Therefore, it is to be understood that the present invention is not limited to the above-described embodiments. Therefore, the true technical protection scope of the present invention will be defined by the technical spirit of the appended claims. It is also to be understood that the invention includes all modifications, equivalents, and alternatives falling within the spirit and scope of the invention as defined by the appended claims.

Claims (7)

  1. 편백나무의 원목을 포함하는 원료를 추출용매로 추출하고 이를 여과하여 나무 추출액을 제조하는 S1단계;
    상기 나무 추출액을 바인더와 혼합하여 원단 코팅액을 제조하는 S2단계;
    상기 원단 코팅액을 원단의 일면에 분무하거나 도포하는 S3단계; 및
    상기 S3단계를 거친 원단을 열처리하여 코팅층을 형성하는 S4단계;
    를 포함하는 것을 특징으로 하는 나무 추출액이 코팅된 원단의 제조방법.
    S1 step of extracting the raw material containing the wood of the cypress with an extraction solvent and filtering the same to produce a wood extract;
    S2 step of preparing a fabric coating solution by mixing the wood extract with a binder;
    S3 step of spraying or applying the fabric coating liquid to one side of the fabric; And
    S4 step of forming a coating layer by heat-treating the fabric through the S3 step;
    Method of producing a fabric coated with a tree extract, characterized in that it comprises a.
  2. 제1항에 있어서,
    상기 S1단계의 원료는 상기 편백나무의 잎, 열매, 뿌리 및 줄기로 이루어지는 군에서 선택되는 적어도 하나를 더 포함하여, 상기 편백나무의 원목과 함께 추출되는 것을 특징으로 하는 나무 추출액이 코팅된 원단의 제조방법.
    The method of claim 1,
    The raw material of the step S1 further comprises at least one selected from the group consisting of leaves, berries, roots and stems of the cypress tree, the extract of the fabric coated with the wood extract, characterized in that extracted with the solid wood of the cypress Manufacturing method.
  3. 제1항에 있어서,
    상기 S1단계에서 상기 추출용매는 알콜 또는 알콜 수용액이고,
    상기 원료와 상기 추출용매는 1:5 ~ 1:10의 중량비로 혼합된 상태에서 5~10 시간 동안 추출이 이루어지는 것을 특징으로 하는 나무 추출액이 코팅된 원단의 제조방법.
    The method of claim 1,
    In the step S1 the extraction solvent is an alcohol or an aqueous alcohol solution,
    The raw material and the extraction solvent is a method of manufacturing a fabric extract coated fabric, characterized in that the extraction is carried out for 5 to 10 hours in a mixed state in a weight ratio of 1: 5 to 1:10.
  4. 제1항에 있어서,
    상기 바인더는,
    에폭시, 아크릴, 비닐, 폴리에틸렌, 폴리프로필렌, 폴리에스테르, 폴리에테르, 폴리우레탄, 폴리이소시아네이트 및 폴리아미드로 이루어지는 군에서 적어도 하나 선택되는 제1성분; 및
    알코올, 케톤, 글리콜 및 에테르로 이루어지는 군에서 적어도 하나 선택되는 제2성분;을 포함하는 것을 특징으로 하는 나무 추출액이 코팅된 원단의 제조방법.
    The method of claim 1,
    Wherein the binder comprises:
    At least one first component selected from the group consisting of epoxy, acrylic, vinyl, polyethylene, polypropylene, polyester, polyether, polyurethane, polyisocyanate and polyamide; And
    A method of manufacturing a fabric coated with a tree extract, comprising; a second component selected from the group consisting of alcohols, ketones, glycols and ethers.
  5. 제1항에 있어서,
    상기 S4단계의 열처리는 한 쌍의 히팅 롤러에 의해 80~150℃에서 1~5분 동안 이루어지는 것을 특징으로 하는 나무 추출액이 코팅된 원단의 제조방법.
    The method of claim 1,
    The heat treatment of the step S4 is a method of manufacturing a fabric extract coated fabric, characterized in that made for 1 to 5 minutes at 80 ~ 150 ℃ by a pair of heating roller.
  6. 제1항에 있어서,
    상기 S4단계를 거친 후, 편백정유 성분을 함유하는 편백정유 코팅층을 형성하는 S5단계를 더 포함하는 것을 특징으로 하는 나무 추출액이 코팅된 원단의 제조방법.
    The method of claim 1,
    After the step S4, the method of producing a fabric extract coated with wood extract, characterized in that it further comprises a step S5 to form a cypress essential oil coating layer containing a cypress essential oil component.
  7. 청구항 1 내지 청구항 6 중에서 어느 하나의 제조방법에 의해 제조되는 것을 특징으로 하는 나무 추출액이 코팅된 원단.A fabric coated with a tree extract, characterized in that it is produced by any one of the manufacturing method of claim 1.
KR1020110116170A 2011-11-09 2011-11-09 Fabrics coated by chamaecyparis obtusa extract and manufacturing method thereof KR101271877B1 (en)