KR101066778B1 - 형상 불량 요인 특정 방법, 장치 및 프로그램 - Google Patents
형상 불량 요인 특정 방법, 장치 및 프로그램 Download PDFInfo
- Publication number
- KR101066778B1 KR101066778B1 KR1020097006287A KR20097006287A KR101066778B1 KR 101066778 B1 KR101066778 B1 KR 101066778B1 KR 1020097006287 A KR1020097006287 A KR 1020097006287A KR 20097006287 A KR20097006287 A KR 20097006287A KR 101066778 B1 KR101066778 B1 KR 101066778B1
- Authority
- KR
- South Korea
- Prior art keywords
- elastic recovery
- stress
- workpiece
- shape
- main influence
- Prior art date
Abstract
Description
Claims (9)
- 탄성 회복 전의 가공품 형상에 대해 탄성 회복 전의 가공품 전체에 작용하는 응력 분포를 부여한 경우의, 탄성 회복 전후에 있어서의 상기 가공품에 정해진 임의 평가점의 탄성 회복을 기초로 하는 변형량을 취득하는 동시에,미리 설정된 복수의 영역으로 가공품 형상을 분할하고, 탄성 회복 전의 가공품 전체에 작용하는 응력 분포를 상기 복수의 영역으로 분할하여, 탄성 회복 전의 가공품 형상에 대해 상기 영역마다, 상기 분할한 응력 분포를 부여한 경우의, 탄성 회복 전후의 상기 평가점의 탄성 회복을 기초로 하는 영역별 응력 부여 변형량을, 상기 분할한 응력 분포를 부여한 상기 각 영역에 대해 취득하고,상기 변형량과 상기 각 영역의 영역별 응력 부여 변형량을 비교하여, 이들 차가 가장 작아지는 영역을, 탄성 회복 전후의 상기 평가점의 형상 불량에 가장 관여하는 응력 분포 영역인 주 영향 영역으로 특정하는 처리를,컴퓨터에 실행시키는 형상 불량 요인 특정 프로그램을 기록한 컴퓨터로 읽을 수 있는 기록 매체.
- 제1항에 있어서, 탄성 회복 전의 가공품 형상에 대해, 상기 주 영향 영역에 작용하는 응력 분포를, 직교 좌표계의 각 방향 성분으로 분해하여 부여한 경우의, 탄성 회복 전후의 상기 평가점의 탄성 회복을 기초로 하는 성분별 응력 부여 변형량을 취득하고,상기 주 영향 영역의 응력 분포를 부여한 경우의 영역별 응력 부여 변형량과, 상기 성분별 응력 부여 변형량을 비교하여, 이들 차가 가장 작아지는 방향의 응력 성분을, 탄성 회복 전후의 상기 평가점의 형상 불량에 가장 관여하는 응력 성분인 주 영향 응력 성분으로 특정하는 처리를,또한 컴퓨터에 실행시키는 것을 특징으로 하는 형상 불량 요인 특정 프로그램을 기록한 컴퓨터로 읽을 수 있는 기록 매체.
- 제2항에 있어서, 탄성 회복 전의 가공품 형상에 대해, 상기 주 영향 영역의 판 두께 방향 중앙에 작용하는 주 영향 응력 성분을, 주 영향 영역의 판 두께 방향 전역에 균등하게 분포시킨 응력 분포를 부여한 경우의, 탄성 회복 전후의 상기 평가점의 탄성 회복을 기초로 하는 변형량을 취득하고,상기 변형량과, 상기 주 영향 영역에 주 영향 응력 성분을 부여한 경우의 성분별 응력 부여 변형량을 비교하고, 상기 주 영향 응력 성분의 판 두께 표리의 응력차가, 탄성 회복 전후의 상기 평가점의 형상 불량에 미치는 영향의 유무를 판정하는 처리를,또한 컴퓨터에 실행시키는 것을 특징으로 하는 형상 불량 요인 특정 프로그램을 기록한 컴퓨터로 읽을 수 있는 기록 매체.
- 탄성 회복 전의 가공품 전체에 작용하는 응력 분포를 산출하는 응력 분포 연산부와,탄성 회복 전의 가공품 형상에 대해 상기 응력 분포를 부여한 경우의, 탄성 회복 전후에 있어서의 상기 가공품에 정해진 임의 평가점의 탄성 회복을 기초로 하는 변형량을 산출하는 탄성 회복량 연산부와,미리 설정된 복수의 영역으로 상기 가공품 형상을 분할하고, 탄성 회복 전의 가공품 전체에 작용하는 응력 분포를 상기 복수의 영역으로 분할하여, 탄성 회복 전의 가공품 형상에 대해 상기 영역마다, 상기 분할한 응력 분포를 부여한 경우의, 탄성 회복 전후의 상기 평가점의 탄성 회복을 기초로 하는 영역별 응력 부여 변형량을, 상기 분할한 응력 분포를 부여한 상기 각 영역에 대해 산출하는 탄성 회복량 연산부와,상기 변형량과 상기 각 영역의 영역별 응력 부여 변형량을 비교하여, 이들 차가 가장 작아지는 영역을, 탄성 회복 전후의 상기 평가점의 형상 불량에 가장 관여하는 응력 분포 영역인 주 영향 영역으로 특정하는 비교 연산부를 구비하는, 형상 불량 요인 특정 장치.
- 제4항에 있어서, 탄성 회복 전의 가공품 형상에 대해, 상기 주 영향 영역에 작용하는 응력 분포를, 직교 좌표계의 각 방향 성분으로 분해하여 부여한 경우의, 탄성 회복 전후의 상기 평가점의 탄성 회복을 기초로 하는 성분별 응력 부여 변형량을 산출하는 탄성 회복량 연산부와,상기 주 영향 영역의 응력 분포를 부여한 경우의 영역별 응력 부여 변형량과, 상기 성분별 응력 부여 변형량을 비교하여, 이들 차가 가장 작아지는 방향의 응력 성분을, 탄성 회복 전후의 상기 평가점의 형상 불량에 가장 관여하는 응력 성분인 주 영향 응력 성분으로 특정하는 비교 연산부를 더 구비하는 것을 특징으로 하는, 형상 불량 요인 특정 장치.
- 제5항에 있어서, 탄성 회복 전의 가공품 형상에 대해, 상기 주 영향 영역의 판 두께 방향 중앙에 작용하는 주 영향 응력 성분을, 주 영향 영역의 판 두께 방향 전역에 균등하게 분포시킨 응력 분포를 부여한 경우의, 탄성 회복 전후의 상기 평가점의 탄성 회복을 기초로 하는 변형량을 산출하는 탄성 회복량 연산부와,상기 변형량과, 상기 주 영향 영역에 주 영향 응력 성분을 부여한 경우의 성분별 응력 부여 변형량을 비교하고, 상기 주 영향 응력 성분의 판 두께 표리의 응력차가, 탄성 회복 전후의 상기 평가점의 형상 불량에 미치는 영향의 유무를 판정하는 연산 처리부를 더 구비하는 것을 특징으로 하는, 형상 불량 요인 특정 장치.
- 탄성 회복 전의 가공품 전체에 작용하는 응력 분포를 산출하는 응력 분포 연산 공정과,탄성 회복 전의 가공품 형상에 대해 상기 응력 분포를 부여한 경우의, 탄성 회복 전후에 있어서의 상기 가공품에 정해진 임의 평가점의 탄성 회복을 기초로 하는 변형량을 산출하는 탄성 회복량 연산 공정과,미리 설정된 복수의 영역으로 상기 가공품 형상을 분할하고, 탄성 회복 전의 가공품 전체에 작용하는 응력 분포를 상기 복수의 영역으로 분할하여, 탄성 회복 전의 가공품 형상에 대해 상기 영역마다, 상기 분할한 응력 분포를 부여한 경우의, 탄성 회복 전후의 상기 평가점의 탄성 회복을 기초로 하는 영역별 응력 부여 변형량을, 상기 분할한 응력 분포를 부여한 상기 각 영역에 대해 산출하는 탄성 회복량 연산 공정과,상기 변형량과 상기 각 영역의 영역별 응력 부여 변형량을 비교하여, 이들 차가 가장 작아지는 영역을, 탄성 회복 전후의 상기 평가점의 형상 불량에 가장 관여하는 응력 분포 영역인 주 영향 영역으로 특정하는 비교 연산 공정을 포함하는, 형상 불량 요인 특정 방법.
- 제7항에 있어서, 탄성 회복 전의 가공품 형상에 대해, 상기 주 영향 영역에 작용하는 응력 분포를, 직교 좌표계의 각 방향 성분으로 분해하여 부여한 경우의, 탄성 회복 전후의 상기 평가점의 탄성 회복을 기초로 하는 성분별 응력 부여 변형량을 산출하는 탄성 회복량 연산 공정과,상기 주 영향 영역의 응력 분포를 부여한 경우의 영역별 응력 부여 변형량과, 상기 성분별 응력 부여 변형량을 비교하여, 이들 차가 가장 작아지는 방향의 응력 성분을, 탄성 회복 전후의 상기 평가점의 형상 불량에 가장 관여하는 응력 성분인 주 영향 응력 성분으로 특정하는 비교 연산 공정을 더 포함하는 것을 특징으로 하는, 형상 불량 요인 특정 방법.
- 제8항에 있어서, 탄성 회복 전의 가공품 형상에 대해, 상기 주 영향 영역의 판 두께 방향 중앙에 작용하는 주 영향 응력 성분을, 주 영향 영역의 판 두께 방향 전역에 균등하게 분포시킨 응력 분포를 부여한 경우의, 탄성 회복 전후의 상기 평가점의 탄성 회복을 기초로 하는 변형량을 산출하는 탄성 회복량 연산 공정과,상기 변형량과, 상기 주 영향 영역에 주 영향 응력 성분을 부여한 경우의 성분별 응력 부여 변형량을 비교하고, 상기 주 영향 응력 성분의 판 두께 표리의 응력차가, 탄성 회복 전후의 상기 평가점의 형상 불량에 미치는 영향의 유무를 판정하는 연산 처리 공정을 더 포함하는 것을 특징으로 하는, 형상 불량 요인 특정 방법.