KR100602998B1 - That do remains of human bodies box that use charcoal and the manufacture method - Google Patents
That do remains of human bodies box that use charcoal and the manufacture method Download PDFInfo
- Publication number
- KR100602998B1 KR100602998B1 KR1020040087076A KR20040087076A KR100602998B1 KR 100602998 B1 KR100602998 B1 KR 100602998B1 KR 1020040087076 A KR1020040087076 A KR 1020040087076A KR 20040087076 A KR20040087076 A KR 20040087076A KR 100602998 B1 KR100602998 B1 KR 100602998B1
- Authority
- KR
- South Korea
- Prior art keywords
- charcoal
- molding
- drying
- thickness
- moisture
- Prior art date
Abstract
본 발명은 채취한 원목을 자연 건조하여 25∼39%의 수분을 함습하도록 한 후 일정한 크기와 두께를 갖는 판넬형태로 성형물을 제조하는 성형물 제조과정(20)과; 일정한 크기와 두께를 갖는 판넬형태로 제조된 성형물을 자연건조에 의해 20∼25%의 수분이 함유되도록 건조하는 성형물 자연건조과정(30)과; 성형물을 건조할 로에 공급한 후 진공상태에서 120∼180℃의 온도로 15∼30시간동안 건조과정을 수행한 후, 200∼280℃의 온도에서 4시간 정도 건조과정을 수행하여 유기물에 포함된 수분이 모두 제거되도록 하는 진공 강제 건조과정(40)과; 250∼800℃까지 6∼10시간 동안 가열하여 유기물이 완전히 배출되도록 하는 추가 건조과정(50)과; 온도를 800∼1250℃까지 상승시켜 숯으로 성형된 상태에서 유기물 및 유리수분이 완전하게 제거되는 소성과정(60)과; 숯으로 제조된 성형물을 로에서 꺼내어 유골함(100)의 내부에 설치하거나 성형물이 유골함(100)으로 제조되도록 하는 두께와 크기로 숯 성형물을 가공하는 숯 성형물 가공과정(70)과; 몸체(110)의 내부에 내부 숯함(130)과 내부 숯덮개(140)를 성형하여 유골함(100)을 완성시키는 숯 성형물 조립과정(80)을 통하여 성형됨을 특징으로 하는 것이다.The present invention is a molded article manufacturing process for producing a molded article in the form of a panel having a predetermined size and thickness after drying the collected solid wood to moisten 25 to 39% moisture; A molding natural drying process 30 for drying a molded article manufactured in a panel form having a predetermined size and thickness so as to contain 20 to 25% of moisture by natural drying; After supplying the molded product to the furnace to be dried, the drying process for 15-30 hours at a temperature of 120 ~ 180 ℃ in a vacuum state, followed by a drying process for about 4 hours at a temperature of 200 ~ 280 ℃ to moisture contained in the organic material A vacuum forced drying process 40 for removing all of them; An additional drying process (50) for heating for 6 to 10 hours to 250 to 800 ℃ to completely discharge the organic matter; A calcination process 60 in which the organic material and the free moisture are completely removed in a state of forming a charcoal by raising the temperature to 800 to 1250 ° C .; Charcoal molding processing process 70 for removing the molding made of charcoal from the furnace to install the interior of the ash box 100 or to process the charcoal molding to a thickness and size such that the molding is made into the ash box 100; It is characterized in that it is molded through the process of assembling the charcoal molding 80 to complete the ash box 100 by molding the inner charcoal 130 and the inner charcoal 140 in the interior of the body 110.
유골함, 숯Ashes, charcoal
Description
도 1 은 본 발명의 바람직한 실시예를 나타낸 제조과정도1 is a manufacturing process showing a preferred embodiment of the present invention
도 2 는 본 발명의 실시예를 나타낸 외형 사시도2 is a perspective view showing an embodiment of the present invention
도 3 은 본 발명의 유골함에 대한 분리 사시도3 is an exploded perspective view of the ashes of the present invention;
도 4 는 본 발명의 유골함에 대한 단면도4 is a cross-sectional view of the ashes of the present invention.
도 5 는 본 발명의 유골함에 대한 요부 확대 단면도5 is an enlarged cross-sectional view showing main parts of the ashes of the present invention;
도 6 은 본 발명의 다른 실시예를 나타낸 단면도6 is a cross-sectional view showing another embodiment of the present invention.
도 7 은 본 발명의 또다른 실시예를 나타낸 단면도Figure 7 is a cross-sectional view showing another embodiment of the present invention
[도면의 주요 부분에 대한 부호의 설명][Description of Symbols for Main Parts of Drawing]
20 : 성형물 제조과정 30 : 자연 건조과정20: molding process 30: natural drying process
40 : 진공 강제 건조과정 50 : 진공 후 건조과정40: forced vacuum drying process 50: drying process after vacuum
60 : 소성과정 70 : 숯 성형물 가공과정 60: firing process 70: charcoal molding process
80 : 숯 성형물 조립과정 100 : 유골함80: charcoal molding assembly process 100: ashes
110 : 몸체 120 : 덮개110: body 120: cover
130 : 내부 숯함 131 : 공간130: inner charcoal 131: space
140 : 내부 숯덮개 141 : 턱140: inner charcoal cover 141: jaw
150 : 외부 숯함 160 : 외부 숯덮개150: outer charcoal 160: outer charcoal cover
170 : 숯함체 180 : 숯덮개170: charcoal container 180: charcoal cover
본 발명은 원목을 판넬형으로 가공한 후 숯으로 가공하여 유골함으로 사용할 수 있도록 하는 것으로,The present invention is to be able to be used as ashes by processing the wood into a panel-shaped charcoal,
더욱 상세하게는 원목을 가공한 후 가열방법에 의하여 숯으로 제조하되, 숯의 효능을 그대로 제공할 수 있도록 하며 강도가 유지되도록 제조하는 숯 성형물을 이용한 유골함 및 그 제조방법 에 관한 것이다.More specifically, to process the wood and to produce a charcoal by the heating method, but to provide the efficacy of the charcoal as it relates to the ashes using the charcoal molded to be manufactured to maintain the strength and its manufacturing method.
숯의 효능Benefits of Charcoal
종래 숯을 이용한 성형물 또는 성형체를 제조하는 방법에 대하여는 대한민국 특허 공개번호 제2003-68097호(2003. 08. 19. 공개)와 특허 공개번호 제2003-58981호(2003. 07. 07. 공개)가 있다.Regarding a method of manufacturing a molded article or a molded article using a conventional charcoal, Korean Patent Publication No. 2003-68097 (published Aug. 19, 2003) and Patent Publication No. 2003-58981 (published Jul. 07, 2003) have.
특허 공개번호 제2003-68097호는 주재료를 숯 분말로 구성하고 그 숯 분말에 각종 불순물을 투입한 상태에서 열건조, 표면연마, 냉각등의 별도 처리를 행하여 숯 자체의 기능과 더불어 강도 증가, 무흡습성, 표면 탈색방지의 기능을 갖도록 하 였다.Patent Publication No. 2003-68097 is composed of charcoal powder as the main material and heat treatment, surface polishing, cooling, etc., with the various impurities added to the charcoal powder to perform separate treatment such as charcoal itself to increase its strength, Hygroscopicity and surface discoloration prevention function.
특허 공개번호 제2003-58981호는 미세분말상의 숯, 휘발분, 회분 및 목초액을 일정비율로 혼합하여 일정형상으로 성형한 후 가열과 재가열 및 미세분말상의 숯과 테프론 불소수지액의 혼합물에 의한 코팅층을 형성하여 조리물이 들러붙거나 타는 것을 방지할 수 있도록 하는 탄소성형체의 제조방법이 제안된 바 있다.Patent Publication No. 2003-58981 discloses a coating layer formed by mixing a fine powder of charcoal, volatile powder, ash and wood vinegar at a predetermined ratio to form a certain shape and then heating and reheating the mixture of a fine powder of charcoal and Teflon fluorine resin solution. There has been proposed a method for producing a carbon molded body that can be formed to prevent the food from sticking or burning.
그러나 이러한 종래의 성형물 또는 성형체의 제조방법은 나무를 이용하여 숯을 만든 후 숯을 분말상태로 제조하여 다른 불순물을 혼합하여 얻어지는 것이므로 숯의 고유한 기능을 제공할 수 없었던 것이다.However, the conventional method of manufacturing a molded article or molded article is that the charcoal is made of wood, and then the charcoal is prepared by mixing the other impurities, so that the charcoal cannot provide a unique function of the charcoal.
종래 원목으로 이루어지는 가공품은 목기, 제기, 쌀 뒤지 등 다양한 제품이 제안되고 있으나 이를 숯으로 변환하여 사용하려면 원목으로 가공된 가공품이 숯으로 변환되는 과정에서 뒤틀리거나 갈라지는 다양한 변형에 의하여 사용이 불가능한 제품으로 변하게 된다.Conventionally, processed products made of solid wood have been proposed for various products such as wood, filed, rice backing, etc.However, in order to convert them to charcoal, processed products made of wood cannot be used due to various deformations that are distorted or cracked in the process of being converted into charcoal. Will change.
또한 변형된 제품을 재 가공하여 사용할 수 없는 것이며, 원목 가공품이 숯으로 변환된다고 하더라도 강도가 약하므로 일상 생활용품으로 사용할 수 없는 결점을 갖게 된다.In addition, the deformed products can not be reprocessed and used, even if the wood products are converted to charcoal strength is weak, so can not be used as a daily necessities.
원목 가공품은 괴목, 물푸레, 야사, 은행나무 등 다양한 나무를 이용하여 자연 건조한 후 원목을 회전시키면서 칼날을 이용하여 목기나 제기 등 다양한 물품을 가공한 후 건조시켜 옻칠을 통하여 사용되도록 하였으나, 원목 가공품을 원형 그대로 보존한 숯으로 제공한 예는 없었다.Solid wood processed products are naturally dried using various trees such as lumps, ash, yasa, ginkgo, and then rotated to process wood and knives and other various items such as wood and knives using blades, and then dried and used for lacquering. There was no example provided with charcoal preserved intact.
특히, 유골함은 주로 도자기로 제작되거나 통나무를 절단하여 함으로 성형하 여 사용하므로 내부에서 발생되는 습기를 제공하지 못하고 통기성이 부족하여 유충이 발생되는 결점이 있었다.In particular, the ashes are mainly made of porcelain or molded by cutting logs, so they do not provide moisture generated inside, and there is a defect in that larvae are generated due to lack of breathability.
이러한 결점을 해소하기 위한 종래의 유골함은 실용신안등록번호 제20-0277152호(2002. 5. 21. 등록, 이중 숯층을 가지는 유골함)는 나무로 제작되는 유골함의 내부에 공간을 형성하여 숯을 삽입하는 것이며, 실용신안등록번호 제20-0348458호(2004. 4. 12. 등록, 숯층을 갖는 유골함)은 유골함에 숯층을 형성하고 이 숯층이 내부와 통기되도록 하였다.Conventional ashes to solve this drawback is Utility Model Registration No. 20-0277152 (registered May 21, 2002, ashes having a double charcoal layer) inserts char by forming a space inside the ashes made of wood. Utility Model Registration No. 20-0348458 (registered on April 12, 2004, ashes having a charcoal layer) forms a charcoal layer in the ashes and allows the charcoal layer to be vented with the inside.
그러나 이러한 종래의 유골함은 성형된 숯을 분말화한 후 일정한 공간을 형성하여 이 공간에 숯 분말을 삽입하여 숯의 효능을 제공하도록 하였으므로, 숯의 기능을 제대로 수행하지 못하게 되는 결점이 있었다.However, the ashes of the related art have a drawback in that the charcoal is powdered to form a predetermined space, thereby inserting the charcoal powder into the space to provide the efficacy of the charcoal.
본 발명은 이러한 종래의 결점을 해소시키기 위하여 안출된 것으로, 자연 건조된 원목을 이용하여 성형된 판넬을 원형 그대로 보존한 숯으로 제조한 후, 후가공에 의하여 원목으로 제조된 유골함의 내부에 설치되거나, 숯으로만 유골함을 제조함을 목적으로 하는 것이다.The present invention has been devised to solve such a conventional drawback, after the panel formed by using the natural dried wood made of charcoal preserved intact as it is, installed in the ash box made of wood by post-processing, It is intended to produce ashes only with charcoal.
본 발명은 원목으로 성형된 가공품을 원형 그대로 보존하는 숯으로 제조한 후 일상 생활에서 사용할 수 있도록 강도가 부여되도록 함을 목적으로 하는 것이다.An object of the present invention is to provide a strength to be used in daily life after the manufacture of the processed material molded of solid wood as charcoal.
본 발명은 숯으로 제조된 판넬을 제공하여 숯의 기능인 원적외선 상사기능, 음이온 방출기능, 부패방지 및 탈취기능 등의 작용을 통해 보관물의 냄새를 탈취함은 물론, 유해 중금속이 흡착 제거되도록 하는 것이다.The present invention is to provide a panel made of charcoal to deodorize the smell of the storage, as well as adsorption and removal of harmful heavy metals through the action of far-infrared similarity function, anion release function, anti-corruption and deodorizing function of the charcoal.
본 발명은 채취한 원목을 자연 건조하여 25∼39%의 수분을 함습하도록 한 후 일정한 크기와 두께를 갖는 판넬형태로 성형물을 제조하는 성형물 제조과정과;The present invention is a molded article manufacturing process for producing a molded article in the form of a panel having a predetermined size and thickness after natural drying the collected wood to moisten 25 to 39% moisture;
일정한 크기와 두께를 갖는 판넬형태로 제조된 성형물을 자연건조에 의해 20∼25%의 수분이 함유되도록 건조하는 성형물 자연건조과정과;Molding natural drying process of drying a molded article manufactured in the form of a panel having a predetermined size and thickness so as to contain 20 to 25% of moisture by natural drying;
성형물을 건조할 로에 공급한 후 진공상태에서 120∼180℃의 온도로 15∼30시간동안 건조과정을 수행한 후, 200∼280℃의 온도에서 4시간 정도 건조과정을 수행하여 유기물에 포함된 수분이 모두 제거되도록 하는 진공 강제 건조과정과;After supplying the molded product to the furnace to be dried, the drying process for 15-30 hours at a temperature of 120 ~ 180 ℃ in a vacuum state, followed by a drying process for about 4 hours at a temperature of 200 ~ 280 ℃ to moisture contained in the organic material A vacuum forced drying process for removing all of them;
250∼800℃까지 6∼10시간 동안 가열하여 유기물이 완전히 배출되도록 하는 추가 건조과정과;An additional drying process in which the organic material is completely discharged by heating for 250 to 800 ° C. for 6 to 10 hours;
온도를 800∼1250℃까지 상승시켜 숯으로 성형된 상태에서 유기물 및 유리수분이 완전하게 제거되는 소성과정과;Firing the temperature to 800 to 1250 ° C. to completely remove organic matter and free moisture in a state of shaping into charcoal;
숯으로 제조된 성형물을 로에서 꺼내어 유골함의 내부에 설치하거나 성형물이 유골함으로 제조되도록 하는 두께와 크기로 숯 성형물을 가공하는 숯 성형물 가공과정과;A charcoal molding process for removing charcoal moldings from a furnace and installing the charcoal moldings to a thickness and size such that the moldings are installed in the ashes or the moldings are made into ashes;
몸체의 내부에 내부 숯함과 내부 숯덮개를 성형하여 유골함을 완성시키는 숯 성형물 조립과정을 통하여 성형됨을 특징으로 하는 것이다.
It is characterized in that it is molded through the process of assembling the charcoal molding to complete the ashes by molding the inner charcoal and the inner charcoal inside the body.
자연 건조된 통상의 원목을 이용하여 일정한 두께를 갖도록 성형물을 성형하고 자연 건조시켜 진공상태에서 원형을 보존하는 숯을 제조하는 것이다.It is to form a charcoal to have a certain thickness by using a natural natural dried wood and to naturally dry the charcoal to preserve the original shape in a vacuum.
상기 원목은 괴목(느티나무), 물푸레, 야사, 은행나무, 참나무, 소나무, 대나무 등 성형 가능한 모든 것을 사용할 수 있는 것이다.The solid wood can be used to form all that is possible, such as lumps (zelkova), ash, yasa, ginkgo, oak, pine, bamboo.
성형물을 성형하면 25∼30%의 수분을 함유하고 있으며, 비틀림, 크랙 등을 방지하기 위하여 성형물을 자연 건조시키어 20∼25%의 수분을 함유하도록 한다.When molding the molding, it contains 25 to 30% of moisture, and the molding is naturally dried to contain 20 to 25% of moisture to prevent torsion and cracking.
자연 건조된 성형물은 성형로 또는 전기로와 같은 진공이 가능한 다양한 로를 통하여 원형 그대로 보존되는 숯을 제조한다.The naturally dried moldings produce charcoal that is preserved intact through various furnaces capable of vacuum, such as molding furnaces or electric furnaces.
성형물을 가공하여 강제로 건조시키는 경우에는 건조로의 내부에 설치되는 성형물 받침대에 서로 닿지 않도록 올려놓아 가열기구와 열선을 통하여 가열하면서 내부 공간을 진공상태로 만든다.When the molding is processed and forced to dry, the inner space is made into a vacuum while being heated by means of a heating mechanism and a heating wire by placing them on the molding pedestal installed inside the drying furnace so as not to touch each other.
상온에서 시작하여 진공상태에서 120∼180 ℃의 온도로 15∼30시간동안 건조과정을 수행한다.Starting at room temperature, the drying process is performed for 15 to 30 hours at a temperature of 120 to 180 ℃ in a vacuum.
건조과정을 수행한 후 200∼280℃의 온도에서 4시간 정도 건조과정을 수행하여 유기물에 포함된 수분이 제거되므로 화학적 수분을 제외한 나머지 수분이 모두 제거되는 것이다.After the drying process is carried out for about 4 hours at a temperature of 200 ~ 280 ℃ to remove the moisture contained in the organic material is to remove all moisture except the chemical moisture.
이제는 화학적 수분만 남게 되므로 250∼800℃까지 6∼10시간 동안 가열하여 유기물을 완전 배출하여 완전건조 되도록 한다.Now only chemical moisture remains, so it is heated to 250-800 ℃ for 6-10 hours to completely discharge the organic matter and allow it to dry completely.
건조과정에서 발생되는 목초액은 진공펌프를 이용하여 외부로 배출시킨다.Wood liquor generated during the drying process is discharged to the outside using a vacuum pump.
또한 건조과정에서 목초액이 배출되면서 성형물의 체적이 20∼25%정도 감소 하게 되며 원형 그대로 보존하는 숯으로 제조된다.In addition, as the wood vinegar is discharged during the drying process, the volume of the molded product is reduced by 20 to 25%, and is made of charcoal which is preserved as it is.
이와 같이 숯으로 제조된 성형물은 원목 가공품 상태에서 성형물로 체적이 변화된 상태의 숯으로 제조된다.Thus, the molded article made of charcoal is manufactured from charcoal in a state where the volume of the molded article is changed from a solid wood processed product state.
성형물을 그대로 사용하지 않는 경우에는 온도를 계속해서 상승시켜 800∼1250℃까지 상승시키면 숯으로 성형된 상태에서 유기물 및 유리수분이 완전하게 제거되면서 소성되므로 강도가 증진되어 성형물을 완성시키게 된다.If the molded product is not used as it is, the temperature is continuously raised to 800 to 1250 ° C., and the organic matter and free moisture are completely removed while being fired while being molded into charcoal, thereby increasing the strength to complete the molded product.
소성과정에서는 원목이 비교적 강한 경우에는 1000℃이하에서도 일상생활에 사용할 수 있을 정도의 강도가 제공되는 것이나, 원목이 비교적 약한 경우에는 100℃보다 온도를 약간 상승시켜 1250℃정도 까지 온도를 상승시켜야 충분한 강도가 제공된다.In the sintering process, if the timber is relatively strong, the strength is enough to be used in everyday life even under 1000 ℃. If the timber is relatively weak, the temperature should be raised to 1250 ℃ by raising the temperature slightly above 100 ℃. Strength is provided.
이때 온도를 높일수록 강도를 향상되나, 숯의 기능이 저하되는 단점이 있으므로 유의해야 한다.At this time, as the temperature is increased, the strength is improved, but there is a disadvantage in that the function of the char is lowered.
본 발명의 유골함(100)은 내부공간(112)을 갖고 상측으로 걸림턱(111)이 형성된 몸체(110)의 상측으로 덮개(120)가 설치되는 통상의 유골함에 있어서, 몸체(110)의 내부에 바닥면과 사방의 측면을 일정한 두께의 판넬형으로 성형되는 내부 숯함(130)을 설치하고 그 숯함(130)의 상측으로 내부 숯덮개(140)가 설치되며 그 내부 숯덮개(140)에는 턱(141)이 형성되어 함과 같이 조립이 이루어지도록 하는 것이다.The
유골함(100)의 내부 숯함(130)에는 공간(131)이 형성되어 있으므로 이 공간 (131)에 유골을 보관할 수 있도록 하며, 이 공간(31)은 전체면이 숯으로 형성된 판넬이 감싸고 있게 되므로 냄새, 습기를 제거하고 유골을 천연상태로 장기간 보관할 수 있도록 하는 것이다.The
상기 내부 숯함(130)과 내부 숯덮개(140)는 원목을 가공하여 판넬 형태의 숯으로 성형된 것이며, 후가공에 의하여 성형되는 것이다.The
또한 도 7 에 도시한 바와 같이 몸체(110)와 덮개(120)를 원목으로 성형하지 않고 숯으로 성형하여 외부 숯함(150)과 외부 숯덮개(160)로 성형한 후 그 내부에는 도 2 내지 도 5 에 도시한 바와 같이 내부 숯함(130)과 외부 숯덮개(140)를 설치하여 숯이 이중으로 이루어진 유골함(100)을 제공할 수 있는 것이다.In addition, as shown in FIG. 7, the
숯이 이중으로 이루어진 유골함(100)은 일반적으로 사용할 수 있는 충분한 강도를 제공할 수 있지만, 외부 숯함(150)이 검정색이므로 외관이 미려하지 않아서 외관에 옷칠을 한 후 그림이나 다양한 모양을 새겨넣을 수 있는 것이나 이러한 기술내용은 통상적인 지식을 가진 자가 용이하게 실시할 수 있는 것이므로 본 발명의 권리범위에서 벗어날 수 없는 것이다.Charcoal box made of a
또한 도 7 에 도시한 바와 같이 숯으로 성형되는 판넬의 두께를 매우 두껍게 성형하여 외부 숯함(150)과 내부 숯함(130)의 두께에 해당되는 숯함체(170)와, 외부 숯덮개(160)와 내부 숯덮개(140)의 두께에 해당되는 숯덮개(180)를 하나로 성형하여 유골함(100)을 성형할 수 있는 것이다.In addition, as shown in Figure 7 by forming a very thick thickness of the panel formed of
본 발명의 숯을 이용한 유골함(100)은 숯의 두께가 두꺼울수록 그 작용이 향 상되므로 기존의 유골함 내주에 설치할 수 있도록 하거나 숯을 이중으로 할 수 있는 동시에 숯을 두껍게 성형하여 단일 숯의 구조로 유골함을 성형할 수 있는 것이다.The
이러한 구성으로 이루어진 본 발명의 바람직한 실시예를 첨부시킨 도면에 따라서 상세하게 설명하기로 한다.According to the accompanying drawings, preferred embodiments of the present invention having such a configuration will be described in detail.
[실시예 1]Example 1
(1) 성형물 제조과정(20)(1) Molding process (20)
채취한 원목을 자연 건조하여 25∼39%의 수분을 함습하도록 한 후 일정한 크기와 두께를 갖는 판넬형태로 성형물을 제조한다.The dried wood is naturally dried to moisten 25 to 39% of moisture, and then the molding is manufactured in the form of a panel having a certain size and thickness.
(2) 성형물 자연건조과정(30)(2) Natural drying process of moldings (30)
일정한 크기와 두께를 갖는 판넬형태로 제조된 성형물을 자연건조에 의해 20∼25%의 수분이 함유되도록 건조하는 것이다.The molded product manufactured in the form of a panel having a constant size and thickness is dried to contain 20 to 25% of moisture by natural drying.
(3) 진공 강제 건조과정(40)(3) Forced vacuum drying process (40)
성형물을 건조할 로에 공급한 후 가열기구와 열선을 이용하여 내부를 상온에서부터 가열하여 진공상태를 유지하도록 한다.After the molding is supplied to the furnace to be dried, the inside is heated from room temperature using a heating mechanism and a heating wire to maintain a vacuum state.
진공상태에서 120∼180℃의 온도로 15∼30시간동안 건조과정을 수행한 후, 200∼280℃의 온도에서 4시간 정도 건조과정을 수행하여 유기물에 포함된 수분이 모두 제거되도록 하는 것이다.After the drying process for 15 to 30 hours at a temperature of 120 ~ 180 ℃ in a vacuum state, the drying process for about 4 hours at a temperature of 200 ~ 280 ℃ to remove all the moisture contained in the organic material.
(4) 진공 후 건조과정(50)(4) Drying process after vacuum (50)
이제는 화학적 수분만 남게 되므로 250∼800℃까지 6∼10시간 동안 가열하여 유기물이 완전히 배출되도록 하는 추가 건조과정을 수행한다.Since only chemical moisture is left, it is heated for 6-10 hours to 250 ~ 800 ℃ to perform additional drying process to completely discharge organic matter.
건조과정과 추가 건조과정에서 발생되는 목초액은 진공펌프를 이용하여 밸브를 개방시켜 외부로 배출하도록 한다.Wood liquor generated during the drying process and additional drying process is discharged to the outside by opening the valve using a vacuum pump.
이때 목초액이 배출되면서 성형물의 체적이 20∼25%정도 감소하게 되며 원형이 흐트러지지 않고 그대로 보존하면서 숯으로 제조된다.At this time, the volume of the molded product is reduced by 20 to 25% as the wood vinegar is discharged and is made of charcoal while preserving the original shape as it is.
(5) 소성과정(60)(5) firing process (60)
성형물을 그대로 사용하지 않는 경우에는 온도를 계속해서 상승시켜 800∼1250℃까지 상승시키면 숯으로 성형된 상태에서 유기물 및 유리수분이 완전하게 제거되면서 소성되므로 강도가 증진되어 성형물의 강도를 향상시키게 된다.If the molded product is not used as it is, the temperature is continuously raised to 800 to 1250 ° C., and the organic matter and free moisture are completely removed while being fired while being molded into charcoal, thereby increasing the strength to improve the strength of the molded product.
(6) 숯 성형물 가공과정(70)(6) Charcoal molding process (70)
숯으로 제조된 성형물을 로에서 꺼내어 유골함(100)의 내부에 설치하거나 성형물이 유골함(100)으로 제조되도록 하는 두께와 크기로 숯 성형물을 가공하게 된다.Take out the molding made of charcoal in the furnace to install the interior of the
(7) 숯 성형물 조립과정(80)(7) Charcoal molding assembly process (80)
몸체(110)의 내부에 내부 숯함(130)과 내부 숯덮개(140)를 성형하여 유골함(100)을 완성시키게 된다.The
본 발명은 자연 건조된 원목을 이용하여 성형된 판넬을 원형 그대로 보존한 숯으로 제조한 후, 후가공에 의하여 원목으로 제조된 유골함의 내부에 설치되거나, 숯으로 만 형성된 유골함을 제공하는 것이다.The present invention is to provide a ash box made of charcoal or installed inside the ash box made of wood by the post-processing after the panel formed by using the natural dried wood as charcoal preserved as it is.
본 발명은 원목으로 성형된 가공품을 원형 그대로 보존하는 숯으로 제조한 후 일상 생활에서 사용할 수 있도록 강도가 부여되므로 장기간 사용할 수 있도록 하는 것이다.The present invention is to be used for a long time because the strength is given so that it can be used in daily life after the production of the processed material molded of solid wood as charcoal.
본 발명은 숯으로 제조된 판넬을 제공하여 숯의 기능인 원적외선 방사기능, 음이온 방출기능, 부패방지 및 탈취기능 등의 작용을 통해 보관물의 냄새를 탈취함은 물론, 유해 중금속이 흡착 제거되도록 하므로 유골이 내부에 보관되는 경우에도 습도를 유지하고 냄새를 제거하여 천연의 상태로 유골을 장기간 보존할 수 있는 것이다.
The present invention provides a panel made of charcoal to deodorize the odor of the storage through the action of far-infrared radiation function, negative ion release function, anti-corruption and deodorizing function of the charcoal, as well as to remove the harmful heavy metal adsorption ashes Even when stored inside, it can maintain the humidity and remove the odor to preserve the ashes in a natural state for a long time.
Claims (5)