KR20060037962A - A deodorizer that use charcoal and the manufacture method - Google Patents
A deodorizer that use charcoal and the manufacture method Download PDFInfo
- Publication number
- KR20060037962A KR20060037962A KR1020040087070A KR20040087070A KR20060037962A KR 20060037962 A KR20060037962 A KR 20060037962A KR 1020040087070 A KR1020040087070 A KR 1020040087070A KR 20040087070 A KR20040087070 A KR 20040087070A KR 20060037962 A KR20060037962 A KR 20060037962A
- Authority
- KR
- South Korea
- Prior art keywords
- charcoal
- deodorant
- molding
- drying
- molded
- Prior art date
Abstract
본 발명은 원목을 이용하여 계란 형태의 성형물을 가공한 후 숯으로 성형하여 탈취제로 사용할 수 있도록 하는 것으로,The present invention is to be used as a deodorant by processing the molded article in the form of eggs using wood to form a charcoal,
더욱 상세하게는 원목을 가공한 후 가열방법에 의하여 숯으로 제조하되, 숯의 효능을 그대로 제공할 수 있도록 하며 강도가 유지되도록 제조하는 숯 성형물을 이용한 탈취제 및 그 제조방법 에 관한 것이다.More specifically, it relates to a deodorant and a method for manufacturing the same using a charcoal molded product which is manufactured to be processed to charcoal by heating and then to provide the efficacy of the charcoal as it is.
이러한 본 발명은 원목으로 성형된 성형물로부터 체적이 20∼25%정도 감소하게 되며 원형이 흐트러지지 않고 그대로 보존하면서 일체형의 숯으로 탈취제(10)가 성형됨을 특징으로 하는 것이다.The present invention is characterized in that the volume is reduced by 20 to 25% from the molding formed from solid wood, and the deodorant 10 is molded into an integral charcoal while being preserved as it is without disturbing the original shape.
탈취제, 숯, 장신구Deodorant, Charcoal, Ornaments
Description
도 1 은 본 발명의 바람직한 실시예를 나타낸 제조과정도1 is a manufacturing process showing a preferred embodiment of the present invention
도 2 는 본 발명의 실시예를 나타낸 외형 사시도2 is a perspective view showing an embodiment of the present invention
도 3 은 본 발명의 탈취제에 대한 단면도3 is a cross-sectional view of the deodorant of the present invention
도 4 는 본 발명을 장신구로 사용하는 상태의 예시도Figure 4 is an illustration of a state using the present invention as ornaments
[도면의 주요 부분에 대한 부호의 설명][Description of Symbols for Main Parts of Drawing]
1 : 성형물 제조과정 2 : 자연 건조과정1: molding process 2: natural drying process
3 : 진공 강제 건조과정 4 : 진공 후 건조과정3: vacuum forced drying process 4: vacuum and drying process
5 : 소성과정 6 : 숯 성형물 가공과정5: firing process 6: charcoal molding process
10 : 탈취제 11 : 장신구10: deodorant 11: jewelry
12 : 고정스프링 13 : 받침대12: fixed spring 13: stand
14 : 접착제14: adhesive
본 발명은 원목을 이용하여 계란 형태의 성형물을 가공한 후 숯으로 성형하여 탈취제로 사용할 수 있도록 하는 것으로,The present invention is to be used as a deodorant by processing the molded article in the form of eggs using wood to form a charcoal,
더욱 상세하게는 원목을 가공한 후 가열방법에 의하여 숯으로 제조하되, 숯의 효능을 그대로 제공할 수 있도록 하며 강도가 유지되도록 제조하는 숯 성형물을 이용한 탈취제 및 그 제조방법 에 관한 것이다.More specifically, it relates to a deodorant and a method for manufacturing the same using a charcoal molded product which is manufactured to be processed to charcoal by heating and then to provide the efficacy of the charcoal as it is.
숯의 효능Benefits of Charcoal
종래 숯을 이용한 성형물 또는 성형체를 제조하는 방법에 대하여는 대한민국 특허 공개번호 제2003-68097호(2003. 08. 19. 공개)와 특허 공개번호 제2003-58981호(2003. 07. 07. 공개)가 있다.Regarding a method of manufacturing a molded article or a molded article using a conventional charcoal, Korean Patent Publication No. 2003-68097 (published Aug. 19, 2003) and Patent Publication No. 2003-58981 (published Jul. 07, 2003) have.
특허 공개번호 제2003-68097호는 주재료를 숯 분말로 구성하고 그 숯 분말에 각종 불순물을 투입한 상태에서 열건조, 표면연마, 냉각등의 별도 처리를 행하여 숯 자체의 기능과 더불어 강도 증가, 무흡습성, 표면 탈색방지의 기능을 갖도록 하였다.Patent Publication No. 2003-68097 is composed of charcoal powder as the main material and heat treatment, surface polishing, cooling, etc., with the various impurities added to the charcoal powder to perform separate treatment such as charcoal itself to increase its strength, Hygroscopicity and surface discoloration prevention function.
특허 공개번호 제2003-58981호는 미세분말상의 숯, 휘발분, 회분 및 목초액을 일정비율로 혼합하여 일정형상으로 성형한 후 가열과 재가열 및 미세분말상의 숯과 테프론 불소수지액의 혼합물에 의한 코팅층을 형성하여 조리물이 들러붙거나 타는 것을 방지할 수 있도록 하는 탄소성형체의 제조방법이 제안된 바 있다.Patent Publication No. 2003-58981 discloses a coating layer formed by mixing a fine powder of charcoal, volatile powder, ash and wood vinegar at a predetermined ratio to form a certain shape and then heating and reheating the mixture of a fine powder of charcoal and Teflon fluorine resin solution. There has been proposed a method for producing a carbon molded body that can be formed to prevent the food from sticking or burning.
그러나 이러한 종래의 성형물 또는 성형체의 제조방법은 나무를 이용하여 숯 을 만든 후 숯을 분말상태로 제조하여 다른 불순물을 혼합하여 얻어지는 것이므로 숯의 고유한 기능을 제공할 수 없었던 것이다.However, the conventional method of manufacturing a molded article or molded article was made by using charcoal to make charcoal, and then the charcoal was prepared by mixing different impurities, so it could not provide a unique function of charcoal.
종래 원목으로 이루어지는 가공품은 목기, 제기, 쌀 뒤지 등 다양한 제품이 제안되고 있으나 이를 숯으로 변환하여 사용하려면 원목으로 가공된 가공품이 숯으로 변환되는 과정에서 뒤틀리거나 갈라지는 다양한 변형에 의하여 사용이 불가능한 제품으로 변하게 된다.Conventionally, processed products made of solid wood have been proposed for various products such as wood, filed, rice backing, etc.However, in order to convert them to charcoal, processed products made of wood cannot be used due to various deformations that are distorted or cracked in the process of being converted into charcoal. Will change.
또한 변형된 제품을 재 가공하여 사용할 수 없는 것이며, 원목 가공품이 숯으로 변환된다고 하더라도 강도가 약하므로 일상 생활용품으로 사용할 수 없는 결점을 갖게 된다.In addition, the deformed products can not be reprocessed and used, even if the wood products are converted to charcoal strength is weak, so can not be used as a daily necessities.
원목 가공품은 괴목, 물푸레, 야사, 은행나무 등 다양한 나무를 이용하여 자연 건조한 후 원목을 회전시키면서 칼날을 이용하여 목기나 제기 등 다양한 물품을 가공한 후 건조시켜 옻칠을 통하여 사용되도록 하였으나, 원목 가공품을 원형 그대로 보존한 숯으로 제공한 예는 없었다.Solid wood processed products are naturally dried using various trees such as lumps, ash, yasa, ginkgo, and then rotated to process wood and knives and other various items such as wood and knives using blades, and then dried and used for lacquering. There was no example provided with charcoal preserved intact.
특히, 탈취제는 계란의 크기보다 약간 작게 성형되며 향기를 제공하거나 탈취기능을 제공하는 원목을 그대로 가공하여 냉장고속에 넣거나 쌀속에 넣어 사용하게 되며, 장식용 또는 탈취용으로 다양하게 사용된다.In particular, the deodorant is molded to be slightly smaller than the size of the egg and the fragrance or wood to provide a deodorizing function is processed as it is used in the refrigerator or put in the rice, it is used in various ways for decoration or deodorization.
그러나 종래의 탈취제는 원목을 그대로 사용하는 것이므로 시간이 경과되면 재사용 할 수 없으며, 그 기능과 효과가 쉽게 상실되는 결점이 있었다.However, the conventional deodorant is to use the solid wood as it is, can not be reused over time, the function and effect was easily lost.
본 발명은 이러한 종래의 결점을 해소시키기 위하여 안출된 것으로, 자연 건조된 원목을 이용하여 숯 성형물을 성형하여 원형 그대로 보존한 숯으로 제조한 후, 후가공에 의하여 탈취제를 제조함을 목적으로 하는 것이다. The present invention has been made in order to solve the above-mentioned drawbacks, it is intended to produce a deodorant by post-processing after the charcoal molded by using a natural dried wood to form a charcoal preserved as it is.
본 발명은 원목으로 성형된 성형물을 원형 그대로 보존하는 숯으로 제조한 후 일상 생활에서 사용할 수 있도록 강도가 부여되도록 함을 목적으로 하는 것이다.The present invention is intended to provide strength to be used in everyday life after the molded product molded from solid wood as charcoal to preserve as it is.
본 발명은 숯으로 제조된 탈취제가 숯의 기능인 원적외선 방사기능, 음이온 방출기능, 부패방지 및 탈취기능 등의 작용을 통해 보관물의 냄새를 탈취함은 물론, 유해 중금속이 흡착 제거되도록 하는 것이다.The present invention is to deodorize the odors of the storage, as well as to remove the harmful heavy metal through the action of the deodorant made of charcoal, such as far infrared radiation function, anion release function, anti-corruption and deodorizing function of the charcoal.
본 발명은 원목으로 성형된 성형물로부터 체적이 20∼25%정도 감소하게 되며 원형이 흐트러지지 않고 그대로 보존하면서 일체형의 숯으로 탈취제가 성형됨을 특징으로 하는 것이다.
The present invention is characterized in that the volume is reduced by 20 to 25% from the molding formed from solid wood, and the deodorant is molded into an integral charcoal while being preserved as it is without disturbing the original shape.
자연 건조된 통상의 원목을 이용하여 일정한 크기를 갖도록 성형물을 성형하고 자연 건조시켜 진공상태에서 원형을 보존하는 숯을 제조하는 것이다.It is to produce a char to preserve the original shape in a vacuum by molding the molded article to have a constant size using natural solid wood naturally dried.
상기 원목은 괴목(느티나무), 물푸레, 야사, 은행나무, 참나무, 소나무, 대나무 등 성형 가능한 모든 것을 사용할 수 있는 것이다.The solid wood can be used to form all that is possible, such as lumps (zelkova), ash, yasa, ginkgo, oak, pine, bamboo.
성형물을 성형하면 25∼30%의 수분을 함유하고 있으며, 비틀림, 크랙 등을 방지하기 위하여 성형물을 자연 건조시키어 20∼25%의 수분을 함유하도록 한다.When molding the molding, it contains 25 to 30% of moisture, and the molding is naturally dried to contain 20 to 25% of moisture to prevent torsion and cracking.
자연 건조된 성형물은 성형로 또는 전기로와 같은 진공이 가능한 다양한 로를 통하여 원형 그대로 보존되는 숯을 제조한다.The naturally dried moldings produce charcoal that is preserved intact through various furnaces capable of vacuum, such as molding furnaces or electric furnaces.
성형물을 가공하여 강제로 건조시키는 경우에는 건조로의 내부에 설치되는 성형물 받침대에 서로 닿지 않도록 올려놓아 가열기구와 열선을 통하여 가열하면서 내부 공간을 진공상태로 만든다.When the molding is processed and forced to dry, the inner space is made into a vacuum while being heated by means of a heating mechanism and a heating wire by placing them on the molding pedestal installed inside the drying furnace so as not to touch each other.
상온에서 시작하여 진공상태에서 120∼180 ℃의 온도로 15∼30시간동안 건조과정을 수행한다.Starting at room temperature, the drying process is performed for 15 to 30 hours at a temperature of 120 to 180 ℃ in a vacuum.
건조과정을 수행한 후 200∼280℃의 온도에서 4시간 정도 건조과정을 수행하여 유기물에 포함된 수분이 제거되므로 화학적 수분을 제외한 나머지 수분이 모두 제거되는 것이다.After the drying process is carried out for about 4 hours at a temperature of 200 ~ 280 ℃ to remove the moisture contained in the organic material is to remove all moisture except the chemical moisture.
이제는 화학적 수분만 남게 되므로 250∼800℃까지 6∼10시간 동안 가열하여 유기물을 완전 배출하여 완전건조 되도록 한다.Now only chemical moisture remains, so it is heated to 250-800 ℃ for 6-10 hours to completely discharge the organic matter and allow it to dry completely.
건조과정에서 발생되는 목초액은 진공펌프를 이용하여 외부로 배출시킨다.Wood liquor generated during the drying process is discharged to the outside using a vacuum pump.
또한 건조과정에서 목초액이 배출되면서 성형물의 체적이 20∼25%정도 감소하게 되며 원형 그대로 보존하는 숯으로 제조된다.In addition, as the wood vinegar is discharged during the drying process, the volume of the molded product is reduced by 20 to 25%, and is made of charcoal which is preserved as it is.
이와 같이 숯으로 제조된 성형물은 원목 가공품 상태에서 성형물로 체적이 변화된 상태의 숯으로 제조된다.Thus, the molded article made of charcoal is manufactured from charcoal in a state where the volume of the molded article is changed from a solid wood processed product state.
성형물을 그대로 사용하지 않는 경우에는 온도를 계속해서 상승시켜 800∼1250℃까지 상승시키면 숯으로 성형된 상태에서 유기물 및 유리수분이 완전하게 제거되면서 소성되므로 강도가 증진되어 성형물을 완성시키게 된다.If the molded product is not used as it is, the temperature is continuously raised to 800 to 1250 ° C., and the organic matter and free moisture are completely removed while being fired while being molded into charcoal, thereby increasing the strength to complete the molded product.
소성과정에서는 원목이 비교적 강한 경우에는 1000℃이하에서도 일상생활에 사용할 수 있을 정도의 강도가 제공되는 것이나, 원목이 비교적 약한 경우에는 100℃보다 온도를 약간 상승시켜 1250℃정도 까지 온도를 상승시켜야 충분한 강도가 제공된다.In the sintering process, if the timber is relatively strong, the strength is enough to be used in everyday life even under 1000 ℃. If the timber is relatively weak, the temperature should be raised to 1250 ℃ by raising the temperature slightly above 100 ℃. Strength is provided.
이때 온도를 높일수록 강도를 향상되나, 숯의 기능이 저하되는 단점이 있으므로 유의해야 한다.At this time, as the temperature is increased, the strength is improved, but there is a disadvantage in that the function of the char is lowered.
본 발명의 탈취제(10)는 도 2 와 도 3 에 도시한 바와 같이 계란 형태로 성형되거나 원형으로 성형되는 것이다.
상기 탈취제(10)는 원목을 이용하여 미리 가공한 상태를 숯으로 성형하여 마감 가공하는 공정만으로 완성되는 것이며, 도 4 에 도시한 바와 같이 탈취제(10)의 하측에서 고정스프링(12)에 고정되도록 하고 그 하측으로 받침대(13)를 형성하여 접착제(14)로 원하는 곳에 장신구(11)로 고정되도록 하는 것이다.The deodorant (10) is to be completed only by the process of forming the finish processing by shaping charcoal in advance using a solid wood, as shown in Figure 4 to be fixed to the fixed
또한 탈취제(10)는 다수개를 한 묶음으로 하여 냉장고의 내부에 보관하거나 쌀 속에 넣어 놓으면, 주변의 습기와 냄새를 제거하는 기능을 제공하는 것이다.In addition, the deodorant (10) is to provide a function to remove the moisture and odor of the surrounding when stored in the inside of the refrigerator or put in a bundle of a plurality in a bundle.
그러나 탈취제(10)는 장시간 사용하는 경우에는 유해성분이 스며들어 쌓이게 되므로 기능성이 저하되거나 상실된다.However, when the
유해성분이 스며든 상태의 경우에는 100℃로 끓는 물에 농축 목초액을 2방울 공급하여 희석시킨 후 탈취제(10)를 넣어 5∼30분 정도 경과시키면 숯으로 이루어진 탈취제(10)에 스며든 유해 성분이 모두 외부로 배출되므로 건조시켜 재사용할 수 있는 것이다.When the harmful ingredients are infiltrated, supply 2 drops of concentrated wood vinegar to boiling water at 100 ℃, dilute it, and then add about 5 ~ 30 minutes to the deodorant (10). Since all are discharged to the outside, it can be dried and reused.
이러한 구성으로 이루어진 본 발명의 바람직한 실시예를 첨부시킨 도면에 따라서 상세하게 설명하기로 한다.According to the accompanying drawings, preferred embodiments of the present invention having such a configuration will be described in detail.
[실시예 1]Example 1
(1) 성형물 제조과정(1) Molding process
채취한 원목을 자연 건조하여 25∼39%의 수분을 함습하도록 한 후 일정한 크기를 갖는 계란 형태의 탈취제(10)와 같이 성형물을 제조(1)한다.The dried wood is naturally dried to moisten 25 to 39% of moisture, and then a molded product is prepared (1), such as an
(2) 성형물 자연건조과정(2) Natural drying process of moldings
일정한 크기로 제조된 성형물을 각각 자연건조에 의해 20∼25%의 수분이 함유되도록 건조(2)하는 것이다.The molded product manufactured to a constant size is dried (2) so as to contain 20 to 25% of water by natural drying, respectively.
(3) 진공 강제 건조과정(3) vacuum forced drying process
성형물을 건조할 로에 공급한 후 가열기구와 열선을 이용하여 내부를 상온에서부터 가열하여 진공상태를 유지하도록 한다.After the molding is supplied to the furnace to be dried, the inside is heated from room temperature using a heating mechanism and a heating wire to maintain a vacuum state.
진공상태에서 120∼180℃의 온도로 15∼30시간동안 건조과정을 수행한 후, 200∼280℃의 온도에서 4시간 정도 건조과정을 수행하여 유기물에 포함된 수분이 모두 제거(3)되도록 하는 것이다.After the drying process for 15-30 hours at a temperature of 120 ~ 180 ℃ in a vacuum state, the drying process for 4 hours at a temperature of 200 ~ 280 ℃ to remove all the moisture contained in the organic matter (3) will be.
(4) 진공 후 건조과정(4) Drying process after vacuum
이제는 화학적 수분만 남게 되므로 250∼800℃까지 6∼10시간 동안 가열하여 유기물이 완전히 배출되도록 하는 후 건조과정(4)을 수행한다.Since only chemical moisture is left now, heating is performed for 6 to 10 hours to 250 to 800 ° C. so that organic matter is completely discharged.
건조과정과 추가 건조과정에서 발생되는 목초액은 진공펌프를 이용하여 밸브를 개방시켜 외부로 배출하도록 한다.Wood liquor generated during the drying process and additional drying process is discharged to the outside by opening the valve using a vacuum pump.
이때 목초액이 배출되면서 성형물의 체적이 20∼25%정도 감소하게 되며 원형이 흐트러지지 않고 그대로 보존하면서 숯으로 제조된다.At this time, the volume of the molded product is reduced by 20 to 25% as the wood vinegar is discharged and is made of charcoal while preserving the original shape as it is.
(5) 소성과정(5) firing process
성형물을 그대로 사용하지 않는 경우에는 온도를 계속해서 상승시켜 800∼1250℃까지 상승시키면 숯으로 성형된 상태에서 유기물 및 유리수분이 완전하게 제거되면서 소성(5)되므로 강도가 증진되어 성형물의 강도를 향상시키게 된다.If the molded product is not used as it is, the temperature is continuously raised and raised to 800 to 1250 ° C. Thus, the organic matter and free moisture are completely removed and calcined (5) in the form of charcoal. Let's go.
(6) 숯 성형물 가공과정(6) Charcoal molding process
숯 성형물의 체적이 감소된 상태에서 원형이 보존되어 있으므로 외부를 센딩처리하는 가공과정(6)을 통하여 탈취제(10)를 완성시키게 된다.Since the original shape is preserved in a state in which the volume of the char molding is reduced, the
본 발명은 자연 건조된 원목을 이용하여 숯 성형물을 성형하여 원형 그대로 보존한 숯으로 제조한 후, 후가공에 의하여 탈취제를 제공하는 것이다.The present invention is to provide a deodorant by post-processing after the charcoal molded by using the natural dried wood to form a charcoal preserved as it is.
본 발명은 원목으로 성형된 성형물을 원형 그대로 보존하는 숯으로 제조한 후 일상 생활에서 사용할 수 있도록 강도가 부여되도록 하는 것이다.The present invention is to give strength to be used in everyday life after the molded product molded from solid wood charcoal to preserve as it is.
본 발명은 숯으로 제조된 탈취제가 숯의 기능인 원적외선 방사기능, 음이온 방출기능, 부패방지 및 탈취기능 등의 작용을 통해 보관물의 냄새를 탈취함은 물론, 유해 중금속이 흡착 제거되도록 하는 것이다. The present invention is to deodorize the odors of the storage, as well as to remove the harmful heavy metal through the action of the deodorant made of charcoal, such as far infrared radiation function, anion release function, anti-corruption and deodorizing function of the charcoal.
본 발명은 탈취제가 성형물로부터 체적이 20∼25%정도 감소하게 되며 원형이 흐트러지지 않고 그대로 보존하면서 일체형의 숯으로 성형됨을 특징으로 하는 것이다.The present invention is characterized in that the deodorizing agent is reduced by 20 to 25% in volume from the molded product and is molded into an integral charcoal while being preserved as it is without disturbing the original shape.
본 발명은 탈취제를 장기간 사용하게 되면 유해성분이 숯에 흡착되어 있으므로 끓는물에 농축 목초액을 2방울 공급한 후 숯 걸름 용기를 넣어 숯에 흡착된 유해물질을 모두 배출시켜 재사용할 수 있도록 하는 것이다.According to the present invention, when the deodorant is used for a long time, the harmful ingredients are adsorbed on the charcoal, so that two drops of concentrated wood vinegar is supplied to boiling water, and then the charcoal filtering container is discharged to reuse all the harmful substances adsorbed on the charcoal.
Claims (4)