JPWO2022259838A5 - - Google Patents
Download PDFInfo
- Publication number
- JPWO2022259838A5 JPWO2022259838A5 JP2022551344A JP2022551344A JPWO2022259838A5 JP WO2022259838 A5 JPWO2022259838 A5 JP WO2022259838A5 JP 2022551344 A JP2022551344 A JP 2022551344A JP 2022551344 A JP2022551344 A JP 2022551344A JP WO2022259838 A5 JPWO2022259838 A5 JP WO2022259838A5
- Authority
- JP
- Japan
- Prior art keywords
- less
- steel sheet
- temperature
- seconds
- strength steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Links
- 229910000831 Steel Inorganic materials 0.000 claims 13
- 239000010959 steel Substances 0.000 claims 13
- 238000004519 manufacturing process Methods 0.000 claims 5
- 238000000137 annealing Methods 0.000 claims 3
- 238000007747 plating Methods 0.000 claims 3
- 229910001566 austenite Inorganic materials 0.000 claims 2
- 238000001816 cooling Methods 0.000 claims 2
- 238000000034 method Methods 0.000 claims 2
- 239000000203 mixture Substances 0.000 claims 2
- 230000000717 retained effect Effects 0.000 claims 2
- 239000002344 surface layer Substances 0.000 claims 2
- 238000005496 tempering Methods 0.000 claims 2
- 229910000859 α-Fe Inorganic materials 0.000 claims 2
- OKTJSMMVPCPJKN-UHFFFAOYSA-N Carbon Chemical compound [C] OKTJSMMVPCPJKN-UHFFFAOYSA-N 0.000 claims 1
- 229910052799 carbon Inorganic materials 0.000 claims 1
- 239000010960 cold rolled steel Substances 0.000 claims 1
- 238000005097 cold rolling Methods 0.000 claims 1
- 238000005098 hot rolling Methods 0.000 claims 1
- 239000012535 impurity Substances 0.000 claims 1
- 239000010410 layer Substances 0.000 claims 1
- 229910000734 martensite Inorganic materials 0.000 claims 1
- 238000005554 pickling Methods 0.000 claims 1
- 238000003303 reheating Methods 0.000 claims 1
Claims (7)
- 質量％で、
Ｃ：０．１５％以上、０．４５％以下、
Ｓｉ：０．５０％以上、２．００％以下、
Ｍｎ：１．５０％以上、３．５０％以下、
Ｐ：０．１００％以下、
Ｓ：０．０２００％以下、
Ａｌ：０．０１０％以上、１．０００％以下、
Ｎ：０．０１００％以下、
Ｈ：０．００２０％以下を含有し、
残部がＦｅおよび不可避的不純物からなる成分組成と、
焼戻マルテンサイトが面積分率で８０％以上、
残留オーステナイトが体積分率で５％以上１５％以下、
フェライトおよびベイニティックフェライトの合計が面積分率で１０％以下であり、
残留オーステナイト中の炭素濃度が０．５０％以上であり、
以下の（１）および（２）で規定する式を満たす組織を有する高強度鋼板。
ＫＡＭ（Ｓ）／ＫＡＭ（Ｃ） ＜ １．００ ・・・・・（１）
ここで、ＫＡＭ（Ｓ）は鋼板表層部のＫＡＭ（Ｋｅｒｎｅｌ Ａｖｅｒａｇｅ Ｍｉｓｏｒｉｅｎｔａｔｉｏｎ）値、ＫＡＭ（Ｃ）は鋼板中心部のＫＡＭ値を示す。
Ｈｖ（Ｑ）－ Ｈｖ（Ｓ） ≧ ８ ・・・・・（２）
ここで、Ｈｖ（Ｑ）は板厚１／４部の硬度、Ｈｖ（Ｓ）は鋼板表層部の硬度を示す。 - 成分組成として、さらに、質量％で、
Ｔｉ：０．１００％以下、
Ｂ：０．０１００％以下、
Ｎｂ：０．１００％以下、
Ｃｕ：１．００％以下、
Ｃｒ：１．００％以下、
Ｖ：０．１００％以下、
Ｍｏ：０．５００％以下、
Ｎｉ：０．５０％以下、
Ｓｂ：０．２００％以下、
Ｓｎ：０．２００％以下、
Ａｓ：０．１００％以下、
Ｔａ：０．１００％以下、
Ｃａ：０．０２００％以下、
Ｍｇ：０．０２００％以下、
Ｚｎ：０．０２０％以下、
Ｃｏ：０．０２０％以下、
Ｚｒ：０．０２０％以下、
ＲＥＭ：０．０２００％以下のうちから選ばれる１種または２種以上の元素を含有する請求項１に記載の高強度鋼板。 - 鋼板表面にめっき層を有する請求項１または２に記載の高強度鋼板。
- 請求項１または２に記載の高強度鋼板の製造方法であって、
鋼スラブに熱間圧延、酸洗および冷間圧延を施し作製した冷延鋼板を、
温度Ｔ１が８５０℃以上１０００℃以下であり、
前記Ｔ１での保持時間ｔ１が１０秒以上１０００秒以下である条件で焼鈍した後、
１００℃以上３００℃以下の温度Ｔ２まで冷却した後、
温度Ｔ３がＴ２以上４５０℃以下であり、
温度Ｔ３での保持時間ｔ３が１．０秒以上１０００．０秒以下である条件で再加熱処理を行い、
１００℃以下まで冷却し、
１００℃となった時点から経過時間ｔ４が１０００秒以下のうちに加工を開始し、
前記加工は加工開始温度Ｔ４が８０℃以下であり、
前記加工は相当塑性歪が０．１０％以上５．００％以下である条件で加工を施し、
温度Ｔ５が１００℃以上４００℃以下であり、
前記温度Ｔ５での保持時間ｔ５が１．０秒以上１０００．０秒以下である条件で焼戻し、
前記温度Ｔ５から８０℃までの冷却速度θ１が１００℃／秒以下の条件で冷却する
高強度鋼板の製造方法。 - 前記焼戻前の加工工程にて２回以上に分けて加工による歪付与を実施し、各加工の前記相当塑性歪の合計が０．１０％以上である条件で加工が施される請求項４に記載の高強度鋼板の製造方法。
- 前記焼鈍から加工までの間に、めっき処理を施す請求項４に記載の高強度鋼板の製造方法。
- 前記焼鈍から加工までの間に、めっき処理を施す請求項５に記載の高強度鋼板の製造方法。