JPWO2020149321A1 - 方向性電磁鋼板の製造方法 - Google Patents

方向性電磁鋼板の製造方法 Download PDF

Info

Publication number
JPWO2020149321A1
JPWO2020149321A1 JP2020566441A JP2020566441A JPWO2020149321A1 JP WO2020149321 A1 JPWO2020149321 A1 JP WO2020149321A1 JP 2020566441 A JP2020566441 A JP 2020566441A JP 2020566441 A JP2020566441 A JP 2020566441A JP WO2020149321 A1 JPWO2020149321 A1 JP WO2020149321A1
Authority
JP
Japan
Prior art keywords
annealing
steel sheet
hot
rolled
cold
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2020566441A
Other languages
English (en)
Other versions
JP7299511B2 (ja
Inventor
真介 高谷
義行 牛神
修一 中村
俊介 奥村
翔二 長野
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nippon Steel Corp
Original Assignee
Nippon Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel Corp filed Critical Nippon Steel Corp
Publication of JPWO2020149321A1 publication Critical patent/JPWO2020149321A1/ja
Application granted granted Critical
Publication of JP7299511B2 publication Critical patent/JP7299511B2/ja
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

この方向性電磁鋼板の製造方法は、脱炭焼鈍工程で酸化度ＰＨ２Ｏ／ＰＨ２を制御し、焼鈍分離剤塗布工程で焼鈍分離剤のＭｇＯとＡｌ２Ｏ３との質量比率を制御し、仕上げ焼鈍工程で水素を含有する場合には酸化度を不活性ガスからなる場合には露点を制御し、絶縁被膜形成工程で焼付け温度および熱処理温度を制御する。

Description

本発明は、方向性電磁鋼板の製造方法に関する。
本願は、２０１９年１月１６日に、日本に出願された特願２０１９−００５４００号に基づき優先権を主張し、その内容をここに援用する。
方向性電磁鋼板は、主として変圧器に使用される。変圧器は据え付けられてから廃棄されるまでの長期間にわたり、連続的に励磁され、エネルギー損失を発生し続けることから、交流で磁化された際のエネルギー損失、即ち、鉄損が、変圧器の性能を決定する主要な指標となる。
方向性電磁鋼板の鉄損を低減するため、今まで、多くの手法が提案されてきた。例えば、鋼板組織に関して、ゴス方位と呼ばれる｛１１０｝＜００１＞方位への集積を高める手法、鋼板に関して、電気抵抗を高めるＳｉ等の固溶元素の含有量を高める手法、鋼板の板厚を薄くする手法等である。
また、鋼板に張力を付与することが、鉄損の低減に有効な手法であることが知られている。そのため、通常、鉄損を低下させることを目的として、方向性電磁鋼板の表面には、被膜が形成されている。この被膜は、方向性電磁鋼板に張力を付与することにより、鋼板単板としての鉄損を低下させる。この被膜はさらに、方向性電磁鋼板を積層して使用する際に、鋼板間の電気的絶縁性を確保することにより、鉄心としての鉄損を低下させる。
被膜が形成された方向性電磁鋼板としては、母鋼板の表面に、Ｍｇを含有する酸化被膜であるフォルステライト被膜が形成されて、さらに、そのフォルステライト被膜の表面上に絶縁被膜が形成されたものがある。つまり、この場合、母鋼板上の被膜は、フォルステライト被膜と、絶縁被膜とを含む。フォルステライト被膜及び絶縁被膜の各々は、絶縁性機能及び母鋼板への張力付与機能の両方の機能を担っている。
Ｍｇを含有する酸化被膜であるフォルステライト被膜は、鋼板に二次再結晶を生じさせる仕上げ焼鈍にて、マグネシア（ＭｇＯ）を主成分とする焼鈍分離剤と脱炭焼鈍時に母鋼板上に形成された酸化珪素（ＳｉＯ２）とが、９００〜１２００℃で３０時間以上施される熱処理中に反応することにより、形成される。
絶縁被膜は、仕上げ焼鈍後の母鋼板に、例えば、リン酸又はリン酸塩、コロイダルシリカ、及び、無水クロム酸又はクロム酸塩を含むコ−ティング溶液を塗布し、３００〜９５０℃で１０秒以上焼き付け乾燥することにより、形成される。
被膜が、絶縁性及び母鋼板への張力付与の機能を発揮するために、これらの被膜と母鋼板との間に高い密着性が要求される。
従来、上記密着性は、主として、母鋼板とフォルステライト被膜との界面の凹凸によるアンカー効果によって確保されてきた。しかしながら、近年、この界面の凹凸が、方向性電磁鋼板が磁化される際の磁壁移動の障害にもなるので、低鉄損化を妨げる要因にもなっていることが明らかになった。
そこで、さらに低鉄損化するために、Ｍｇを含有する酸化被膜であるフォルステライト被膜を存在させずに、上述の界面を平滑化した状態で絶縁被膜の密着性を確保する技術が、たとえば、特開昭４９−０９６９２０号公報（特許文献１）及び国際公開第２００２／０８８４０３号（特許文献２）に提案されている。
特許文献１に開示された方向性電磁鋼板の製造方法では、フォルステライト被膜を酸洗等により除去し、母鋼板表面を化学研磨又は電解研磨で平滑にする。特許文献２に開示された方向性電磁鋼板の製造方法では、仕上げ焼鈍時にアルミナ（Ａｌ２Ｏ３）を含む焼鈍分離剤を用いて、フォルステライト被膜の形成自体を抑制して、母鋼板表面を平滑化する。
しかしながら、特許文献１及び特許文献２の製造方法では、母鋼板表面に接触して（母鋼板表面上に直接）絶縁被膜を形成する場合、母鋼板表面に対して絶縁被膜が密着しにくい（十分な密着性が得られない）という問題があった。
日本国特開昭４９−０９６９２０号公報 国際公開第２００２／０８８４０３号
本発明は、上記の課題に鑑みてなされた。本発明は、フォルステライト被膜を有さず、かつ、磁気特性（特に鉄損）および被膜密着性に優れる方向性電磁鋼板の製造方法を提供することを目的とする。
本発明者らは、低鉄損化のために、フォルステライト被膜を生成させず、鋼板表面を平滑化した方向性電磁鋼板用鋼板の表面に、絶縁被膜を形成することを前提とし、鋼板と絶縁被膜との密着性（被膜密着性）を向上させる方法について検討を行った。
その結果、所定の工程を適切に組み合わせることで、フォルステライト被膜を有さず、かつ、磁気特性および被膜密着性に優れる方向性電磁鋼板を製造できることを見出した。
本発明の要旨は、次のとおりである。
（１）本発明の一態様に係る方向性電磁鋼板の製造方法は、
化学組成として、質量％で、
Ｃ：０．０３０〜０．１００％、
Ｓｉ：０．８０〜７．００％、
Ｍｎ：０．０１〜１．００％、
Ｓ及びＳｅの合計：０〜０．０６０％、
酸可溶性Ａｌ：０．０１０〜０．０６５％、
Ｎ：０．００４〜０．０１２％、
Ｃｒ：０〜０．３０％、
Ｃｕ：０〜０．４０％、
Ｐ：０〜０．５０％、
Ｓｎ：０〜０．３０％、
Ｓｂ：０〜０．３０％、
Ｎｉ：０〜１．００％、
Ｂ：０〜０．００８％、
Ｖ：０〜０．１５％、
Ｎｂ：０〜０．２０％、
Ｍｏ：０〜０．１０％、
Ｔｉ：０〜０．０１５％、
Ｂｉ：０〜０．０１０％、を含有し、
残部がＦｅおよび不純物からなる鋼片を、熱間圧延して熱延鋼板を得る熱延工程と、
前記熱延鋼板に冷間圧延を施して冷延鋼板を得る冷延工程と、
前記冷延鋼板に脱炭焼鈍を行って脱炭焼鈍板を得る脱炭焼鈍工程と、
前記脱炭焼鈍板に、Ａｌ２Ｏ３とＭｇＯとを含有する焼鈍分離剤を塗布して乾燥させる焼鈍分離剤塗布工程と、
前記焼鈍分離剤が塗布された前記脱炭焼鈍板に仕上げ焼鈍を行い、仕上げ焼鈍板を得る仕上げ焼鈍工程と、
前記仕上げ焼鈍板の表面から余剰の焼鈍分離剤を除去する焼鈍分離剤除去工程と、
前記仕上げ焼鈍板の表面に絶縁被膜を形成する絶縁被膜形成工程と、
を備え、
前記脱炭焼鈍工程では、
酸化度であるＰＨ２Ｏ／ＰＨ２が０．０１〜０．１５である雰囲気下で、焼鈍温度７５０〜９００℃で、１０〜６００秒保持を行い、
前記焼鈍分離剤塗布工程では、
前記焼鈍分離剤における、前記ＭｇＯと前記Ａｌ２Ｏ３との質量比率であるＭｇＯ／（ＭｇＯ＋Ａｌ２Ｏ３）を５〜５０％、水和水分を１．５質量％以下とし、
前記仕上げ焼鈍工程では、
雰囲気が、水素を含有する場合には、酸化度を０．０００１０〜０．２とし、水素を含有しない不活性ガスからなる場合には、露点を０℃以下とし、
前記絶縁被膜形成工程では、
リン酸塩またはコロイダルシリカを主成分とする絶縁被膜のコーティング液を塗布し、３５０〜６００℃で焼付け、８００〜１０００℃の温度で熱処理して絶縁被膜を形成する。
（２）上記（１）に記載の方向性電磁鋼板の製造方法では、前記熱延工程と前記冷延工程との間に、前記熱延鋼板を焼鈍する熱延板焼鈍工程、または酸洗を行う熱延板酸洗工程の少なくとも１つを備えてもよい。
（３）上記（１）又は（２）に記載の方向性電磁鋼板の製造方法では、前記脱炭焼鈍工程で、前記冷延鋼板を、アンモニアを含有する雰囲気中で焼鈍する窒化処理を行ってもよい。
（４）上記（１）〜（３）のいずれか１つに記載の方向性電磁鋼板の製造方法では、前記冷延工程と前記脱炭焼鈍工程との間、前記脱炭焼鈍工程と前記焼鈍分離剤塗布工程との間、前記焼鈍分離剤除去工程と前記絶縁被膜形成工程との間、または前記絶縁被膜形成工程後のいずれかに、磁区制御処理を行う磁区制御工程を備えてもよい。
（５）上記（１）〜（４）のいずれか１つに記載の方向性電磁鋼板の製造方法では、前記焼鈍分離剤除去工程で、水洗後に、体積比濃度が２０％未満の酸性溶液を用いて酸洗を行ってもよい。
（６）上記（１）〜（５）のいずれか１つに記載の方向性電磁鋼板の製造方法では、前記鋼片が、化学組成として、質量％で、
Ｃｒ：０．０２〜０．３０％、
Ｃｕ：０．０５〜０．４０％、
Ｐ：０．００５〜０．５０％、
Ｓｎ：０．０２〜０．３０％、
Ｓｂ：０．０１〜０．３０％、
Ｎｉ：０．０１〜１．００％、
Ｂ：０．０００５〜０．００８％、
Ｖ：０．００２〜０．１５％、
Ｎｂ：０．００５〜０．２０％、
Ｍｏ：０．００５〜０．１０％、
Ｔｉ：０．００２〜０．０１５％、及び
Ｂｉ：０．００１〜０．０１０％、
からなる群から選択される少なくとも１種を含有してもよい。
本発明の上記態様によれば、フォルステライト被膜を有さず、かつ、磁気特性および被膜密着性に優れる方向性電磁鋼板の製造方法を提供できる。
本発明の一実施形態に係る方向性電磁鋼板の製造方法を示すフローチャートである。
以下に、本発明の好適な実施の形態について詳細に説明する。ただ、本発明は本実施形態に開示の構成のみに制限されることなく、本発明の趣旨を逸脱しない範囲で種々の変更が可能である。また、本実施形態にて示す数値限定範囲には、下限値及び上限値がその範囲に含まれる。「超」または「未満」と示す数値は、その値が数値範囲に含まれない。各元素の含有量に関する「％」は、特に指定しない限り「質量％」を意味する。
本発明の一実施形態に係る方向性電磁鋼板の製造方法（以下「本実施形態に係る方向性電磁鋼板の製造方法」ということがある。）は、フォルステライト被膜を有さない方向性電磁鋼板の製造方法であって、以下の工程を備える。
（ｉ）所定の化学組成を有する鋼片を、熱間圧延して熱延鋼板を得る熱延工程
（ｉｉ）前記熱延鋼板を、１回または中間焼鈍を挟む２回以上の冷間圧延を施して冷延鋼板を得る冷延工程
（ｉｉｉ）前記冷延鋼板に脱炭焼鈍を行って脱炭焼鈍板を得る脱炭焼鈍工程
（ｉｖ）前記脱炭焼鈍板に、Ａｌ２Ｏ３とＭｇＯとを含有する焼鈍分離剤を塗布して乾燥させる焼鈍分離剤塗布工程
（ｖ）焼鈍分離剤が塗布された前記脱炭焼鈍板に仕上げ焼鈍を行い、仕上げ焼鈍板を得る仕上げ焼鈍工程
（ｖｉ）前記仕上げ焼鈍板の表面から余剰の焼鈍分離剤を、水洗または酸洗の一方または両方を含む方法によって除去する焼鈍分離剤除去工程
（ｖｉｉ）前記仕上げ焼鈍板の表面に絶縁被膜を形成する絶縁被膜形成工程
また、本実施形態に係る方向性電磁鋼板の製造方法は、さらに以下の工程を備えてもよい。
（Ｉ）熱延鋼板を焼鈍する熱延板焼鈍工程
（ＩＩ）熱延鋼板を酸洗する熱延板酸洗工程
（ＩＩＩ）磁区制御処理を行う磁区制御工程
本実施形態に係る方向性電磁鋼板の製造方法は、上記した工程の内、単に一つの工程を制御すればよいわけではなく、上記した各工程を複合的に且つ不可分に制御する必要がある。各工程のすべてを所定の条件で制御することで、鉄損を低下させ、かつ被膜密着性を向上させることができる。
以下、各工程について詳細に説明する。
＜熱延工程＞
熱延工程では、化学組成として、質量％で、Ｃ：０．０３０〜０．１００％、Ｓｉ：０．８０〜７．００％、Ｍｎ：０．０１〜１．００％、Ｓ＋Ｓｅの合計：０〜０．０６０％、酸可溶性Ａｌ：０．０１０〜０．０６５％、Ｎ：０．００４〜０．０１２％、Ｃｒ：０〜０．３０％、Ｃｕ：０〜０．４０％、Ｐ：０〜０．５０％、Ｓｎ：０〜０．３０％、Ｓｂ：０〜０．３０％、Ｎｉ：０〜１．００％、Ｂ：０〜０．００８％、Ｖ：０〜０．１５％、Ｎｂ：０〜０．２０％、Ｍｏ：０〜０．１０％、Ｔｉ：０〜０．０１５％、Ｂｉ：０〜０．０１０％、を含有し、残部がＦｅおよび不純物からなる鋼片を、熱間圧延して熱延鋼板を得る。本実施形態では、熱延工程後の鋼板を、熱延鋼板と呼ぶ。
熱延工程に供する鋼片（スラブ）の製造方法については限定されない。例えば所定の化学組成を有する溶鋼を溶製し、その溶鋼を用いてスラブを製造すればよい。連続鋳造法によりスラブを製造してもよく、溶鋼を用いてインゴットを製造し、インゴットを分塊圧延してスラブを製造してもよい。また、他の方法によりスラブを製造してもよい。
スラブの厚さは、特に限定されないが、たとえば、１５０〜３５０ｍｍである。スラブの厚さは好ましくは、２２０〜２８０ｍｍである。スラブとして、厚さが１０〜７０ｍｍの、いわゆる薄スラブを用いてもよい。
まず、鋼片の化学組成の限定理由について説明する。以下、化学組成に関する％は質量％を意味する。
［Ｃ：０．０３０〜０．１００％］
Ｃ（炭素）は、一次再結晶組織の制御に有効な元素であるが、磁気特性に悪影響を及ぼすので、仕上げ焼鈍前に脱炭焼鈍で除去する元素である。鋼片のＣ含有量が０．１００％を超えると、脱炭焼鈍時間が長くなり、生産性が低下する。そのため、Ｃ含有量は０．１００％以下とする。好ましくは０．０８５％以下、より好ましくは０．０７０％以下である。
Ｃ含有量は低い方が好ましいが、工業生産における生産性や製品の磁気特性を考慮した場合、Ｃ含有量の実質的な下限は０．０３０％である。
［Ｓｉ：０．８０〜７．００％］
シリコン（Ｓｉ）は、方向性電磁鋼板の電気抵抗を高めて鉄損を低下させる。Ｓｉ含有量が０．８０％未満であれば、仕上げ焼鈍時にγ変態が生じて、方向性電磁鋼板の結晶方位が損なわれてしまう。したがって、Ｓｉ含有量は０．８０％以上である。Ｓｉ含有量は好ましくは２．００％以上であり、より好ましくは２．５０％以上である。
一方、Ｓｉ含有量が７．００％を超えれば、冷間加工性が低下して、冷間圧延時に割れが発生しやすくなる。したがって、Ｓｉ含有量は７．００％以下である。Ｓｉ含有量は好ましくは４．５０％以下であり、さらに好ましくは４．００％以下である。
［Ｍｎ：０．０１〜１．００％］
マンガン（Ｍｎ）は、方向性電磁鋼板の電気抵抗を高めて鉄損を低下させる。また、Ｍｎは、Ｓ又はＳｅと結合して、ＭｎＳ、又は、ＭｎＳｅを生成し、インヒビターとして機能する。Ｍｎ含有量が０．０１〜１．００％の範囲内にある場合に、二次再結晶が安定する。したがって、Ｍｎ含有量は、０．０１〜１．００％である。Ｍｎ含有量の好ましい下限は０．０８％であり、さらに好ましくは０．０９％である。Ｍｎ含有量の好ましい上限は０．５０％であり、さらに好ましくは０．２０％である。
［Ｓ及びＳｅのいずれかまたは両方の合計：０〜０．０６０％］
Ｓ（硫黄）及びＳｅ（セレン）は、Ｍｎと結合して、インヒビターとして機能するＭｎＳ及び／又はＭｎＳｅを形成する元素である。
Ｓ及びＳｅのいずれかまたは両方の合計（Ｓ＋Ｓｅ）が０．０６０％超であると、熱間圧延後にＭｎＳやＭｎＳｅの析出分散が不均一となる。この場合、所望の二次再結晶組織が得られず、磁束密度が低下したり、純化後にＭｎＳが鋼中に残存し、ヒステリシス損が劣化したりする。そのため、ＳとＳｅとの合計含有量は、０．０６０％以下とする。
ＳとＳｅとの合計含有量の下限は、特に制限されず、０％であればよい。この下限は、０．００３％以上としてもよい。インヒビターとして用いる場合、好ましくは０．０１５％以上である。
［酸可溶性Ａｌ（Ｓｏｌ．Ａｌ）：０．０１０〜０．０６５％］
酸可溶性Ａｌ（アルミニウム）（Ｓｏｌ．Ａｌ）は、Ｎと結合して、インヒビターとして機能するＡｌＮや（Ａｌ、Ｓｉ）Ｎを生成する元素である。酸可溶性Ａｌが０．０１０％未満では、効果が十分に発現せず、二次再結晶が十分に進行しない。そのため、酸可溶性Ａｌ含有量は０．０１０％以上とする。酸可溶性Ａｌ含有量は好ましくは０．０１５％以上、より好ましくは０．０２０％以上である。
一方、酸可溶性Ａｌ含有量が０．０６５％を超えると、ＡｌＮや（Ａｌ、Ｓｉ）Ｎの析出分散が不均一になり、所要の二次再結晶組織が得られず、磁束密度が低下する。そのため、酸可溶性Ａｌ（Ｓｏｌ．Ａｌ）は０．０６５％以下とする。酸可溶性Ａｌは好ましくは０．０５５％以下、より好ましくは０．０５０％以下である。
［Ｎ：０．００４〜０．０１２％］
Ｎ（窒素）は、Ａｌと結合して、インヒビターとして機能するＡｌＮや（Ａｌ、Ｓｉ）Ｎを形成する元素である。Ｎ含有量が０．００４％未満では、ＡｌＮや（Ａｌ、Ｓｉ）Ｎの形成が不十分となるので、Ｎは０．００４％以上とする。好ましくは０．００６％以上、より好ましくは０．００７％以上である。
一方、Ｎ含有量が０．０１２％超であると、鋼板中にブリスター（空孔）が形成されることが懸念される。そのため、Ｎ含有量を０．０１２％以下とする。
上記鋼片の化学組成は、上記元素を含み、残部がＦｅ及び不純物からなる。しかしながら、化合物形成によるインヒビター機能の強化や磁気特性への影響を考慮して、Ｆｅの一部に代えて、選択元素の１種または２種以上を以下の範囲で含有してもよい。Ｆｅの一部に代えて含有される選択元素として、たとえば、Ｃｒ、Ｃｕ、Ｐ、Ｓｎ、Ｓｂ、Ｎｉ、Ｂ、Ｖ、Ｎｂ、Ｍｏ、Ｔｉ、Ｂｉが挙げられる。ただし、選択元素は含まれなくてもよいので、その下限は、それぞれ０％である。また、これらの選択元素が不純物として含有されても、上記効果は損なわれない。なお、「不純物」とは、鋼を工業的に製造する際に、原料としての鉱石やスクラップから、または製造環境等から混入するものを指す。
［Ｃｒ：０〜０．３０％］
Ｃｒ（クロム）は、Ｓｉと同様に、電気抵抗を高めて鉄損を低減するのに有効な元素である。従って、Ｃｒを含有させてもよい。上記効果を得る場合、Ｃｒ含有量は、０．０２％以上であることが好ましく、０．０５％以上であることがより好ましい。
一方で、Ｃｒ含有量が０．３０％を超えると、磁束密度の低下が問題となるので、Ｃｒ含有量の上限は、０．３０％であることが好ましく、０．２０％であることがより好ましく、０．１２％であることがさらに好ましい。
［Ｃｕ：０〜０．４０％］
Ｃｕ（銅）も、電気抵抗を高めて鉄損を低減するのに有効な元素である。従って、Ｃｕを含有させてもよい。この効果を得る場合、Ｃｕ含有量は、０．０５％以上であることが好ましく、０．１０％以上であることがより好ましい。
一方、Ｃｕ含有量が０．４０％を超えると、鉄損低減効果が飽和してしまうとともに、熱間圧延時に“カッパーヘゲ”なる表面疵の原因になることがある。そのため、Ｃｕ含有量の上限は、０．４０％であることが好ましく、０．３０％であることがより好ましく、０．２０％であることがさらに好ましい。
［Ｐ：０〜０．５０％］
Ｐ（リン）も、電気抵抗を高めて鉄損を低減するのに有効な元素である。従って、Ｐを含有させてもよい。この効果を得る場合、Ｐ含有量は、０．００５％以上であることが好ましく、０．０１０％以上であることがより好ましい。
一方、Ｐ含有量が０．５０％を超えると、圧延性に問題が生じることがある。そのため、Ｐ含有量の上限は、０．５０％であることが好ましく、０．２０％であることがより好ましく、０．１５％であることがさらに好ましい。
［Ｓｎ：０〜０．３０％］
［Ｓｂ：０〜０．３０％］
Ｓｎ（スズ）およびＳｂ（アンチモン）は、二次再結晶を安定化させ、｛１１０｝＜００１＞方位を発達させるのに有効な元素である。従って、ＳｎまたはＳｂを含有させてもよい。この効果を得る場合、Ｓｎ含有量は、０．０２％以上であることが好ましく、０．０５％以上であることがより好ましい。また、Ｓｂ含有量は、０．０１％以上であることが好ましく、０．０３％以上であることがより好ましい。
一方、Ｓｎが０．３０％超、またはＳｂが０．３０％超となると、磁気特性に悪影響を及ぼすおそれがある。そのため、Ｓｎ含有量、Ｓｂ含有量の上限をそれぞれ０．３０％とすることが好ましい。Ｓｎ含有量の上限は、０．１５％であることがより好ましく、０．１０％であることがさらに好ましい。Ｓｂ含有量の上限は、０．１５％であることがより好ましく、０．１０％であることがさらに好ましい。
［Ｎｉ：０〜１．００％］
Ｎｉ（ニッケル）も、電気抵抗を高めて鉄損を低減するのに有効な元素である。また、Ｎｉは、熱延鋼板の金属組織を制御して、磁気特性を高めるうえで有効な元素である。従って、Ｎｉを含有させてもよい。上記効果を得る場合、Ｎｉ含有量は、０．０１％以上であることが好ましく、０．０２％以上であることがより好ましい。
一方、Ｎｉ含有量が１．００％を超えると、二次再結晶が不安定になることがある。そのため、Ｎｉ含有量を１．００％以下とすることが好ましく、０．２０％以下とすることがより好ましく、０．１０％以下とすることがさらに好ましい。
［Ｂ：０〜０．００８％］
Ｂ（ボロン）は、Ｎと結合してインヒビター効果を発揮するＢＮを形成するのに有効な元素である。従って、Ｂを含有させてもよい。上記効果を得る場合、Ｂ含有量は、０．０００５％以上であることが好ましく、０．００１０％以上であることがより好ましい。
一方、Ｂ含有量が０．００８％を超えると、磁気特性に悪影響を及ぼすおそれがある。そのため、Ｂ含有量の上限は、０．００８％であることが好ましく、０．００５％であることがより好ましく、０．００３％であることがさらに好ましい。
［Ｖ：０〜０．１５％］
［Ｎｂ：０〜０．２０％］
［Ｔｉ：０〜０．０１５％］
Ｖ（バナジウム）、Ｎｂ（ニオブ）、及びＴｉ（チタン）は、ＮやＣと結合してインヒビターとして機能する元素である。従って、Ｖ、Ｎｂ、またはＴｉを含有させてもよい。上記効果を得る場合、Ｖ含有量は、０．００２％以上であることが好ましく、０．０１０％以上であることがより好ましい。Ｎｂ含有量は、０．００５％以上であることが好ましく、０．０２０％以上であることがより好ましい。Ｔｉ含有量は、０．００２％以上であることが好ましく、０．００４％以上であることがより好ましい。
一方、鋼片がＶを０．１５％超、Ｎｂを０．２０％超、Ｔｉを０．０１５％超の範囲で含有すると、これらの元素が最終製品に残留して、最終製品として、Ｖ含有量が０．１５％を超え、Ｎｂ含有量が０．２０％を超え、またはＴｉ含有量が０．０１５％を超える場合がある。この場合、最終製品（電磁鋼板）の磁気特性が劣化するおそれがある。
そのため、Ｖ含有量の上限は、０．１５％であることが好ましく、０．１０％であることがより好ましく、０．０５％であることがさらに好ましい。Ｔｉ含有量の上限は、０．０１５％であることが好ましく、０．０１０％であることがより好ましく、０．００８％であることがさらに好ましい。Ｎｂ含有量の上限は、０．２０％であることが好ましく、０．１０％であることがより好ましく、０．０８％であることがさらに好ましい。
［Ｍｏ：０〜０．１０％］
Ｍｏ（モリブデン）も、電気抵抗を高めて鉄損を低減するのに有効な元素である。従って、Ｍｏを含有させてもよい。上記効果を得る場合、Ｍｏ含有量は、０．００５％以上であることが好ましく、０．０１％以上であることがより好ましい。
一方、Ｍｏ含有量が０．１０％を超えると、鋼板の圧延性に問題が生じることがある。そのため、Ｍｏ含有量の上限は、０．１０％であることが好ましく、０．０８％であることがより好ましく、０．０５％であることがさらに好ましい。
［Ｂｉ：０〜０．０１０％］
Ｂｉ（ビスマス）は、硫化物等の析出物を安定化してインヒビターとしての機能を強化するのに有効な元素である。従って、Ｂｉを含有させてもよい。上記効果を得る場合、Ｂｉ含有量は、０．００１％以上であることが好ましく、０．００２％以上であることがより好ましい。
一方、Ｂｉ含有量が０．０１０％を超えると、磁気特性に悪影響を及ぼすことがある。そのため、Ｂｉ含有量の上限は、０．０１０％であることが好ましく、０．００８％であることがより好ましく、０．００６％であることがさらに好ましい。
上記した化学組成は、鋼の一般的な分析方法によって測定すればよい。例えば、化学組成は、ＩＣＰ−ＡＥＳ（Ｉｎｄｕｃｔｉｖｅｌｙ Ｃｏｕｐｌｅｄ Ｐｌａｓｍａ−Ａｔｏｍｉｃ Ｅｍｉｓｓｉｏｎ Ｓｐｅｃｔｒｏｍｅｔｒｙ）を用いて測定すればよい。なお、ｓｏｌ．Ａｌは、試料を酸で加熱分解した後の濾液を用いてＩＣＰ−ＡＥＳによって測定すればよい。また、ＣおよびＳは燃焼−赤外線吸収法を用い、Ｎは不活性ガス融解−熱伝導度法を用い、Ｏは不活性ガス融解−非分散型赤外線吸収法を用いて測定すればよい。
続いて、上記鋼片を熱間圧延する際の条件について説明する。
熱間圧延条件については特に限定されない。例えば、以下の条件である。
熱間圧延に先立ちスラブを加熱する。スラブを周知の加熱炉又は周知の均熱炉に装入して、加熱する。１つの方法として、スラブを１２８０℃以下に加熱する。スラブの加熱温度を１２８０℃以下とすることにより、たとえば、１２８０℃よりも高い温度で加熱した場合の諸問題（専用の加熱炉が必要なこと、及び溶融スケール量の多さ等）を回避することができる。スラブの加熱温度の下限値は特に限定されない。加熱温度が低すぎる場合、熱間圧延が困難になって、生産性が低下することがある。したがって、加熱温度は、１２８０℃以下の範囲で生産性を考慮して設定すればよい。スラブの加熱温度の好ましい下限は１１００℃である。スラブの加熱温度の好ましい上限は１２５０℃である。
また、別の方法として、スラブを１３２０℃以上の高い温度に加熱する。１３２０℃以上の高温まで加熱することにより、ＡｌＮ、Ｍｎ（Ｓ，Ｓｅ）を溶解させ、その後の工程で微細析出させることにより、二次再結晶を安定的に発現することができる。
スラブ加熱工程そのものを省略して、鋳造後、スラブの温度が下がるまでに熱間圧延を開始することも可能である。
次に、加熱されたスラブに対して、熱間圧延機を用いた熱間圧延を実施して、熱延鋼板を製造する。熱間圧延機はたとえば、粗圧延機と、粗圧延機の下流に配置された仕上げ圧延機とを備える。粗圧延機は、一列に並んだ粗圧延スタンドを備える。各粗圧延スタンドは、上下に配置された複数のロールを含む。仕上げ圧延機も同様に、一列に並んだ仕上げ圧延スタンドを備える。各仕上げ圧延スタンドは、上下に配置される複数のロールを含む。加熱された鋼材を粗圧延機により圧延した後、さらに、仕上げ圧延機により圧延して、熱延鋼板を製造する。
熱延工程における仕上げ温度（仕上げ圧延機にて最後に鋼板を圧下する仕上げ圧延スタンドの出側での鋼板温度）は、たとえば７００〜１１５０℃である。以上の熱延工程により、熱延鋼板を製造する。
＜熱延板焼鈍工程＞
熱延板焼鈍工程では、必要に応じて、熱延工程によって得られた熱延鋼板に対して、焼鈍（熱延板焼鈍）を行って熱延焼鈍板を得る。本実施形態では、熱延板焼鈍工程後の鋼板を、熱延焼鈍板と呼ぶ。
熱延板焼鈍は、熱間圧延時に生じた不均一組織をできるだけ均一化し、インヒビターであるＡｌＮの析出を制御し（微細析出）、第二相／固溶炭素を制御すること等を目的として行う。焼鈍条件は、目的に応じて公知の条件を選択すればよい。例えば熱間圧延時に生じた不均一組織を均一化する場合、熱延鋼板を、焼鈍温度（熱延板焼鈍炉での炉温）が、７５０〜１２００℃で、３０〜６００秒保持する。
熱延板焼鈍は必ずしも行う必要がなく、熱延板焼鈍工程の実施の有無は、最終的に製造される方向性電磁鋼板に要求される特性及び製造コストに応じて決定すればよい。
＜熱延板酸洗工程＞
熱延板酸洗工程では、熱延工程後の熱延鋼板、または熱延板焼鈍を行った場合には、熱延板焼鈍工程後の熱延焼鈍板に対し、必要に応じて、表面に生成したスケールを除去するため、酸洗を行う。酸洗条件については特に限定されず、公知の条件で行えばよい。
＜冷延工程＞
冷延工程では、熱延工程後、熱延板焼鈍工程後、または熱延板酸洗工程後の熱延鋼板または熱延焼鈍板に対し、１回または中間焼鈍を挟む２回以上の冷間圧延を施して冷延鋼板とする。本実施形態では、冷延工程後の鋼板を、冷延鋼板と呼ぶ。
最終の冷間圧延における好ましい冷間圧延率（中間焼鈍を行わない累積冷間圧延率、または中間焼鈍を行った後の累積冷間圧延率）は、好ましくは８０％以上であり、より好ましくは９０％以上である。最終の冷間圧延率の好ましい上限は９５％である。
ここで、最終の冷間圧延率（％）は次のとおり定義される。
最終の冷間圧延率（％）＝（１−最終の冷間圧延後の鋼板の板厚／最終の冷間圧延前の鋼板の板厚）×１００
＜脱炭焼鈍工程＞
脱炭焼鈍工程では、冷延工程により製造された冷延鋼板に対して、必要に応じて磁区制御処理を行った後、脱炭焼鈍を実施して一次再結晶させる。また、脱炭焼鈍では、磁気特性に悪影響を及ぼすＣを鋼板から除去する。本実施形態では、脱炭焼鈍工程後の鋼板を、脱炭焼鈍板と呼ぶ。
上記の目的のため、脱炭焼鈍では、焼鈍雰囲気（炉内雰囲気）における酸化度（ＰＨ２Ｏ／ＰＨ２）を０．０１〜０．１５として、焼鈍温度７５０〜９００℃で、１０〜６００秒保持を行う。なお、酸化度であるＰＨ２Ｏ／ＰＨ２は、雰囲気中の水蒸気分圧ＰＨ２Ｏ（ａｔｍ）と水素分圧ＰＨ２（ａｔｍ）との比によって定義できる。
酸化度（ＰＨ２Ｏ／ＰＨ２）が、０．０１未満であると、脱炭速度が遅くなり生産性が低下するだけでなく、脱炭不良が生じ、仕上げ焼鈍後の磁性が劣化する。一方、０．１５超であると、Ｆｅ系酸化物が形成され、仕上げ焼鈍後の界面平滑化が困難となる。
また、焼鈍温度が７５０℃未満であると、脱炭速度が遅くなり生産性が低下するだけでなく、脱炭不良が生じ、仕上げ焼鈍後の磁性が劣化する。一方、９００℃超であると一次再結晶粒径が所望のサイズを超えてしまうため、仕上げ焼鈍後の磁性が劣化する。
また、保持時間が１０秒未満であると、脱炭を充分に行うことができない。一方、６００秒超であると生産性が低下する上、一次再結晶粒径が所望のサイズを超えてしまうため、仕上げ焼鈍後の磁性が劣化する。
なお、上記の酸化度（ＰＨ２Ｏ／ＰＨ２）に応じて、焼鈍温度までの昇温過程における加熱速度を制御してもよい。例えば、誘導加熱を含む加熱を行う場合には、平均加熱速度を、５〜１０００ ℃／秒とすればよい。また、通電加熱を含む加熱を行う場合には、平均加熱速度を、５〜３０００℃／秒とすればよい。
また、脱炭焼鈍工程では、さらに、上記の保持の前、途中、後のいずれか一つ、または二つ以上の段階でアンモニアを含有する雰囲気中で焼鈍して冷延鋼板を窒化する、窒化処理を行ってもよい。スラブ加熱温度が低い場合には脱炭焼鈍工程が窒化処理を含むことが好ましい。脱炭焼鈍工程にて、さらに窒化処理を行うことで、仕上げ焼鈍工程の二次再結晶前までにＡｌＮや（Ａｌ，Ｓｉ）Ｎ等のインヒビターが生成するので、二次再結晶を安定的に発現することができる。
窒化処理の条件については特に限定されないが、窒素含有量が０．００３％以上、好ましくは０．００５％以上、更に好ましくは０．００７％以上増加するように窒化処理を行うことが好ましい。窒素（Ｎ）含有量が、０．０３０％以上となると効果が飽和するので、０．０３０％以下となるように窒化処理を行ってもよい。
窒化処理の条件については特に限定されず、公知の条件で行えばよい。
例えば、窒化処理を、酸化度（ＰＨ２Ｏ／ＰＨ２）を０．０１〜０．１５、７５０〜９００℃で１０〜６００秒保持した後に行う場合には、冷延鋼板を室温まで冷却することなく、降温の過程でアンモニアを含有する雰囲気中で保持して窒化処理を行う。降温の過程で酸化度（ＰＨ２Ｏ／ＰＨ２）を０．０００１〜０．０１の範囲とすることが好ましい。窒化処理を、酸化度（ＰＨ２Ｏ／ＰＨ２）を０．０１〜０．１５、７５０〜９００℃で１０〜６００秒の保持中に行う場合には、この酸化度の雰囲気ガスにアンモニアを導入すればよい。
＜焼鈍分離剤塗布工程＞
焼鈍分離剤塗布工程では、脱炭焼鈍工程後の脱炭焼鈍板（窒化処理を行った脱炭焼鈍板も含む）に対し、必要に応じて磁区制御処理を行った後、Ａｌ２Ｏ３とＭｇＯとを含有する焼鈍分離剤を塗布し、塗布した焼鈍分離剤を乾燥させる。
焼鈍分離剤が、ＭｇＯを含み、Ａｌ２Ｏ３を含まない場合、仕上げ焼鈍工程にて、鋼板上にフォルステライト被膜が形成される。一方、焼鈍分離剤がＡｌ２Ｏ３を含み、ＭｇＯを含まない場合には、鋼板にムライト（３Ａｌ２Ｏ３・２ＳｉＯ２）が形成される。このムライトは、磁壁移動の障害となるので、方向性電磁鋼板の磁気特性の劣化の原因となる。
そのため、本実施形態に係る方向性電磁鋼板の製造方法では、焼鈍分離剤として、Ａｌ２Ｏ３とＭｇＯとを含有する焼鈍分離剤を用いる。Ａｌ２Ｏ３とＭｇＯとを含有する焼鈍分離剤を用いることで、仕上げ焼鈍後に、表面にフォルステライト被膜が形成されず、かつ平滑な表面の鋼板を得ることができる。
焼鈍分離剤は、ＭｇＯとＡｌ２Ｏ３との質量比率であるＭｇＯ／（ＭｇＯ＋Ａｌ２Ｏ３）を５〜５０％とし、水和水分を１．５質量％以下とする。
ＭｇＯ／（ＭｇＯ＋Ａｌ２Ｏ３）が５％未満では、多量のムライトが形成されるため、鉄損が劣化する。一方、５０％超では、フォルステライトが形成されるため、鉄損が劣化する。
また、焼鈍分離剤における水和水分が１．５質量％超であると、二次再結晶が不安定になったり、仕上げ焼鈍中に鋼板表面が酸化され（ＳｉＯ２が形成され）、鋼板表面の平滑化が困難となる場合がある。水和水分の下限は、特に制限されないが、例えば０．１質量％とすればよい。
焼鈍分離剤は、水スラリー塗布又は静電塗布等で鋼板表面に塗布する。焼鈍分離剤塗布工程では、さらに、窒化マンガン、窒化鉄や窒化クロムなど、仕上げ焼鈍工程で二次再結晶前に分解して脱炭鋼板または脱炭窒化板を窒化する窒化物を焼鈍分離剤に添加してもよい。
＜仕上げ焼鈍工程＞
上記焼鈍分離剤が塗布された脱炭焼鈍板に仕上げ焼鈍を行い、仕上げ焼鈍板とする。焼鈍分離剤を塗布した脱炭焼鈍板に仕上げ焼鈍を施すことで、二次再結晶が進行し、結晶方位が｛１１０｝＜００１＞方位に集積する。本実施形態では、仕上げ焼鈍工程後の鋼板を、仕上げ焼鈍板と呼ぶ。
仕上げ焼鈍に際しては、雰囲気（炉内雰囲気）が、水素を含有する場合には、酸化度（ＰＨ２Ｏ／ＰＨ２）を０．０００１０〜０．２とし、水素を含有しない不活性ガス（窒素やアルゴンなど）からなる場合には、露点を０℃以下とする。
雰囲気に応じて露点、または酸化度を上記の範囲とすることで、二次再結晶を安定して発現して方位集積度を高めることができる。
雰囲気が水素を含有する場合に、酸化度が０．０００１０未満であると、脱炭焼鈍で形成した稠密な表面シリカ膜が仕上げ焼鈍の二次再結晶前に還元して二次再結晶が不安定となる。一方、酸化度が０．２超であると、ＡｌＮや（Ａｌ，Ｓｉ）Ｎ等のインヒビターの分解が促進されて二次再結晶が不安定となる。また、雰囲気が水素を含有しない不活性ガスの場合には、露点が０℃超であると、ＡｌＮや（Ａｌ，Ｓｉ）Ｎ等のインヒビターの分解が促進されて二次再結晶が不安定となる。露点の下限は、特に制限されないが、例えば−３０℃とすればよい。
＜焼鈍分離剤除去工程＞
焼鈍分離剤除去工程では、仕上げ焼鈍後の鋼板（仕上げ焼鈍板）の表面から、仕上げ焼鈍で鋼板と反応しなかった未反応の焼鈍分離剤等の余剰な焼鈍分離剤を、水洗または酸洗の一方または両方を含む方法によって除去する。
鋼板表面の余剰な焼鈍分離剤の除去が不十分な場合、占積率が悪化し、鉄心としての性能が低下してしまう。
余剰な焼鈍分離剤を除去するため、水洗、酸洗に加えて、さらにスクラバーを用いて除去を行ってもよい。スクラバーを用いることで、絶縁被膜形成工程での濡れ性を悪化させる余剰な焼鈍分離剤の除去を確実に行うことができる。
また、余剰な焼鈍分離剤を除去するために酸洗を行う場合には、体積比濃度が２０％未満の酸性溶液を用いて酸洗を行えばよい。例えば、硫酸、硝酸、塩酸、リン酸、塩素酸、酸化クロム水溶液、クロム硫酸、過マンガン酸、ペルオキソ硫酸及びペルオキソリン酸の１種または２種以上を合計で２０体積％未満含有する溶液を用いることが好ましく、より好ましくは１０体積％未満である。体積比濃度の下限は、特に制限されないが、例えば０．１体積％とすればよい。このような溶液を用いることで、鋼板表面の余剰な焼鈍分離剤を効率的に除去することができる。なお、体積％は、室温での体積を基準とした比率とすればよい。
また、酸洗を行う場合、溶液の液温を２０〜８０℃とすることが好ましい。液温を上記範囲とすることで、鋼板表面の余剰焼鈍分離剤を効率的に除去することができる。
＜絶縁被膜形成工程＞
絶縁被膜形成工程では、焼鈍分離剤除去工程後の仕上げ焼鈍板の表面に、必要に応じて磁区制御処理を行った後、絶縁被膜を形成する。本実施形態では、絶縁被膜形成工程後の鋼板を、方向性電磁鋼板と呼ぶ。
この絶縁被膜は、方向性電磁鋼板に張力を付与することにより、鋼板単板としての鉄損を低下させるとともに、方向性電磁鋼板を積層して使用する際に、鋼板間の電気的絶縁性を確保することにより、鉄心としての鉄損を低下させる。
絶縁被膜は、仕上げ焼鈍板の表面に、リン酸塩またはコロイダルシリカの少なくとも一方を主成分とする絶縁被膜のコーティング液を塗布し、３５０〜６００℃で焼付け、その後、８００〜１０００℃の温度で熱処理することで形成される。
リン酸塩として、Ｃａ、Ａｌ、Ｓｒ等のリン酸塩が好ましく、中でも、リン酸アルミニウム塩がより好ましい。コロイダルシリカは、特に、特定の性状のコロイダルシリカに限定されない。粒子サイズも、特に、特定の粒子サイズに限定されないが、２００ｎｍ（数平均粒径）以下が好ましい。例えば５〜３０ｎｍである。粒子サイズが２００ｎｍを超えると、塗布液中で沈降する場合がある。また、塗布液は、さらに、無水クロム酸又はクロム酸塩を含んでもよい。
絶縁被膜の焼付温度が３５０℃未満であると、絶縁被膜が通板中に液ダレを起こし、外観不良の原因となるとともに、十分な密着性を有する絶縁被膜が得られない。また、６００℃超であると、加熱速度が速すぎることから絶縁被膜の最表面のみ硬化が進行し、内部の硬化が遅れることから、被膜形成不良の原因となり、被膜密着性が不十分となる。また、焼付後の熱処理温度が８００℃未満であると、被膜形成不良（硬化不足）となり、十分な被膜張力が得られない。また、１０００℃超であるとリン酸塩の分解が起こり、被膜形成不良となり被膜密着性が不十分となる。
被膜の形成に際しては、雰囲気の酸化度（ＰＨ２Ｏ／ＰＨ２）を０．０１〜１．５とすることで、必要以上にリン酸塩を分解させることなく、絶縁被膜形成を行うことが可能となるので好ましい。
絶縁被膜形成用塗布液は、例えば、ロールコーター等の湿式塗布方法で鋼板表面に塗布することができる。
＜磁区制御工程＞
本実施形態に係る方向性電磁鋼板の製造方法では、冷延工程と脱炭焼鈍工程との間（第１）、脱炭焼鈍工程と焼鈍分離剤塗布工程との間（第２）、焼鈍分離剤除去工程と絶縁被膜形成工程との間（第３）、または絶縁被膜形成工程後（第４）のいずれかに、磁区制御処理を行う磁区制御工程を備えてもよい。
磁区制御処理を行うことで、方向性電磁鋼板の鉄損をより低減させることができる。磁区制御処理を、冷延工程と脱炭焼鈍工程との間、脱炭焼鈍工程と焼鈍分離剤塗布工程との間、焼鈍分離剤除去工程と絶縁被膜形成工程との間に行う場合には、圧延方向に交差する方向に延びる線状、または点状の溝部を、圧延方向に沿って所定間隔で形成することにより、１８０°磁区の幅を狭く（１８０°磁区を細分化）すればよい。
また、磁区制御処理を絶縁被膜形成工程後に行う場合には、圧延方向に交差する方向に延びる線状、または点状の応力歪部や溝部を、圧延方向に沿って所定間隔で形成することにより、１８０°磁区の幅を狭く（１８０°磁区を細分化）すればよい。
応力歪部を形成する場合には、レーザビーム照射、電子線照射などが適用できる。また、溝部を形成する場合には、歯車などによる機械的溝形成法、電解エッチングによって溝を形成する化学的溝形成法、および、レーザ照射による熱的溝形成法などが適用できる。応力歪部や溝部の形成によって絶縁被膜に損傷が発生して絶縁性等の特性が劣化するような場合には、再度絶縁被膜を形成して損傷を補修してもよい。
本実施形態に係る方向性電磁鋼板の製造方法の一例を図１に示す。実線で囲まれた工程は必須工程、破線で囲まれた工程は任意の工程であることを示す。
本実施形態に係る製造方法で製造した方向性電磁鋼板は、フォルステライト被膜を有さない。具体的には、この方向性電磁鋼板は、母鋼板と、母鋼板上に接して配された中間層と、中間層上に接して配されて最表面となる絶縁被膜とを有する。
方向性電磁鋼板がフォルステライト被膜を有さないことは、Ｘ線回折によって確認すればよい。例えば、方向性電磁鋼板から絶縁被膜を除去した表面に対してＸ線回折を行い、得られたＸ線回折スペクトルをＰＤＦ（Ｐｏｗｄｅｒ Ｄｉｆｆｒａｃｔｉｏｎ Ｆｉｌｅ）と照合すればよい。例えば、フォルステライト（Ｍｇ２ＳｉＯ４）の同定には、ＪＣＰＤＳ番号：３４−１８９を用いればよい。本実施形態では、上記Ｘ線回折スペクトルの主な構成がフォルステライトでない場合に、方向性電磁鋼板がフォルステライト被膜を有さないと判断する。
なお、方向性電磁鋼板から絶縁被膜のみを除去するには、被膜を有する方向性電磁鋼板を、高温のアルカリ溶液に浸漬すればよい。具体的には、ＮａＯＨ：３０質量％＋Ｈ２Ｏ：７０質量％の水酸化ナトリウム水溶液に、８０℃で２０分間、浸漬した後に、水洗して乾燥することで、方向性電磁鋼板から絶縁被膜を除去できる。通常、アルカリ溶液によって絶縁被膜のみが溶解され、塩酸などの酸性溶液によってフォルステライト被膜が溶解される。
本実施形態に係る製造方法で製造した方向性電磁鋼板は、フォルステライト被膜を有さないので磁気特性（鉄損特性）に優れ、且つ製造工程それぞれを最適に制御しているので被膜密着性にも優れる。
次に、本発明の実施例について説明するが、実施例での条件は、本発明の実施可能性及び効果を確認するために採用した一条件例であり、本発明は、この一条件例に限定されるものではない。本発明は、本発明の要旨を逸脱せず、本発明の目的を達成する限り、種々の条件を採用し得るものである。
表１に示す化学組成の鋼スラブのうち、Ｎｏ．Ａ１３及びＮｏ．ａ１１を、１３５０℃に加熱して熱間圧延に供し、板厚２．６ｍｍの熱延鋼板とした。この熱延鋼板に、一回の冷間圧延又は中間焼鈍を挟む複数回の冷間圧延を施して、最終板厚０．２２ｍｍの冷延鋼板とした。板厚０．２２ｍｍの冷延鋼板に対し、脱炭焼鈍工程として、表２〜４に示す条件で脱炭焼鈍を施した。
また、表１に示す化学組成の鋼スラブのうち、Ｎｏ．Ａ１３及びＮｏ．ａ１１以外を、１１５０℃に加熱して熱間圧延に供し、板厚２．６ｍｍの熱延鋼板とした。この熱延鋼板に、一回の冷間圧延又は中間焼鈍を挟む複数回の冷間圧延を施して、最終板厚０．２２ｍｍの冷延鋼板とした。板厚０．２２ｍｍの冷延鋼板に対し、脱炭焼鈍工程として、表２〜４に示す条件で脱炭焼鈍を施し、降温途中でアンモニアを含有する雰囲気中で保持する窒化処理を施した。
なお、Ｎｏ．Ｂ５については、熱延後の熱延鋼板に対し１１００℃で焼鈍し、引き続き９００℃で焼鈍する熱延板焼鈍を施した後、酸洗を行って表面に生成したスケールを除去してから冷間圧延を行った。
また、脱炭焼鈍の際、焼鈍温度までの昇温過程における平均加熱速度は、１５℃／秒以上であった。
上記した脱炭焼鈍後の脱炭焼鈍板に対し、Ａｌ２Ｏ３とＭｇＯとの比率（ＭｇＯ／（Ａｌ２Ｏ３＋ＭｇＯ））および水和水分が表２〜４に示す条件の焼鈍分離剤を塗布して乾燥させた。
焼鈍分離剤を塗布した脱炭焼鈍板に対し、１１００℃もしくは１２００℃で２０時間の仕上げ焼鈍を行った。その際、表５〜７に示すように、雰囲気が水素（Ｈ２）を含む場合には、酸化度を制御し、水素を含まない場合には、露点を制御した。
仕上げ焼鈍後、表中で酸洗「無し」の実施例については、鋼板から余剰の焼鈍分離剤を水洗によって除去し、表中で酸洗「有」の実施例については、余剰の焼鈍分離剤を水洗して更に硫酸水溶液中（硫酸の体積比濃度：１体積％）に浸漬することで酸洗を行った。
その後、コロイダルシリカとリン酸塩とを主体とし、必要に応じて無水クロム酸を添加した絶縁被膜のコーティング液を塗布し、表５〜７に示す焼付け温度で焼付け、さらに表５〜７に示す温度で熱処理を行って絶縁被膜を形成させた。
また、各実施例では、表８〜１０に示すように、冷延工程と脱炭焼鈍工程との間（第１）、脱炭焼鈍工程と焼鈍分離剤塗布工程との間（第２）、焼鈍分離剤除去工程と絶縁被膜形成工程との間（第３）、または絶縁被膜形成工程後（第４）のいずれかの時点で磁区制御を行った。磁区制御では、機械的、または化学的に溝を形成するか、レーザを用いて、応力歪部または溝部を形成した。
得られた方向性電磁鋼板Ｎｏ．Ｂ１〜Ｂ４３、ｂ１〜ｂ２８について、鉄損及び被膜密着性を評価した。
＜鉄損＞
作製した方向性電磁鋼板から採取した試料に対し、ＪＩＳ Ｃ ２５５０−１：２０００に基づき、エプスタイン試験により励磁磁束密度１．７Ｔ、周波数５０Ｈｚにおける鉄損Ｗ１７／５０（Ｗ／ｋｇ）を測定した。磁区制御を行った方向性電磁鋼板については、鉄損Ｗ１７／５０が０．７Ｗ／ｋｇ未満の場合を合格と判断した。また、磁区制御を行わない方向性電磁鋼板については、鉄損Ｗ１７／５０が１．０Ｗ／ｋｇ未満の場合を合格と判断した。
＜被膜密着性＞
製造した方向性電磁鋼板から採取した試験片を、直径２０ｍｍの円筒に巻き付け（１８０°曲げ）、曲げ戻した時の被膜残存面積率で、絶縁被膜の被膜密着性を評価した。絶縁被膜の被膜密着性の評価は、目視で絶縁被膜の剥離の有無を判断した。鋼板から剥離せず、被膜残存面積率が９０％以上を◎（ＶＥＲＹ ＧＯＯＤ）、８５％以上９０％未満を〇（ＧＯＯＤ）、８０％以上８５％未満を△（ＰＯＯＲ）、８０％未満を×（ＮＧ）とした。被膜残存面積率が８５％以上の場合（上記の◎または〇）を合格と判断した。
結果を表８〜１０に示す。
Figure 2020149321
Figure 2020149321
Figure 2020149321
Figure 2020149321
Figure 2020149321
Figure 2020149321
Figure 2020149321
Figure 2020149321
Figure 2020149321
Figure 2020149321
表１〜１０から分かるように、発明例であるＮｏ．Ｂ１〜Ｂ４３はすべての工程条件が本発明範囲を満足しており、鉄損が低かった。また、被膜密着性にも優れていた。
これに対し、比較例であるＮｏ．ｂ１〜ｂ２８については、１つ以上の工程条件が本発明範囲を外れており、鉄損及び／または被膜密着性が劣っていた。なお、比較例Ｎｏ．ｂ２０については、圧延ができなかったので、それ以降の評価を行っていない。
本発明の上記態様によれば、フォルステライト被膜を有さず、かつ、磁気特性および被膜密着性に優れる方向性電磁鋼板の製造方法を提供できる。得られた方向性電磁鋼板は、磁気特性および被膜密着性に優れるので、本発明は産業上の利用可能性が高い。

Claims (6)

  1. 化学組成として、質量％で、
    Ｃ：０．０３０〜０．１００％、
    Ｓｉ：０．８０〜７．００％、
    Ｍｎ：０．０１〜１．００％、
    Ｓ及びＳｅの合計：０〜０．０６０％、
    酸可溶性Ａｌ：０．０１０〜０．０６５％、
    Ｎ：０．００４〜０．０１２％、
    Ｃｒ：０〜０．３０％、
    Ｃｕ：０〜０．４０％、
    Ｐ：０〜０．５０％、
    Ｓｎ：０〜０．３０％、
    Ｓｂ：０〜０．３０％、
    Ｎｉ：０〜１．００％、
    Ｂ：０〜０．００８％、
    Ｖ：０〜０．１５％、
    Ｎｂ：０〜０．２０％、
    Ｍｏ：０〜０．１０％、
    Ｔｉ：０〜０．０１５％、
    Ｂｉ：０〜０．０１０％、を含有し、
    残部がＦｅおよび不純物からなる鋼片を、熱間圧延して熱延鋼板を得る熱延工程と、
    前記熱延鋼板に冷間圧延を施して冷延鋼板を得る冷延工程と、
    前記冷延鋼板に脱炭焼鈍を行って脱炭焼鈍板を得る脱炭焼鈍工程と、
    前記脱炭焼鈍板に、Ａｌ２Ｏ３とＭｇＯとを含有する焼鈍分離剤を塗布して乾燥させる焼鈍分離剤塗布工程と、
    前記焼鈍分離剤が塗布された前記脱炭焼鈍板に仕上げ焼鈍を行い、仕上げ焼鈍板を得る仕上げ焼鈍工程と、
    前記仕上げ焼鈍板の表面から余剰の焼鈍分離剤を除去する焼鈍分離剤除去工程と、
    前記仕上げ焼鈍板の表面に絶縁被膜を形成する絶縁被膜形成工程と、
    を備え、
    前記脱炭焼鈍工程では、
    酸化度であるＰＨ２Ｏ／ＰＨ２が０．０１〜０．１５である雰囲気下で、焼鈍温度７５０〜９００℃で、１０〜６００秒保持を行い、
    前記焼鈍分離剤塗布工程では、
    前記焼鈍分離剤における、前記ＭｇＯと前記Ａｌ２Ｏ３との質量比率であるＭｇＯ／（ＭｇＯ＋Ａｌ２Ｏ３）を５〜５０％、水和水分を１．５質量％以下とし、
    前記仕上げ焼鈍工程では、
    雰囲気が、水素を含有する場合には、酸化度を０．０００１０〜０．２とし、水素を含有しない不活性ガスからなる場合には、露点を０℃以下とし、
    前記絶縁被膜形成工程では、
    リン酸塩またはコロイダルシリカを主成分とする絶縁被膜のコーティング液を塗布し、３５０〜６００℃で焼付け、８００〜１０００℃の温度で熱処理して絶縁被膜を形成する
    ことを特徴とする方向性電磁鋼板の製造方法。
  2. 前記熱延工程と前記冷延工程との間に、
    前記熱延鋼板を焼鈍する熱延板焼鈍工程、または酸洗を行う熱延板酸洗工程の少なくとも１つを備える
    ことを特徴とする請求項１に記載の方向性電磁鋼板の製造方法。
  3. 前記脱炭焼鈍工程では、前記冷延鋼板を、アンモニアを含有する雰囲気中で焼鈍する窒化処理を行う
    ことを特徴とする請求項１または２に記載の方向性電磁鋼板の製造方法。
  4. 前記冷延工程と前記脱炭焼鈍工程との間、前記脱炭焼鈍工程と前記焼鈍分離剤塗布工程との間、前記焼鈍分離剤除去工程と前記絶縁被膜形成工程との間、または前記絶縁被膜形成工程後のいずれかに、磁区制御処理を行う磁区制御工程を備える
    ことを特徴とする請求項１〜３のいずれか一項に記載の方向性電磁鋼板の製造方法。
  5. 前記焼鈍分離剤除去工程では、水洗後に、体積比濃度が２０％未満の酸性溶液を用いて酸洗を行う
    ことを特徴とする請求項１〜４のいずれか一項に記載の方向性電磁鋼板の製造方法。
  6. 前記鋼片が、化学組成として、質量％で、
    Ｃｒ：０．０２〜０．３０％、
    Ｃｕ：０．０５〜０．４０％、
    Ｐ：０．００５〜０．５０％、
    Ｓｎ：０．０２〜０．３０％、
    Ｓｂ：０．０１〜０．３０％、
    Ｎｉ：０．０１〜１．００％、
    Ｂ：０．０００５〜０．００８％、
    Ｖ：０．００２〜０．１５％、
    Ｎｂ：０．００５〜０．２０％、
    Ｍｏ：０．００５〜０．１０％、
    Ｔｉ：０．００２〜０．０１５％、及び
    Ｂｉ：０．００１〜０．０１０％、
    からなる群から選択される少なくとも１種を含有する
    ことを特徴とする請求項１〜５のいずれか一項に記載の方向性電磁鋼板の製造方法。
JP2020566441A 2019-01-16 2020-01-16 方向性電磁鋼板の製造方法 Active JP7299511B2 (ja)