JPWO2011152314A1 - 太陽電池モジュール用封止材及びその製造方法 - Google Patents
太陽電池モジュール用封止材及びその製造方法 Download PDFInfo
- Publication number
- JPWO2011152314A1 JPWO2011152314A1 JP2012518365A JP2012518365A JPWO2011152314A1 JP WO2011152314 A1 JPWO2011152314 A1 JP WO2011152314A1 JP 2012518365 A JP2012518365 A JP 2012518365A JP 2012518365 A JP2012518365 A JP 2012518365A JP WO2011152314 A1 JPWO2011152314 A1 JP WO2011152314A1
- Authority
- JP
- Japan
- Prior art keywords
- solar cell
- sealing material
- cell module
- layer
- polymerization initiator
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明の太陽電池モジュール用封止材を製造するための太陽電池モジュール用封止材組成物(以下、単に、「封止材組成物」ともいう)は、密度が0.900g/cm3以下のポリエチレン系樹脂を90%以上含有する樹脂組成物と、重合開始剤と、を必須成分として含有する。
ベース樹脂として、本発明においては密度が0.900g/cm3以下の低密度ポリエチレン(LDPE)、好ましくは直鎖低密度ポリエチレン(LLDPE)を用いる。直鎖低密度ポリエチレンはエチレンとα−オレフィンとの共重合体であり、本発明においては、その密度が0.900g/cm3以下、好ましくは0.870〜0.890g/cm3の範囲である。この範囲であれば、シート加工性を維持しつつ良好な透明性と耐熱性を付与することができる。
MFR(g/10min):JIS K7210に準拠して測定。具体的には、ヒーターで加熱された円筒容器内で合成樹脂を、190℃で加熱・加圧し、容器底部に設けられた開口部(ノズル)から10分間あたりに押出された樹脂量を測定した。試験機械は押出し形プラストメータを用い、押出し荷重については2.16kgとした。
尚、多層フィルムである封止材シートについては、全ての層が一体積層された多層状態のまま、上記処理による測定を行い、得た測定値を当該多層の封止材シートのMFR値とした。
本発明においては、従来知られている太陽電池モジュール用封止材組成物の一般的な架橋処理を行う場合とは異なり、太陽電池モジュール用封止材組成物に対する重合開始剤の含有量が、一般的な架橋処理の場合よりも少ない特定の範囲の含有量となるように重合開始剤を使用する。重合開始剤の含有量は、太陽電池モジュール用封止材組成物中に0.02質量%以上0.5質量%未満であり、上限は好ましくは0.2質量%以下、より好ましくは0.1質量%以下である。この範囲未満であると上記ポリエチレン系樹脂の弱架橋が進まず耐熱性が不足する。また、この範囲を超えると、成形中にゲルが発生する等して製膜性が低下し、透明性も低下する。
本発明においては、一般的な架橋処理とは異なり、架橋助剤は使用しない。ここで架橋助剤とは、例えば、多官能ビニル系モノマー及び/又は多官能エポキシ系モノマー等であり、具体的には、トリアリルイソシアヌレート(TAIC)、トリアリルシアヌレート、ジアリルフタレート、ジアリルフマレート、ジアリルマレエート等のポリアリル化合物、トリメチロールプロパントリメタクリレート(TMPT)、トリメチロールプロパントリアクリレート(TMPTA)、エチレングリコールジアクリレート、エチレングリコールジメタクリレート、1,4−ブタンジオールジアクリレート、1,6−ヘキサンジオールジアクリレート、1,9−ノナンジオールジアクリレート等のポリ(メタ)アクリロキシ化合物、二重結合とエポキシ基を含むグリシジルメタクリレート、4−ヒドロキシブチルアクリレートグリシジルエーテル及びエポキシ基を2つ以上含有する1,6−ヘキサンジオールジグリシジルエーテル、1,4−ブタンジオールジグリシジルエーテル、シクロヘキサンジメタノールジグリシジルエーテル、トリメチロールプロパンポリグリシジルエーテル等のエポキシ系化合物を挙げることができる。
太陽電池モジュール用封止材組成物には、更にその他の成分を含有させることができる。例えば、本発明の太陽電池モジュール用封止材組成物から作製された太陽電池モジュール用封止材に耐候性を付与するための耐候性マスターバッチ、各種フィラー、光安定化剤、紫外線吸収剤、熱安定剤等の成分が例示される。これらの含有量は、その粒子形状、密度等により異なるものではあるが、それぞれ太陽電池モジュール用封止材組成物中に0.001〜5質量%の範囲内であることが好ましい。これらの添加剤を含むことにより、太陽電池モジュール用封止材組成物に対して、長期に亘って安定した機械強度や、黄変やひび割れ等の防止効果等を付与することができる。
ゲル分率(%):架橋後封止材1g秤量し、80メッシュの金網袋に入れる。次いで、ソックスレー抽出器内に金網ごとサンプル投入し、キシレンを沸点下において還流させる。10時間連続抽出したのち、金網ごとサンプルを取出し乾燥処理後秤量し、抽出前後の質量比較を行い残留不溶分の質量%を測定しこれをゲル分率とした。なお、多層フィルムである封止材シートのゲル分率については、全ての層が積層された多層状態のままで、上記処理を行い、得られた測定値を、当該多層の封止材シートのゲル分率とした。
次に、本発明の太陽電池モジュールの一例について、図面を参照しながら説明する。図1は、本発明の太陽電池モジュールについて、その層構成の一例を示す断面図である。本発明の太陽電池モジュール1は、入射光の受光面側から、透明前面基板2、前面封止材層3、太陽電池素子4、背面封止材層5、及び裏面保護シート6が順に積層されている。本発明の太陽電池モジュール1は、前面封止材層3及び背面封止材層5の少なくとも一方に上記の太陽電池モジュール用封止材を使用する。
<太陽電池モジュール用封止材の製造>
(単層フィルム)
下記表1の組成の封止材組成物を混合し単層用のブレンドとした。上記ブレンドをφ30mm押出し機、200mm幅のTダイスを有するフィルム成形機を用いて、押出し温度210℃、引き取り速度1.1m/minで総厚600μmの単層の太陽電池モジュール用封止材を作製した(実施例1〜5、比較例1〜4、参考例1、2)。尚、参考例1、2は、下記多層フィルムにおいてそれぞれ内層用、外層用に用いたフィルムと同組成のものである。
(多層フィルム)
また、下記表2の組成の封止材組成物を混合し3層のフィルムを成型するための内層用及び外層用のブレンドとした。上記ブレンドを、それぞれ、φ30mm押出し機、200mm幅のTダイスを有するフィルム成形機を用いて、押出し温度210℃、引き取り速度1.1m/minでフィルム成型し、それらを積層して、3層の太陽電池モジュール用封止材を作製した。この封止材の層厚は、総厚を600μmとし、外層:内層:外層の厚さの比を1:5:1とした。(実施例6)。
シラン変性透明樹脂(Si):密度0.881g/cm3であり、190℃でのMFRが2g/10分であるメタロセン系直鎖状低密度ポリエチレン(M−LLDPE)98質量部に対して、ビニルトリメトキシシラン2質量部と、ラジカル発生剤(反応触媒)としてのジクミルパーオキサイド0.1質量部とを混合し、200℃で溶融、混練し、密度0.884g/cm3、190℃でのMFRが1.8g/10分であるシラン変性透明樹脂を得た。
耐候性マスターバッチ(耐候):密度0.880g/cm3のチーグラー直鎖状低密度ポリエチレンを粉砕したパウダー100質量部に対して、ベンゾフェノール系紫外線吸収剤3.8質量部とヒンダードアミン系光安定化剤5質量部と、リン系熱安定化剤0.5質量部とを混合して溶融、加工し、ペレット化したマスターバッチを得た。
重合開始剤コンパウンド樹脂1(重合1):密度0.880g/cm3、190℃でのMFRが3.1g/10分のM−LLDPEペレット100質量部に対して、t−アミル−パーオキシ−2−エチルヘキシルカーボネート(重合開始剤A)0.1質量部を含浸させコンパウンドペレットを得た。
重合開始剤コンパウンド樹脂2(重合2):密度0.880g/cm3、190℃でのMFRが2.2g/10分のM−LLDPEペレット100質量部に対して、t−アミル−パーオキシ−2−エチルヘキシルカーボネート(重合開始剤A)0.1質量部を含浸させコンパウンドペレットを得た。
重合開始剤コンパウンド樹脂3(重合3):密度0.880g/cm3、190℃でのMFRが3.1g/10分のM−LLDPEペレット100質量部に対して、t−ブチル−パーオキシ2−エチルヘキシルカーボネート(重合開始剤B)0.1質量部を含浸させコンパウンドペレットを得た。
重合開始剤コンパウンド樹脂4(重合4):密度0.880g/cm3、190℃でのMFRが2.2g/10分のM−LLDPEペレット100質量部に対して、t−ブチル−パーオキシ2−エチルヘキシルカーボネート(重合開始剤B)0.1質量部を含浸させコンパウンドペレットを得た。
重合開始剤コンパウンド樹脂5(重合5):密度0.880g/cm3、190℃でのMFRが3.1g/10分のM−LLDPEペレット100質量部に対して、2,5‐ジメチル‐2,5‐ジ(t‐ブチルパーオキシ)ヘキサン(重合開始剤C)0.032質量部を含浸させコンパウンドペレットを得た。
重合開始剤コンパウンド樹脂6(重合6):密度0.880g/cm3、190℃でのMFRが3.5g/10分のM−LLDPEペレット100質量部に対して、2,5‐ジメチル‐2,5‐ジ(t‐ブチルパーオキシ)ヘキサン(重合開始剤C)0.032質量部を含浸させコンパウンドペレットを得た。
重合開始剤コンパウンド樹脂7(重合7):密度0.880g/cm3、190℃でのMFRが3.5g/10分のM−LLDPEペレット100質量部に対して、2,5‐ジメチル‐2,5‐ジ(t‐ブチルパーオキシ)ヘキサン(重合開始剤C)0.041質量部を含浸させコンパウンドペレットを得た。
M−LLDPE1(ML1):密度0.880g/cm3、190℃でのMFRが3.1g/10分のメタロセン系直鎖状低密度ポリエチレン
M−LLDPE2(ML2):密度0.880g/cm3、190℃でのMFRが1.0g/10分のメタロセン系直鎖状低密度ポリエチレン
M−LLDPE3(ML3):密度0.901g/cm3、190℃でのMFRが2.0g/10分のメタロセン系直鎖状低密度ポリエチレン
上記の方法で作製した実施例1から6、比較例1から3及び参考例1、2の太陽電池モジュール用封止材について、全光線透過率(JIS K6911)、曇度(JIS K6911)、耐熱性試験、成形時の負荷電流の値、及び多層フィルムのモルディング特性について評価した。負荷電流の値が高いことは押出時の負荷が大きいことを意味する。その結果を表3及び4に示す。モルディング特性が良好であることは、モジュール化の際の密着性能に優れることを意味する。
耐熱性試験:250mm角の半強化ガラス上に上記実施例及び比較例の太陽電池モジュール用封止材を75mm×50mmの大きさにカットしたものを2枚、75mm×50mmの半強化ガラス1枚を順に積層した上で、太陽電池モジュールの製造用の真空ラミネータにて150℃で15分間圧着し、上記ラミネートサンプルを45度に傾けた状態で120℃のオーブン中で12時間静置し、半強化ガラスのずれた距離を以って耐熱性の評価を実施した。
密着性試験:150mm四方にカットした実施例6、参考例1〜2の太陽電池モジュール用封止材を150mmの青板ガラス2枚に挟持し、この際、青板ガラスの内側片方に幅10mm、長さ100mm、厚み300μmのアルミテープを張り付けた状態で真空ラミネートを実施。ラミネート後のサンプルを4℃の環境下に1週間静置し、アルミテープの周囲に生ずるデラミネーションの有無を確認した。モルディング特性が弱い場合、ラミネート強度が低いため上記条件でデラミネーションが生じるため、デラミネーションの有無によりモルディング特性の良し悪しを判断した。尚、実施例6、参考例1〜2の太陽電池モジュール用封止材については、MFRの値を予め測定した。
実施例2について、製膜前後においての、密度、MFR、重量平均分子量の変化を測定した結果を表5に示す。
重合開始剤コンパウンド樹脂として、密度0.880g/cm3、190℃でのMFRが3.5g/10分のM−LLDPEペレット100質量部に対して、α,α’−ジ(t−ブチルペロキシ)ジソプロピルベンゾン(重合開始剤D)を0質量部(比較例5)/0.01質量部(比較例6)/0.04質量部(実施例7)/0.05質量部(実施例8)の4水準で含浸させコンパウンドペレットを得て、それぞれのコンパウンド樹脂のみで実施例1と同様にして製膜を行ない、製膜後の190℃におけるMFRを測定した結果を表6に示す。
2 透明前面基板
3 前面封止材層
4 太陽電池素子
5 背面封止材層
6 裏面保護シート
Claims (15)
- 架橋助剤を実質的に含有せず、密度0.900g/cm3以下のポリエチレン系樹脂を90質量%以上含有する樹脂組成物で構成される単層又は多層フィルムであって、
JIS K7210に準拠して測定した190℃、荷重2.16kgにおける前記単層又は多層フィルムのMFRが0.1g/10min以上1.0g/10min未満である太陽電池モジュール用封止材。 - 前記ポリエチレン系樹脂がメタロセン系直鎖状低密度ポリエチレンである請求項1に記載の太陽電池モジュール用封止材。
- 前記ポリエチレン系樹脂がα−オレフィンとエチレン性不飽和シラン化合物とをコモノマーとして共重合してなる共重合体を含有する請求項1又は2に記載の太陽電池モジュール用封止材。
- ゲル分率が25%以下である請求項1から3のいずれかに記載の太陽電池モジュール用封止材。
- ポリスチレン換算の重量平均分子量が12万以上30万以下である請求項1から4のいずれかに記載の太陽電池モジュール用封止材。
- 前記太陽電池モジュール用封止材が、前記MRFの異なる2層以上で構成されている請求項1から5のいずれかに記載の太陽電池モジュール用封止材。
- 前記MRFの高い層が最外層として配置され、前記MFRの低い層が中間層として配置されている請求項6に記載の太陽電池モジュール用封止材。
- 請求項1から7のいずれかに記載の太陽電池モジュール用封止材を使用した太陽電池モジュール。
- 密度0.900g/cm3以下のポリエチレン系樹脂と、組成物中に0.02質量%以上0.5質量%未満含有する重合開始剤と、を含む樹脂組成物を溶融成形する太陽電池モジュール用封止材の製造方法。
- 前記重合開始剤を、前記組成物中に0.02質量%以上0.2%以下含有する請求項9に記載の太陽電池モジュール用封止材の製造方法。
- 前記重合開始剤が有機過酸化物である請求項9又は10に記載の太陽電池モジュール用封止材の製造方法。
- 前記ポリエチレン系樹脂の融点+50℃以上で前記溶融成形を行う請求項9から11のいずれかに記載の太陽電池モジュール用封止材の製造方法。
- 溶融成形前後の前記樹脂組成物の密度差が0.05g/cm3以内であり、
溶融成形前後の前記樹脂組成物のJIS K7210に準拠して測定した190℃、荷重2.16kgにおけるMFR差が1.0g/10min以上である請求項9から12のいずれかに記載の太陽電池モジュール用封止材の製造方法。 - 前記太陽電池モジュール用封止材が、前記重合開始剤の含有量の異なる2層以上で構成されている請求項9から13のいずれかに記載の太陽電池モジュール用封止材の製造方法。
- 前記重合開始剤の含有量の低い層が最外層として配置され、前記重合開始剤の含有量の高い層が中間層として配置されている請求項14に記載の太陽電池モジュール用封止材の製造方法。