JPWO2008015980A1 - 吸水性樹脂粒子、その製造方法、およびそれを用いた吸収体 - Google Patents
吸水性樹脂粒子、その製造方法、およびそれを用いた吸収体Info
- Publication number
- JPWO2008015980A1 JPWO2008015980A1 JP2008527730A JP2008527730A JPWO2008015980A1 JP WO2008015980 A1 JPWO2008015980 A1 JP WO2008015980A1 JP 2008527730 A JP2008527730 A JP 2008527730A JP 2008527730 A JP2008527730 A JP 2008527730A JP WO2008015980 A1 JPWO2008015980 A1 JP WO2008015980A1
- Authority
- JP
- Japan
- Prior art keywords
- water
- absorbent resin
- resin particles
- particle
- absorbent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
特に最近の吸水性樹脂粒子は、その吸水性能を向上させる目的で、例えば、吸水性樹脂粒子の表面層の架橋密度を高めているため、吸水性樹脂粒子の破壊が起こると、架橋密度の低い粒子内部が表面に露出し、顕著な性能低下を引き起こしやすい。
従って、機械的な衝撃に対する粒子強度が高く、吸水性能が低下しない吸水性樹脂粒子が求められている。
本発明は、さらに、上記の吸水性樹脂粒子を用いた吸収体に関する。
1 ビュレット部
10 ビュレット
11 空気導入管
12 コック
13 コック
14 ゴム栓
2 導管
3 測定台
4 測定部
40 円筒
41 ナイロンメッシュ
42 重り
5 吸水性樹脂粒子
Y 衝突試験装置
101 ホッパー
102 加圧空気導入管
103 射出ノズル
104 衝突板
105 流量計
106 吸水性樹脂粒子
本発明の吸水性樹脂粒子の水分率は10〜20%、好ましくは11〜18%、より好ましくは12〜18%である。吸水性樹脂粒子の水分率が10%未満の場合、機械的な衝撃に対して粒子の破壊が起こり易くなり、十分な強度が得られないおそれがある。また、吸水性樹脂粒子の水分率が20%を超える場合、吸水性樹脂の粉体流動性が悪化し、取り扱いが困難になるおそれがある。
なお、吸水性樹脂粒子の水分率は、後述する「(1)水分率」に記載されている測定方法に従って測定したときの値である。
なお、吸水性樹脂粒子の粒子衝突試験前後における粒子径保持率は、後述する「(6)粒子衝突試験前後における粒子径保持率」に記載されている測定方法に従って測定したときの値である。
なお、吸水性樹脂粒子の粒子衝突試験前後における加圧吸水能保持率は、後述する「(7)粒子衝突試験前後における加圧吸水能保持率」に記載されている測定方法に従って測定したときの値である。
水溶性エチレン性不飽和単量体水溶液の濃度は、20質量%〜飽和濃度であることが好ましい。
また、水溶性ラジカル重合開始剤と亜硫酸塩、L−アスコルビン酸、硫酸第一鉄等と併用することにより、レドックス系重合開始剤として用いることもできる。
これらの中では、入手が容易で保存安定性が良好である観点から、過硫酸カリウム、過硫酸アンモニウムおよび過硫酸ナトリウムが好ましい。
なお、吸水性樹脂粒子の質量平均粒子径は、後述する「(5)質量平均粒子径」に記載されている測定方法に従って測定したときの値である。
また、吸水性樹脂粒子に非晶質シリカ粒子を添加することにより、粒子間に間隙ができ、吸収液の浸透性が改善される。
吸収体の密度は、0.1〜0.5g/cm3であることが好ましく、0.2〜0.4g/cm3であることがより好ましい。
内容積500mlの三角フラスコに80質量%のアクリル酸水溶液92gを入れ、氷冷しながら20.0質量%水酸化ナトリウム水溶液154.1gを滴下してアクリル酸の中和を行い、アクリル酸部分中和塩水溶液を調製した。得られたアクリル酸部分中和塩水溶液に、架橋剤としてN,N’−メチレンビスアクリルアミド9.2mgおよび水溶性ラジカル重合開始剤として過硫酸カリウム0.11gを添加し、これを単量体水溶液とした。
一方、攪拌機、2段パドル翼、還流冷却器、滴下ロートおよび窒素ガス導入管を備えた内容積2リットルの五つ口円筒型丸底フラスコに、n−ヘプタン340gと、界面活性剤として、ショ糖ステアリン酸エステル(三菱化学フーズ株式会社の商品名;リョートーシュガーエステルS−370)0.92gを加えてn−ヘプタンに溶解させた後、上記の重合用の単量体水溶液を加えて35℃に保ち攪拌下で懸濁した。その後、系内を窒素で置換後、70℃の水浴を用いて昇温して逆相懸濁重合を行った。
第1段目の逆相懸濁重合の終了後、重合スラリーを冷却し、第2段目重合用の単量体水溶液を系内に滴下し、23℃に保ちながら30分間攪拌を行った。その後、系内を窒素で置換し、70℃の水浴を用いて昇温して第2段目の逆相懸濁重合を行った。重合終了後、120℃の油浴で加熱し、共沸蒸留により、266gの水を系外に除去し、2質量%エチレングリコールジグリシジルエーテル水溶液8.83gを添加し、80℃で2時間保持し、後架橋処理を行った。さらに水およびn−ヘプタンを蒸留により除去して乾燥し、質量平均粒子径が360μm、水分率5%の吸水性樹脂粒子227.2gを得た。
製造例1と同様にして得られた吸水性樹脂粒子200gに非晶質シリカ粒子1g((株)トクヤマ製、トクシールNP)を添加、混合後、内容積2リットルのセパラブルフラスコに入れ、撹拌しながら室温下、加湿機((株)トヨトミ製、ハイブリッド加湿器)により水添加量0.4L/hで20分間、セパラブルフラスコ内を加湿し、水分率11%の吸水性樹脂を得た。
製造例1と同様にして得られた吸水性樹脂粒子200gに非晶質シリカ粒子1g((株)トクヤマ製、ファインシールT−32)を添加、混合後、内容積2リットルのセパラブルフラスコに入れ、撹拌しながら室温下、加湿機((株)トヨトミ製、ハイブリッド加湿器)により水添加量0.4L/hで30分間、セパラブルフラスコ内を加湿し、水分率13%の吸水性樹脂を得た。
製造例1と同様にして得られた吸水性樹脂粒子200gに非晶質シリカ粒子2g((株)トクヤマ製、トクシールNP)を添加、混合後、内容積2リットルのセパラブルフラスコに入れ、撹拌しながら室温下、加湿機((株)トヨトミ製、ハイブリッド加湿器)により水添加量0.4L/hで45分間、セパラブルフラスコ内を加湿し、水分率17%の吸水性樹脂粒子を得た。
製造例1と同様にして第1段目および第2段目の逆相懸濁重合を行った。重合終了後、120℃の油浴で加熱し、共沸蒸留により、255gの水を系外に除去し、2質量%エチレングリコールジグリシジルエーテル水溶液4.43gを添加し、80℃で2時間保持し、架橋処理を行った。さらに水およびn−ヘプタンを蒸留により除去して乾燥し、非晶質シリカ粒子1.5g((株)トクヤマ製、トクシールNP)を添加、混合することにより、質量平均粒子径が370μm、水分率13%の吸水性樹脂粒子233.5gを得た。
製造例1と同様にして水分率5%の吸水性樹脂粒子を得た。
製造例1と同様にして得られた吸水性樹脂粒子200gを内容積2リットルのセパラブルフラスコに入れ、撹拌しながら室温下、加湿機((株)トヨトミ製、ハイブリッド加湿器)により水添加量0.4L/hで15分間、セパラブルフラスコ内を加湿し、水分率8%の吸水性樹脂を得た。
製造例1と同様にして得られた吸水性樹脂粒子200gを内容積2リットルのセパラブルフラスコに入れ、撹拌しながら室温下、加湿機((株)トヨトミ製、ハイブリッド加湿器)により水添加量0.4L/hで45分間、セパラブルフラスコ内を加湿し、水分率17%の吸水性樹脂を得た。この吸水性樹脂は、粘着性を有しており粉体の流動性が悪く、粒度分布の測定、後述する衝突試験および吸収体コアの作成が不可能であった。
製造例1と同様にして得られた吸水性樹脂粒子200gを内容積2リットルのセパラブルフラスコに入れ、撹拌しながら室温下加湿機((株)トヨトミ製、ハイブリッド加湿器)により水添加量0.4L/hで60分間、セパラブルフラスコ内を加湿し、水分率23%の吸水性樹脂を得た。この吸水性樹脂は、粘着性を有しており粉体の流動性が悪く、粒度分布の測定、後述する衝突試験および吸収体コアの作成が不可能であった。
吸水性樹脂粒子2gを、あらかじめ恒量(Wa(g))としたアルミホイールケース(8号)にとり精秤した(Wd(g))。上記サンプルを、内温を105℃に設定した熱風乾燥機(ADVANTEC社製)で2時間乾燥させた後、デシケーター中で放冷して、乾燥後の質量We(g)を測定した。以下の式から、吸水性樹脂粒子の水分率を算出した。
水分率(%)=[(Wd−Wa)−(We−Wa)]/(Wd−Wa)×100
吸水性樹脂粒子2.00gを、綿袋(メンブロード60番、横100mm×縦200mm)に入れ、500mLのビーカー内に入れた。この綿袋内に生理食塩水500gを注ぎ込み、開口部を輪ゴムで縛り、1時間放置した。その後、遠心力167Gの脱水機(国産遠心機(株)製、品番H−122)を用いて、前記綿袋を1分間脱水し、脱水後の膨潤ゲルを含んだ綿袋の質量Wa(g)を測定した。吸水性樹脂を添加せずに同様の操作を行い、綿袋の湿潤時空質量Wb(g)を測定し、次式により生理食塩水保水能を算出した。
生理食塩水保水能(g/g)=[Wa−Wb](g)/2.00(g)
100mlのビーカーに、25±0.2℃の温度の生理食塩水50±0.1gを入れ、マグネチックスターラーバー(8mmφ×30mm)を用いて、600rpmになるように調整した。次に吸水性樹脂2.0±0.002gを前記ビーカーに素早く添加し、添加し終わると同時にストップウォッチをスタートした。吸水性樹脂が生理食塩水を吸水し、渦がなくなるまでの時間(秒)をストップウォッチで測定し、吸水速度とした。
吸水性樹脂粒子の加圧吸水能は、図1に概略を示した測定装置Xを用いて測定した。
図1に示した測定装置Xは、ビュレット部1と導管2、測定台3、測定台3上に置かれた測定部4からなっている。ビュレット部1は、ビュレット10の上部にゴム栓14、下部に吸気導入管11とコック12が連結されており、さらに、吸気導入管11は先端にコック13を有している。ビュレット部1から測定台3までは、導管2が取り付けられており、導管2の直径は6mmである。測定台3の中央部には、直径2mmの穴があいており、導管2が連結されている。測定部4は、円筒40と、この円筒40の底部に貼着されたナイロンメッシュ41と、重り42とを有している。円筒40の内径は、20mmである。ナイロンメッシュ41は、200メッシュ(目開き75μm)に形成されている。そして、ナイロンメッシュ41上に所定量の吸水性樹脂粒子5が均一に撒布されるようになっている。重り42は、直径19mm、質量59.8gである。この重りは、吸水性樹脂粒子5上に置かれ、吸水性樹脂粒子5に対して2.07kPaの荷重を加えることができるようになっている。
次に、測定台3中心部の導管口から出てくる0.9質量%食塩水の水面と、測定台3の上面とが同じ高さになるように測定台3の高さの調整を行う。
吸水性樹脂粒子5が吸水し始めた時点から継続的に、ビュレット10内の0.9質量%食塩水の減少量(すなわち、吸水性樹脂粒子5が吸水した0.9質量%食塩水量)Wc(ml)を読み取る。吸水開始から60分間経過後における吸水性樹脂粒子5の加圧吸水能は、以下の式により求めた。
加圧吸水能(ml/g)=Wc÷0.10
JIS標準篩を上から、目開き500μm(30メッシュ)、目開き355μm(42メッシュ)、目開き300μm(50メッシュ)、目開き250μm(60メッシュ)、目開き150μm(100メッシュ)、目開き75μm(200メッシュ)、受け皿の順に組み合わせ、最上の篩に吸水性樹脂約100gを入れ、ロータップ式振とう器を用いて、20分間振とうさせた。
次に、各篩上に残った吸水性樹脂の質量を全量に対する質量百分率として計算し、粒子径の大きい方から順に積算することにより、篩の目開きと篩上に残った質量百分率の積算値との関係を対数確率紙にプロットした。確率紙上のプロットを直線で結ぶことにより、積算質量百分率50質量%に相当する粒子径を質量平均粒子径とした。
吸水性樹脂粒子の粒子衝突試験における粒子径保持率は、図2に概略を示した試験装置Yを用いて、吸水性樹脂粒子を衝突板に衝突させた時、その粒子径分布を測定することにより求めた。
得られた測定値を用いて、粒子衝突試験前後の粒子径保持率を次式により求めた。
粒子衝突試験前後の粒子径保持率(%)=[A2÷A1]×100
吸水性樹脂粒子100gを、前記「(6)粒子衝突試験前後の粒子径保持率」に記載の方法にしたがって、粒子衝突試験に供した。
回収した吸水性樹脂粒子を用いて、加圧吸水能を前記の方法にしたがって測定し、粒子衝突試験後の加圧吸水能(B2)を求めた。
あらかじめ、粒子衝突試験前に測定した加圧吸水能(B1)と粒子衝突試験後の加圧吸水能(B2)とから、粒子衝突試験前後の加圧吸水能保持率を次式により求めた。
粒子衝突試験前後の加圧吸水能保持率(%)=[B2÷B1]×100
実施例1の粒子衝突試験後の吸水性樹脂粒子8gと粉砕パルプ(レオニア社製レイフロック)12gを用い、空気抄造によって均一混合することにより、42cm×12cmの大きさのシート状の吸収体コアを作製した。
次に、吸収体コアの上下を坪量16g/m2のティッシュッペーパーではさんだ状態で、ロールプレスを用いて圧縮することにより、密度0.2g/cm3の吸収体を作製した。
さらに吸収体の上面に坪量22g/m2のポリエチレン不織布のトップシート(レンゴー製)を置き試験用吸収体とした。
実施例5において、実施例2の粒子衝突試験後の吸水性樹脂粒子を用いた以外は、実施例5と同様にして試験用吸収体を得た。
実施例5において、比較例1の粒子衝突試験後の吸水性樹脂粒子を用いた以外は、実施例5と同様にして試験用吸収体を得た。
実施例3の粒子衝突試験後の吸水性樹脂粒子12gと粉砕パルプ(レオニア社製レイフロック)8gを用い、空気抄造によって均一混合することにより、42cm×12cmの大きさのシート状の吸収体コアを作製した。
次に吸収体の上下を坪量16g/m2のティッシュッペーパーではさんだ状態で、ロールプレスを用いて圧縮することにより、密度0.4g/cm3の吸収体を作製した。
さらに吸収体の上面に坪量22g/m2のポリエチレン不織布のトップシート(レンゴー社製)を置き試験用吸収体とした。
実施例7において、実施例4の粒子衝突試験後の吸水性樹脂粒子を用いた以外は、実施例7と同様にして試験用吸収体を得た。
実施例7において、比較例2の粒子衝突試験後の吸水性樹脂粒子を用いた以外は、実施例7と同様にして試験用吸収体を得た。
吸収体の質量と厚みから以下の計算式により吸収体密度を算出した。
なお、吸収体の厚みは、厚み計((株)尾崎製作所製PEACOCK J−B)を用いて測定した。
吸収体密度(g/cm3)=吸収体質量(g)/(吸収体面積(cm2)×厚み(cm))
試験用吸収体を45度傾斜台に貼り付け、貼り付けた試験用吸収体の上端より10cm、左右中心の場所に、試験用吸収体から上方へ2cmに設置したビュレットにより70mlの人工尿を10秒で滴下する。滴下と同時にストップウォッチをスタートさせ、10分後にビュレットより再び人工尿70mlを滴下する。この操作を繰返し、下端より試験液が漏れるまでの液吸収量を測定した。
Claims (6)
- 水溶性エチレン性不飽和単量体を水溶性ラジカル重合開始剤を用いて、要すれば架橋剤の存在下に重合し、吸水性樹脂粒子前駆体を得た後、後架橋剤を添加して粒子の表面層を架橋し、非晶質シリカ粒子を添加して得られる吸水性樹脂粒子であって、水分率が10〜20%であり、粒子衝突試験前後における粒子径保持率が90%以上であることを特徴とする吸水性樹脂粒子。
- 粒子衝突試験前後における加圧吸水能保持率が60%以上であることを特徴とする請求項1記載の吸水性樹脂粒子。
- 水溶性エチレン性不飽和単量体を水溶性ラジカル重合開始剤を用いて、要すれば架橋剤の存在下に重合し、吸水性樹脂粒子前駆体を得た後、後架橋剤を添加して前記粒子の表面層を架橋し、非晶質シリカ粒子を添加して得られる吸水性樹脂粒子の水分率を10〜20%に調整することを特徴とする、粒子衝突試験前後における粒子径保持率が90%以上である吸水性樹脂粒子の製造方法。
- 請求項1または2に記載の吸水性樹脂粒子と親水性繊維と透水性シートからなる吸収体。
- 吸収体における密度が0.1〜0.5g/cm3である請求項4記載の吸収体。
- 吸収体における吸水性樹脂粒子と親水性繊維との割合が、30:70〜80:20の質量比である請求項4または5記載の吸収体。