JPS6362793A - 光記録媒体 - Google Patents
光記録媒体Info
- Publication number
- JPS6362793A JPS6362793A JP61205868A JP20586886A JPS6362793A JP S6362793 A JPS6362793 A JP S6362793A JP 61205868 A JP61205868 A JP 61205868A JP 20586886 A JP20586886 A JP 20586886A JP S6362793 A JPS6362793 A JP S6362793A
- Authority
- JP
- Japan
- Prior art keywords
- recording
- layer
- recording medium
- optical recording
- metal fine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
［産業上の利用分野］
本発明は光記録媒体に関し、特にレーザー光によって情
報を記録し、すぐにその情報を再生できる、いわゆるＤ
ＲＡＷ （ダイレクト リード アフター ライト；
Ｄｉｒｅｃｔ Ｒｅａｄ Ａｆｔｅｒ Ｗｒｉｔｅ）型
光記録媒体に関するものである。
報を記録し、すぐにその情報を再生できる、いわゆるＤ
ＲＡＷ （ダイレクト リード アフター ライト；
Ｄｉｒｅｃｔ Ｒｅａｄ Ａｆｔｅｒ Ｗｒｉｔｅ）型
光記録媒体に関するものである。
［従来の技術］
従来、レーザー光で情報を記録・再生するＤＲＡ！＃型
光記録媒体として、基板上に低融点金属＠ＳＳを設け、
これに記録情報信号によって変調したレーザー光を照射
して、この情報に応じた局部的加熱によって低融点金属
薄膜層を溶融ないしは蒸発させ、ここに穴部、すなわち
記録ビットを形成するようにした形状変化による記録を
行う光記録媒体が提案されている。
光記録媒体として、基板上に低融点金属＠ＳＳを設け、
これに記録情報信号によって変調したレーザー光を照射
して、この情報に応じた局部的加熱によって低融点金属
薄膜層を溶融ないしは蒸発させ、ここに穴部、すなわち
記録ビットを形成するようにした形状変化による記録を
行う光記録媒体が提案されている。
しかしながら、このような記録ビットを形成するものは
、その書き込みに大きなパワーを必要とし、記録感度が
低いという欠点を有していた。さらに、記録時に金属層
の溶融・蒸発によりビットを形成する際、この形状変化
を許容する空間、すなわち例えばビットを形成するに伴
うビット周縁における金属の表面張力による盛り上がり
（以下、「リム」と称す）を許容する空間が必要である
ので、光記録媒体を実装する際に貼り合わせ構造をとる
ことができないという欠点があった。
、その書き込みに大きなパワーを必要とし、記録感度が
低いという欠点を有していた。さらに、記録時に金属層
の溶融・蒸発によりビットを形成する際、この形状変化
を許容する空間、すなわち例えばビットを形成するに伴
うビット周縁における金属の表面張力による盛り上がり
（以下、「リム」と称す）を許容する空間が必要である
ので、光記録媒体を実装する際に貼り合わせ構造をとる
ことができないという欠点があった。
［発明が解決しようとする問題点］
本発明は、レーザー光によって情報を記録・再生するＤ
ＲＡ’Ｗ型光記録媒体において、記録感度を向上させ、
かつ貼り合わせ構造が可能な光記録媒体を提供すること
を目的とする。
ＲＡ’Ｗ型光記録媒体において、記録感度を向上させ、
かつ貼り合わせ構造が可能な光記録媒体を提供すること
を目的とする。
［問題点を解決するための手段］
即ち、本発明はレーザー光によって情報を記録・再生す
る光記録媒体において、記録層が情報を記録するレーザ
ー光の照射により被照射部が溶融して平滑化される金属
微粒子層からなることを特徴とする光記録媒体である。
る光記録媒体において、記録層が情報を記録するレーザ
ー光の照射により被照射部が溶融して平滑化される金属
微粒子層からなることを特徴とする光記録媒体である。
以下、本発明の詳細な説明する。
本発明の光記録媒体は記録層が金属微粒子層からなり、
レーザー光を照射することにより１局所的に前記金属微
粒子層を溶融・平滑化して情報を記録することを特徴と
するものである。
レーザー光を照射することにより１局所的に前記金属微
粒子層を溶融・平滑化して情報を記録することを特徴と
するものである。
本発明におい１、前記記録層の金属微粒子層を構成する
金属は、Ｔｅ、 Ｂｉ、 Ｉｎ、 Ｓｅ、 Ｓｎ、 Ｚ
ｎ、 Ｔｉ）およびＰｂ等の低融点金属のうちの少なく
とも１種を含有するものからなる。
金属は、Ｔｅ、 Ｂｉ、 Ｉｎ、 Ｓｅ、 Ｓｎ、 Ｚ
ｎ、 Ｔｉ）およびＰｂ等の低融点金属のうちの少なく
とも１種を含有するものからなる。
本発明による光記録媒体における記録・再生の方法を模
式図を用いて説明する。第１図は本発明の光記録媒体の
一例を示す断面図である。同第１図において、本発明の
光記録媒体はガラス基板ｌ上に、上述した低融点金属を
含有する金属微粒子層からなる記ＱＭ２を形成し、さら
に必要に応じて保存安定性を向上させるために保護層３
を積層してなるものである。
式図を用いて説明する。第１図は本発明の光記録媒体の
一例を示す断面図である。同第１図において、本発明の
光記録媒体はガラス基板ｌ上に、上述した低融点金属を
含有する金属微粒子層からなる記ＱＭ２を形成し、さら
に必要に応じて保存安定性を向上させるために保護層３
を積層してなるものである。
上述した低融点金属の微粒子を含有する記録層の形成に
は種々の方法を行うことができる。その−例としては５
例えば機械的粉砕法や蒸発法などにより、まず所望の粒
径をもつ低融点金属の微粒子を形成し、この低融点金属
の微粒子を有機高分子化合物や有機溶剤に分散或は溶解
させたものをガラス、プラスチック等の基板上にスピン
コード法、バーコード法、ロールコート法等により塗布
する形成方法がある。なお、蒸発法とは真空に引いた容
器内にＡｒやｌｉｅなどの不活性ガスを封入し、容器内
の金属を加熱して蒸発させ、蒸発した金属原子が不活性
ガス分子に衝突し冷えて凝集することを利用した金属微
粒子形成方法であり、不活性ガスのガス圧等を調整する
ことにより粒径を制御することができる。
は種々の方法を行うことができる。その−例としては５
例えば機械的粉砕法や蒸発法などにより、まず所望の粒
径をもつ低融点金属の微粒子を形成し、この低融点金属
の微粒子を有機高分子化合物や有機溶剤に分散或は溶解
させたものをガラス、プラスチック等の基板上にスピン
コード法、バーコード法、ロールコート法等により塗布
する形成方法がある。なお、蒸発法とは真空に引いた容
器内にＡｒやｌｉｅなどの不活性ガスを封入し、容器内
の金属を加熱して蒸発させ、蒸発した金属原子が不活性
ガス分子に衝突し冷えて凝集することを利用した金属微
粒子形成方法であり、不活性ガスのガス圧等を調整する
ことにより粒径を制御することができる。
次に、本発明の光記録媒体における記録・再生の方法に
ついて説明する。
ついて説明する。
上記の様に形成された本発明の光記録媒体の記録層に記
録用のレーザー光を照射すると、金属微粒子層のレーザ
ー照射部の表面あるいは被照射部の全体が溶融し、記録
層の表面は平滑になり記録ビットが形成される。非記録
部は金属微粒子の表面散乱によフて反射率が低下してい
るのに比べ、前記記録ビット部は表面が平滑化されてい
るため反射率が高くなり、再生用レーザー光により反射
光量の大・小で記録ビットの有・無を読み出すことが可
能となる。
録用のレーザー光を照射すると、金属微粒子層のレーザ
ー照射部の表面あるいは被照射部の全体が溶融し、記録
層の表面は平滑になり記録ビットが形成される。非記録
部は金属微粒子の表面散乱によフて反射率が低下してい
るのに比べ、前記記録ビット部は表面が平滑化されてい
るため反射率が高くなり、再生用レーザー光により反射
光量の大・小で記録ビットの有・無を読み出すことが可
能となる。
本発明の光記録媒体への情報の記録方法においては、低
融点金属の金属微粒子層の表面を溶融させるだけでよい
ので、ビット形成時よりも低い記録パワーで記録が可能
となる。
融点金属の金属微粒子層の表面を溶融させるだけでよい
ので、ビット形成時よりも低い記録パワーで記録が可能
となる。
本発明の記録層に用いられる金属微粒子の粒径は、１０
０ Ａ−１００，０００Ａが適し、特に１００ＯＡ〜５
０．０ＯＯＡが好ましい。１００ Ａ未満では金属微粒
子の表面散乱による反射率の低下が充分におこらず、ま
たｔｏｏ、ｏｏｏ Ａをこえると記録ビットの形状が悪
くなるため適さない。
０ Ａ−１００，０００Ａが適し、特に１００ＯＡ〜５
０．０ＯＯＡが好ましい。１００ Ａ未満では金属微粒
子の表面散乱による反射率の低下が充分におこらず、ま
たｔｏｏ、ｏｏｏ Ａをこえると記録ビットの形状が悪
くなるため適さない。
本発明の光記録媒体に用いられる基板としては、ガラス
の他に、紙や鉄、アルミニウム、スズ、銅、亜鉛などの
金属、あるいはポリメタアクリル系樹脂、ポリスチレン
系樹脂、ポリビニルエステル系樹脂、ポリ塩化ビニル系
樹脂、ポリオレフィン系樹脂、ポリブチラール系樹脂、
ポリカーボネート系樹脂、ポリエステル系樹脂、ポリア
ミド系樹脂、ポリイミド系樹脂、ポリウレタン系樹脂、
ボリアリレート系樹脂、エポキシ系樹脂、フェノキシ樹
脂、セルロース系樹脂、不飽和ポリエステル系樹脂など
の有機系樹脂などが用いられ、通常０．０１ｍｍ〜１０
ｍｍ程度の厚さで、使用する形態、例えばディスク、カ
ード、テープ等の形態に応じて所望の形状や大きさに成
形されたものを使用することができる。
の他に、紙や鉄、アルミニウム、スズ、銅、亜鉛などの
金属、あるいはポリメタアクリル系樹脂、ポリスチレン
系樹脂、ポリビニルエステル系樹脂、ポリ塩化ビニル系
樹脂、ポリオレフィン系樹脂、ポリブチラール系樹脂、
ポリカーボネート系樹脂、ポリエステル系樹脂、ポリア
ミド系樹脂、ポリイミド系樹脂、ポリウレタン系樹脂、
ボリアリレート系樹脂、エポキシ系樹脂、フェノキシ樹
脂、セルロース系樹脂、不飽和ポリエステル系樹脂など
の有機系樹脂などが用いられ、通常０．０１ｍｍ〜１０
ｍｍ程度の厚さで、使用する形態、例えばディスク、カ
ード、テープ等の形態に応じて所望の形状や大きさに成
形されたものを使用することができる。
また、保護層は金属微粒子金属層の保存安定性を向上さ
せることを目的とし、具体的にはＴｉ１２＊ＡＲ２０３
，ＳｉＯ２，Ｓｉｎ、 Ａｊ）Ｎ、 ＭｇＦｚ、 ５ｉ
３Ｎｓ、 ＺｎＳ。
せることを目的とし、具体的にはＴｉ１２＊ＡＲ２０３
，ＳｉＯ２，Ｓｉｎ、 Ａｊ）Ｎ、 ＭｇＦｚ、 ５ｉ
３Ｎｓ、 ＺｎＳ。
ＺｒＯ２，↑ａ２０５ 、 ＨｆＯ２、Ｎｂ２Ｏ５等か
らなる透明誘電体やＡｌ、 Ｃｕ、 Ｘｉ、 Ｃｒ、
Ｔｉ、 Ｎｏ、 Ｗ、 Ｔａ等の金属を用いることがで
きる。
らなる透明誘電体やＡｌ、 Ｃｕ、 Ｘｉ、 Ｃｒ、
Ｔｉ、 Ｎｏ、 Ｗ、 Ｔａ等の金属を用いることがで
きる。
また、基板に金属保護層を用いる場合は、基板として透
明基板を用いて情報の記録・再生は基板側から行う、こ
れらの保護層は、高周波スパッタ法、直流スパッタ法、
イオンビームスパッタ法、イオンブレーティング法ある
いはエレクトロンビーム法等の各製膜法により形成され
る。
明基板を用いて情報の記録・再生は基板側から行う、こ
れらの保護層は、高周波スパッタ法、直流スパッタ法、
イオンビームスパッタ法、イオンブレーティング法ある
いはエレクトロンビーム法等の各製膜法により形成され
る。
［作 用］
本発明の光記録媒体は記録層が情報を記録するレーザー
光の照射により被照射部が溶融して平滑化される金属微
粒子層からなるので、レーザー光によって情報の記録を
行うと被照射部は溶融・平滑化され、通常のビット記録
の様なリムを形成する空間を必要としないためエアーサ
ンドウィッチ構造をとる必要はなく、貼り合わせ構造を
とることができる。
光の照射により被照射部が溶融して平滑化される金属微
粒子層からなるので、レーザー光によって情報の記録を
行うと被照射部は溶融・平滑化され、通常のビット記録
の様なリムを形成する空間を必要としないためエアーサ
ンドウィッチ構造をとる必要はなく、貼り合わせ構造を
とることができる。
［実施例］
以下に実施例を示して、本発明をさらに詳細に説明する
。
。
実施例１
厚さ１ＩＩＩｌのガラス基板上に、蒸発法により作製し
た粒径的３００ＯＡのＴｅ微粒子を塗布することにより
厚さ１０，０ＯＯＡのＴｅ微粒子記録層を形成し、その
上に真空蒸着装置を用いてＳｉＯ□保護膜を′ｍ層して
光記録媒体を作製した。
た粒径的３００ＯＡのＴｅ微粒子を塗布することにより
厚さ１０，０ＯＯＡのＴｅ微粒子記録層を形成し、その
上に真空蒸着装置を用いてＳｉＯ□保護膜を′ｍ層して
光記録媒体を作製した。
この光記録媒体に波長８３００Ａの半導体レーザーを使
用して、記録媒体面上５！ＩＷのパワーて、ビーム径２
ｇ１１に集光した記録用レーザー光をガラス基板側から
照射したところ、直径３！１１のビットが記録された。
用して、記録媒体面上５！ＩＷのパワーて、ビーム径２
ｇ１１に集光した記録用レーザー光をガラス基板側から
照射したところ、直径３！１１のビットが記録された。
記録ビット部の面は平滑で、反射率は非記録部に比べて
５％以上高い値が得られた。
５％以上高い値が得られた。
実施例２
実施例１と同様な方法で、ポリカーボネイトＣＰＣ）、
２！ｉ板上に粒子径１０，０ＯＯＡの厚さ３０，０ＯＯ
ＡのＢｉ粒子居を形成し、その上に５ｉｎ２保護膜を積
層した光記録媒体を２個作製し、両者の記録層をはさみ
込む様にして、接着剤を用いて第２図に示す様な貼り合
わせ構造の光記録媒体を作成した。第２図中の１が基板
、２が記録層、４が接着層である。
２！ｉ板上に粒子径１０，０ＯＯＡの厚さ３０，０ＯＯ
ＡのＢｉ粒子居を形成し、その上に５ｉｎ２保護膜を積
層した光記録媒体を２個作製し、両者の記録層をはさみ
込む様にして、接着剤を用いて第２図に示す様な貼り合
わせ構造の光記録媒体を作成した。第２図中の１が基板
、２が記録層、４が接着層である。
この光記録媒体に波長８３００Ａの半導体レーザーによ
り、記録媒体面上４ｍ９１のパワーで、ビーム径３ｇｃ
ｍに集光した記録用レーザー光をＰＣ基板側から照射し
たところ、直径５終１のビットが記録され、記録ビット
部の反射率は非記録部に比べて８％以上高い値が得られ
た。
り、記録媒体面上４ｍ９１のパワーで、ビーム径３ｇｃ
ｍに集光した記録用レーザー光をＰＣ基板側から照射し
たところ、直径５終１のビットが記録され、記録ビット
部の反射率は非記録部に比べて８％以上高い値が得られ
た。
［発明の効果］
以上、説明した様に、本発明の光記録媒体は、ＤＲＡＷ
型光記録媒体の記録層として低融点金属を含有する金属
微粒子層を用いることによって、記録感度を向上させ、
かつ貼り合わせ構造が回部な光記録媒体を提供すること
ができる優れた効果がある。
型光記録媒体の記録層として低融点金属を含有する金属
微粒子層を用いることによって、記録感度を向上させ、
かつ貼り合わせ構造が回部な光記録媒体を提供すること
ができる優れた効果がある。
第１図は本発明の光記録媒体の一例を示す断面図および
第２図は他の例を示す断面図である。
第２図は他の例を示す断面図である。
Claims (2)
- （１）レーザー光によって情報を記録・再生する光記録
媒体において、記録層が情報を記録するレーザー光の照
射により被照射部が溶融して平滑化される金属微粒子層
からなることを特徴とする光記録媒体。 - （２）前記金属微粒子層は、Ｔｅ、Ｂｉ、Ｉｎ、Ｓｅ、
Ｓｎ、Ｚｎ、ＴｌおよびＰｂ等の低融点金属のうちの少
なくとも１種を含有する特許請求の範囲第１項記載の光
記録媒体。（３）前記金属微粒子層が粒径１００Å〜１
００，０００Åの金属微粒子から構成される特許請求の
範囲第１項記載の光記録媒体。