JPS63160167A - アルカリ蓄電池用カドミウム陰極板の製造方法 - Google Patents
アルカリ蓄電池用カドミウム陰極板の製造方法Info
- Publication number
- JPS63160167A JPS63160167A JP61313847A JP31384786A JPS63160167A JP S63160167 A JPS63160167 A JP S63160167A JP 61313847 A JP61313847 A JP 61313847A JP 31384786 A JP31384786 A JP 31384786A JP S63160167 A JPS63160167 A JP S63160167A
- Authority
- JP
- Japan
- Prior art keywords
- paste
- active material
- short fibers
- cadmium
- anode plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
産業上の利用分野
本発明はポリビニルアルコールやカルボキシメチルセル
ロースなどの粘着剤の水溶液または有機溶剤溶液と酸化
カドミウムを主成分とする活物質を混練してペースト状
となし、これを金網 属やなどの多孔基板に塗着し乾燥するアルカリ蓄電池用
カドミウム陰極板の製造方法に関するものである。
ロースなどの粘着剤の水溶液または有機溶剤溶液と酸化
カドミウムを主成分とする活物質を混練してペースト状
となし、これを金網 属やなどの多孔基板に塗着し乾燥するアルカリ蓄電池用
カドミウム陰極板の製造方法に関するものである。
従来の技術
従来アルカリ蓄電池用の陰極板としては、ニッケル粉末
を焼結した基板に活物質を充填した焼結式極板、酸化カ
ドミウムを主成分とする活物質成型体をニッケルメッキ
した多孔性の鉄製容器で被覆したポケット式極板などが
用いられていた。
を焼結した基板に活物質を充填した焼結式極板、酸化カ
ドミウムを主成分とする活物質成型体をニッケルメッキ
した多孔性の鉄製容器で被覆したポケット式極板などが
用いられていた。
しかしながら、焼結式極板は薄形極板が得られるので高
率放電特性が優れている反面、極板中に占めるニッケル
焼結基板の重量、体積が大きく、重量効率や容積効率が
悪い欠点を有している。また、ポケット式極板は厚いた
め活物質の利用率が低く、容積効率が低い欠点を有して
いる。
率放電特性が優れている反面、極板中に占めるニッケル
焼結基板の重量、体積が大きく、重量効率や容積効率が
悪い欠点を有している。また、ポケット式極板は厚いた
め活物質の利用率が低く、容積効率が低い欠点を有して
いる。
このため、これらの欠点を除去すべくペースト式極板が
提案されている。このペース式極板は、酸化カドミウム
を主成分とする活物質を粘着剤溶液で混練してペースト
状となし、これをパンチングメタルなどの金属多孔板に
塗着後乾燥して得られる。
提案されている。このペース式極板は、酸化カドミウム
を主成分とする活物質を粘着剤溶液で混練してペースト
状となし、これをパンチングメタルなどの金属多孔板に
塗着後乾燥して得られる。
発明が解決しようとする問題点
しかしながら、ペースト式陰極板は焼結式極板のように
ニッケル焼結体からなる集電体構造を有していないので
、充放電を綴り返し行ったり、放電状態で放置しておく
としだいに活物質粒子が粗大化、あるいは不活性化して
しまうため充電されにくくなるといった欠点を有してい
た。
ニッケル焼結体からなる集電体構造を有していないので
、充放電を綴り返し行ったり、放電状態で放置しておく
としだいに活物質粒子が粗大化、あるいは不活性化して
しまうため充電されにくくなるといった欠点を有してい
た。
問題点を解決するための手段
本発明は上記の如き欠点を除去するもので。
カルシウム化合物の微粉末を含有せるポリオレフィン系
の微多孔短繊維と酸化カドミウムを主成分とする活物質
との粘着剤溶液で混練したペーストを多孔基板に塗着乾
燥して目的の極板を得るものである。
の微多孔短繊維と酸化カドミウムを主成分とする活物質
との粘着剤溶液で混練したペーストを多孔基板に塗着乾
燥して目的の極板を得るものである。
作用
ペースト式カドミウム陰極板の活物質粒子が、ポリオレ
フィン系の微多孔短繊維から溶出したカルシウムイオン
の作用（詳細な作用機構は不明）により、充放電を繰返
し行ったり、放電状態で放置しても粗大化しにくくなり
、充電性が向上する。
フィン系の微多孔短繊維から溶出したカルシウムイオン
の作用（詳細な作用機構は不明）により、充放電を繰返
し行ったり、放電状態で放置しても粗大化しにくくなり
、充電性が向上する。
実施例
ペレット状の低密度ポリエチレン２５重量部とシリカ微
粉末２０重量部、水酸化カルシウムの微粉末５重量部と
可を剤ジオクチルフタレート５０重量部をミキサーで混
合した後２００±１０°Ｃにて加熱混練しなから押出成
形を行った。
粉末２０重量部、水酸化カルシウムの微粉末５重量部と
可を剤ジオクチルフタレート５０重量部をミキサーで混
合した後２００±１０°Ｃにて加熱混練しなから押出成
形を行った。
しかる後可塑剤をトリクロルエチレン溶液で抽出して微
孔を形成した。このようにして得られた微多孔短繊維２
１と酸化カドミウム２００？とを混合して後ｔｙのポリ
ビニルアルコールを８０ｄのエチレングリコールに溶解
させた溶液を添加し混練を行う。かくして得られたペー
ストをニッケルメッキした鉄のパンチングメタルの両面
から塗着し、加熱乾燥して目的の極板を得た。
孔を形成した。このようにして得られた微多孔短繊維２
１と酸化カドミウム２００？とを混合して後ｔｙのポリ
ビニルアルコールを８０ｄのエチレングリコールに溶解
させた溶液を添加し混練を行う。かくして得られたペー
ストをニッケルメッキした鉄のパンチングメタルの両面
から塗着し、加熱乾燥して目的の極板を得た。
本発明によればペースト式陰極板の充電性の改良を図る
ことができた。
ことができた。
本発明の効果
上述したように本発明によれば、充放電を繰り返し行っ
たり、放電状態で放置しても活物質粒子が粗大化しにく
く充電性が大幅に向上する等工業的価値共だ大なるもの
である。
たり、放電状態で放置しても活物質粒子が粗大化しにく
く充電性が大幅に向上する等工業的価値共だ大なるもの
である。
Claims (1)
- カルシウム化合物の微粉末を含有せるポリオレフィン系
の微多孔短繊維と酸化カドミウムを主成分とする活物質
とを既粘着剤の水溶液あるいは有機溶剤溶液で混練した
ペーストを多孔板に塗着乾燥することを特徴とするアル
カリ蓄電池用カドミウム陰極板の製造方法。