JPS6314888Y2 - - Google Patents
Info
- Publication number
- JPS6314888Y2 JPS6314888Y2 JP1982057506U JP5750682U JPS6314888Y2 JP S6314888 Y2 JPS6314888 Y2 JP S6314888Y2 JP 1982057506 U JP1982057506 U JP 1982057506U JP 5750682 U JP5750682 U JP 5750682U JP S6314888 Y2 JPS6314888 Y2 JP S6314888Y2
- Authority
- JP
- Japan
- Prior art keywords
- oxygen
- layer
- indicator
- absorbent
- layered
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
本考案は、酸素吸収と同時に酸素吸収度合を検
知することができる酸素吸収剤に関するものであ
る。 食品等の内容物を包装した容器内の酸素を除去
すれば、容器内の内容物の酸化防止、細菌類によ
る腐敗の防止、昆虫等のふ化防止、栄養分の分解
防止、変色褪色防止が可能である。 この酸素を除去する方法としては、窒素ガス、
炭酸ガスによるガス置換法、真空包装法、酸素吸
収剤による酸素吸収法が実用されている。 一方容器内の酸素存在の有無を検知するインジ
ケーターは、容器内の酸素が所期どおり除去され
たか、包装材料の欠陥、包装作業中の事故、流通
過程における事故等の確認のため用いられてい
る。 酸素を吸収する酸素吸収剤とインジケーター
は、現在それぞれ別個に使用されていて、それぞ
れの酸素吸収剤が適格に作用しているか、容器内
のすべての箇所で酸素吸収が確実に行なわれたか
を確認することができなかつた。 本考案は、これら従来の欠点を改良したもの
で、酸素吸収剤と酸素インジケーターとを一体化
した酸素吸収剤である。 以下図面に従い本考案を詳細に説明する。 まず本考案は、第１図に示すように、層状化し
た酸素吸収層１と層状化したインジケーター層２
を積層してなる酸素吸収剤である。 また第２図に示すようにインジケーター層２を
２つの酸素吸収層１，１間に積層してなる酸素吸
収剤である。 この酸素吸収層１は、鉄粉、第一鉄塩、亜ニチ
オン酸塩、亜硫酸塩、ポリフエノール類、糖類、
アスコルビン酸系のいずれかの酸素吸収主剤を結
晶セルローズ、ポリビニルアルコール、ペクチ
ン、デスストリン、ゼラチン、ブドウ糖等の糖
類、食塩、パラフイン、ポリエチレングリコー
ル、合成ゼオライト、タルク等の結合剤とを組合
せて層状化したものである。 この中でもアスコルビン酸系の酸素吸収主剤と
結晶セルロースの結合剤を組合せたものが好まし
い。 インジケーター層２は、メチレンブルー、イン
ジゴカルミン、キシレンブルー、アシルレツド等
の電子供与型の色素と少量のＬ−アスコルビン酸
ナトリウム、ブドウ糖、第一鉄塩、ヒドラジン等
の還元剤を加えたものである。 上記酸素吸収剤層とインジケーター層に用いら
れる薬剤は、顆粒状が最も好ましいが、流動性を
有する粉末状態のものであれば問題なく使用でき
る。 本考案の酸素吸収剤は、使用前は透明で酸素遮
断性、水素気遮断性の優れた包装材料により包装
されており、その包装形態は、従来の包装形態の
いずれでもよい。 本考案の酸素吸収剤は、上記構成なので、無
色、淡色の酸素吸収層を有する酸素吸収剤ばかり
でなく、黒色のように濃色の酸素吸収層を有する
酸素吸収剤であつても、酸素吸収能力の適否が目
視により容易に判断でき、容器内の酸素吸収剤の
それぞれの箇所で適格に酸素吸収が行われている
か容易に検知できる。 以下本考案の実施例について説明する。 表−１に示される組成の混合粉末から成る酸素
吸収組成物と、表−２に示される、組成の混合粉
末から成るインジケーターを菊水製作所多層錠剤
機（RT−3L−36）にて打錠し、下部、酸素吸収
剤、上部酸素インジケーターより成る２層円筒状
錠剤を得た。尚、直径は15mm、全体高さが15mmで
酸素吸収剤層とインジケーター層部分はそれぞれ
10mm、５mmであつた。
知することができる酸素吸収剤に関するものであ
る。 食品等の内容物を包装した容器内の酸素を除去
すれば、容器内の内容物の酸化防止、細菌類によ
る腐敗の防止、昆虫等のふ化防止、栄養分の分解
防止、変色褪色防止が可能である。 この酸素を除去する方法としては、窒素ガス、
炭酸ガスによるガス置換法、真空包装法、酸素吸
収剤による酸素吸収法が実用されている。 一方容器内の酸素存在の有無を検知するインジ
ケーターは、容器内の酸素が所期どおり除去され
たか、包装材料の欠陥、包装作業中の事故、流通
過程における事故等の確認のため用いられてい
る。 酸素を吸収する酸素吸収剤とインジケーター
は、現在それぞれ別個に使用されていて、それぞ
れの酸素吸収剤が適格に作用しているか、容器内
のすべての箇所で酸素吸収が確実に行なわれたか
を確認することができなかつた。 本考案は、これら従来の欠点を改良したもの
で、酸素吸収剤と酸素インジケーターとを一体化
した酸素吸収剤である。 以下図面に従い本考案を詳細に説明する。 まず本考案は、第１図に示すように、層状化し
た酸素吸収層１と層状化したインジケーター層２
を積層してなる酸素吸収剤である。 また第２図に示すようにインジケーター層２を
２つの酸素吸収層１，１間に積層してなる酸素吸
収剤である。 この酸素吸収層１は、鉄粉、第一鉄塩、亜ニチ
オン酸塩、亜硫酸塩、ポリフエノール類、糖類、
アスコルビン酸系のいずれかの酸素吸収主剤を結
晶セルローズ、ポリビニルアルコール、ペクチ
ン、デスストリン、ゼラチン、ブドウ糖等の糖
類、食塩、パラフイン、ポリエチレングリコー
ル、合成ゼオライト、タルク等の結合剤とを組合
せて層状化したものである。 この中でもアスコルビン酸系の酸素吸収主剤と
結晶セルロースの結合剤を組合せたものが好まし
い。 インジケーター層２は、メチレンブルー、イン
ジゴカルミン、キシレンブルー、アシルレツド等
の電子供与型の色素と少量のＬ−アスコルビン酸
ナトリウム、ブドウ糖、第一鉄塩、ヒドラジン等
の還元剤を加えたものである。 上記酸素吸収剤層とインジケーター層に用いら
れる薬剤は、顆粒状が最も好ましいが、流動性を
有する粉末状態のものであれば問題なく使用でき
る。 本考案の酸素吸収剤は、使用前は透明で酸素遮
断性、水素気遮断性の優れた包装材料により包装
されており、その包装形態は、従来の包装形態の
いずれでもよい。 本考案の酸素吸収剤は、上記構成なので、無
色、淡色の酸素吸収層を有する酸素吸収剤ばかり
でなく、黒色のように濃色の酸素吸収層を有する
酸素吸収剤であつても、酸素吸収能力の適否が目
視により容易に判断でき、容器内の酸素吸収剤の
それぞれの箇所で適格に酸素吸収が行われている
か容易に検知できる。 以下本考案の実施例について説明する。 表−１に示される組成の混合粉末から成る酸素
吸収組成物と、表−２に示される、組成の混合粉
末から成るインジケーターを菊水製作所多層錠剤
機（RT−3L−36）にて打錠し、下部、酸素吸収
剤、上部酸素インジケーターより成る２層円筒状
錠剤を得た。尚、直径は15mm、全体高さが15mmで
酸素吸収剤層とインジケーター層部分はそれぞれ
10mm、５mmであつた。
【表】
【表】
この錠剤をポリ塩化ビニル（300μ）／ポリエ
チレン（50μ）の透明複合シートをポリエチレン
側が内側になる様に、直径20mm、深さ20mmに形成
した円筒状のトレーに収容する。次にトレーの開
孔フランジ部にポリ塩化ビニリデンコート延伸プ
ロピレン（20μ）／ポリエチレン（40μ）よりな
る複合透明フイルムを熱圧着して密封シールし円
筒状の包装体を得た。インジケーターは打錠直後
は青色であつたが、密封シール後は酸素吸収剤の
酸素吸収作用により、直ちに白色に変化した。 次に本包装体の上部に注射針にてピンホールを
設けたあと、塩化ビニリデンコーテングポリプロ
ピレン（20μ）／ポリエチレン（40μ）よりなる
複合フイルムを用いた袋体に空気200c.c.とともに
密封して24時間後インジケーターの色変化及び袋
体内のガス組成を調べた。 その結果、インジケーターは白色を示し、ガス
組成は酸素及び炭酸ガス濃度がそれぞれ0.1％以
下、21.0％を示しており、インジケーター及び酸
素吸収剤の能力はそれぞれ良好に発揮されている
ことが容易に判明できた。
チレン（50μ）の透明複合シートをポリエチレン
側が内側になる様に、直径20mm、深さ20mmに形成
した円筒状のトレーに収容する。次にトレーの開
孔フランジ部にポリ塩化ビニリデンコート延伸プ
ロピレン（20μ）／ポリエチレン（40μ）よりな
る複合透明フイルムを熱圧着して密封シールし円
筒状の包装体を得た。インジケーターは打錠直後
は青色であつたが、密封シール後は酸素吸収剤の
酸素吸収作用により、直ちに白色に変化した。 次に本包装体の上部に注射針にてピンホールを
設けたあと、塩化ビニリデンコーテングポリプロ
ピレン（20μ）／ポリエチレン（40μ）よりなる
複合フイルムを用いた袋体に空気200c.c.とともに
密封して24時間後インジケーターの色変化及び袋
体内のガス組成を調べた。 その結果、インジケーターは白色を示し、ガス
組成は酸素及び炭酸ガス濃度がそれぞれ0.1％以
下、21.0％を示しており、インジケーター及び酸
素吸収剤の能力はそれぞれ良好に発揮されている
ことが容易に判明できた。
図面は、本考案の実施例を示すもので、第１図
および第２図は、酸素吸収剤の断面図である。 １……酸素吸収層、２……インジケーター層。
および第２図は、酸素吸収剤の断面図である。 １……酸素吸収層、２……インジケーター層。
Claims (1)
- 【実用新案登録請求の範囲】 (1) 層状化した酸素吸収層と層状化したインジケ
ーター層を積層した酸素吸収剤。 (2) インジケーター層が酸素吸収層間に積層して
なる実用新案登録請求の範囲第１項記載の酸素
吸収剤。