JPS62277452A - 塩素含有樹脂組成物 - Google Patents
塩素含有樹脂組成物Info
- Publication number
- JPS62277452A JPS62277452A JP11989586A JP11989586A JPS62277452A JP S62277452 A JPS62277452 A JP S62277452A JP 11989586 A JP11989586 A JP 11989586A JP 11989586 A JP11989586 A JP 11989586A JP S62277452 A JPS62277452 A JP S62277452A
- Authority
- JP
- Japan
- Prior art keywords
- chlorine
- containing resin
- group
- resin composition
- metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
本発明は加工時の着色防止性に優れた塩素含有樹脂組成
物に関する。
物に関する。
一般に塩素を含有する樹脂は熱に対する安定性に難があ
り、加熱成型加工を行なう際に、主として脱塩化水素に
起因する熱分解を起こしやすく、このため加工製品の色
調の悪化を生じ、著しい不利益をまねく恐れがある。か
かる不利益をさけるために、塩素含有樹脂の成型加工時
には、現在、金属石ケン、有機亜リン酸エステル、エポ
キシ化合物、酸化防止剤、多価アルコール、β−ジケト
ン化合物等が使用されているが、これらの化合物では未
だに十分ではない。
り、加熱成型加工を行なう際に、主として脱塩化水素に
起因する熱分解を起こしやすく、このため加工製品の色
調の悪化を生じ、著しい不利益をまねく恐れがある。か
かる不利益をさけるために、塩素含有樹脂の成型加工時
には、現在、金属石ケン、有機亜リン酸エステル、エポ
キシ化合物、酸化防止剤、多価アルコール、β−ジケト
ン化合物等が使用されているが、これらの化合物では未
だに十分ではない。
本発明者らはかかる状況に鑑み研究を重ねた結果、熱に
よる着色に対する防止能が非常に優れた塩素含有樹脂組
成物を開発することに成功した。
よる着色に対する防止能が非常に優れた塩素含有樹脂組
成物を開発することに成功した。
すなわち本発明は、塩素含有樹脂に式(1)で表わされ
る化合物の金属塩(ただし金属はBa、Ca、Mg、A
fI、Br、Sn、Zn。
る化合物の金属塩(ただし金属はBa、Ca、Mg、A
fI、Br、Sn、Zn。
Na、に、Li)の少なくとも1種を含有する塩素含有
樹脂組成物を提供するものである。
樹脂組成物を提供するものである。
H
(ただしR、Rはアルキル基、アルケニル基、フェニル
基、シクロアルキル基、アルキルアリール基、置換アリ
ール基、ハロゲン置換アルキル基を示し、同一あるいは
異っていてもよい。) 本発明の塩素含有樹脂とは、塩化ビニル単独重合体又は
塩化ビニルを主体とした樹脂等であって、例えば塩化ビ
ニルと、酢酸ビニル・塩化ビニリデン・エチレン・プロ
ピレン・メタアクリル酸エステル・ウレタン樹脂等との
共重合体やグラフト重合体、あるいはこれらの樹脂との
ブレンド物等である。
基、シクロアルキル基、アルキルアリール基、置換アリ
ール基、ハロゲン置換アルキル基を示し、同一あるいは
異っていてもよい。) 本発明の塩素含有樹脂とは、塩化ビニル単独重合体又は
塩化ビニルを主体とした樹脂等であって、例えば塩化ビ
ニルと、酢酸ビニル・塩化ビニリデン・エチレン・プロ
ピレン・メタアクリル酸エステル・ウレタン樹脂等との
共重合体やグラフト重合体、あるいはこれらの樹脂との
ブレンド物等である。
次に本発明で用いられる式〔■〕で表わされる化合物の
金属塩としては、例えば2,4−ジヒドロキシ−3,5
−ジアセチルビラン−2−オン(以下HAPOと略す)
亜鉛、HAPOカルシウム、HAPOバリウム、HAP
Oナトリウム、HAPOマグネシウム、HAPOカリウ
ム、HAPOスズ、HAPOリチウム、HAPOストロ
ンチウム、HAPOアルミニウム、2,4−ジヒドロキ
シ−3゜5−ジベンゾイルビラン−2−オン(以下HB
POと略す)亜鉛、HBPOカルシウム、HBPOバリ
ウム、HBPOナトリウム、2゜4−ジヒドロキシ−3
,5−ジステアロイルビラン−2−オン(以下H3PO
と略す)亜鉛、H3POカルシウム、H3P0マグネン
ウム、HSPOカリウム、H3P○スズ、H8Poスト
ロンチウム等が挙げられる。これらは単独あるいは併用
してもよく、塩素含有樹脂100重量部に対して通常0
.001〜3重量部用いられ、さらに好ましくは0.0
1〜0.5重量部用いられる。
金属塩としては、例えば2,4−ジヒドロキシ−3,5
−ジアセチルビラン−2−オン(以下HAPOと略す)
亜鉛、HAPOカルシウム、HAPOバリウム、HAP
Oナトリウム、HAPOマグネシウム、HAPOカリウ
ム、HAPOスズ、HAPOリチウム、HAPOストロ
ンチウム、HAPOアルミニウム、2,4−ジヒドロキ
シ−3゜5−ジベンゾイルビラン−2−オン(以下HB
POと略す)亜鉛、HBPOカルシウム、HBPOバリ
ウム、HBPOナトリウム、2゜4−ジヒドロキシ−3
,5−ジステアロイルビラン−2−オン(以下H3PO
と略す)亜鉛、H3POカルシウム、H3P0マグネン
ウム、HSPOカリウム、H3P○スズ、H8Poスト
ロンチウム等が挙げられる。これらは単独あるいは併用
してもよく、塩素含有樹脂100重量部に対して通常0
.001〜3重量部用いられ、さらに好ましくは0.0
1〜0.5重量部用いられる。
また本発明において、従来より塩素含有樹脂に使用され
ている、可塑剤、エポキシ化合物、金属石ケン、充てん
剤、流滴剤、強化剤、加工助剤、有機面リン酸エステル
、有機リン酸エステル、有機リン酸金属塩、酸化防止剤
、紫外線吸収剤、ヒンダードアミン系等の耐光性改良剤
、無機塩、顔料、滑剤、難燃剤、プレートアウト防止剤
等を併用してもよいことはいうまでもない。以下実施例
により具体的に説明する。
ている、可塑剤、エポキシ化合物、金属石ケン、充てん
剤、流滴剤、強化剤、加工助剤、有機面リン酸エステル
、有機リン酸エステル、有機リン酸金属塩、酸化防止剤
、紫外線吸収剤、ヒンダードアミン系等の耐光性改良剤
、無機塩、顔料、滑剤、難燃剤、プレートアウト防止剤
等を併用してもよいことはいうまでもない。以下実施例
により具体的に説明する。
実施例1
表1の配合物を180℃のロールで5分間混練して、厚
さ0.5mmのシートを作成した。
さ0.5mmのシートを作成した。
次いでこのシートを170°Cで20分間プレス加工を
行ない、着色防止性を評価した。
行ない、着色防止性を評価した。
実施例2
農ビ配合における効果をみるために、表2の配合物を実
施例1と同様に評価した。
施例1と同様に評価した。
実施例3
PVC−MBSポリマーブレンド系における効果をみる
ため、表3の配合物を実施例1と同様に評価した。
ため、表3の配合物を実施例1と同様に評価した。
実施例4
ポリ塩化ビニル−酢酸ビニル−メタアクリル樹脂系にお
ける効果をみるため、表4の配合物を実施例1と同様に
評価した。
ける効果をみるため、表4の配合物を実施例1と同様に
評価した。
Claims (1)
- 【特許請求の範囲】 塩素含有樹脂に、式〔 I 〕で表わされる化 合物の金属塩(ただし金属は、Ba、Ca、Mg、Al
、Br、Sn、Zn、Na、K、Li)の少なくとも1
種を含有する塩素含有樹脂組成物。 ▲数式、化学式、表等があります▼〔 I 〕 (ただしR^1、R^2はアルキル基、アルケニル基、
フェニル基、シクロアルキル基、アルキルアリール基、
置換アリール基、ハロゲン置換アルキル基を示し、同一
あるいは異っていてもよい。)