JPS6027723B2 - 溶融鉄中への酸素吹込み羽口の保護方法 - Google Patents
溶融鉄中への酸素吹込み羽口の保護方法Info
- Publication number
- JPS6027723B2 JPS6027723B2 JP13396880A JP13396880A JPS6027723B2 JP S6027723 B2 JPS6027723 B2 JP S6027723B2 JP 13396880 A JP13396880 A JP 13396880A JP 13396880 A JP13396880 A JP 13396880A JP S6027723 B2 JPS6027723 B2 JP S6027723B2
- Authority
- JP
- Japan
- Prior art keywords
- molten iron
- tuyere
- tuyeres
- oxygen
- tip
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【発明の詳細な説明】
本発明は溶融鉄中への酸素吹込み羽口の保護方法に関す
るものである。
るものである。
周知のごとく、溶融鉄中へ酸素吹込み精錬を行う場合、
酸化反応点からの高温の鯛射熱、また羽□先への溶融鉄
の接触、侵入による羽□パイプの酸化等により、損耗が
著るしい。その対策として、従来方法は、羽口を2重管
構造とし「内筒から酸素ガスを、外筒から冷却媒体とし
てプロパンガス、灯油等を吹込むことにより耐用性を改
善することが知られている。
酸化反応点からの高温の鯛射熱、また羽□先への溶融鉄
の接触、侵入による羽□パイプの酸化等により、損耗が
著るしい。その対策として、従来方法は、羽口を2重管
構造とし「内筒から酸素ガスを、外筒から冷却媒体とし
てプロパンガス、灯油等を吹込むことにより耐用性を改
善することが知られている。
かかる方法は、第1図において酸素吹込(矢印A)用内
筒1を有する2重管羽口の外筒2から冷却媒体(矢印B
)を吹込むことで羽口先端に地金殻3を凝固形成させ精
錬中の溶融鉄4と羽□先との間の隔離を成し、羽□の港
損を防止するものである。
筒1を有する2重管羽口の外筒2から冷却媒体(矢印B
)を吹込むことで羽口先端に地金殻3を凝固形成させ精
錬中の溶融鉄4と羽□先との間の隔離を成し、羽□の港
損を防止するものである。
従って地金殻の凝固、生長維持の安定性がかかる方法で
は非常に重要である。しかし、羽口先端での地金殻の生
成状態を常に一定に保つことは困難であり、冷却が不足
の場合は溶損が進行する。過冷却の場合には地金殻が成
長しすぎ羽口の有効口径を変動させ、ガス吹込み上の不
都合が生ずるまた地金殻が脱落し、次の地金殻が生成す
るまでの間に溶損が進行する場合もある。本発明は従来
方法の欠点を回避するため、羽口先端に地金殻を生成さ
せずに充分な保護効果を得るためになされたものであり
、溶融鉄中へ酸素を吹込むに通した溶中に浸簿された2
重管羽口において、内筒から精錬用酸素ガスを又外筒か
ら酸素以外のガスをキャリア一として粉末状物質を外筒
〜内簡閲断面積1のあたり0.5k9/分以上の速度で
、実質的に吹込み時間全般にわたって吹込むことを特徴
とする羽□の保護方法である。
は非常に重要である。しかし、羽口先端での地金殻の生
成状態を常に一定に保つことは困難であり、冷却が不足
の場合は溶損が進行する。過冷却の場合には地金殻が成
長しすぎ羽口の有効口径を変動させ、ガス吹込み上の不
都合が生ずるまた地金殻が脱落し、次の地金殻が生成す
るまでの間に溶損が進行する場合もある。本発明は従来
方法の欠点を回避するため、羽口先端に地金殻を生成さ
せずに充分な保護効果を得るためになされたものであり
、溶融鉄中へ酸素を吹込むに通した溶中に浸簿された2
重管羽口において、内筒から精錬用酸素ガスを又外筒か
ら酸素以外のガスをキャリア一として粉末状物質を外筒
〜内簡閲断面積1のあたり0.5k9/分以上の速度で
、実質的に吹込み時間全般にわたって吹込むことを特徴
とする羽□の保護方法である。
溶融鉄中への酸素吹込み羽口の溶損原因は2500℃に
達する高温反応点(火点)からの韓射熱、羽□先への溶
融鉄の接触侵入が着火源となり、酸素ガスによって酸化
溶損が進行するものである。
達する高温反応点(火点)からの韓射熱、羽□先への溶
融鉄の接触侵入が着火源となり、酸素ガスによって酸化
溶損が進行するものである。
本発明方法では第2図に示す如く内筒1、外筒2よりな
る羽□の先端部に酸素ガス(矢印A)を取り囲む形で酸
素ガス以外のガスと粉体状物質5からなる混合層(矢印
C)を形成することにより韓射熱の遮蔽効果をもたらす
と共に流体をガス十固体粉体とすることによるモーメン
タムの増大による羽口先への溶融鉄の流入を抑止し羽口
への着火源を断ち切ることにある。ここで外筒へ使用す
るガスとしては〜, C02,N2,LDG,BFG等が用いられる。
る羽□の先端部に酸素ガス(矢印A)を取り囲む形で酸
素ガス以外のガスと粉体状物質5からなる混合層(矢印
C)を形成することにより韓射熱の遮蔽効果をもたらす
と共に流体をガス十固体粉体とすることによるモーメン
タムの増大による羽口先への溶融鉄の流入を抑止し羽口
への着火源を断ち切ることにある。ここで外筒へ使用す
るガスとしては〜, C02,N2,LDG,BFG等が用いられる。
また外筒へ吹込む粉末状物質としては安価な耐火性粉末
が好ましく、Ca0,CaC03,M奴,MgC○3、
ドロマイト、Si02,AI203,Hg0一C,Zr
02,C等が用いられる。粉末の粒度は1.仇吻以下に
調整したのが、安定した吹込みを行う上で好ましい。
が好ましく、Ca0,CaC03,M奴,MgC○3、
ドロマイト、Si02,AI203,Hg0一C,Zr
02,C等が用いられる。粉末の粒度は1.仇吻以下に
調整したのが、安定した吹込みを行う上で好ましい。
粉末の吹込み量は羽口先端でのガス+粉末層の状態を左
右する重要因子であるが、実験の結果外筒と内筒の間に
形成される断面積1地あたり0.5kg/分以上の吹込
み量が必要であった。
右する重要因子であるが、実験の結果外筒と内筒の間に
形成される断面積1地あたり0.5kg/分以上の吹込
み量が必要であった。
即ち0.5k9/洲・分以上において外筒、内筒とも建
全な先端形状を維持することが出来、0.5k9/地・
分未満では羽口先に形成される流体層中の粉末濃度が充
分に得られず従来法にみられるような地金殻の形成や、
羽口の溶損が認められた。
全な先端形状を維持することが出来、0.5k9/地・
分未満では羽口先に形成される流体層中の粉末濃度が充
分に得られず従来法にみられるような地金殻の形成や、
羽口の溶損が認められた。
また吹込み途中で粉体の供給を停止した場合も従来法に
みられるような地金殻の形成、羽口の溶損が認められ、
特に地金殻が形成した場合その後の粉末吹込みが困難と
なる。従って本法に於いては実質的に吹込時間全般にわ
たって外筒への粉末吹込みを行うことが必須条件である
。
みられるような地金殻の形成、羽口の溶損が認められ、
特に地金殻が形成した場合その後の粉末吹込みが困難と
なる。従って本法に於いては実質的に吹込時間全般にわ
たって外筒への粉末吹込みを行うことが必須条件である
。
次に本法を用いる態様としては、酸素ガスを用いる溶銑
、および渚鋼の精錬において、浸債ランスのノズル部、
炉に固定配置されたノズル部の保護を目的として効果を
発揮することができる。
、および渚鋼の精錬において、浸債ランスのノズル部、
炉に固定配置されたノズル部の保護を目的として効果を
発揮することができる。
表1に比較例と共に実施例を示す。表1
〔実施例〕
〔比較例〕
第1図は従来法における羽口先端部の状態を示す立断面
図、第2図は本発明方法における羽口先端部の状態の1
例を示す立断面図である。 図中1は内筒、2は外筒、3は地金殻、4は溶融鉄、5
は粉状物質。 オー図 外2図
図、第2図は本発明方法における羽口先端部の状態の1
例を示す立断面図である。 図中1は内筒、2は外筒、3は地金殻、4は溶融鉄、5
は粉状物質。 オー図 外2図
Claims (1)
- 1 溶融鉄中へ酸素を吹込むに適した溶中に浸漬された
2重管羽口において、内筒から精錬用酸素ガスを又外筒
から酸素以外のガスをキヤリアーとして粉末状物質を外
筒〜内筒間断面積1cm^2あたり0.5kg/分以上
の速度で実質的に吹込み時間全般にわたつて吹込むこと
を特徴とする羽口の保護方法。