JPH06316829A - Polyester-base conjugate yarn - Google Patents
Polyester-base conjugate yarnInfo
- Publication number
- JPH06316829A JPH06316829A JP5105424A JP10542493A JPH06316829A JP H06316829 A JPH06316829 A JP H06316829A JP 5105424 A JP5105424 A JP 5105424A JP 10542493 A JP10542493 A JP 10542493A JP H06316829 A JPH06316829 A JP H06316829A
- Authority
- JP
- Japan
- Prior art keywords
- polyester
- composite yarn
- boiling water
- denier
- multifilament
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明はポリエステル系複合糸に
関するものであり、さらに詳しくは、着用感の優れた布
帛が製造可能なポリエステル系複合糸に関するものであ
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a polyester-based composite yarn, and more particularly to a polyester-based composite yarn capable of producing a cloth having a good wearing feeling.
【０００２】[0002]
【従来の技術】従来より、嵩高性に優れ、かつソフトな
風合を有する布帛が製造可能なポリエステル系複合糸が
種々提案されてきた。2. Description of the Related Art Conventionally, various polyester-based composite yarns have been proposed which are capable of producing a fabric having excellent bulkiness and soft texture.
【０００３】例えば特開平３―１９３９４５号公報に
は、防皺性と嵩高性を有しかつ超ソフト風合を呈する織
物を得ることが可能な複合糸の製造方法が開示されてい
るが、該複合糸を構成する繊維は捲縮を発現しないフラ
ットヤーンであるため、織物のストレッチ性が不足して
着用感が損なわれるという問題を有していた。For example, Japanese Unexamined Patent Publication (Kokai) No. 3-193945 discloses a method for producing a composite yarn capable of obtaining a woven fabric having a wrinkle-proof property and a bulkiness and exhibiting an ultra-soft feeling. Since the fibers constituting the composite yarn are flat yarns that do not exhibit crimps, there is a problem that the stretchability of the woven fabric is insufficient and the wearing feeling is impaired.
【０００４】一方、特開平４―２４０２３１号公報に
は、乾熱収縮率差を有する、ポリエステルマルチフィラ
メントと自発伸長性を有するコンジュゲートフィラメン
トからなる混繊糸が開示されている。On the other hand, Japanese Unexamined Patent Publication (Kokai) No. 4-240231 discloses a mixed fiber comprising polyester multifilaments having a difference in dry heat shrinkage and conjugate filaments having spontaneous elongation.
【０００５】しかしながら、該混繊糸はコンジュゲート
フィラメントが熱処理により自発伸長するため、布帛に
した場合芯部にフラットなマルチフィラメント、鞘部に
コンジュゲートフィラメントが配置され、捲縮によるス
トレッチ性が不足する上肌ざわりが悪く、着用感が損な
われるという問題を有していた。However, since the conjugate filament of the mixed yarn is spontaneously elongated by heat treatment, a flat multifilament is arranged in the core portion and the conjugate filament is arranged in the sheath portion when it is made into a fabric, and the stretchability due to crimping is insufficient. In addition, it has a problem that the skin feels bad and the feeling of wearing is impaired.
【０００６】[0006]
【発明が解決しようとする課題】本発明の目的は、嵩高
性に富み、ソフトな風合を有するとともに、ストレッチ
性に優れ着用感の改善された布帛が製造可能な複合糸を
提供することにある。SUMMARY OF THE INVENTION An object of the present invention is to provide a composite yarn which is rich in bulkiness, has a soft texture, and is excellent in stretchability and capable of producing a fabric having an improved wearing feeling. is there.
【０００７】[0007]
【課題を解決するための手段】本発明者らが上記目的を
達成するため鋭意検討した結果、少なくとも２種類のポ
リエステル系マルチフィラメントを混繊または交撚して
なる複合糸において、芯部に自発伸長性を有しない潜在
捲縮糸を配置し、複合糸の糸使いと集合体構造を巧みに
組み合わせることにより、所望の布帛が製造可能な複合
糸が得られることを究明した。Means for Solving the Problems As a result of intensive studies conducted by the present inventors in order to achieve the above-mentioned object, as a result of spontaneous blending or twisting of at least two types of polyester-based multifilaments, a spontaneous yarn is formed in the core portion. By arranging latent crimped yarns having no extensibility and skillfully combining the yarn use of the composite yarn and the aggregate structure, it was clarified that a composite fabric capable of producing a desired fabric can be obtained.
【０００８】かくして本発明によれば、少なくとも２種
類のポリエステル系マルチフィラメントＡおよびＢが混
繊されてなる複合糸であって、該マルチフィラメントＡ
が下記 (１) 〜 (２) の特性を満足し、かつ該マルチフ
ィラメントＢが下記 (ａ) 〜(ｃ) の特性を満足する、
機械的捲縮加工を施すことなく沸騰水中で捲縮を発現す
ることが可能なコンジュゲートフィラメントであること
を特徴とするポリエステル系複合糸。 (1) 切断伸度が50％以上 (2) 200 ℃における熱収縮応力が0.04ｇ／デニール以下 (a) 捲縮率が 5〜30％ (b) 沸騰水収縮率が 0％を越え20％以下 (c) 160 ℃における熱収縮応力が0.08ｇ／デニール以上Thus, according to the present invention, there is provided a composite yarn in which at least two types of polyester-based multifilaments A and B are mixed, and the multifilament A is used.
Satisfies the following characteristics (1) to (2), and the multifilament B satisfies the following characteristics (a) to (c):
A polyester-based composite yarn, which is a conjugate filament capable of developing crimps in boiling water without mechanical crimping. (1) Cutting elongation of 50% or more (2) Thermal shrinkage stress at 200 ° C of 0.04 g / denier or less (a) Crimping rate of 5 to 30% (b) Boiling water shrinkage of more than 0% to 20% (C) Heat shrinkage stress at 160 ℃ is 0.08g / denier or more
【０００９】以下、本発明を詳細に説明する。本発明の
複合糸は、布帛にした後の染色やプレセット、ファイナ
ルセットなどの熱処理により、フィラメントＡとフィラ
メントＢの特性および集合体構造が発現して、所望の布
帛が得られる。The present invention will be described in detail below. The composite yarn of the present invention exhibits the characteristics and aggregate structure of the filaments A and B by dyeing after the formation of a cloth and heat treatment such as presetting and final setting to obtain a desired cloth.
【００１０】本発明に用いるポリエステルマルチフィラ
メントＡは、テレフタル酸を主たる酸成分とし、アルキ
レングリコールを主たるグリコール成分とするポリエス
テル、例えばポリエチレンテレフタレート、ポリブチレ
ンテレフタレート、ポリエチレンナフタレート、ポリヘ
キサメチレンナフタレートなどのポリエステルや、これ
らのポリエステルとポリエチレンイソフタレートなどと
の共重合体、あるいは前記の各種ポリエステルのブレン
ド物等からなる。The polyester multifilament A used in the present invention is a polyester containing terephthalic acid as a main acid component and alkylene glycol as a main glycol component, such as polyethylene terephthalate, polybutylene terephthalate, polyethylene naphthalate and polyhexamethylene naphthalate. It is made of polyester, a copolymer of these polyesters and polyethylene isophthalate, or a blend of the above various polyesters.
【００１１】上記ポリエステルには、その他必要に応
じ、難燃剤、蛍光増白剤、艶消剤、着色剤あるいは制電
剤などの任意の添加剤を添加してもよい。Other additives such as flame retardants, optical brighteners, matting agents, coloring agents or antistatic agents may be added to the polyester, if necessary.
【００１２】該ポリエステルマルチフィラメントの伸度
は５０％以上必要である。伸度が５０％未満では繊維の
配向度が高く、従ってモジュラスも高くなり、布帛にソ
フトな風合を付与することができない。The elongation of the polyester multifilament must be 50% or more. If the elongation is less than 50%, the degree of orientation of the fibers is high and therefore the modulus is also high, and it is not possible to give the fabric a soft feel.
【００１３】一方、伸度があまり高すぎると布帛の膝抜
け、肘抜けの原因になるので、高々２００％程度に止め
るのが良い。好ましい伸度範囲は６０〜１８０％であ
る。On the other hand, if the elongation is too high, the fabric may come off the knees and elbows. Therefore, it is better to stop the fabric at about 200% at most. A preferred elongation range is 60 to 180%.
【００１４】また、上記ポリエステルマルチフィラメン
トの２００℃における熱応力は０．０４ｇ／デニール以
下であることが必要である。即ち、通常の染色仕上げ工
程ではファイナルセットを１６０〜２００℃で実施する
場合が多いので、２００℃における熱応力が０．０４ｇ
／デニール以下であれば、マルチフィラメントＢとの収
縮差により、充分な嵩高性が付与される。The thermal stress at 200 ° C. of the polyester multifilament should be 0.04 g / denier or less. That is, in the usual dyeing finishing process, the final set is often carried out at 160 to 200 ° C., so that the thermal stress at 200 ° C. is 0.04 g.
If it is less than / denier, sufficient bulkiness is given due to the difference in shrinkage with the multifilament B.
【００１５】該熱応力が０．０４ｇ／デニールを越える
場合には収縮が大きくなりすぎ、得られる布帛の粗硬感
が増すばかりでなく、極端な場合には芯部と鞘部のマル
チフィラメントの構成が逆転し、本発明の目的が達せら
れない。When the thermal stress exceeds 0.04 g / denier, the shrinkage becomes too large, which not only increases the coarse and hard feeling of the obtained fabric, but also, in an extreme case, the multifilament of the core and the sheath. The configuration is reversed and the object of the present invention cannot be achieved.
【００１６】上記ポリエステルマルチフィラメントを得
る方法としては、紡糸速度１０００ｍ／分で紡糸した後
予熱しながら低倍率延伸する方法、あるいは紡糸速度２
０００〜５０００ｍ／分で高速紡糸する方法等が例示さ
れる。The polyester multifilament may be obtained by spinning at a spinning speed of 1000 m / min and then drawing at a low draw ratio while preheating, or spinning speed 2
Examples include a method of high speed spinning at 000 to 5000 m / min.
【００１７】一方、ポリエステルマルチフィラメントＢ
は、仮撚加工等の機械的捲縮加工を施すことなく沸騰水
中で捲縮を発現することが可能なコンジュゲートフィラ
メントであって、該捲縮は座屈や角張った部分のない、
曲線状の三次元的な捲縮であることが必要である。On the other hand, polyester multifilament B
Is a conjugate filament capable of expressing crimps in boiling water without performing mechanical crimping such as false twisting, the crimps having no buckling or angular portions,
It is necessary to have a curved three-dimensional crimp.
【００１８】上記のコンジュゲートフィラメントとして
は、ポリブチレンテレフタレートおよびポリエチレンテ
レフタレートを主たる構成成分とする２種の成分がサイ
ドバイサイド型または偏芯シースコア型に複合紡糸され
たコンジュゲートフィラメント、あるいは固有粘度が異
なるポリエチレンテレフタレートがサイドバイサイド型
または偏芯シースコア型に複合紡糸されたコンジュゲー
トフィラメントなどが例示され、ポリブチレンテレフタ
レートおよびポリエチレンテレフタレートを主たる構成
成分とする２種の成分がサイドバイサイド型に複合紡糸
されたコンジュゲートフィラメントが特に好ましく例示
できる。As the above-mentioned conjugate filament, a conjugate filament in which two kinds of components having polybutylene terephthalate and polyethylene terephthalate as main constituents are composite-spun into a side-by-side type or an eccentric sheath core type, or have different intrinsic viscosities An example is a conjugate filament in which polyethylene terephthalate is composite-spun into a side-by-side type or an eccentric sheath core type, and a conjugate in which two kinds of components mainly composed of polybutylene terephthalate and polyethylene terephthalate are side-by-side type composite-spun. A filament is a particularly preferable example.
【００１９】上記コンジュゲートフィラメントは、５〜
３０％、好ましくは１０〜２０％の捲縮率を有すること
が必要である。捲縮率が５％未満の場合は伸縮性が不足
し、一方３０％を越える場合には複合糸の締め付けが起
こるので好ましくない。The above conjugate filament has 5 to
It is necessary to have a crimp rate of 30%, preferably 10-20%. If the crimp ratio is less than 5%, the elasticity is insufficient, while if it exceeds 30%, the composite yarn is tightened, which is not preferable.
【００２０】また、上記コンジュゲートフィラメント
は、０％を越え２０％以下の沸騰水収縮率を有すること
が必要である。沸騰水収縮率が０％以下（自発伸長）の
場合はコンジュゲートフィラメントが芯部に配置され
ず、本発明の目的を達成することができない。一方、２
０％を越える場合には複合糸の締め付けが起こるので好
ましくない。好ましい沸騰水収縮率の範囲は８〜１２％
である。Further, the above conjugate filament is required to have a boiling water shrinkage ratio of more than 0% and 20% or less. When the boiling water shrinkage is 0% or less (spontaneous extension), the conjugate filament is not arranged in the core, and the object of the present invention cannot be achieved. On the other hand, 2
If it exceeds 0%, tightening of the composite yarn occurs, which is not preferable. The preferred range of boiling water shrinkage is 8-12%
Is.
【００２１】さらに、上記コンジュゲートフィラメント
の１６０℃における熱応力は０．０８ｇ／デニール以上
必要である。即ち、前述のように通常の染色仕上げ工程
ではファイナルセットを１６０〜２００℃で実施する場
合が多く、少なくともこの温度で芯糸の捲縮が発現する
ことが布帛の着用感を改善するために必要となるからで
ある。Further, the thermal stress at 160 ° C. of the above conjugate filament is required to be 0.08 g / denier or more. That is, as described above, the final set is often carried out at 160 to 200 ° C. in the usual dyeing and finishing step, and it is necessary that the crimp of the core yarn is developed at least at this temperature in order to improve the wearing feeling of the cloth. It is because
【００２２】次いで、上記マルチフィラメントとコンジ
ュゲートフィラメントは常法に従い混繊される。Next, the multifilament and the conjugate filament are mixed by a conventional method.
【００２３】混繊は、例えば上記２種類のフィラメント
をインターレースノズルに導き、ゲージ圧１〜５ｋｇ／
ｃｍ2 の圧空により交絡させれば良い。また、上記２種
類のフィラメントを撚糸機上で引き揃えた後撚糸する方
法、あるいは撚糸前に引き揃えて巻取った後撚糸する方
法等任意の方法を採用して良い。For the mixed fiber, for example, the above-mentioned two kinds of filaments are guided to an interlace nozzle, and a gauge pressure of 1 to 5 kg /
It may be entangled with compressed air of cm 2 . Further, any method such as a method of aligning the above two kinds of filaments on a twisting machine and then twisting them, or a method of aligning before winding and winding and then twisting them may be adopted.
【００２４】また、嵩高性をさらに向上させたい場合
は、混繊時に鞘部に配置されるマルチフィラメントを
０．５〜１０％程度オーバーフィードすれば良い。If it is desired to further improve the bulkiness, the multifilament arranged in the sheath portion at the time of mixing fibers may be over-fed by about 0.5 to 10%.
【００２５】さらに、本発明の目的を損なわない範囲
で、上記２種類のフィラメント以外のマルチフィラメン
ト等を同時に混繊しても構わない。Further, multifilaments other than the above-mentioned two types of filaments may be mixed at the same time as long as the object of the present invention is not impaired.
【００２６】[0026]
【作用】本発明は以上の構成を採っているので、以下の
作用を奏する。即ち、本発明の複合糸は、熱収縮率の異
なる２種以上のマルチフィラメントから構成されるの
で、布帛にした後熱処理された場合、まず収縮差による
嵩高性が発現する。Since the present invention has the above-mentioned structure, it has the following effects. That is, since the composite yarn of the present invention is composed of two or more kinds of multifilaments having different heat shrinkage rates, when the cloth is heat-treated after being made into a fabric, bulkiness due to the difference in shrinkage is first expressed.
【００２７】また、コンジュゲートフィラメント（Ｂ）
は低配向のマルチフィラメント（Ａ）よりも大きな熱収
縮を示すので、コンジュゲートフィラメントがより芯部
に配置される。Further, the conjugate filament (B)
Shows a larger heat shrinkage than the low orientation multifilament (A), so that the conjugate filament is arranged more in the core portion.
【００２８】しかも、該コンジュゲートフィラメントが
捲縮を有しているので、複合糸にストレッチ性が付与さ
れるばかりでなく、該捲縮が三次元的なものであるため
芯部を構成するモノフィラメント間に空隙が生じ、複合
糸の嵩高性がさらに増加する。Moreover, since the conjugate filament has crimps, not only stretchability is imparted to the composite yarn, but also because the crimps are three-dimensional, the monofilament constituting the core portion is formed. Voids are generated between them, which further increases the bulkiness of the composite yarn.
【００２９】この際、コンジュゲートフィラメントとし
て、ポリブチレンテレフタレートおよびポリエチレンテ
レフタレートを主たる構成成分とする２種の成分がサイ
ドバイサイド型に複合紡糸されたコンジュゲートフィラ
メントを用いれば、弾性回復が良好でヘタリの少ないス
トレッチ特性が得られ、複合糸の嵩高性はさらに向上す
る。At this time, if a conjugate filament in which two kinds of components having polybutylene terephthalate and polyethylene terephthalate as main constituent components are composite-spun in a side-by-side type is used as the conjugate filament, elastic recovery is good and less sagging occurs. Stretch properties are obtained and the bulkiness of the composite yarn is further improved.
【００３０】さらに、鞘部に配置されるマルチフィラメ
ントは低配向であるため肌ざわりが良く、芯部のフィラ
メントが有する曲線状捲縮の効果と相俟ってソフトな風
合を呈し、着用感の良好な布帛が得られるのである。Further, since the multifilament arranged in the sheath portion has a low orientation, it has a good texture and, in combination with the effect of the curved crimps of the filament in the core portion, exhibits a soft texture and gives a feeling of wearing. A good fabric can be obtained.
【００３１】上述の如く、本発明の複合糸は、芯部およ
び鞘部を構成するフィラメントにそれぞれの機能を分担
させるとともに、集合体構造を巧みに組み合わせること
によりその効果を高め、得られる布帛の着用感を著しく
改善したものである。As described above, in the composite yarn of the present invention, the filaments constituting the core portion and the sheath portion are allowed to share their respective functions, and the effect is enhanced by skillfully combining the aggregate structure to obtain a fabric. The feeling of wearing is remarkably improved.
【００３２】[0032]
【実施例】以下、実施例により本発明をさらに具体的に
説明する。なお、実施例中の各物性は下記の方法により
測定したものである。EXAMPLES The present invention will be described in more detail below with reference to examples. In addition, each physical property in an Example is measured by the following method.
【００３３】(１) 切断伸度 定速伸長型引張試験機を用い、試料の初荷重を１／３０
ｇ／デニール、試料長１０ｃｍ、引張速度２０ｃｍ／
分、チャート速度１０ｃｍ／分の条件で測定を行なっ
た。測定は５回実施し、その平均値で表わした。(1) Cutting elongation Using a constant speed elongation type tensile tester, the initial load of the sample was 1/30
g / denier, sample length 10 cm, pulling speed 20 cm /
The measurement was performed under the conditions of 10 minutes / chart speed and 10 cm / minute. The measurement was performed 5 times, and the average value was shown.
【００３４】(２) 熱収縮応力 鐘紡エンジニアリング製熱応力測定機（ＴＹＰＥ ＫＥ
―II）を用い、試料を長さ１０ｃｍのループ状にして、
昇温速度３００℃／１２０秒の条件で温度―熱応力曲線
をチャート上に記録した。(2) Thermal shrinkage stress Kanebo Engineering's thermal stress measuring instrument (TYPE KE
-II) is used to make the sample into a loop with a length of 10 cm,
A temperature-thermal stress curve was recorded on the chart under the condition of a temperature rising rate of 300 ° C./120 seconds.
【００３５】測定は３回実施し、マルチフィラメントは
２００℃、コンジュゲートフィラメントは１６０℃にお
ける熱応力値を読み取り、その平均値で表わした。The measurement was carried out three times, and the thermal stress values at 200 ° C. for the multifilament and at 160 ° C. for the conjugate filament were read and expressed as the average value.
【００３６】(３) 沸騰水収縮率および捲縮率 複合糸を３０００デニールの綛状にし、この綛に２ｍｇ
／デニールの軽荷重を吊るした後、更に０．２ｇ／デニ
ールの重荷重を吊し、１分間放置した後綛の長さ
（ｌ0 ）を読み取る。次に重荷重を取り外し、沸騰水中
で20分間処理した後取り出して軽荷重を外し２４時間風
乾する。風乾後軽荷重および重荷重を吊し、１分間放置
後綛の長さ（ｌ1 ）を読み取る。次に重荷重を外し、綛
の長さ（ｌ2 ）を読み取る。沸騰水収縮率および捲縮率
はそれぞれ次式により算出する。 沸騰水収縮率（％）＝(l0 -l1 )/(l0 ) ×100 捲縮率（％）＝(l1 -l2 )/(l0 ) ×100 測定は５回実施し、その平均値で表した。(3) Boiling water shrinkage rate and crimp rate The composite yarn was made into a denier shape of 3000 denier, and 2 mg was applied to this crease.
/ After suspending a light load of denier, further suspending a heavy load of 0.2 g / denier, leaving it for 1 minute, and then reading the length (l 0 ) of the ridge. Then, remove the heavy load, treat for 20 minutes in boiling water, remove it, remove the light load, and air dry for 24 hours. After air-drying, light and heavy loads are hung, left for 1 minute, and the length (l 1 ) of the ridge is read. Then, remove the heavy load and read the length of the ridge (l 2 ). The boiling water shrinkage ratio and the crimping ratio are calculated by the following equations. Boiling water shrinkage (%) = (l 0 -l 1 ) / (l 0 ) × 100 Crimping ratio (%) = (l 1 -l 2 ) / (l 0 ) × 100 The measurement was performed 5 times, The average value is shown.
【００３７】[0037]
【実施例１】極限粘度０．６７のポリエチレンテレフタ
レートを常法に従って２８００ｍ／分の速度で紡糸した
後延伸・熱処理して、表１に示す特性を有する５０デニ
ール／２４フィラメントのマルチフィラメントＡを得
た。Example 1 Polyethylene terephthalate having an intrinsic viscosity of 0.67 was spun at a speed of 2800 m / min according to a conventional method, then stretched and heat-treated to obtain a 50 denier / 24 filament multifilament A having the properties shown in Table 1. It was
【００３８】また、複合紡糸機を用い、極限粘度０．８
６のポリブチレンテレフタレートと極限粘度０．５０の
ポリエチレンテレフタレートを１：１の割合でサイドバ
イサイド型コンジュゲートフィラメントとして紡出し速
度２５００ｍ／分で巻取って、８０デニール／２４フィ
ラメントのピーナツ型断面を有するコンジュゲートフィ
ラメントを得た。Further, using a composite spinning machine, an intrinsic viscosity of 0.8
No. 6 polybutylene terephthalate and polyethylene terephthalate having an intrinsic viscosity of 0.50 were wound as side-by-side type conjugated filaments at a ratio of 1: 1 at a spinning speed of 2500 m / min, and had a denaturing section of 80 denier / 24 filaments. A gate filament was obtained.
【００３９】次いで、上記コンジュゲートフィラメント
を種々の条件で延伸し、表１に示す特性を有するコンジ
ュゲートフィラメントＢを得た。Then, the above conjugate filament was drawn under various conditions to obtain a conjugate filament B having the characteristics shown in Table 1.
【００４０】引き続いて、上記コンジュゲートフィラメ
ントとマルチフィラメントを引き揃え、インターレース
ノズルを用いて圧空圧２ｋｇ／ｃｍ2 、オーバーフィー
ド率２．０％で混繊して複合糸を得た。Subsequently, the conjugate filament and the multifilament were aligned and mixed with each other using an interlace nozzle at a compressed air pressure of 2 kg / cm 2 and an overfeed rate of 2.0% to obtain a composite yarn.
【００４１】上記複合糸を経糸および緯糸に用いて平織
物を製織し、常法に従って染色仕上げを行なった。A plain woven fabric was woven using the above-mentioned composite yarn as a warp yarn and a weft yarn, and dyed and finished according to a conventional method.
【００４２】得られた織物を用いてズボンを縫製し、熟
練者５名による着用試験を行ない、着用感を判定した。Pants were sewn using the obtained woven fabric, and a wearing test was carried out by 5 experts to judge the wearing feeling.
【００４３】着用感とはストレッチ性、軽さおよび肌ざ
わりなどを総合した官能判定で、◎（極めて良好）、○
（良好）、△（やや不良）、×（不良）の４段階で評価
した。結果を表１に示す。The feeling of wearing is a sensory evaluation that comprehensively evaluates stretchability, lightness, and feel of the skin, and is ◎ (extremely good), ○
The evaluation was made in four grades of (good), Δ (somewhat bad), and × (bad). The results are shown in Table 1.
【００４４】[0044]
【表１】 [Table 1]
【００４５】本発明の複合糸を用いた織物は肌ざわり、
ストレッチ性、軽さ、着脱時の抵抗などに優れ、着用感
の良好なものであった。一方、比較例の織物はストレッ
チ性が不足し、着用感が劣るものであった。A woven fabric using the composite yarn of the present invention has a smooth texture,
It was excellent in stretchability, lightness, resistance when putting on and taking off, and had a good feeling of wearing. On the other hand, the woven fabrics of Comparative Examples lacked stretchability and were inferior in wearing feeling.
【００４６】[0046]
【発明の効果】本発明の複合糸を用いれば、嵩高性に富
み、ソフトな風合を有するとともに、ストレッチ性に優
れた着用感の改善された布帛が製造可能であり、フォー
マル衣料等に好適に使用できる。EFFECTS OF THE INVENTION By using the composite yarn of the present invention, it is possible to manufacture a fabric which is rich in bulkiness, has a soft texture, and has excellent stretchability and improved wearing feeling, and is suitable for formal clothing and the like. Can be used for
Claims (3)
チフィラメントＡおよびＢが混繊されてなる複合糸であ
って、該マルチフィラメントＡが下記 (１)〜 (２) の
特性を満足し、かつ該マルチフィラメントＢが下記
(ａ) 〜 (ｃ) の特性を満足する、機械的捲縮加工を施
すことなく沸騰水中で捲縮を発現することが可能なコン
ジュゲートフィラメントであることを特徴とするポリエ
ステル系複合糸。 (1) 切断伸度が50％以上 (2) 200 ℃における熱収縮応力が0.04ｇ／デニール以下 (a) 捲縮率が 5〜30％ (b) 沸騰水収縮率が 0％を越え20％以下 (c) 160 ℃における熱収縮応力が0.08ｇ／デニール以上1. A composite yarn obtained by mixing at least two types of polyester-based multifilaments A and B, wherein the multifilament A satisfies the following characteristics (1) to (2) and Filament B is below
A polyester-based composite yarn satisfying the characteristics (a) to (c), which is a conjugate filament capable of expressing crimp in boiling water without mechanical crimping. (1) Cutting elongation of 50% or more (2) Thermal shrinkage stress at 200 ° C of 0.04 g / denier or less (a) Crimping rate of 5 to 30% (b) Boiling water shrinkage of more than 0% to 20% (C) Heat shrinkage stress at 160 ℃ is 0.08g / denier or more
縮率が 8〜12％である請求項１記載のポリエスル系複合
糸。2. The polyester-based composite yarn according to claim 1, wherein the shrinkage rate of boiling water of the conjugate filament is 8 to 12%.
チレンテレフタレートおよびポリエチレンテレフタレー
トを主たる構成成分とする２種の成分がサイドバイサイ
ド型に複合紡糸されたコンジュゲートフィラメントであ
る請求項１または２記載のポリエスル系複合糸。3. The polyester composite yarn according to claim 1 or 2, wherein the conjugate filament is a conjugate filament in which two kinds of components mainly composed of polybutylene terephthalate and polyethylene terephthalate are side-by-side type composite spun. .