JPH0429414B2 - - Google Patents
Info
- Publication number
- JPH0429414B2 JPH0429414B2 JP9655884A JP9655884A JPH0429414B2 JP H0429414 B2 JPH0429414 B2 JP H0429414B2 JP 9655884 A JP9655884 A JP 9655884A JP 9655884 A JP9655884 A JP 9655884A JP H0429414 B2 JPH0429414 B2 JP H0429414B2
- Authority
- JP
- Japan
- Prior art keywords
- cristobalite
- moisture absorption
- humidity
- absorption rate
- calcium chloride
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【発明の詳細な説明】
この発明は天然産のクリストバライトに塩化カ
ルシウム、または塩化リチウムを担持させた、湿
度の変化に比例して吸湿率の変化する吸湿剤に関
するものである。 従来一般に使用されている吸湿剤としては、合
成ゼオライト、シリカゲル、塩化カルシウム、塩
化リチウム等があり、それぞれ長所と欠点を有す
る。そして一般に吸湿剤に要求される性能として
は、湿度に比例して吸湿量が増加し、湿度を調整
したり制御したりすることができることである。 合成ゼオライトは低湿度での吸湿率は高いが高
湿度においては吸湿率がそれほど高くならない。
またアルミナ系の吸湿剤は低湿度での吸湿率は低
く高湿度で急激に吸湿率を増す。シリカゲルにつ
いても高湿度での吸湿率が高い。 本発明者は、クリストバライトを用いる吸湿剤
について種々研究した結果、天然産のクリストバ
ライトは多孔質材料であつて比表面積が大であり
それのみでも若干の吸湿性能を示すが、このクリ
ストバライトに塩化カルシウム等を担持せしめれ
ば湿度の変化に比例して吸湿率が変化する性質の
ものとなることを知見した。 この発明はこれらの知見に基づくものであつて
クリストバライトを主体とする材料に塩化カルシ
ウム、塩化リチウムのうち少くとも一種を担持さ
せたことを特徴とする吸湿剤である。 この発明に用いる塩化カルシウムはCaCl2で示
される物質であつて、塩化リチウムはLiClで示さ
れる物質である。そしていずれも純度等が制限さ
れることはない。またこの発明におけるクリスト
バライトは天然産の多孔質材料であつて、ケイ酸
分80〜90％を含み、クリストバライトを主たる構
成鉱物とする素材である。そして直径５〜10μｍ
の球体の集合体であつて、その中に直径20〜200
〓の微細孔を有し、表面積は60〜70cm2／ｇであつ
て天然ゼオライトの約３倍以上を示す。また見掛
気孔率は40〜50％である。そしてこのクリストバ
ライトは単味でも吸湿性能を示す。 つぎにこのクリストバライトをこの発明に用い
る場合は、目的に応じて粉砕して適当な粒径範囲
の粒状物とするか、または粒砕産物を造粒して粒
状物とすることが望ましい。またクリストバライ
ト単味でも用いることができるが、他の無害な材
料を混合して用いることもできる。 この発見において、クリストバライトを主体と
する材料に塩化カルシウム等を担持せしめる方法
は、所定の粒径に調整した材料を塩化カルシウム
塩化リチウムの水溶液に一定時間浸漬したのち固
液分離し、その材料を乾燥させる方法か、粉末状
の材料に硫化カルシウム等及びバインダーを添加
して混練したのちに成形する方法が望ましい。 そしてこの発見において用いる塩化カルシウム
等の溶液の濃度、担持せしめる割合は吸湿剤の用
途、要求される性能により定められるもので敵宜
調整することができる。 上述のように本発明によれば湿度の変化に比例
して吸湿率が変化する性質の吸湿剤を得ることが
できるほか、天然産のクリストバライトを素材と
して用いるので安価で容易に得ることができる。 実施例 天然産のクリストバライトを粉砕し、粒径1.2
〜1.4mmに調整し乾燥したものを試料１として、
さらに試料１を塩化リチウム溶液（LiCl25％），
塩化カルシウム溶液（CaCl22.5％）にそれぞれ浸
漬し７時間後に固液分離し、そのクリストバライ
トを100℃で４時間乾燥したものを試料２，３と
した。 つぎにこの試料１〜２を湿度をそれぞれ20％，
50，90％に調整したデシケータの中に置き、48時
間後に取出して重量を測定し、吸湿前の重量との
差から吸湿率を算出した結果を第１表に示す。 なお、吸湿率は吸湿による増加量を吸湿前重量
に対する100分率で示す。 【表】
ルシウム、または塩化リチウムを担持させた、湿
度の変化に比例して吸湿率の変化する吸湿剤に関
するものである。 従来一般に使用されている吸湿剤としては、合
成ゼオライト、シリカゲル、塩化カルシウム、塩
化リチウム等があり、それぞれ長所と欠点を有す
る。そして一般に吸湿剤に要求される性能として
は、湿度に比例して吸湿量が増加し、湿度を調整
したり制御したりすることができることである。 合成ゼオライトは低湿度での吸湿率は高いが高
湿度においては吸湿率がそれほど高くならない。
またアルミナ系の吸湿剤は低湿度での吸湿率は低
く高湿度で急激に吸湿率を増す。シリカゲルにつ
いても高湿度での吸湿率が高い。 本発明者は、クリストバライトを用いる吸湿剤
について種々研究した結果、天然産のクリストバ
ライトは多孔質材料であつて比表面積が大であり
それのみでも若干の吸湿性能を示すが、このクリ
ストバライトに塩化カルシウム等を担持せしめれ
ば湿度の変化に比例して吸湿率が変化する性質の
ものとなることを知見した。 この発明はこれらの知見に基づくものであつて
クリストバライトを主体とする材料に塩化カルシ
ウム、塩化リチウムのうち少くとも一種を担持さ
せたことを特徴とする吸湿剤である。 この発明に用いる塩化カルシウムはCaCl2で示
される物質であつて、塩化リチウムはLiClで示さ
れる物質である。そしていずれも純度等が制限さ
れることはない。またこの発明におけるクリスト
バライトは天然産の多孔質材料であつて、ケイ酸
分80〜90％を含み、クリストバライトを主たる構
成鉱物とする素材である。そして直径５〜10μｍ
の球体の集合体であつて、その中に直径20〜200
〓の微細孔を有し、表面積は60〜70cm2／ｇであつ
て天然ゼオライトの約３倍以上を示す。また見掛
気孔率は40〜50％である。そしてこのクリストバ
ライトは単味でも吸湿性能を示す。 つぎにこのクリストバライトをこの発明に用い
る場合は、目的に応じて粉砕して適当な粒径範囲
の粒状物とするか、または粒砕産物を造粒して粒
状物とすることが望ましい。またクリストバライ
ト単味でも用いることができるが、他の無害な材
料を混合して用いることもできる。 この発見において、クリストバライトを主体と
する材料に塩化カルシウム等を担持せしめる方法
は、所定の粒径に調整した材料を塩化カルシウム
塩化リチウムの水溶液に一定時間浸漬したのち固
液分離し、その材料を乾燥させる方法か、粉末状
の材料に硫化カルシウム等及びバインダーを添加
して混練したのちに成形する方法が望ましい。 そしてこの発見において用いる塩化カルシウム
等の溶液の濃度、担持せしめる割合は吸湿剤の用
途、要求される性能により定められるもので敵宜
調整することができる。 上述のように本発明によれば湿度の変化に比例
して吸湿率が変化する性質の吸湿剤を得ることが
できるほか、天然産のクリストバライトを素材と
して用いるので安価で容易に得ることができる。 実施例 天然産のクリストバライトを粉砕し、粒径1.2
〜1.4mmに調整し乾燥したものを試料１として、
さらに試料１を塩化リチウム溶液（LiCl25％），
塩化カルシウム溶液（CaCl22.5％）にそれぞれ浸
漬し７時間後に固液分離し、そのクリストバライ
トを100℃で４時間乾燥したものを試料２，３と
した。 つぎにこの試料１〜２を湿度をそれぞれ20％，
50，90％に調整したデシケータの中に置き、48時
間後に取出して重量を測定し、吸湿前の重量との
差から吸湿率を算出した結果を第１表に示す。 なお、吸湿率は吸湿による増加量を吸湿前重量
に対する100分率で示す。 【表】
Claims (1)
- １ クリストバライトを主体とする材料に塩化カ
ルシウム、塩化リチウムのうち少くとも一種を担
持させたことを特徴とする吸湿剤。