JPH04202386A - 記録液 - Google Patents
記録液Info
- Publication number
- JPH04202386A JPH04202386A JP2329961A JP32996190A JPH04202386A JP H04202386 A JPH04202386 A JP H04202386A JP 2329961 A JP2329961 A JP 2329961A JP 32996190 A JP32996190 A JP 32996190A JP H04202386 A JPH04202386 A JP H04202386A
- Authority
- JP
- Japan
- Prior art keywords
- recording
- liquid
- recording liquid
- viscosity
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は、全体が圧電素材で作られた記録ヘッドを用い
て記録を行うインクジェット記録用の記録液に関するも
のである。
て記録を行うインクジェット記録用の記録液に関するも
のである。
インクジェット記録は、低騒音で高速印字が可能な記録
方法であり、最近急速に普及しつつある記録方法である
。このようなインクジェット記録は、記録液を加熱ある
いは加圧といった方法により小液滴として飛翔させ、こ
れを紙等の被記録部材に付着させて記録を行うものであ
る。
方法であり、最近急速に普及しつつある記録方法である
。このようなインクジェット記録は、記録液を加熱ある
いは加圧といった方法により小液滴として飛翔させ、こ
れを紙等の被記録部材に付着させて記録を行うものであ
る。
用いられる記録液は、通常水あるいは非水系液体を液媒
体とし、これに記録剤である。染料あるいは顔料を添加
して作製されている。
体とし、これに記録剤である。染料あるいは顔料を添加
して作製されている。
加圧により小液滴を形成する従来の方式の記録ヘッドは
一般に、記録液室壁面の一部に圧電素子を積層したもの
で、その圧電素子の変形により小液滴を飛翔させて記録
を行っている。この場合実際に作用する部分の面積が小
さく変位量が小さくなってしまうので、粘度の高い記録
液を吐出することは不可能であった。このため従来の記
録液は25℃における粘度がl0cP以下でなげればな
らないという制約を受けていた。
一般に、記録液室壁面の一部に圧電素子を積層したもの
で、その圧電素子の変形により小液滴を飛翔させて記録
を行っている。この場合実際に作用する部分の面積が小
さく変位量が小さくなってしまうので、粘度の高い記録
液を吐出することは不可能であった。このため従来の記
録液は25℃における粘度がl0cP以下でなげればな
らないという制約を受けていた。
また記録液の液媒体として非水系液体を用いると、非水
系液体が紙に非常に濡れ易く、このため普通紙上への印
字が大きく広がり、いわゆる滲み現象を起こしてしまう
。従ってこの場合普通紙対応の印字ができないという問
題があった。
系液体が紙に非常に濡れ易く、このため普通紙上への印
字が大きく広がり、いわゆる滲み現象を起こしてしまう
。従ってこの場合普通紙対応の印字ができないという問
題があった。
そこで本発明の目的は、液媒体として非水系液体を用い
て、かつ、滲み現象を抑制した記録液を提供することで
ある。
て、かつ、滲み現象を抑制した記録液を提供することで
ある。
すなわち、本発明の記録液はインクジェット記録用の記
録液であって、液媒体が非水性液体であり、25℃にお
ける粘度が10〜50cpであることを特徴とするもの
である。
録液であって、液媒体が非水性液体であり、25℃にお
ける粘度が10〜50cpであることを特徴とするもの
である。
本発明の記録液は、全体を圧電素材で作製した記録ヘッ
ド用の記録液である。この記録ヘッドは記録液室の壁面
全体を変形させることが容易であり、そのため高粘度の
記録液でも吐出することが可能という特徴をもっている
。
ド用の記録液である。この記録ヘッドは記録液室の壁面
全体を変形させることが容易であり、そのため高粘度の
記録液でも吐出することが可能という特徴をもっている
。
また、本発明の記録液は粘度が高いため、液媒体として
非水系液体を用いているにもかかわらず紙上での広がり
、滲みが抑制され、普通紙上でもきれいに印字すること
が可能である。
非水系液体を用いているにもかかわらず紙上での広がり
、滲みが抑制され、普通紙上でもきれいに印字すること
が可能である。
本発明の記録液は、少なくとも液媒体として非水系液体
、記録剤として染料あるいは顔料、および粘度調整剤と
して有機高分子材料あるいは無機微粒子等からなるもの
である。また、必要に応じて添加剤等を加えても良い。
、記録剤として染料あるいは顔料、および粘度調整剤と
して有機高分子材料あるいは無機微粒子等からなるもの
である。また、必要に応じて添加剤等を加えても良い。
本発明において非水系液体としてはたとえば、n−へキ
サン、n−へブタン等の脂肪族炭化水素、トルエン、キ
シレン等の芳香族炭化水素、n−プロピルアルコール、
シクロヘキシルアルコール等のアルコール、トリエチレ
ンクリコール、ジプロピレングリコール等のグリコール
、トリプロピレフ3”)っ−ヤ毛”1lfyウエーヶ、
い、ヤ。ッ7い、・アセテート等のグリコール誘導体、
酢酸エチル、酢酸イソプロピル等のエステル、メチルイ
ソブチルケトン、シクロヘキサノン等のケトン等が挙げ
られる。
サン、n−へブタン等の脂肪族炭化水素、トルエン、キ
シレン等の芳香族炭化水素、n−プロピルアルコール、
シクロヘキシルアルコール等のアルコール、トリエチレ
ンクリコール、ジプロピレングリコール等のグリコール
、トリプロピレフ3”)っ−ヤ毛”1lfyウエーヶ、
い、ヤ。ッ7い、・アセテート等のグリコール誘導体、
酢酸エチル、酢酸イソプロピル等のエステル、メチルイ
ソブチルケトン、シクロヘキサノン等のケトン等が挙げ
られる。
染料としてはたとえば、直接染料、酸性染料、塩基性染
料、および種々の油溶性染料等が挙げられる。また顔料
としてはたとえば、アゾ系、フタロシアニン系、キナク
リドン系、アンスラキノン系、ジオキサジン系、インジ
ゴ系、チオインジゴ系、ペリレン系、ペリレン系、イソ
インドリノン系、キノフタロy系、酸化チタン、カドミ
ウム系、酸化鉄系、カーボンブラック等が挙げられる。
料、および種々の油溶性染料等が挙げられる。また顔料
としてはたとえば、アゾ系、フタロシアニン系、キナク
リドン系、アンスラキノン系、ジオキサジン系、インジ
ゴ系、チオインジゴ系、ペリレン系、ペリレン系、イソ
インドリノン系、キノフタロy系、酸化チタン、カドミ
ウム系、酸化鉄系、カーボンブラック等が挙げられる。
有機高分子材料としてはたとえば、ロジン誘導体、マレ
イン酸樹脂、フマル酸樹脂、フェノール樹脂、キシノン
樹脂、尿素樹脂、メラミン樹脂、ケトン樹脂、アルキド
樹脂、ポリアミド樹脂、アクリル樹脂、ポリ塩化ビニル
、ポリ酢酸ビニル、ポリビニルアルコール、ブチラール
樹脂、スチレン樹脂、エポキシ樹脂、ポリウレタン、セ
ルロース誘導体等が挙げられる。また無機微粒子として
ハタとえば、SiO2、Al2O3、Fed。
イン酸樹脂、フマル酸樹脂、フェノール樹脂、キシノン
樹脂、尿素樹脂、メラミン樹脂、ケトン樹脂、アルキド
樹脂、ポリアミド樹脂、アクリル樹脂、ポリ塩化ビニル
、ポリ酢酸ビニル、ポリビニルアルコール、ブチラール
樹脂、スチレン樹脂、エポキシ樹脂、ポリウレタン、セ
ルロース誘導体等が挙げられる。また無機微粒子として
ハタとえば、SiO2、Al2O3、Fed。
Fe2O3、Cab、MgO、ゼオライト等が挙げられ
る。
る。
以上列挙した液媒体、記録剤および粘度調整剤は互いの
親和性および粘度等所望の特性を満足し得るように選択
して使用されるものである。
親和性および粘度等所望の特性を満足し得るように選択
して使用されるものである。
添加剤は、作製する記録液に必要に応じて適宜添加する
ものである。そのような添加剤としてはたとえば、分散
剤、表面張力調整剤、酸化防止剤、紫外線吸収剤、安定
剤等が挙げられる。
ものである。そのような添加剤としてはたとえば、分散
剤、表面張力調整剤、酸化防止剤、紫外線吸収剤、安定
剤等が挙げられる。
次に、本発明を実施例により更に詳しく説明する。
(実施例1)
トリエチーレングリコールモノーn−ブチルエーテル忙
ポリビニルブチラールを溶解し、このポリマ溶液に銅フ
タロシアニンブルー(粒子径z。
ポリビニルブチラールを溶解し、このポリマ溶液に銅フ
タロシアニンブルー(粒子径z。
μm)を遊星ボールミルを用いて分散して、下記の組成
の記録液を作製した。得られた記録液の分散状態は良好
で、安定であった。
の記録液を作製した。得られた記録液の分散状態は良好
で、安定であった。
く組成〉
トリエチレングリコール 92重量%七ノー〇
−プチルエーテル ポリビニルブチラール 3重量%銅フタロ
シアニンブルー 5重量%この記録液の粘度
は25℃で27.Ocpであった。
−プチルエーテル ポリビニルブチラール 3重量%銅フタロ
シアニンブルー 5重量%この記録液の粘度
は25℃で27.Ocpであった。
(実施例2)
トリプロピレングリコールモノメチルエーテルにポリビ
ニルピロリドンを溶解し、このポリマ溶液にカーボンブ
ラック(1次粒子径24nm、pH8)およびSiO2
微粒子(1次粒子径12n m )を遊星ボールミルを
用いて分散して、下記の組成の記録液を作製した。得ら
れた記録液の分散状前は良好で、安定であった。
ニルピロリドンを溶解し、このポリマ溶液にカーボンブ
ラック(1次粒子径24nm、pH8)およびSiO2
微粒子(1次粒子径12n m )を遊星ボールミルを
用いて分散して、下記の組成の記録液を作製した。得ら
れた記録液の分散状前は良好で、安定であった。
く組成〉
トリプロピレングリコール 85重量%モノメチ
ルエーテル ポリビニルピロリドン 8重量%カーボン
ブラック 4重量%SiO□微粒子
3重量%この記録液の粘度は2
5°Cで27.6CI)であった。
ルエーテル ポリビニルピロリドン 8重量%カーボン
ブラック 4重量%SiO□微粒子
3重量%この記録液の粘度は2
5°Cで27.6CI)であった。
(実施例3)
キシレンにポリスチレンを溶解し、サラニオイルブラッ
クHBBを溶解して下記の組成の記録液を作製した。
クHBBを溶解して下記の組成の記録液を作製した。
く組成〉
キシレン 83重量%ポリスチ
レン lO重量%オイルブラック
HBB 7重量%この記録液の粘度は2
5℃で14.7cpであった。
レン lO重量%オイルブラック
HBB 7重量%この記録液の粘度は2
5℃で14.7cpであった。
(実施例4)
実施例1〜3で作製した記録液をそれぞれ、全体が圧電
素材で作製されている記録ヘッドに搭載し、数種の普通
紙上に印字を行った。その結果各記録液とも良好に飛翔
した。また、印字について検討したところすべての紙に
対して広がりの少ない、円形のドツトが得られた。
素材で作製されている記録ヘッドに搭載し、数種の普通
紙上に印字を行った。その結果各記録液とも良好に飛翔
した。また、印字について検討したところすべての紙に
対して広がりの少ない、円形のドツトが得られた。
(比較例1)
実施例1においてポリビニルブチラールの量を減らし、
下記の組成の記録液を作製した。
下記の組成の記録液を作製した。
く組成〉
トリエチレングリコール 94重量%七ノー〇
−ブチルエーテル ポリビニルブチラール 1重量%銅フタロ
シアニンブルー 5重量%この記録液の粘度
は25℃で7.9Cpであった。
−ブチルエーテル ポリビニルブチラール 1重量%銅フタロ
シアニンブルー 5重量%この記録液の粘度
は25℃で7.9Cpであった。
(比較例2)
実施例2においてポリビニルピロリドンの量を減らし、
S iO2微粒子を添加せずに下記の組成の記録液を作
製した。
S iO2微粒子を添加せずに下記の組成の記録液を作
製した。
〈組成〉
トリプロピレングリコール 95重量%モノメチ
ルエーテル ポリビニルピロリドン 1重量%カーボ
ンブラック 4重量%この記録液の粘
度は25℃で5.2CI)であった。
ルエーテル ポリビニルピロリドン 1重量%カーボ
ンブラック 4重量%この記録液の粘
度は25℃で5.2CI)であった。
(比較例3)
実施例3においてポリスチレンの量を減らし、下記の組
成の記録液を作製した。
成の記録液を作製した。
く組成〉
キシレン 90重量%ポリスチ
レン 3重量%オイルブラックH
B8 7重量%どの記録液の粘度は25
°Cで3.5Cpであった。
レン 3重量%オイルブラックH
B8 7重量%どの記録液の粘度は25
°Cで3.5Cpであった。
(比較例4)
比較例1〜3で作製した記録液をそれぞれ、一実施例4
で用いたのと同じ記録ヘッドに搭載シ、同様に印字を行
った。各記録液の飛翔状況レマ良好であったが、印字は
大きく滲み、形状の悪(・ト°ットしか得られなかった
。
で用いたのと同じ記録ヘッドに搭載シ、同様に印字を行
った。各記録液の飛翔状況レマ良好であったが、印字は
大きく滲み、形状の悪(・ト°ットしか得られなかった
。
本発明の記録液は液媒体として非水性液体を用いている
にもかかわらず、粘度が高いため、紙等の被記録部材上
での広がり、滲みを抑制することができる。そのため本
発明の記録液は、普通紙上にもきれいに印字することが
可能で、被記録部材を選ぶ必要がない。
にもかかわらず、粘度が高いため、紙等の被記録部材上
での広がり、滲みを抑制することができる。そのため本
発明の記録液は、普通紙上にもきれいに印字することが
可能で、被記録部材を選ぶ必要がない。
Claims (1)
- インクジェット記録用の記録液において、液媒体が非水
性液体であり、25℃における粘度が10〜50cpで
あることを特徴とする記録液。