JPH04202207A - ゴム組成物 - Google Patents
ゴム組成物Info
- Publication number
- JPH04202207A JPH04202207A JP33178490A JP33178490A JPH04202207A JP H04202207 A JPH04202207 A JP H04202207A JP 33178490 A JP33178490 A JP 33178490A JP 33178490 A JP33178490 A JP 33178490A JP H04202207 A JPH04202207 A JP H04202207A
- Authority
- JP
- Japan
- Prior art keywords
- rubber composition
- sensitive adhesive
- pressure
- base
- acrylate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
〈産業上の利用分野〉
本発明は、粘着テープ基材に適したゴム組成物に関する
ものである。
ものである。
〈従来の技術〉
自動車のボディ側にサイドプロテクションモール（以下
モールという）を装着するために使用される粘着テープ
は、アクリルゴムの基材に粘着材が塗布されて構成され
ている。
モールという）を装着するために使用される粘着テープ
は、アクリルゴムの基材に粘着材が塗布されて構成され
ている。
〈発明が解決しようとする課題〉
ところが、洗車時において自動車に塗布されたワックス
を拭き取るためにワックスリムーバーを用いたり、ガソ
リン等の燃料の補給時にこれを誤ってこぼしたりして、
これ等ワックスリムーバー、ガソリン等の溶剤が付着し
て粘着剤とアクリルゴム基材の間で剥離する可能性があ
る。
を拭き取るためにワックスリムーバーを用いたり、ガソ
リン等の燃料の補給時にこれを誤ってこぼしたりして、
これ等ワックスリムーバー、ガソリン等の溶剤が付着し
て粘着剤とアクリルゴム基材の間で剥離する可能性があ
る。
本発明の目的は上記問題点を解消し、被着体との密着性
が良く、粘着剤との界面剥離を防止するゴム組成物を提
供するものである。
が良く、粘着剤との界面剥離を防止するゴム組成物を提
供するものである。
く課題を解決するための手段〉
使用するゴム組成物とはエチルアクリ１００重量部、グ
リシジルアクリレート０．２〜３０重量部、ｎ−ブチル
アクリレート１０〜５００重量部の共重合物に、アクリ
ルロトリル単独重合物１〜３０重量部を混合してなるゴ
ム組成物である。このようにゴム組成物にアクリロニト
リル単独重合物を混合させた目的は耐油性を向上させる
ものである。グリシジルアクリレートは、０．２重量部
以下でも３０重量部をこえても粘着テープの基材に適し
た軟らかいものが得られない。アクリロニトリルは、１
重量部以下では耐油性に欠け、３０重量部をこえても効
果があがらない。
リシジルアクリレート０．２〜３０重量部、ｎ−ブチル
アクリレート１０〜５００重量部の共重合物に、アクリ
ルロトリル単独重合物１〜３０重量部を混合してなるゴ
ム組成物である。このようにゴム組成物にアクリロニト
リル単独重合物を混合させた目的は耐油性を向上させる
ものである。グリシジルアクリレートは、０．２重量部
以下でも３０重量部をこえても粘着テープの基材に適し
た軟らかいものが得られない。アクリロニトリルは、１
重量部以下では耐油性に欠け、３０重量部をこえても効
果があがらない。
く作用・効果〉
上記手段を採用することにより、本発明のゴム組成物か
ら成る粘着テープ基材と粘着剤との分子間強さが向上す
るため、密着性が高められる。
ら成る粘着テープ基材と粘着剤との分子間強さが向上す
るため、密着性が高められる。
〈実施例〉
以下に、本発明を具体化した実施例について説明する。
ａ）試験片の製作
表に示す各種ゴム組成物を室温でシート状に押し出し、
そのシートの上に粘着剤を塗布後、１゜Ｏ°ＣＸ２分間
乾燥を行い、その後、他のアクリルゴム組成物を重ね合
わせて、引っ張り剪断用のテストピースとした。
そのシートの上に粘着剤を塗布後、１゜Ｏ°ＣＸ２分間
乾燥を行い、その後、他のアクリルゴム組成物を重ね合
わせて、引っ張り剪断用のテストピースとした。
ｂ）接着剤及び混合剤調製
ｎ−ブチルアクリレート１００重量部にアクリル酸５部
の３０％溶液と過酸化ベンゾイル（Ｂ。
の３０％溶液と過酸化ベンゾイル（Ｂ。
Ｐ、Ｏｏ）を７０℃Ｘ１５時間反応を行った。溶剤組成
はトルエン２０重量％、酢酸エチル８０重量％を用いて
粘着剤、混合剤の重合を行った。
はトルエン２０重量％、酢酸エチル８０重量％を用いて
粘着剤、混合剤の重合を行った。
溶剤としては、ベンゼン、トルエン、キシレン、酢酸メ
チル、酢酸エチル、酢酸イソプロピル、酢酸ブチル、ア
セトン、メチルエチルケトン、メチルインプロピルケト
ン、メチルイソブチルケトン、ヘプタン、ペンタン、ヘ
キサン、イソオクタン、デカン、シクロヘキサン、シク
ロヘキサノン、トリクレン等の育機溶剤が例示できる。
チル、酢酸エチル、酢酸イソプロピル、酢酸ブチル、ア
セトン、メチルエチルケトン、メチルインプロピルケト
ン、メチルイソブチルケトン、ヘプタン、ペンタン、ヘ
キサン、イソオクタン、デカン、シクロヘキサン、シク
ロヘキサノン、トリクレン等の育機溶剤が例示できる。
これらのゴム組成物を用いた剪断強さの試験結果を表に
示す。表から明らかなように、これらのゴム組成物を用
いた場合は、いずれの場合も高い剪断強さを示し、また
粘着テープ基材に適した軟らかいものが得られることが
わかる。
示す。表から明らかなように、これらのゴム組成物を用
いた場合は、いずれの場合も高い剪断強さを示し、また
粘着テープ基材に適した軟らかいものが得られることが
わかる。
（以下余白）
Claims (1)
- エチルアクリレート１００重量部に対して、グリシジ
ルアクリレート０．２〜３０重量部、ｎ−ブチルアクリ
レート１０〜５００重量部を混合重合した共重合体（Ａ
）よりなるゴム組成物。ただし、アクリロニトリル単独
重合体を加えてもよい。