JPH04202550A - ゴム組成物 - Google Patents
ゴム組成物Info
- Publication number
- JPH04202550A JPH04202550A JP33793690A JP33793690A JPH04202550A JP H04202550 A JPH04202550 A JP H04202550A JP 33793690 A JP33793690 A JP 33793690A JP 33793690 A JP33793690 A JP 33793690A JP H04202550 A JPH04202550 A JP H04202550A
- Authority
- JP
- Japan
- Prior art keywords
- pts
- weight
- copolymer
- parts
- rubber composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
〈産業上の利用分野〉
本発明は、粘着テープ基材に適したゴム組成物に関する
ものである。
ものである。
〈従来の技術〉
自動車のボディ側にサイドプロテクションモール(以下
モールという)を装着するために使用される粘着テープ
は、アクリルゴムの基材に粘着材が塗布されて構成され
ている。
モールという)を装着するために使用される粘着テープ
は、アクリルゴムの基材に粘着材が塗布されて構成され
ている。
〈発明が解決しようとする課題〉
ところが、洗車時において自動車に塗布されたワックス
を拭き取るためにワックスリムーバーを用いたり、ガソ
リン等の燃料の補給時にこれを誤ってこぼしたりして、
これ等ワックスリムーバー、ガソリン等の溶剤が付着し
て粘着剤とアクリルゴム基材の間で剥離する可能性があ
る。
を拭き取るためにワックスリムーバーを用いたり、ガソ
リン等の燃料の補給時にこれを誤ってこぼしたりして、
これ等ワックスリムーバー、ガソリン等の溶剤が付着し
て粘着剤とアクリルゴム基材の間で剥離する可能性があ
る。
本発明の目的は上記問題点を解消し、被着体との密着性
が良く、粘着剤との界面剥離を防止するゴム組成物を提
供するものである。
が良く、粘着剤との界面剥離を防止するゴム組成物を提
供するものである。
く課題を解決するための手段〉
本発明のゴム組成物とはエチルアクリレート、アリルグ
リシジルエーテルの共重合物100重量部に対して、n
−ブチルアクリレート100重量部、アクリロニトリル
1〜30重量部の共重合体を混合してなるゴム組成物で
ある。このようにアクリロニトリルを共重合させた目的
は耐油性を向上させるもので、1重量部以下では耐油性
に欠け、30重量部をこえても効果があがらない。
リシジルエーテルの共重合物100重量部に対して、n
−ブチルアクリレート100重量部、アクリロニトリル
1〜30重量部の共重合体を混合してなるゴム組成物で
ある。このようにアクリロニトリルを共重合させた目的
は耐油性を向上させるもので、1重量部以下では耐油性
に欠け、30重量部をこえても効果があがらない。
〈作用・効果〉
上記手段を採用することにより、本発明のゴム組成物か
ら成る一粘着テープ基材と粘着剤との分子間強さが向上
するため、密着性が高められる。
ら成る一粘着テープ基材と粘着剤との分子間強さが向上
するため、密着性が高められる。
〈実施例〉
以下に、本発明を具体化した実施例について説明する。
a)試験片の製作
表に示す各種ゴム組成物を室温でシート状に押し出し、
そのシートの上に粘着剤を塗布後、100℃×2分間乾
燥を行い、その後、他のアクリルゴム組成物を重ね合わ
せて、引っ張り剪断用のテストピースとした。
そのシートの上に粘着剤を塗布後、100℃×2分間乾
燥を行い、その後、他のアクリルゴム組成物を重ね合わ
せて、引っ張り剪断用のテストピースとした。
b)粘着剤及び混合剤の調製
アクリルモノマーの30%溶液と過酸化ベンゾイル(B
、P、O,)を70℃×15時間反応を行なった。溶剤
組成はトルエン20重量%、酢酸エテル80重量%を用
いて粘着剤、混合剤の重合を行なった・ 溶剤としては、ベンゼン、トルエン、キシレン、酢酸メ
チル、酢酸エチル、酢酸イソプロピル、酢酸ブチル、ア
セトン、メチルエチルケトン、メチルイソプロピルケト
ン、メチルイソブチルケトン、ヘプタン、ペンタン、ヘ
キサン、イソオクタン、デカン、シクロヘキサン、シク
ロヘキサノン、トリクレン等の有機溶剤か例示できる。
、P、O,)を70℃×15時間反応を行なった。溶剤
組成はトルエン20重量%、酢酸エテル80重量%を用
いて粘着剤、混合剤の重合を行なった・ 溶剤としては、ベンゼン、トルエン、キシレン、酢酸メ
チル、酢酸エチル、酢酸イソプロピル、酢酸ブチル、ア
セトン、メチルエチルケトン、メチルイソプロピルケト
ン、メチルイソブチルケトン、ヘプタン、ペンタン、ヘ
キサン、イソオクタン、デカン、シクロヘキサン、シク
ロヘキサノン、トリクレン等の有機溶剤か例示できる。
尚、エチルアクリレートーアリルクリシジルエーテル共
重合体の重合は、エチルアクリレート100重量部に対
してアリルグリシジルエーテル0.2〜30重量部(■
0.2.■1゜0.■5゜0、■10.0.■30.0
)、n−ブチルアクリレート−アクリロニトリル共重合
体の重合は、n−ブチルアクリレート100重量部に対
してアクリロニトリル1〜30重量部(■1.0.■5
.0.■10.0.■20.0.■30.0)で70°
C×24時間、過酸化ベンゾイル(B、 P。
重合体の重合は、エチルアクリレート100重量部に対
してアリルグリシジルエーテル0.2〜30重量部(■
0.2.■1゜0.■5゜0、■10.0.■30.0
)、n−ブチルアクリレート−アクリロニトリル共重合
体の重合は、n−ブチルアクリレート100重量部に対
してアクリロニトリル1〜30重量部(■1.0.■5
.0.■10.0.■20.0.■30.0)で70°
C×24時間、過酸化ベンゾイル(B、 P。
0、)0.05重量部を用いておこなった。(■〜■は
、表中の■〜■に対応する。) これらのゴム組成物を用いた剪断強さの試験結果を表に
示す。表から明らかなように、これらのゴム組成物を用
いた場合は、比較例と比べて著しく剪断強さが向上して
いることがわかる。
、表中の■〜■に対応する。) これらのゴム組成物を用いた剪断強さの試験結果を表に
示す。表から明らかなように、これらのゴム組成物を用
いた場合は、比較例と比べて著しく剪断強さが向上して
いることがわかる。
Claims (1)
- エチルアクリレート100重量部に対して、アリルグリ
シジルエーテル0.2〜30重量部を混合重合した共重
合体(A)100重量部と、n−ブチルアクリレート1
00重量部、アクリロニトリル1〜30重量部の共重合
体(B)1〜300重量部よりなるゴム組成物。