JPH04121841A - 光記録媒体と光記録媒体用反射膜 - Google Patents
光記録媒体と光記録媒体用反射膜Info
- Publication number
- JPH04121841A JPH04121841A JP2242110A JP24211090A JPH04121841A JP H04121841 A JPH04121841 A JP H04121841A JP 2242110 A JP2242110 A JP 2242110A JP 24211090 A JP24211090 A JP 24211090A JP H04121841 A JPH04121841 A JP H04121841A
- Authority
- JP
- Japan
- Prior art keywords
- thin film
- optical recording
- recording medium
- mainly composed
- essentially consisting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
産業上の利用分野
本発明はレーザービーム等により、情報を高密基 大容
量で記録再生及び消去できる光記録媒体に関するもので
あも 従来の技術 ビデオディス久 コンパクトディスク等の再生専用の情
報記録媒体や追記型ディス久 書換えが自在な相変化デ
ィス久 光磁気ディスク等のレーザー光による情報の読
み出し或いは記録消去を行う各種情報記録媒体はその背
面に反射金属膜を設けた構造にしたものが広く用いられ
ていも 例えば書換えが自在な相変化型ディスクの構造
は第3図に示すようにあらかじめレーザー光案内用の溝
を形成したポリカーボネート等の透明基板1の溝面側に
第1の誘電体層2、記録膜3、第2の誘電体層4、反射
膜5を順次形成した後、接着剤6により保護板7、また
はもう一つのディスクを貼合わせたものが一般的であも
ここでは第1、第2の誘電体層2.4、記録膜3、反
射層5の形成方法としては 一般的に真空蒸着、スパッ
タリング法が用いられも また反射膜5の材料としては
安価で反射率の高いAlまたはAl合金が一般的に使用
されていも 配板 消去および再生のレーザー光は矢印Aの方向より
入射し 情報に応じて強度変調を施しまた反射光を検出
して行うものであム ここで反射層材料としてAlを用
いた場合その光学特性が劣化して、追記監 あるいは書
換え自在な光記録媒体においてその書き込へ 及び読み
出しの特性が著しく劣化する場合があも これはAlに
よる反射層5が腐食して平面性を失い反射率が低下する
ことに起因するものであム 例えばAlの耐食性は高純
度のAlを用いれば成程度の改善は可能であるが結晶成
長の回避はできない。またAlに添加剤を入れて耐食性
を改善する方法もあるが十分でなしも発明が解決しよう
とする課題 本発明は上述のような反射層を有した光記録媒体に於て
反射層の化学的安定法 経済性にすぐれた光記録媒体を
提供することを目的とすも課題を解決するための手段 本発明は上記課題を解決するために透明基板の一方の面
に記録風 反射層 または第1の誘電体層 記録風 第
2の誘電体層 反射層を順次形成した光記録媒体におい
て前記反射層を少なくとも2層の膜で形成するものであ
も 作用 すなわ板 前記反射層がAlを主成分とする薄膜とAu
を主成分とする薄膜からなり、Alを主成分とする薄膜
の少なくとも一方の面にAuを主成分とする薄膜を形成
することにより保護板 あるいは接着剤を透過してきた
水分や接着剤が硬化するときに出す酸などによる酸化
腐食等を防止できるものであも 実施例 (実施例1) 以下、本発明の1実施例について図面を基に説明すも
第1図において従来と同一構成要素は同一番号で示す。
量で記録再生及び消去できる光記録媒体に関するもので
あも 従来の技術 ビデオディス久 コンパクトディスク等の再生専用の情
報記録媒体や追記型ディス久 書換えが自在な相変化デ
ィス久 光磁気ディスク等のレーザー光による情報の読
み出し或いは記録消去を行う各種情報記録媒体はその背
面に反射金属膜を設けた構造にしたものが広く用いられ
ていも 例えば書換えが自在な相変化型ディスクの構造
は第3図に示すようにあらかじめレーザー光案内用の溝
を形成したポリカーボネート等の透明基板1の溝面側に
第1の誘電体層2、記録膜3、第2の誘電体層4、反射
膜5を順次形成した後、接着剤6により保護板7、また
はもう一つのディスクを貼合わせたものが一般的であも
ここでは第1、第2の誘電体層2.4、記録膜3、反
射層5の形成方法としては 一般的に真空蒸着、スパッ
タリング法が用いられも また反射膜5の材料としては
安価で反射率の高いAlまたはAl合金が一般的に使用
されていも 配板 消去および再生のレーザー光は矢印Aの方向より
入射し 情報に応じて強度変調を施しまた反射光を検出
して行うものであム ここで反射層材料としてAlを用
いた場合その光学特性が劣化して、追記監 あるいは書
換え自在な光記録媒体においてその書き込へ 及び読み
出しの特性が著しく劣化する場合があも これはAlに
よる反射層5が腐食して平面性を失い反射率が低下する
ことに起因するものであム 例えばAlの耐食性は高純
度のAlを用いれば成程度の改善は可能であるが結晶成
長の回避はできない。またAlに添加剤を入れて耐食性
を改善する方法もあるが十分でなしも発明が解決しよう
とする課題 本発明は上述のような反射層を有した光記録媒体に於て
反射層の化学的安定法 経済性にすぐれた光記録媒体を
提供することを目的とすも課題を解決するための手段 本発明は上記課題を解決するために透明基板の一方の面
に記録風 反射層 または第1の誘電体層 記録風 第
2の誘電体層 反射層を順次形成した光記録媒体におい
て前記反射層を少なくとも2層の膜で形成するものであ
も 作用 すなわ板 前記反射層がAlを主成分とする薄膜とAu
を主成分とする薄膜からなり、Alを主成分とする薄膜
の少なくとも一方の面にAuを主成分とする薄膜を形成
することにより保護板 あるいは接着剤を透過してきた
水分や接着剤が硬化するときに出す酸などによる酸化
腐食等を防止できるものであも 実施例 (実施例1) 以下、本発明の1実施例について図面を基に説明すも
第1図において従来と同一構成要素は同一番号で示す。
反射層5はAlを主成分とした薄膜5−a、Auを主成
分とした薄膜5−bからなっていも ここでハAuを主
成分とした薄膜5−bはAlを主成分とした薄膜の外側
に形成していも これにより保護板7、あるいは接着剤
6を透過してきた水分、あるいは接着剤5の硬化時に出
す酸などの影響を化学的に安定なAuを主成分とする薄
膜のバリア層によって阻止しAlを主成分とする薄膜の
腐九 酸化を防止できるものであも ここで反射層5−
aの膜厚でAlを主成分とする薄膜の膜厚は10〜15
0nmの範囲がよく、好ましくは60〜130nmの範
囲が′よ(〜 またAuを主成分とする薄膜5−bの膜
厚は10〜30nmの範囲がよLy 9層mよりも薄
くなると完全な膜にならず島状の膜となるためバリア層
としての効果が小さくなり、逆に40nmよりも厚くす
ると高価になるため好ましくな(t そのためAuを主
成分とする薄膜の膜厚は10〜30nm範囲が適当であ
も 本実施例のディスク構成において、第1の誘電体層
約150nm、記録膜約30nm、第2の誘電体層約2
0nm、 Alを主成分とする薄膜1100n、 Au
を主成分とする薄膜20nmを順次形成した檄 紫外線
硬化型の接着剤により保護板を貼り合わせてディスク化
した このディスクを80℃で相対湿度80%の雰囲気
で一ケ月間加速試験を行った檄 取り出して反射膜の腐
食状態を調べたが劣化が認められなかった (実施例2) 次に第2の実施例について説明すも 第2図において、
同一構成要素は同一番号で示す。第1の実施例と異なる
ところは反射層の構成であって、Alを主成分とする薄
膜の両側にAuを主成分とする薄膜を形成するものであ
ム この場合、記録膜側のAuを主成分とする薄膜5−
cは反射率を向上させる効果があa ここでAuを主成
分とした薄膜5−b、5−cの膜厚はそれぞれ10〜3
0n[[lの範囲がよ11Xo9nm以下にすると膜が
島状になり薄膜5−Cの場合反射率を向上させる効果が
小さくな4薄膜5−bの場合膜厚が9層m以下の場合は
島状の膜のすきまから水分等が侵入してAlを主成分に
した薄膜が劣化するため好ましくない。膜厚は40nm
より厚くすると高価になり経済性が悪t、% 従って
薄膜5−b、5−cの膜厚は10〜30nmの範囲が適
当であも またAlを主成分とする薄膜の両側に化学的
に安定なAuを主成分とする薄膜を設けているたべ 保
護板 あるいは接着剤を透過してきた水分、あるいは接
着剤が硬化時に出す酸等の影響については更に強くなる
ものであも 本実施例のディスク構成において第1、第
2の誘電体層、 記録膜の膜厚は実施例1と同一にし
反射層の構成をAuを主成分とする薄膜5−cの膜厚を
20nm、Alを主成分とする薄膜の膜厚を100nm
、 Auを主成分とする薄膜の膜厚5−bを20nmを
順次形成して紫外線硬化型接着剤により保護板を貼合わ
せてディスク化しへ このディスクを80℃で相対湿度
80%の雰囲気中で一ケ月間加速試験を行ったが反射膜
の腐食等による劣化は認められなかった 発明の詳細 な説明してきたように反射層の膜厚構成を少なくとも2
層の膜からなるように構成し?、Alを主成分とする薄
膜の少なくとも一方の面に化学的に安定なAuを主成分
とする薄膜を形成することにより水分の侵入や接着剤が
硬化するときに出す酸等による腐食 あるいは酸化を防
止することができ耐食性が向上すム またAuを主成分
とする薄膜は 薄<Alを主成分とする薄膜にコーティ
ングするだけでよく経済的になム
分とした薄膜5−bからなっていも ここでハAuを主
成分とした薄膜5−bはAlを主成分とした薄膜の外側
に形成していも これにより保護板7、あるいは接着剤
6を透過してきた水分、あるいは接着剤5の硬化時に出
す酸などの影響を化学的に安定なAuを主成分とする薄
膜のバリア層によって阻止しAlを主成分とする薄膜の
腐九 酸化を防止できるものであも ここで反射層5−
aの膜厚でAlを主成分とする薄膜の膜厚は10〜15
0nmの範囲がよく、好ましくは60〜130nmの範
囲が′よ(〜 またAuを主成分とする薄膜5−bの膜
厚は10〜30nmの範囲がよLy 9層mよりも薄
くなると完全な膜にならず島状の膜となるためバリア層
としての効果が小さくなり、逆に40nmよりも厚くす
ると高価になるため好ましくな(t そのためAuを主
成分とする薄膜の膜厚は10〜30nm範囲が適当であ
も 本実施例のディスク構成において、第1の誘電体層
約150nm、記録膜約30nm、第2の誘電体層約2
0nm、 Alを主成分とする薄膜1100n、 Au
を主成分とする薄膜20nmを順次形成した檄 紫外線
硬化型の接着剤により保護板を貼り合わせてディスク化
した このディスクを80℃で相対湿度80%の雰囲気
で一ケ月間加速試験を行った檄 取り出して反射膜の腐
食状態を調べたが劣化が認められなかった (実施例2) 次に第2の実施例について説明すも 第2図において、
同一構成要素は同一番号で示す。第1の実施例と異なる
ところは反射層の構成であって、Alを主成分とする薄
膜の両側にAuを主成分とする薄膜を形成するものであ
ム この場合、記録膜側のAuを主成分とする薄膜5−
cは反射率を向上させる効果があa ここでAuを主成
分とした薄膜5−b、5−cの膜厚はそれぞれ10〜3
0n[[lの範囲がよ11Xo9nm以下にすると膜が
島状になり薄膜5−Cの場合反射率を向上させる効果が
小さくな4薄膜5−bの場合膜厚が9層m以下の場合は
島状の膜のすきまから水分等が侵入してAlを主成分に
した薄膜が劣化するため好ましくない。膜厚は40nm
より厚くすると高価になり経済性が悪t、% 従って
薄膜5−b、5−cの膜厚は10〜30nmの範囲が適
当であも またAlを主成分とする薄膜の両側に化学的
に安定なAuを主成分とする薄膜を設けているたべ 保
護板 あるいは接着剤を透過してきた水分、あるいは接
着剤が硬化時に出す酸等の影響については更に強くなる
ものであも 本実施例のディスク構成において第1、第
2の誘電体層、 記録膜の膜厚は実施例1と同一にし
反射層の構成をAuを主成分とする薄膜5−cの膜厚を
20nm、Alを主成分とする薄膜の膜厚を100nm
、 Auを主成分とする薄膜の膜厚5−bを20nmを
順次形成して紫外線硬化型接着剤により保護板を貼合わ
せてディスク化しへ このディスクを80℃で相対湿度
80%の雰囲気中で一ケ月間加速試験を行ったが反射膜
の腐食等による劣化は認められなかった 発明の詳細 な説明してきたように反射層の膜厚構成を少なくとも2
層の膜からなるように構成し?、Alを主成分とする薄
膜の少なくとも一方の面に化学的に安定なAuを主成分
とする薄膜を形成することにより水分の侵入や接着剤が
硬化するときに出す酸等による腐食 あるいは酸化を防
止することができ耐食性が向上すム またAuを主成分
とする薄膜は 薄<Alを主成分とする薄膜にコーティ
ングするだけでよく経済的になム
第1図は本発明の第1実施例を示す光記録媒体の一部省
略断面図 第2図は本発明の第2の実施例を示す光記録
媒体の一部省略断面図 第3図は従来の構成を示す光記
録媒体の一部省略断面図であ4 1・・・・ディスク基板、 2・・・・第1の誘電休息
3・・・・記録j14・・・・第2の誘電体層、射!i
k 5−a・・・・Alを主成分とする薄A5−c・・
・・Auを主成分とする薄罠代理人の氏名 弁理士 小
鍜治 明 ほか2名5・・・・反 −b1 第 図 富 図 第 図 \ ’/ ティスフ暮預 7隙!1lfi ゝ2 電Iの譜電俸1 7保躇預
略断面図 第2図は本発明の第2の実施例を示す光記録
媒体の一部省略断面図 第3図は従来の構成を示す光記
録媒体の一部省略断面図であ4 1・・・・ディスク基板、 2・・・・第1の誘電休息
3・・・・記録j14・・・・第2の誘電体層、射!i
k 5−a・・・・Alを主成分とする薄A5−c・・
・・Auを主成分とする薄罠代理人の氏名 弁理士 小
鍜治 明 ほか2名5・・・・反 −b1 第 図 富 図 第 図 \ ’/ ティスフ暮預 7隙!1lfi ゝ2 電Iの譜電俸1 7保躇預
Claims (7)
- (1)透明基板の一方の面に、記録膜、反射層を、また
は第1の誘電体層、記録膜、第2の誘電体層、反射層を
順次形成した光記録媒体であって、前記反射層が少なく
とも2層の膜からなることを特徴とする光記録媒体。 - (2)反射層がAlを主成分とする材料と、Auを主成
分とする材料からなることを特徴とする請求項1記載の
光記録媒体。 - (3)反射層がAlを主成分とする薄膜の少なくとも1
方の面にAuを主成分とする薄膜を形成してなることを
特徴とする請求項1または2記載の光記録媒体。 - (4)Alを主成分とする材料とAuを主成分とする材
料を積層してなる光記録媒体用反射膜。 - (5)Alを主成分とする薄膜の膜厚を10〜150n
m、Auを主成分とする薄膜の膜厚を5〜30nmの範
囲にすることを特徴とする光記録媒体。 - (6)透明基板の一方の面に記録膜と、Alを主成分と
する薄膜の少なくとも一方の面にAuを主成分とした薄
膜を形成した反射層とを形成した光記録媒体。 - (7)透明基板の一方の面に、第1の誘電体層、記録膜
、第2の誘電体層、Alを主成分とする薄膜の少なくと
も一方の面にAuを主成分とする薄膜を形成した反射層
を、順次形成した光記録媒体。