JPH0334474B2 - - Google Patents
Info
- Publication number
- JPH0334474B2 JPH0334474B2 JP59002083A JP208384A JPH0334474B2 JP H0334474 B2 JPH0334474 B2 JP H0334474B2 JP 59002083 A JP59002083 A JP 59002083A JP 208384 A JP208384 A JP 208384A JP H0334474 B2 JPH0334474 B2 JP H0334474B2
- Authority
- JP
- Japan
- Prior art keywords
- heat
- color
- substance
- sensitive recording
- recording material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
本発明は感熱記録体に関するもので、更にくわ
しくは発色画像の可塑剤に対する安定性を向上さ
せた感熱記録体に関するものである。 従来より例えばクリスタルバイオレツトラクト
ンのような発色性物質と、フエノール性物質が反
応して発色することは知られており、これらを用
いて熱的に発色させることも、たとえば米国特許
第3539375号において公知である。 しかしながら発色性物質とフエノール性物質な
いし有機酸の熱反応により得られる発色画像は、
一般に光や温度、湿度の変化に対して非常に不安
定である。のみならずゴム、プラスチツク等に使
用される各種の可塑剤、たとえばフタル酸ジオク
チル、フタル酸ジブチル、フタル酸ジヘキシル、
フタル酸ブチルベンジル、リン酸トリクレジル、
アジピン酸ジオクチル等に対しても不安定で、こ
れらの可塑剤が添加されたゴム、プラスチツク等
と発色画像が接触すると、画像が消えてしまつた
り、変色してしまうといつた大きな欠点を有して
いる。光、温度、湿度の変化に対する発色画像の
安定性の向上はもちろん重要であり、従つて少く
とも同時に又は独立に解決されるべき問題も残さ
れているが、本発明はゴム、プラスチツク等に使
用される可塑剤に対する発色画像の安定性(以下
耐可塑剤性という)向上に関するものである。 近年フアクシミリ、電子計算機、テレツクスな
どの情報用機器の入出力端で使用される記録媒
体、また駅務省力化機器など輸送関連分野で使用
される入出力記録媒体として感熱記録材料が増加
しており、これら感熱記録材料が各種の可塑剤を
含むプラスチツクシートや定期券入れ等に直接間
接に接触する機会が増加している。そこで感熱記
録材料を発色させて長期間使用し可塑剤と接触さ
せた場合の記録媒体としての信頼性の改善が急務
であつた。もとよりこれら要求性能を向上させる
べき努力がなされているが未だ満足な性能を有す
るものが得られていないのが現状である。 本発明者らはこの欠点を改良すべく種々検討し
た結果、感熱記録体のフエノール物質として一般
式 (ただしnは1〜10) で表わされる物質を感熱層中に含有させることに
より、発色部分の耐可塑剤性が著しく向上するこ
とを見出し、本発明をなすに至つた。 本発明において上記一般式で表わされる物質
は、感熱記録層の全固形分中に1〜40重量%含有
させることにより目的を達することができる。ま
た上記一般式で表わされる物質と、他の公知のフ
エノール性物質とを併用することも可能である。 本発明で使用される無色ないし淡色の発色性物
質は、フエノール性物質と熱時反応して発色する
物質であつて、たとえばトリフエニルメタン系、
トリフエニルメタンフタリド系、フルオラン系、
ロイコオーラミン系、スピロピラン系などの各種
のロイコ化合物があげられる。 微粒子状に分散された発色性物質とフエノール
性物質は、感熱記録材料として保存中発色しない
ように接着剤によつて互に隔離して固着される。
本発明の感熱記録体に使用される接着剤は、たと
えばカゼイン、ゼラチン、変性澱粉、カルボキシ
メチルセルロース、ヒドロキシエチルセルロー
ス、ポリビニルアルコール、ポリビニルピロリド
ン、スチレン無水マレイン酸共重合物とこのアル
カリ溶解物、ポリアクリルアマイド、スチレンブ
タジエン共重合体、ポリ酢酸ビニル、ポリアクリ
ル酸エステルのラテツクス類などがあげられる。 本発明の感熱記録体には、必要に応じて記録層
中に他の添加物質、例えば記録特性向上のための
各種ワツクス類、脂肪酸アミド類、ステイツク防
止のための各種脂肪酸金属塩、表面の白色度、自
然性、筆記性を良くするために白色顔料、填料、
耐水性向上のための耐水化剤等が添加される。 本発明の感熱記録体は次のようにしてつくられ
る。発色性物質、フエノール性物質、感度調整剤
その他の添加剤を、適当な濃度の接着剤を含む水
系媒体中でボールミルなどの粉砕機を使用して粉
砕分散して感熱組成物を得る。 各構成物質は出来るだけ微粒化することが発色
効率の点で有利であり、1〜3μの粒径に微粒化
することが好ましい。 こうして得られた感熱記録組成物を適当な支持
体に塗布し、乾燥して本発明の感熱記録体を得
る。支持体としては上質紙、中質紙、コート紙を
はじめとする紙、プラスチツクフイルム、フイル
ムラミネート紙、織布シートなどがあげられる。
かくして得られる本発明の感熱記録体は、各種の
可塑剤に対してすぐれた耐可塑剤性を発揮し、発
色画像を長時間これらの可塑剤と接触させても画
像がきえたり変色することがないうえ、地かぶり
などその他の性質も良好である。 本発明を実施例により更に詳細に説明する。 実施例 1 (a) 感熱記録組成物の製造 A液 フルオラン系黒発色染料(新日曹化工製PSD
150) 5重量部 ステアリン酸アミド 15重量部 クレー 20 〃 ポリビニルアルコール10%水溶液 40 〃 水 20 〃 B液 2,2′,4,4′−テトラオキシアジポフエノン
20重量部 クレー 20 〃 ポリビニルアルコール10%水溶液 40 〃 水 20 〃 A液およびB液をそれぞれ別々に遠心ボール
ミルで4時間分散後、A液、B液を混合して感
熱記録組成物(塗料)を調整した。 (b) この感熱記録組成物を50g/m2の一般紙に乾
燥後の塗布量が7g/m2となるように塗布し、
感熱記録体を得た。 (c) ついでこの感熱記録体について次の手順によ
り耐可塑剤性を調べた。先ず感熱記録体を静的
発色試験器(スタンプ式)で圧力2Kg/cm2、温
度130℃、時間1秒で発色させた。次に耐可塑
剤性の試験として感熱記録体の発色部分に市販
のプラスチツク消ゴムをのせ、更に消ゴムの上
に300gの錘をのせ、1日間放置した。 その後試験前後の発色部分の濃度をマクベス反
射濃度計RD−514で測定し、表の結果を得た。 実施例 2 実施例1のB液における2,2′,4,4′−テト
ラオキシアジポフエノンの代りに2,2′,4,
4′−テトラオキシセバチフエノンを使用した以外
は実施例1と全く同様にして感熱記録体を得、耐
可塑剤性の試験を行なつた。結果を表に示す。 比較例1、比較例2 実施例1のB液における2,2′,4,4′−テト
ラオキシアジポフエノンの代りにビスフエノール
Aを使用したものを比較例1、ベンジルP−ヒド
ロキシベンゾエートを使用したものを比較例2と
し、以下実施例1と全く同様にして感熱記録体を
得、耐可塑剤性の試験を行なつた。結果を表に示
す。
しくは発色画像の可塑剤に対する安定性を向上さ
せた感熱記録体に関するものである。 従来より例えばクリスタルバイオレツトラクト
ンのような発色性物質と、フエノール性物質が反
応して発色することは知られており、これらを用
いて熱的に発色させることも、たとえば米国特許
第3539375号において公知である。 しかしながら発色性物質とフエノール性物質な
いし有機酸の熱反応により得られる発色画像は、
一般に光や温度、湿度の変化に対して非常に不安
定である。のみならずゴム、プラスチツク等に使
用される各種の可塑剤、たとえばフタル酸ジオク
チル、フタル酸ジブチル、フタル酸ジヘキシル、
フタル酸ブチルベンジル、リン酸トリクレジル、
アジピン酸ジオクチル等に対しても不安定で、こ
れらの可塑剤が添加されたゴム、プラスチツク等
と発色画像が接触すると、画像が消えてしまつた
り、変色してしまうといつた大きな欠点を有して
いる。光、温度、湿度の変化に対する発色画像の
安定性の向上はもちろん重要であり、従つて少く
とも同時に又は独立に解決されるべき問題も残さ
れているが、本発明はゴム、プラスチツク等に使
用される可塑剤に対する発色画像の安定性(以下
耐可塑剤性という)向上に関するものである。 近年フアクシミリ、電子計算機、テレツクスな
どの情報用機器の入出力端で使用される記録媒
体、また駅務省力化機器など輸送関連分野で使用
される入出力記録媒体として感熱記録材料が増加
しており、これら感熱記録材料が各種の可塑剤を
含むプラスチツクシートや定期券入れ等に直接間
接に接触する機会が増加している。そこで感熱記
録材料を発色させて長期間使用し可塑剤と接触さ
せた場合の記録媒体としての信頼性の改善が急務
であつた。もとよりこれら要求性能を向上させる
べき努力がなされているが未だ満足な性能を有す
るものが得られていないのが現状である。 本発明者らはこの欠点を改良すべく種々検討し
た結果、感熱記録体のフエノール物質として一般
式 (ただしnは1〜10) で表わされる物質を感熱層中に含有させることに
より、発色部分の耐可塑剤性が著しく向上するこ
とを見出し、本発明をなすに至つた。 本発明において上記一般式で表わされる物質
は、感熱記録層の全固形分中に1〜40重量%含有
させることにより目的を達することができる。ま
た上記一般式で表わされる物質と、他の公知のフ
エノール性物質とを併用することも可能である。 本発明で使用される無色ないし淡色の発色性物
質は、フエノール性物質と熱時反応して発色する
物質であつて、たとえばトリフエニルメタン系、
トリフエニルメタンフタリド系、フルオラン系、
ロイコオーラミン系、スピロピラン系などの各種
のロイコ化合物があげられる。 微粒子状に分散された発色性物質とフエノール
性物質は、感熱記録材料として保存中発色しない
ように接着剤によつて互に隔離して固着される。
本発明の感熱記録体に使用される接着剤は、たと
えばカゼイン、ゼラチン、変性澱粉、カルボキシ
メチルセルロース、ヒドロキシエチルセルロー
ス、ポリビニルアルコール、ポリビニルピロリド
ン、スチレン無水マレイン酸共重合物とこのアル
カリ溶解物、ポリアクリルアマイド、スチレンブ
タジエン共重合体、ポリ酢酸ビニル、ポリアクリ
ル酸エステルのラテツクス類などがあげられる。 本発明の感熱記録体には、必要に応じて記録層
中に他の添加物質、例えば記録特性向上のための
各種ワツクス類、脂肪酸アミド類、ステイツク防
止のための各種脂肪酸金属塩、表面の白色度、自
然性、筆記性を良くするために白色顔料、填料、
耐水性向上のための耐水化剤等が添加される。 本発明の感熱記録体は次のようにしてつくられ
る。発色性物質、フエノール性物質、感度調整剤
その他の添加剤を、適当な濃度の接着剤を含む水
系媒体中でボールミルなどの粉砕機を使用して粉
砕分散して感熱組成物を得る。 各構成物質は出来るだけ微粒化することが発色
効率の点で有利であり、1〜3μの粒径に微粒化
することが好ましい。 こうして得られた感熱記録組成物を適当な支持
体に塗布し、乾燥して本発明の感熱記録体を得
る。支持体としては上質紙、中質紙、コート紙を
はじめとする紙、プラスチツクフイルム、フイル
ムラミネート紙、織布シートなどがあげられる。
かくして得られる本発明の感熱記録体は、各種の
可塑剤に対してすぐれた耐可塑剤性を発揮し、発
色画像を長時間これらの可塑剤と接触させても画
像がきえたり変色することがないうえ、地かぶり
などその他の性質も良好である。 本発明を実施例により更に詳細に説明する。 実施例 1 (a) 感熱記録組成物の製造 A液 フルオラン系黒発色染料(新日曹化工製PSD
150) 5重量部 ステアリン酸アミド 15重量部 クレー 20 〃 ポリビニルアルコール10%水溶液 40 〃 水 20 〃 B液 2,2′,4,4′−テトラオキシアジポフエノン
20重量部 クレー 20 〃 ポリビニルアルコール10%水溶液 40 〃 水 20 〃 A液およびB液をそれぞれ別々に遠心ボール
ミルで4時間分散後、A液、B液を混合して感
熱記録組成物(塗料)を調整した。 (b) この感熱記録組成物を50g/m2の一般紙に乾
燥後の塗布量が7g/m2となるように塗布し、
感熱記録体を得た。 (c) ついでこの感熱記録体について次の手順によ
り耐可塑剤性を調べた。先ず感熱記録体を静的
発色試験器(スタンプ式)で圧力2Kg/cm2、温
度130℃、時間1秒で発色させた。次に耐可塑
剤性の試験として感熱記録体の発色部分に市販
のプラスチツク消ゴムをのせ、更に消ゴムの上
に300gの錘をのせ、1日間放置した。 その後試験前後の発色部分の濃度をマクベス反
射濃度計RD−514で測定し、表の結果を得た。 実施例 2 実施例1のB液における2,2′,4,4′−テト
ラオキシアジポフエノンの代りに2,2′,4,
4′−テトラオキシセバチフエノンを使用した以外
は実施例1と全く同様にして感熱記録体を得、耐
可塑剤性の試験を行なつた。結果を表に示す。 比較例1、比較例2 実施例1のB液における2,2′,4,4′−テト
ラオキシアジポフエノンの代りにビスフエノール
Aを使用したものを比較例1、ベンジルP−ヒド
ロキシベンゾエートを使用したものを比較例2と
し、以下実施例1と全く同様にして感熱記録体を
得、耐可塑剤性の試験を行なつた。結果を表に示
す。
【表】
試験後濃度
注 ※濃度残存率=
注 ※濃度残存率=
Claims (1)
- 【特許請求の範囲】 1 通常無色ないし淡色の発色性物質と、この発
色性物質を加熱時発色させるフエノール性物質と
を含む感熱層を有する感熱記録体において、フエ
ノール性物質として 一般式 (ただしnは1〜10) であらわされる物質を含有することを特徴とする
感熱記録体。