JPH03290342A - セメント用乾燥収縮低減剤 - Google Patents
セメント用乾燥収縮低減剤Info
- Publication number
- JPH03290342A JPH03290342A JP8957990A JP8957990A JPH03290342A JP H03290342 A JPH03290342 A JP H03290342A JP 8957990 A JP8957990 A JP 8957990A JP 8957990 A JP8957990 A JP 8957990A JP H03290342 A JPH03290342 A JP H03290342A
- Authority
- JP
- Japan
- Prior art keywords
- cement
- acid
- group
- drying
- shrinkage reducing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
[産業上の利用分野コ
本発明は、セメント用乾燥収縮低減剤に関する。
[従来の技術]
従来のセメント用収縮低減剤としてはアミド化合物およ
び/または変性アミド化合物(特開昭56−37258
号公報)及び低級アルコールに少量のエチレンオキサイ
ドを付加させたもの(特開昭56−37259号公報)
等が知られている。
び/または変性アミド化合物(特開昭56−37258
号公報)及び低級アルコールに少量のエチレンオキサイ
ドを付加させたもの(特開昭56−37259号公報)
等が知られている。
口発明が解決しようとする課題]
しかしながら、上記の収縮低減剤にあっては、乾燥初期
の収縮が大きく乾燥初期に発生するひび割れの防止につ
いては、充分ではなかった。
の収縮が大きく乾燥初期に発生するひび割れの防止につ
いては、充分ではなかった。
[課題を解決するための手段]
本発明者らは、上記問題に鑑みて、鋭意検討を重ねた結
果、本発明に至った。
果、本発明に至った。
すなわち本発明は、一般式
%式%(1)
(式中、Rはアルキル基、アルキレン基、不飽和炭化水
素基またはヒドロキシアルキル基; Aは炭素数2〜3
の1種または2種のアルキレン基;nは1〜20の数;
mは1〜3の数である)で示される化合物の1種または
2種以上からなるセメント用乾燥収縮低減剤である。
素基またはヒドロキシアルキル基; Aは炭素数2〜3
の1種または2種のアルキレン基;nは1〜20の数;
mは1〜3の数である)で示される化合物の1種または
2種以上からなるセメント用乾燥収縮低減剤である。
本発明において一般式(1)で示される化合物は、通常
分子中に1〜3個のカルボキシル基を有するカルボン酸
に、エチレンオキシドおよび/またはプロピレンオキシ
ドを付加させることによって容易に得られるほか、分子
中に1〜3個のカルボキシル基を有するカルボン酸と、
ポリエチレングリコールおよび/またはポリプロピレン
グリコールを触媒の存在下、エステル化反応することに
よっても得られる。
分子中に1〜3個のカルボキシル基を有するカルボン酸
に、エチレンオキシドおよび/またはプロピレンオキシ
ドを付加させることによって容易に得られるほか、分子
中に1〜3個のカルボキシル基を有するカルボン酸と、
ポリエチレングリコールおよび/またはポリプロピレン
グリコールを触媒の存在下、エステル化反応することに
よっても得られる。
この時、本発明に彰いて用いられるカルボン酸としては
、具体的には吉草酸、カプロン酸、エナント酸、カプリ
ル酸、ペラルゴン酸、カプリン酸、ウンデシル酸、ラウ
リン酸、 トリデシル酸、ミリスチン酸、ペンタデシル
酸、7寸ルミチン酸、ヘプタデシル酸、ステアリン酸、
ノナデカン酸、ベヘン酸、オレイン酸、エライジン酸、
エルシン酸等の脂肪族モノカルボン酸;マロン酸、コ/
−り酸、グルタル酸、アジピン酸、マレイン酸、フマル
酸、グルチン酸等の脂肪族ジカルボン酸:乳酸、グリセ
リン酸、酒石酸、クエン酸、リンゴ酸等のオキシカルボ
ン酸が挙げられる。これらのうち好ましいのはカプリン
酸である。
、具体的には吉草酸、カプロン酸、エナント酸、カプリ
ル酸、ペラルゴン酸、カプリン酸、ウンデシル酸、ラウ
リン酸、 トリデシル酸、ミリスチン酸、ペンタデシル
酸、7寸ルミチン酸、ヘプタデシル酸、ステアリン酸、
ノナデカン酸、ベヘン酸、オレイン酸、エライジン酸、
エルシン酸等の脂肪族モノカルボン酸;マロン酸、コ/
−り酸、グルタル酸、アジピン酸、マレイン酸、フマル
酸、グルチン酸等の脂肪族ジカルボン酸:乳酸、グリセ
リン酸、酒石酸、クエン酸、リンゴ酸等のオキシカルボ
ン酸が挙げられる。これらのうち好ましいのはカプリン
酸である。
一般式(1)中のRは前記のカルボン酸のカルボキシル
基を除いた残基であり、具体的にはアルキル基、アルキ
レン基、不飽和炭化水素基(アルケニレン基、アルキニ
レン基)またはヒドロキシアルキル基である。
基を除いた残基であり、具体的にはアルキル基、アルキ
レン基、不飽和炭化水素基(アルケニレン基、アルキニ
レン基)またはヒドロキシアルキル基である。
Aは、炭素数2〜3のアルキレン基でありエチレン基お
よび/またはプロピレン基が挙げられる。
よび/またはプロピレン基が挙げられる。
nは1〜20である。nが1未満の場合には、セメント
に混和した場合収縮低減効果が小さいとか、強度を低下
させるなどの問題がある。nが20より大きい場合には
収縮低減効果が著しく低下する。
に混和した場合収縮低減効果が小さいとか、強度を低下
させるなどの問題がある。nが20より大きい場合には
収縮低減効果が著しく低下する。
本発明の収縮低減剤の使用できるセメントとしては、普
通ポルトランドセメント、特殊ポルトランドセメント(
早強ポルトランドセメント中庸熱ポルトランドセメント
)、アルミナセメント、高炉セメント、フライアッシュ
セメントなどがあげられセメントの種類の制約を受けな
い。
通ポルトランドセメント、特殊ポルトランドセメント(
早強ポルトランドセメント中庸熱ポルトランドセメント
)、アルミナセメント、高炉セメント、フライアッシュ
セメントなどがあげられセメントの種類の制約を受けな
い。
さらに、骨材の種類、併用する混和剤および混和材料の
制約を受けない。すなわちコンクリート用減水剤、空気
連行剤、膨張材、本発明以外の収縮低減剤、その他公知
のモルタルまたはコンクリート用混和材料と併用するこ
ともできる。
制約を受けない。すなわちコンクリート用減水剤、空気
連行剤、膨張材、本発明以外の収縮低減剤、その他公知
のモルタルまたはコンクリート用混和材料と併用するこ
ともできる。
本発明の収縮低減剤の使用量は、一般式(1)で示され
る化合物の構造によっても異なるが、セメントに対して
通常0.5〜10重量%である。使用量が0.5重量%
未満では収縮低減効果は少なく、一方10重量%を越え
るとセメント組成物の強度が無添加のものと比較して約
273以下となり実用性において充分でない。
る化合物の構造によっても異なるが、セメントに対して
通常0.5〜10重量%である。使用量が0.5重量%
未満では収縮低減効果は少なく、一方10重量%を越え
るとセメント組成物の強度が無添加のものと比較して約
273以下となり実用性において充分でない。
本発明のセメント用収縮低減剤の添加手段は、普通一般
に行われているセメント飽和剤の場合と同じように使用
できる。例えば混練水に予め適量のセメント用乾燥収縮
低減剤を混和してもよいし、−度練り上がったコンクリ
ート等に添加してもよい。
に行われているセメント飽和剤の場合と同じように使用
できる。例えば混練水に予め適量のセメント用乾燥収縮
低減剤を混和してもよいし、−度練り上がったコンクリ
ート等に添加してもよい。
本発明の収縮低減剤を添加したモルタルまたはコンクリ
ートの施工法は従来の場合と同じでよく、コテ塗り、型
枠への充填、吹き付は塗り、コーキングガンによる注入
などの方法をとりうる。また、養生法としては気乾養生
、湿空養生、水中養生、加熱促進養生(蒸気養生、オー
トクレーブ養生など)のいずれでもよく、各々の併用で
もよい。また各場合の条件も従来と同様でよい。
ートの施工法は従来の場合と同じでよく、コテ塗り、型
枠への充填、吹き付は塗り、コーキングガンによる注入
などの方法をとりうる。また、養生法としては気乾養生
、湿空養生、水中養生、加熱促進養生(蒸気養生、オー
トクレーブ養生など)のいずれでもよく、各々の併用で
もよい。また各場合の条件も従来と同様でよい。
[実施例コ
以下、実施例により本発明を説明するが、本発明はこれ
に限定されるものではない。
に限定されるものではない。
実施例1〜5、比較例1〜2
各種の本発明の収縮低減剤を、それぞれセメントに対し
て2重量%添加したものおよび添加しないものについて
、JIS A 1129のダイヤルゲージ法にて収
縮試験を、JIS A 1116により空気連行量
を、JIS R5201により強度を測定し表−1に
示す結果を得た。なお、水/セメント比は60%、砂/
セメント比は200%である。また、砂としては豊浦探
準砂を用いた。また、養生は水中養生1週間後更に20
℃、相対湿度60%雰囲気下に所定の期間放置して行っ
た。
て2重量%添加したものおよび添加しないものについて
、JIS A 1129のダイヤルゲージ法にて収
縮試験を、JIS A 1116により空気連行量
を、JIS R5201により強度を測定し表−1に
示す結果を得た。なお、水/セメント比は60%、砂/
セメント比は200%である。また、砂としては豊浦探
準砂を用いた。また、養生は水中養生1週間後更に20
℃、相対湿度60%雰囲気下に所定の期間放置して行っ
た。
(以下余白)
[発明の効果]
本発明のセメント用乾燥収縮低減剤は、従来の乾燥収縮
低減剤と比較して乾燥初期において収縮低減効果が大き
いため、乾燥初期の収縮に起因するコンクリート等のひ
び割れを大幅に低減できる。
低減剤と比較して乾燥初期において収縮低減効果が大き
いため、乾燥初期の収縮に起因するコンクリート等のひ
び割れを大幅に低減できる。
また、コンクリート等の強度低下をおこすこともない。
Claims (1)
- 【特許請求の範囲】 1、一般式 R{COO(AO)_n}_mH(1) (式中、Rはアルキル基、アルキレン基、不飽和炭化水
素基またはヒドロキシアルキル基;Aは炭素数2〜3の
1種または2種のアルキレン基;nは1〜20の数;m
は1〜3の数である)で示される化合物の1種または2
種以上からなるセメント用乾燥収縮低減剤。 2、一般式(1)のAOがオキシプロピレン基である請
求項1記載のセメント用乾燥収縮低減剤。 3、Rが炭素数6〜12のアルキル基である請求項1ま
たは2記載のセメント用乾燥収縮低減剤。