JPH03234779A - 耐ブリスター性に優れたカーペット裏打ち用水系接着剤 - Google Patents
耐ブリスター性に優れたカーペット裏打ち用水系接着剤Info
- Publication number
- JPH03234779A JPH03234779A JP2942090A JP2942090A JPH03234779A JP H03234779 A JPH03234779 A JP H03234779A JP 2942090 A JP2942090 A JP 2942090A JP 2942090 A JP2942090 A JP 2942090A JP H03234779 A JPH03234779 A JP H03234779A
- Authority
- JP
- Japan
- Prior art keywords
- water
- copolymer latex
- adhesive
- carpet backing
- carpet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
め要約のデータは記録されません。
Description
水系接着剤に関する。
の織布またはポリプロピレン等合成繊維の織布、不織布
の一次基布にナイロン、アクリル、ウール等の繊維束を
植え込み、裏面に接着剤を塗布した後、ジュート等の二
次基布を貼り合わせ、乾燥固着させたものである。
クスを主たるバインダーとし、重量感を与える炭酸カル
シウム、水酸化アルミニウム等の無機充填剤と充填剤の
沈降防止および塗布性を与えるための増粘剤等が配合さ
れている。
水系接着剤を速く乾燥するためドライヤーの能力を上げ
る傾向にある。
おいて、二次基布のジュートの織目から接着剤が吹き出
すいわゆるブリスター(火ぶくれ)が発生して、カーペ
ットの製品価値を著しく損ない、且つ接着強度にも悪影
響を与えるので、ブリスターの発生を防止する手段を講
じる必要があった。
部の水蒸気の圧力で皮膜を持ち上げるために発生する。
いる。
方法があるが、塗布性や、粘度安定性などの点で限界が
ある。
に添加したり(特開昭46−2834号公報、特開昭5
3−113844号公報)、ポリビニルアルコールのよ
うな感熱溶解性を有する物質を添加する方法(特開昭6
0−149677号公報)もあるが、一般に使われてい
るのは、オルガノポリシロキサンをゲル化剤として添加
する方法(特公昭56−44191号公報)や、でんぷ
んを利用する方法(特公昭57−30429号公報)が
ある。
ち用水系接着剤としては金塩にフオームバッキング用に
使用した例(米国特許第3538025号明細書)があ
るが、フオームバッキングの重要な機能であるクツショ
ン性を得るために炭酸ジルコニルアンモニウムを架橋剤
として泡の形状保持の役目に使用している。したがって
、復元力を備えるために充填剤量は100部前後の低い
フィラー組成物に本質的に限定される。
剤を耐ブリスター剤として利用する場合にはゲル化作用
を発揮させるために合成共重合体ラテックス自体を不安
定にしなければならず、また、添加方法を誤まると合成
共重合体ラテックスが凝集する危険があった。
述の欠点がない代わりに、腐敗が懸念され、大量の殺菌
剤の投与が必要不可欠の上、合成共重合体ラテックスが
備えている性能、例えば、耐折れ割れ性等を低下させる
原因となっている。
重ねた結果、カルボキシ変性合成共重合体ラテックス固
形分100重量部(以下、特にことわらない限り、固形
分重量部をいう)に、無機充填剤200〜600重量部
および炭酸ジルコニルアンモニウムを成分として含むカ
ーペット裏打ち用水系接着剤組成物が優れた耐ブリスタ
ー性を有することを見い出し、本発明を完成するに至っ
た。
ス固形分100重量部当り、無機充填剤200〜600
重量部及び炭酸ジルコニルアンモニウムを含むカーペッ
ト裏打ち用水系接着剤である。
は、エチレン性不飽和カルボン酸を共重合体モノマーと
して1種以上含ませて乳化重合することによって得るこ
とができる。エチレン性不飽和カルボン酸を含まないと
炭酸ジルコニルアンモニウムが作用せず、感熱凝固性が
発現しない。
なる。
、メタクリル酸等の一塩基酸、フマル酸、イタコン酸、
マレイン酸等の二塩基酸等が挙げられる。特に、フマル
酸、イタコン酸等の二塩基酸は、炭酸ジルコニルアンモ
ニウムが少量で済むので好ましい。
ラス転移温度は、本発明においては限定されるものでは
なく、塗布されるカーペットの用途に応じて適切な風合
いが得られるように選択されるべきものである。
ついても本発明において限定されないが、例えばスチレ
ン−ブタジェン共重合体ラテックス、(メタ)アクリレ
ート−ブタジェン共重合体ラテックス、スチレン−ブタ
ジェン−(メタ)アクリレート共重合体ラテックス;ス
チレン−(メタ)アクリレート共重合体ラテックス、ア
クリロニトリル−フタジエン共重合体ラテックス、(メ
タ)アクリレート共重合体ラテックス、エチレン−酢酸
ビニル共重合体ラテックスなどを挙げることができる。
、水酸基、N−メチロール基などの活性基を有する単量
体単位を含有させたラテックスも用いることができる。
れぞれ単独で用いてもよいし、2種以上を組み合わせて
用いてもよい。
キシ変性合成共重合体ラテックス100重量部(固形分
)に対して0.05〜3.0重量部(酸化ジルコニウム
換算)含有するのが好ましい。0.05部未満では耐ブ
リスター性の発現が難しい。また、3.0部を越えると
接着剤の粘度が安定しなくなり、好ましくない。炭酸ジ
ルコニルアンモニウムはあらかじめカルボキシ変性合成
共重合体ラテックスに添加するか、あるいは水系接着剤
を配合製造する時に添加してもよく、本発明は限定され
ない。
ッキング用途よりもむしろ、通常のバッキングに使われ
るもので、いわゆるレギュラータイプ、フロスタイプ、
ハイフロスタイプ等の接着剤であり、クツション性より
も接着性および重量感が重要な機能であって乾燥時に生
ずるブリスタを抑止する接着剤である。したがって、無
機充填剤量は高フィラーが好ましく、カルボキシ変性合
成共重合体ラテックス100重量部当り200〜600
重量部が好ましい。200重量部未満であるとブリスタ
ーが発生し易くなる上、経済上も不利になる。また、6
00重量部を越えると接着強度の低下が著しく実用性に
乏しくなる。
ルミニウム、水酸化マグネシウム、クレイ、酸化チタン
、硫酸バリウムなどが挙げられる。
合わせて用いてもよい。
されている増粘剤を使用することができる。
ルボキシメチルセルロース、ヒドロキシメチルセルロー
ス、メチルセルロース、ポリアクリルアミド、ポリビニ
ルアルコール、ポリビニルピロリドン、ブロック化アル
キルポリエーテルなどの水溶性高分子化合物を挙げるこ
とができる。
あわせて用いてもよい。特にポリアクリル酸ナトリウム
、カルボキシメチルセルロースが好ましい。
目的をそこなわない範囲で、必要に応じて、例えば起泡
剤、分散剤、消泡剤、難燃剤、老化防止剤、帯電防止剤
、防菌・防ばい剤、pH調整剤、キレート化剤、架橋剤
、耐水化剤などを含んでも何らさしつかえない。また、
必要に応じて他の耐ブリスター剤と併用してもよい。
おける、ブリスターの発生を防止するので、カーペット
の生産性を向上することができ、コストダウンを可能に
するなどの特徴を有している。
発明はこれらの例によってなんら限定されるものではな
い。
法に従って求めた。
たカーペット生機にカーペット裏打ち用水系接着剤をブ
リスターが生じ易いように1500ウ工ツトg/n?と
多めに塗布した後、赤外線ヒータ下に置き4分乾燥させ
る。
面にブリスター発生 実施例1〜7及び比較例1〜6 第1表に示すモノマー組成から得られた各種カルボキシ
変性合或共重合体ラテックス100重量部に対し、第2
表(実施例)及び第3表(比較例)に示す量の炭醇ジル
コニルアンモニウムを添加した後、無機充填剤としての
重質炭酸カルシウム(日東粉化製、5S−30)を第2
表に示す量添加した。ついで、該重質炭酸カルシウムが
十分に分散してから増粘剤としてのポリアクリル酸ナト
リウムを第2表に示す量添加して粘度(室温)が18.
000±1,000 CpSになるように調節し、固形
分含量が70%の水系接着剤を調製した。
び老化防止剤を各々1重量部を添加した。
を測定した。その結果を、第2表及び第3表に示す。
Claims (1)
- 1 カルボキシ変性合成共重合体ラテックス固形分10
0重量部当り、無機充填剤200〜600重量部および
炭酸ジルコニルアンモニウムを含むカーペット裏打ち用
水系接着剤。