JPH0245266B2 - - Google Patents
Info
- Publication number
- JPH0245266B2 JPH0245266B2 JP21684783A JP21684783A JPH0245266B2 JP H0245266 B2 JPH0245266 B2 JP H0245266B2 JP 21684783 A JP21684783 A JP 21684783A JP 21684783 A JP21684783 A JP 21684783A JP H0245266 B2 JPH0245266 B2 JP H0245266B2
- Authority
- JP
- Japan
- Prior art keywords
- sheet
- magnetic disk
- flexible magnetic
- rotating part
- coefficient
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
(利用分野)
本発明はフレキシブル磁気デイスクの改良に関
するものである。 (従来技術) フレキシブルな磁気デイスクシートをジヤケツ
トに収納し、ジヤケツトとシートの両方に設けた
中央円孔に書込みあるいは読取り用装置のシート
位置決め部材を係合せしめ、これを回転させてシ
ート上に磁気記録をし、あるいはシートから磁気
再生するものが知られている。この種の磁気デイ
スクはシートがジヤケツトに多少余裕をもつて収
納されているため、保管時、取扱時あるいは携帯
時に中のシートがジヤケツト内で片寄つた位置に
ずれ、装置にデイスクを装填したとき、シート中
央の円孔が装置の位置決め部材(コレツト)の位
置に対して偏心し、位置決め時にシートが偏心し
た位置に保持されてしまうことがある。 第1Aおよび1B図はこの種のフレキシブル磁
気シートを示すもので、中央に円形開口1aを有
する矩形のジヤケツト1の中に、前記中央円形開
口1aの中に中央円孔2aの周縁を露出した円形
のフレキシブル磁気シート2が回転自在に収納さ
れている。 このフレキシブル磁気デイスクを出込みあるい
は読取り装置に装填するとき、第2図に示すよう
に位置決め部材の回転部3をシート2の下から当
て、この上からコレツト4を下げて、回転部3の
円形凹部3aの中に圧入する。このとき、シート
2の中央円孔2aの周縁は回転部3の円形凹部3
aの位置に必ずしも一致しているわけではなく、
ずれていることが多いから、このままコレツト4
を下げると第3図のようにシート2の円孔2aの
周縁の一部がコレツト4と回転部3の凹部3aの
間に挾持され、偏心した状態で回転することにな
る。磁気デイスクシート2は常に中心が正しく回
転中心軸に一致して回転されなければ書込み、読
取りが正しく行なわれないから、このような位置
に保持されることは防止されねばならない。ま
た、このような状態で保持され、回転されると、
シート2の平面性が損なわれ、回転時にがたつく
という問題もある。コレツト4を下げてシート2
を挾持するとき、シート2が第3図のようになら
ずに第4図のように正しくなるためには、第1に
シート2とコレツト4および回転部3との摩擦係
数が小さいこと、第2にシートの円孔2aの周縁
部分の機械的強度が大であることが望まれる。 なお、特開昭57−113422号には、フレキシブル
磁気デイスクの中央孔周縁のシート位置決め部材
と接触する部分に紫外線により重合可能なポリオ
レフイン材と脂肪酸エステルとを含有する保護層
を設けて摩擦係数を減少させる方法が開示されて
いる。また米国特許第4052750号には、リング状
の補強部材(弾性リング)をフレキシブル磁気デ
イスクシートの円孔2aの周縁に接着により結合
せしめ、その部分を機械的に強化する方法が開示
されている。 しかしながら、これらはいずれもフレキシブル
磁気デイスクシートの両者に保護層や弾性リング
を設けるようにしたものであり、それぞれ一長一
短があり、摩擦係数の低下と機械的強度の向上の
両者を兼ね備えたものは実現されていない。 (発明の目的) 本発明の目的は、中心孔2aの周縁部分の摩擦
係数を下げるとともに、機械的に強化させたフレ
キシブル磁気デイスクを提供することにある。 さらに詳しくは、書込みおよび読取り用装置に
偏心することなく装填されかつ、装填時にデイス
クのチヤツキング部が損傷を受けにくいフレキシ
ブル磁気デイスクを提供することを目的とするも
のである。 (発明の構成) 本発明によるフレキシブル磁気デイスクは、フ
レキシブル磁気デイスクシートの中央円孔周縁の
回転部当接側面に紫外線により重合が可能な不飽
和結合を有する化合物を含む組成物よりなり、紫
外線照射により硬化された保護層を設け、コレツ
ト当接側の面に補強用リングを固着したことを特
徴とするものである。 (実施態様) 以下、本発明を図面を用いて詳細に説明する。 第5図および第6図(第1A,1B,2図と共
通な部娯には同じ符号を付した)に示すように、
フレキシブル磁気デイスクシート2の片面9上
に、紫外線により重合が可能な不飽和結合を有す
る組成物(UVインキ)からなる保護層6が形成
される。 紫外線により重合が可能な不飽和結合を有する
化合物としては、炭素−炭素不飽和結合を1個以
上有する化合物であり、アクリロイル基、アクリ
ルアミド基、アリル基、ビニルエーテル基、ビニ
ルチオエーテル基等を含む化合物及び不飽和ポリ
エステルであり、具体的には、アクリル酸メチル
及びその同族体であるアクリル酸アルキルエステ
ル、スチレン及びその同族体であるα−メチルス
チレン、β−クロルスチレンなど、アクリロニト
リル、酢酸ビニル、プロピオン酸ビニルなどが挙
げられる。分子内に不飽和結合が2個以上あつて
もよい。この化合物の例としては「感光性樹脂デ
ーター集」(株)綜合化学研究所昭和43年12月刊行
235〜236頁に掲載されている化合物が挙げられ
る。特に、ポリオールの不飽和エステル類、例え
ばエチレンジアクリレート、ジエチレングリコー
ルジアクリレート、グリセロールトリアクリレー
ト、エチレンジアクリレート、ペンタエリスリト
ールテトラアクリレートなど及びエポキシ環を有
するグリンジルアクリレートなどが好ましい。分
子内に不飽和結合が1個の化合物と2個以上の化
合物を混合して用いてもよい。 また、これらの化合物は高分子量体のものであ
つてもよい。特に好ましくは高分子鎖の主鎖の末
端あるいは側鎖にアクリレート基を有する化合物
であり、これらはA.Vrancken“Fatipec
Congress”11 19(1972)に引用されている。例
えば以下に示す化合物 であり、例示した化合物のポリエステル骨格がポ
リウレタン骨格、エポキシ樹脂の骨格、ポリエー
テル骨格、ポリカボネート骨格であつてもあるい
はこれらの混合された骨格でもよい。分子量とし
ては1000〜20000が好ましいが、特に限定される
ものではない。上記のモノマーとポリマーを混合
して用いてもよい。 上記の化合物は、光重合開始剤を併用して、は
じめて紫外線重合が可能となる。光重合開始剤と
しては、ベンゾフエノン、ベンゾイレエチルエー
テル、ベンジルメチルケタール、1−ヒドロキシ
シクロヘキシルフエニルケトン、ミヒラーズ
(Michler′s)ケトン等の芳香族ケトンを用いるこ
とができる。光重合開始剤は紫外線照射光源とし
て用いられるランプの発光スペクトルで主線源と
なる波長(水銀灯を用いた場合は254313535nm)
において吸光係数の大なるものが望ましい。芳香
族ケトンの混合比率は不飽和結合を有する化合物
100重量部に対して0.5〜20好ましくは2〜15さら
に好ましくは3〜10重量部である。 UVインキには、補助剤として消泡剤、ワツク
ス、レベリング剤、潤滑剤、チキリトロピー化
剤、安定剤等を加えてもよい。シートと回転部と
の摩擦係数を下げるため用いることのできる潤滑
剤としては、飽和及び不飽和の高級脂肪族、脂肪
酸エステル、高級脂肪酸アミド、高級アルコー
ル、シリコーンオイル、鉱油、食物油、フツ素系
化合物などがあり、その添加量は前記不飽和結合
を有する化合物100重量部に対して0.1〜20重量
部、好ましくは1〜15重量部、さらに好ましくは
3〜10重量部である。回転部3との摩擦係数は
0.50以下、好ましくは0.35以下であることが望ま
しい。 UVインキを調整する場合、種々の有機溶媒を
必要に応じて使用できるが、化合物(a)が常温で液
体である場合無溶媒でもよい。使用できる有機溶
媒としてはアセトン、メチルエチルケトン、メチ
ルイソブチルケトン、シクロヘキサノン等のケト
ン系;メタノール、エタノール、プロパノール、
ブタノール等のアルコール系;酢酸メチル、酢酸
エチル、酢酸ブチル、乳酸エチル、酢酸グリコー
ルモノエチルエーテル等のエステル系;エーテ
ル、グリコールジメチルエーテル、グリコールモ
ノエチルエーテル、ジオキサン等のグリコールエ
ーテル系;ベンゼン、トルエン、キシレン等のタ
ール系(芳香族炭化水素);メチレンクロライド、
エチレンクロライド、四塩化炭素、クロロホル
ム、エチレンクロルヒドリン、ジクロルベンゼン
等があげられる。 UVインキの印刷方法としては、スクリーン印
刷ロールコート、グラビアコート等が利用でき
る。保護層の膜厚は1〜50μ、好ましくは5〜
30μ、さらに好ましくは10〜20μmである。幅は
3mm程度が好ましい。 フレキシブル磁気デイスクシート2のUV保護
層6と反対の面8上には、補強リング5を固着す
る。この補強リング5は、膜厚20〜200μmで好
ましくは50〜150μm程度であり、幅は3〜5mm
程度が好ましい。ただし、この時磁気デイスクシ
ートの大きさは直径で200mmあるいは130mm程度で
ある。補強リング5の材質はプラスチツク(ポリ
エステル等)紙等がよい。 補強リング5のフレキシブル磁気デイスクシー
ト2への固着方法は、接着剤による貼着熱或いは
高周波による熔着等種々の周知の固着方法を採用
することができる。 (実施例および発明の効果) 次に、本発明の実施例を、補強リング5、保護
層6ともに設けない場合、いずれか一方を設けた
場合、両面に保護層を設けた場合の各比較例とと
もに、第1表に示す。第2表には、上記例の対回
転部に対する磁気シートの摩擦係数、デイスクド
ライブ装填テストでの不良率を示した。摩擦係数
の測定は、位置決め部材(回転部)を磁気シート
上で送り速度0.8mm/secで摩擦し、その際の付加
荷重を70g重として測定した。 デイスクドライブへの装填テストに使用したド
ライブはY−E・データ社製YA280および380、
松下電工社製VA751、および561、三菱電機社製
M−2894および4853他である。 実施例は磁気デイスクを各ドライブにつき10枚
用い、1枚につき連続50回くりかえし装填を行な
い、全ドライブ中連続50回のテスト中1回でも不
良の生じた磁気デイスクは不良とし、不良の生じ
た枚数より不良率を算出した。 第2表の結果から明らかなように、回転部接触
面と回転部材の摩擦係数が0.35以下になると不良
率が急激に減少する。 実施例1、比較例3、比較例4 さらに比較例3、4に対し、実施例1は高温湿
環境条件下でその効果が顕著であり、これは対回
転部の摩擦係数低下に加えて補強リングによるチ
ヤツキング部の剛性寄与によるものである。 以上述べたところから明らかなように、フレキ
シブル磁気デイスクシートのデイスクドライブへ
の装置を失敗なく行なうには、対回転部との摩擦
係数を低下させることが必要であり、これを達成
するためにはUV硬化形成等による保護層が有効
である。さらにこの特性を高温湿環境条件下でも
達成するためにはUV等による保護層と反対の面
にポリエステル等による補強リングが有効に利用
される。
するものである。 (従来技術) フレキシブルな磁気デイスクシートをジヤケツ
トに収納し、ジヤケツトとシートの両方に設けた
中央円孔に書込みあるいは読取り用装置のシート
位置決め部材を係合せしめ、これを回転させてシ
ート上に磁気記録をし、あるいはシートから磁気
再生するものが知られている。この種の磁気デイ
スクはシートがジヤケツトに多少余裕をもつて収
納されているため、保管時、取扱時あるいは携帯
時に中のシートがジヤケツト内で片寄つた位置に
ずれ、装置にデイスクを装填したとき、シート中
央の円孔が装置の位置決め部材(コレツト)の位
置に対して偏心し、位置決め時にシートが偏心し
た位置に保持されてしまうことがある。 第1Aおよび1B図はこの種のフレキシブル磁
気シートを示すもので、中央に円形開口1aを有
する矩形のジヤケツト1の中に、前記中央円形開
口1aの中に中央円孔2aの周縁を露出した円形
のフレキシブル磁気シート2が回転自在に収納さ
れている。 このフレキシブル磁気デイスクを出込みあるい
は読取り装置に装填するとき、第2図に示すよう
に位置決め部材の回転部3をシート2の下から当
て、この上からコレツト4を下げて、回転部3の
円形凹部3aの中に圧入する。このとき、シート
2の中央円孔2aの周縁は回転部3の円形凹部3
aの位置に必ずしも一致しているわけではなく、
ずれていることが多いから、このままコレツト4
を下げると第3図のようにシート2の円孔2aの
周縁の一部がコレツト4と回転部3の凹部3aの
間に挾持され、偏心した状態で回転することにな
る。磁気デイスクシート2は常に中心が正しく回
転中心軸に一致して回転されなければ書込み、読
取りが正しく行なわれないから、このような位置
に保持されることは防止されねばならない。ま
た、このような状態で保持され、回転されると、
シート2の平面性が損なわれ、回転時にがたつく
という問題もある。コレツト4を下げてシート2
を挾持するとき、シート2が第3図のようになら
ずに第4図のように正しくなるためには、第1に
シート2とコレツト4および回転部3との摩擦係
数が小さいこと、第2にシートの円孔2aの周縁
部分の機械的強度が大であることが望まれる。 なお、特開昭57−113422号には、フレキシブル
磁気デイスクの中央孔周縁のシート位置決め部材
と接触する部分に紫外線により重合可能なポリオ
レフイン材と脂肪酸エステルとを含有する保護層
を設けて摩擦係数を減少させる方法が開示されて
いる。また米国特許第4052750号には、リング状
の補強部材(弾性リング)をフレキシブル磁気デ
イスクシートの円孔2aの周縁に接着により結合
せしめ、その部分を機械的に強化する方法が開示
されている。 しかしながら、これらはいずれもフレキシブル
磁気デイスクシートの両者に保護層や弾性リング
を設けるようにしたものであり、それぞれ一長一
短があり、摩擦係数の低下と機械的強度の向上の
両者を兼ね備えたものは実現されていない。 (発明の目的) 本発明の目的は、中心孔2aの周縁部分の摩擦
係数を下げるとともに、機械的に強化させたフレ
キシブル磁気デイスクを提供することにある。 さらに詳しくは、書込みおよび読取り用装置に
偏心することなく装填されかつ、装填時にデイス
クのチヤツキング部が損傷を受けにくいフレキシ
ブル磁気デイスクを提供することを目的とするも
のである。 (発明の構成) 本発明によるフレキシブル磁気デイスクは、フ
レキシブル磁気デイスクシートの中央円孔周縁の
回転部当接側面に紫外線により重合が可能な不飽
和結合を有する化合物を含む組成物よりなり、紫
外線照射により硬化された保護層を設け、コレツ
ト当接側の面に補強用リングを固着したことを特
徴とするものである。 (実施態様) 以下、本発明を図面を用いて詳細に説明する。 第5図および第6図(第1A,1B,2図と共
通な部娯には同じ符号を付した)に示すように、
フレキシブル磁気デイスクシート2の片面9上
に、紫外線により重合が可能な不飽和結合を有す
る組成物(UVインキ)からなる保護層6が形成
される。 紫外線により重合が可能な不飽和結合を有する
化合物としては、炭素−炭素不飽和結合を1個以
上有する化合物であり、アクリロイル基、アクリ
ルアミド基、アリル基、ビニルエーテル基、ビニ
ルチオエーテル基等を含む化合物及び不飽和ポリ
エステルであり、具体的には、アクリル酸メチル
及びその同族体であるアクリル酸アルキルエステ
ル、スチレン及びその同族体であるα−メチルス
チレン、β−クロルスチレンなど、アクリロニト
リル、酢酸ビニル、プロピオン酸ビニルなどが挙
げられる。分子内に不飽和結合が2個以上あつて
もよい。この化合物の例としては「感光性樹脂デ
ーター集」(株)綜合化学研究所昭和43年12月刊行
235〜236頁に掲載されている化合物が挙げられ
る。特に、ポリオールの不飽和エステル類、例え
ばエチレンジアクリレート、ジエチレングリコー
ルジアクリレート、グリセロールトリアクリレー
ト、エチレンジアクリレート、ペンタエリスリト
ールテトラアクリレートなど及びエポキシ環を有
するグリンジルアクリレートなどが好ましい。分
子内に不飽和結合が1個の化合物と2個以上の化
合物を混合して用いてもよい。 また、これらの化合物は高分子量体のものであ
つてもよい。特に好ましくは高分子鎖の主鎖の末
端あるいは側鎖にアクリレート基を有する化合物
であり、これらはA.Vrancken“Fatipec
Congress”11 19(1972)に引用されている。例
えば以下に示す化合物 であり、例示した化合物のポリエステル骨格がポ
リウレタン骨格、エポキシ樹脂の骨格、ポリエー
テル骨格、ポリカボネート骨格であつてもあるい
はこれらの混合された骨格でもよい。分子量とし
ては1000〜20000が好ましいが、特に限定される
ものではない。上記のモノマーとポリマーを混合
して用いてもよい。 上記の化合物は、光重合開始剤を併用して、は
じめて紫外線重合が可能となる。光重合開始剤と
しては、ベンゾフエノン、ベンゾイレエチルエー
テル、ベンジルメチルケタール、1−ヒドロキシ
シクロヘキシルフエニルケトン、ミヒラーズ
(Michler′s)ケトン等の芳香族ケトンを用いるこ
とができる。光重合開始剤は紫外線照射光源とし
て用いられるランプの発光スペクトルで主線源と
なる波長(水銀灯を用いた場合は254313535nm)
において吸光係数の大なるものが望ましい。芳香
族ケトンの混合比率は不飽和結合を有する化合物
100重量部に対して0.5〜20好ましくは2〜15さら
に好ましくは3〜10重量部である。 UVインキには、補助剤として消泡剤、ワツク
ス、レベリング剤、潤滑剤、チキリトロピー化
剤、安定剤等を加えてもよい。シートと回転部と
の摩擦係数を下げるため用いることのできる潤滑
剤としては、飽和及び不飽和の高級脂肪族、脂肪
酸エステル、高級脂肪酸アミド、高級アルコー
ル、シリコーンオイル、鉱油、食物油、フツ素系
化合物などがあり、その添加量は前記不飽和結合
を有する化合物100重量部に対して0.1〜20重量
部、好ましくは1〜15重量部、さらに好ましくは
3〜10重量部である。回転部3との摩擦係数は
0.50以下、好ましくは0.35以下であることが望ま
しい。 UVインキを調整する場合、種々の有機溶媒を
必要に応じて使用できるが、化合物(a)が常温で液
体である場合無溶媒でもよい。使用できる有機溶
媒としてはアセトン、メチルエチルケトン、メチ
ルイソブチルケトン、シクロヘキサノン等のケト
ン系;メタノール、エタノール、プロパノール、
ブタノール等のアルコール系;酢酸メチル、酢酸
エチル、酢酸ブチル、乳酸エチル、酢酸グリコー
ルモノエチルエーテル等のエステル系;エーテ
ル、グリコールジメチルエーテル、グリコールモ
ノエチルエーテル、ジオキサン等のグリコールエ
ーテル系;ベンゼン、トルエン、キシレン等のタ
ール系(芳香族炭化水素);メチレンクロライド、
エチレンクロライド、四塩化炭素、クロロホル
ム、エチレンクロルヒドリン、ジクロルベンゼン
等があげられる。 UVインキの印刷方法としては、スクリーン印
刷ロールコート、グラビアコート等が利用でき
る。保護層の膜厚は1〜50μ、好ましくは5〜
30μ、さらに好ましくは10〜20μmである。幅は
3mm程度が好ましい。 フレキシブル磁気デイスクシート2のUV保護
層6と反対の面8上には、補強リング5を固着す
る。この補強リング5は、膜厚20〜200μmで好
ましくは50〜150μm程度であり、幅は3〜5mm
程度が好ましい。ただし、この時磁気デイスクシ
ートの大きさは直径で200mmあるいは130mm程度で
ある。補強リング5の材質はプラスチツク(ポリ
エステル等)紙等がよい。 補強リング5のフレキシブル磁気デイスクシー
ト2への固着方法は、接着剤による貼着熱或いは
高周波による熔着等種々の周知の固着方法を採用
することができる。 (実施例および発明の効果) 次に、本発明の実施例を、補強リング5、保護
層6ともに設けない場合、いずれか一方を設けた
場合、両面に保護層を設けた場合の各比較例とと
もに、第1表に示す。第2表には、上記例の対回
転部に対する磁気シートの摩擦係数、デイスクド
ライブ装填テストでの不良率を示した。摩擦係数
の測定は、位置決め部材(回転部)を磁気シート
上で送り速度0.8mm/secで摩擦し、その際の付加
荷重を70g重として測定した。 デイスクドライブへの装填テストに使用したド
ライブはY−E・データ社製YA280および380、
松下電工社製VA751、および561、三菱電機社製
M−2894および4853他である。 実施例は磁気デイスクを各ドライブにつき10枚
用い、1枚につき連続50回くりかえし装填を行な
い、全ドライブ中連続50回のテスト中1回でも不
良の生じた磁気デイスクは不良とし、不良の生じ
た枚数より不良率を算出した。 第2表の結果から明らかなように、回転部接触
面と回転部材の摩擦係数が0.35以下になると不良
率が急激に減少する。 実施例1、比較例3、比較例4 さらに比較例3、4に対し、実施例1は高温湿
環境条件下でその効果が顕著であり、これは対回
転部の摩擦係数低下に加えて補強リングによるチ
ヤツキング部の剛性寄与によるものである。 以上述べたところから明らかなように、フレキ
シブル磁気デイスクシートのデイスクドライブへ
の装置を失敗なく行なうには、対回転部との摩擦
係数を低下させることが必要であり、これを達成
するためにはUV硬化形成等による保護層が有効
である。さらにこの特性を高温湿環境条件下でも
達成するためにはUV等による保護層と反対の面
にポリエステル等による補強リングが有効に利用
される。
【表】
【表】
第1A図はフレキシブル磁気デイスクの例を示
す平面図、第1B図はその断面図、第2図はフレ
キシブル磁気デイスクを装置の位置決め部材に装
填する状態を示す一部断面図、第3図は同じくそ
のシートが偏心したまま保持される状態を出す一
部断面図、第4図は同じくそのシートが正しく位
置決めされた状態を示す一部断面図、第5図は本
発明により改良されたフレキシブル磁気デイスク
の平面図、第6図はその断面図である。 1……ジヤケツト、1a……ジヤケツト開口、
2……磁気シート、2a……中央円孔、3……位
置決め部材(回転部)、3a……円形凹部、4…
…位置決め部材(コレツト)、5……補強用リン
グ、6……UVインキ保護層、8……他面、9…
…片面。
す平面図、第1B図はその断面図、第2図はフレ
キシブル磁気デイスクを装置の位置決め部材に装
填する状態を示す一部断面図、第3図は同じくそ
のシートが偏心したまま保持される状態を出す一
部断面図、第4図は同じくそのシートが正しく位
置決めされた状態を示す一部断面図、第5図は本
発明により改良されたフレキシブル磁気デイスク
の平面図、第6図はその断面図である。 1……ジヤケツト、1a……ジヤケツト開口、
2……磁気シート、2a……中央円孔、3……位
置決め部材(回転部)、3a……円形凹部、4…
…位置決め部材(コレツト)、5……補強用リン
グ、6……UVインキ保護層、8……他面、9…
…片面。
Claims (1)
- 1 フレキシブル磁気デイスクシートの中央円孔
周縁の回転部当接側の面に、紫外線による重合が
可能な不飽和結合を有する化合物を含む組成物よ
りなり、紫外線照射により硬化された保護層を設
け、コレツト当接側の面に、補強用リングを固着
したことを特徴とする、フレキシブル磁気デイス
ク。