JPH02236818A - 磁気記録媒体 - Google Patents
磁気記録媒体Info
- Publication number
- JPH02236818A JPH02236818A JP5812489A JP5812489A JPH02236818A JP H02236818 A JPH02236818 A JP H02236818A JP 5812489 A JP5812489 A JP 5812489A JP 5812489 A JP5812489 A JP 5812489A JP H02236818 A JPH02236818 A JP H02236818A
- Authority
- JP
- Japan
- Prior art keywords
- magnetic
- ether
- magnetic layer
- hydrocarbon group
- recording medium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は、磁気記録媒体に関し、詳しくは耐久性に優れ
た磁気記録媒体に関するものである.〔従来の技術及び
発明が解決しようとする課題〕磁気記録媒体は、記録再
生時に磁気ヘッドやパッドなどと激しく摺動し、磁性層
が摩耗されやすいため、磁性層の摩耗が少なく耐久性に
優れたものが望まれている. このため、磁性層の耐摩耗性を改善する方策として、磁
性層中に種々の潤滑剤を混入する内添法、あるいは磁性
層表面に潤滑層を形成するトップコート法等が行われて
いる. 従来から使用されている潤滑剤としては、高級脂肪酸お
よびそのエステル、脂肪酸アミド、流動パラフィン、シ
リコーンオイル等がある.しかしながら、これらの潤滑
剤は性能面では満足されるものとは言い難いのが現状で
ある.〔課題を解決するための手段〕 本発明者らは、良好な潤滑性が付与され大幅に耐久性が
改善された磁気記録媒体を得るべく鋭意研究の結果本発
明に到達した. 即ち、本発明は、非磁性支持体上に磁性層を有する磁気
記録媒体において、該磁性層が、下記一般式(1)で表
されるエーテルを保持していることを特徴とする磁気記
録媒体を提供するものである. OR! OH (ただし、R.は炭素数2〜30の炭化水素基、R8は
水素原子又は炭素数1〜8の炭化水素基を表わす.) 本発明に係る前記一般式(1)で表されるエーテルにお
いて、前述のようにR,の炭素数は2〜30であるが、
中でも10〜22、更には14〜20が好ましい.また
このR,は直鎖であっても、分岐を有していてもよく、
さらに飽和であっても、不飽和結合を有していてもよい
。
た磁気記録媒体に関するものである.〔従来の技術及び
発明が解決しようとする課題〕磁気記録媒体は、記録再
生時に磁気ヘッドやパッドなどと激しく摺動し、磁性層
が摩耗されやすいため、磁性層の摩耗が少なく耐久性に
優れたものが望まれている. このため、磁性層の耐摩耗性を改善する方策として、磁
性層中に種々の潤滑剤を混入する内添法、あるいは磁性
層表面に潤滑層を形成するトップコート法等が行われて
いる. 従来から使用されている潤滑剤としては、高級脂肪酸お
よびそのエステル、脂肪酸アミド、流動パラフィン、シ
リコーンオイル等がある.しかしながら、これらの潤滑
剤は性能面では満足されるものとは言い難いのが現状で
ある.〔課題を解決するための手段〕 本発明者らは、良好な潤滑性が付与され大幅に耐久性が
改善された磁気記録媒体を得るべく鋭意研究の結果本発
明に到達した. 即ち、本発明は、非磁性支持体上に磁性層を有する磁気
記録媒体において、該磁性層が、下記一般式(1)で表
されるエーテルを保持していることを特徴とする磁気記
録媒体を提供するものである. OR! OH (ただし、R.は炭素数2〜30の炭化水素基、R8は
水素原子又は炭素数1〜8の炭化水素基を表わす.) 本発明に係る前記一般式(1)で表されるエーテルにお
いて、前述のようにR,の炭素数は2〜30であるが、
中でも10〜22、更には14〜20が好ましい.また
このR,は直鎖であっても、分岐を有していてもよく、
さらに飽和であっても、不飽和結合を有していてもよい
。
また、R2は水素原子であるか、炭素数1〜8の炭化水
素基であり、炭化水素基は直鎖であっても分岐鎖であっ
ても良い.好ましくはH(水素原子)又は炭素数1〜4
の炭化水素基である.本発明における一般式(1)で示
されるエーテルは単独で用いることもできるが、他の潤
滑剤、特に汎用のエステル、例えばプチルステアレート
等の高級脂肪酸エステルとの併用が好ましく、特に該エ
ーテル/エステルの重量比が1/99〜60/40にな
るような割合で併用すると良好な潤滑機能が発現される
。また必要に応じて、更に他の汎用潤滑剤、例えば高級
脂肪酸などと併用してもよい。
素基であり、炭化水素基は直鎖であっても分岐鎖であっ
ても良い.好ましくはH(水素原子)又は炭素数1〜4
の炭化水素基である.本発明における一般式(1)で示
されるエーテルは単独で用いることもできるが、他の潤
滑剤、特に汎用のエステル、例えばプチルステアレート
等の高級脂肪酸エステルとの併用が好ましく、特に該エ
ーテル/エステルの重量比が1/99〜60/40にな
るような割合で併用すると良好な潤滑機能が発現される
。また必要に応じて、更に他の汎用潤滑剤、例えば高級
脂肪酸などと併用してもよい。
本発明における前記一般式(1)で表されるエーテル化
合物の磁気記録媒体への添加量は磁性材料100重量部
あたり0.05〜15重量部が好まし《、磁性塗料中に
あらかじめ混入するか、又は磁性塗膜形成後にトツブコ
ート法によって塗膜に含浸して用いることができる。
合物の磁気記録媒体への添加量は磁性材料100重量部
あたり0.05〜15重量部が好まし《、磁性塗料中に
あらかじめ混入するか、又は磁性塗膜形成後にトツブコ
ート法によって塗膜に含浸して用いることができる。
またスバッタあるいは蒸着法により非磁性支持体上に磁
性層を形成する型の磁気記録媒体に対してもトップコー
ト法等の同様な方法で前記一a式(1)で表されるエー
テル化合物を添加して用いることができる. 本発明の磁気記録媒体に使用される磁性粉としては針状
形の微細な7 FezOs+ FesOa+ Cru
xのような金属酸化物、またCo被着γ−FezOzt
Coドーブ7 Fl3t03のような加工処理を施
したγPet’s 、金属鉄粉末、微小板状のバリウム
フェライト及びそのFe原子の一部がTi. Co.
Zn.V, Nb等の1種又は2種以上で置換された磁
性粉、Co, Fe−Go. Fe−Ni等の金属又は
合金の超微粉などが挙げられる.これらのうち金属鉄粉
末は特に化学的に安定性が悪くこの改良のためニッケル
、コバルト、チタン、ケイ素、アルミニウムなどを金属
原子、塩及び酸化物の形で少量加えたり表面処理される
ことがあるが、これらを用いることもできる.金属鉄粉
末は又その安定化のため弱い酸化性雰囲気の中で表面に
薄い酸化被膜を作らせることがあるが、このように処理
された金属粉を用いることもできる.また前述の磁性粉
を2種以上混合して用いてもよい。
性層を形成する型の磁気記録媒体に対してもトップコー
ト法等の同様な方法で前記一a式(1)で表されるエー
テル化合物を添加して用いることができる. 本発明の磁気記録媒体に使用される磁性粉としては針状
形の微細な7 FezOs+ FesOa+ Cru
xのような金属酸化物、またCo被着γ−FezOzt
Coドーブ7 Fl3t03のような加工処理を施
したγPet’s 、金属鉄粉末、微小板状のバリウム
フェライト及びそのFe原子の一部がTi. Co.
Zn.V, Nb等の1種又は2種以上で置換された磁
性粉、Co, Fe−Go. Fe−Ni等の金属又は
合金の超微粉などが挙げられる.これらのうち金属鉄粉
末は特に化学的に安定性が悪くこの改良のためニッケル
、コバルト、チタン、ケイ素、アルミニウムなどを金属
原子、塩及び酸化物の形で少量加えたり表面処理される
ことがあるが、これらを用いることもできる.金属鉄粉
末は又その安定化のため弱い酸化性雰囲気の中で表面に
薄い酸化被膜を作らせることがあるが、このように処理
された金属粉を用いることもできる.また前述の磁性粉
を2種以上混合して用いてもよい。
本発明において用いられる、磁性粉を分散させて磁性層
を形成させるための結合剤の例としては、ポリウレタン
、ポリ塩化ビニル、塩化ビニル酢酸ビニル共重合体、ポ
リアクリル二トリル、ニトリルゴム、エボキシ樹脂、ア
ルキッド樹脂、ボリアミド、ポリアクリル酸エステル、
ポリメタクリル酸エステル、ポリ酢酸ビニル、ボリビニ
ルブチラール、塩化ビニリデン、硝化綿、マレイン酸変
性塩化ビニル・酢酸ビニル共重合体、エチルセルロース
などが挙げられる.これらは単独で用いても、2種以上
混合して用いてもよい。また樹脂の硬さを調節するため
可塑剤や硬化剤を加えて使用することもできる。
を形成させるための結合剤の例としては、ポリウレタン
、ポリ塩化ビニル、塩化ビニル酢酸ビニル共重合体、ポ
リアクリル二トリル、ニトリルゴム、エボキシ樹脂、ア
ルキッド樹脂、ボリアミド、ポリアクリル酸エステル、
ポリメタクリル酸エステル、ポリ酢酸ビニル、ボリビニ
ルブチラール、塩化ビニリデン、硝化綿、マレイン酸変
性塩化ビニル・酢酸ビニル共重合体、エチルセルロース
などが挙げられる.これらは単独で用いても、2種以上
混合して用いてもよい。また樹脂の硬さを調節するため
可塑剤や硬化剤を加えて使用することもできる。
本発明の磁気記録媒体の磁性層には以上の成分の他、こ
の分野で通常、使用される研磨剤、帯電防止剤等の添加
剤を加えることができる。
の分野で通常、使用される研磨剤、帯電防止剤等の添加
剤を加えることができる。
また、本発明の磁気記録媒体を製造する際に用いられる
非磁性支持体としては、ポリエチレンテレフタレートの
ようなポリエステル;ポリエチレン、ボリプロビレン等
のポリオレフィン;セルローストリアセテート、セルロ
ースジアセテート等のセルロース誘導体;ポリカーボネ
ート;ボリ塩化ビニル;ポリイミド;芳香族ボリアミド
等のプラスチック;Al,CLI等の金属;紙等が使用
される。形態はフィルム、テープ、シート、ディスク、
カード、ドラム等いずれでもよい.また支持体表面はコ
ロナ放電、放射線、紫外線等で処理されていても、ある
いは適当な樹脂でプレコートされていてもよい. 〔実施例〕 以下本発明を実施例により更に詳細に説明するが、本発
明がこれら実施例に限定されるものではないことは言う
までもない。
非磁性支持体としては、ポリエチレンテレフタレートの
ようなポリエステル;ポリエチレン、ボリプロビレン等
のポリオレフィン;セルローストリアセテート、セルロ
ースジアセテート等のセルロース誘導体;ポリカーボネ
ート;ボリ塩化ビニル;ポリイミド;芳香族ボリアミド
等のプラスチック;Al,CLI等の金属;紙等が使用
される。形態はフィルム、テープ、シート、ディスク、
カード、ドラム等いずれでもよい.また支持体表面はコ
ロナ放電、放射線、紫外線等で処理されていても、ある
いは適当な樹脂でプレコートされていてもよい. 〔実施例〕 以下本発明を実施例により更に詳細に説明するが、本発
明がこれら実施例に限定されるものではないことは言う
までもない。
実施例1〜4
金属鉄粉末 100重量部塩化ビ
ニルー酢酸ビニル共重合体” 11 jFポリウレ
タン樹脂1 11 #カーボンプラック
(帯電防止剤) 2 〃CrgO. (研磨剤)
10l トルエン 7l#メチルエチル
ケトン 71〃シクロヘキサノン
107#注) 本1:ユニオンカーバイド社製商品名VAGH傘2二日
本ポリウレタン社製商品名N−2301上記組成物をサ
ンドミルにて10時間混合した後、フィルタを通して取
出し、更に塗布直前に硬化剤を4.4重量部添加して撹
拌した.この塗料を32a厚のポリエチレンテレフタレ
ートフィルム上に、乾燥後の磁性層厚みが4μになるよ
うにして両面に塗布し乾燥し巻き取った.これをカレン
ダー処理後硬化をしてから円盤状に打ち抜き、表1に示
される潤滑剤の2.0重量%イソプロバノール溶液を、
表1に示される潤滑剤の塗布量が600■/nfとなる
ように塗布して試料ディスクを作製した. 表 ,1 比較例1〜4 実施例1〜4で用いた潤滑剤の代わりに、表2に示す各
種潤滑剤を用いた他は、実施例1〜4と全く同様にして
試料ディスクを作製した.表 2 H f3b/secである. 一定パス回数後の試料ディスクの磁性層の傷つきを目視
で評価した.傷のまったく無い状態をOとし、以下傷の
少ない順にO、Δ、×として評価した. この結果を表3に示す。
ニルー酢酸ビニル共重合体” 11 jFポリウレ
タン樹脂1 11 #カーボンプラック
(帯電防止剤) 2 〃CrgO. (研磨剤)
10l トルエン 7l#メチルエチル
ケトン 71〃シクロヘキサノン
107#注) 本1:ユニオンカーバイド社製商品名VAGH傘2二日
本ポリウレタン社製商品名N−2301上記組成物をサ
ンドミルにて10時間混合した後、フィルタを通して取
出し、更に塗布直前に硬化剤を4.4重量部添加して撹
拌した.この塗料を32a厚のポリエチレンテレフタレ
ートフィルム上に、乾燥後の磁性層厚みが4μになるよ
うにして両面に塗布し乾燥し巻き取った.これをカレン
ダー処理後硬化をしてから円盤状に打ち抜き、表1に示
される潤滑剤の2.0重量%イソプロバノール溶液を、
表1に示される潤滑剤の塗布量が600■/nfとなる
ように塗布して試料ディスクを作製した. 表 ,1 比較例1〜4 実施例1〜4で用いた潤滑剤の代わりに、表2に示す各
種潤滑剤を用いた他は、実施例1〜4と全く同様にして
試料ディスクを作製した.表 2 H f3b/secである. 一定パス回数後の試料ディスクの磁性層の傷つきを目視
で評価した.傷のまったく無い状態をOとし、以下傷の
少ない順にO、Δ、×として評価した. この結果を表3に示す。
表 3
試験例1
Claims (1)
- 【特許請求の範囲】 1、非磁性支持体上に磁性層を有する磁気記録媒体にお
いて、該磁性層が、下記一般式(1)で表されるエーテ
ルを保持していることを特徴とする磁気記録媒体。 ▲数式、化学式、表等があります▼・・・(1) (ただし、R_1は炭素数2〜30の炭化水素基、R_
2は水素原子又は炭素数1〜8の炭化水素基を表わす。 )