JPH02199622A - 磁気記録媒体 - Google Patents
磁気記録媒体Info
- Publication number
- JPH02199622A JPH02199622A JP1813989A JP1813989A JPH02199622A JP H02199622 A JPH02199622 A JP H02199622A JP 1813989 A JP1813989 A JP 1813989A JP 1813989 A JP1813989 A JP 1813989A JP H02199622 A JPH02199622 A JP H02199622A
- Authority
- JP
- Japan
- Prior art keywords
- magnetic
- carbons
- magnetic layer
- alcohol
- aliphatic hydrocarbon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は磁気記録媒体に関する。詳しくは、耐久性に優
れた磁気記録媒体に関する。
れた磁気記録媒体に関する。
〔従来の技術及び発明が解決しようとする課題〕磁気記
録媒体は、一般にポリエステルフィルムなどの基体上に
、磁性粉末、結合剤樹脂(バインダー)、有機溶剤及び
その他の必要成分からなる磁性塗料を塗着して作られる
が、中でもフロッピーディスクは記録再生時に、磁気ヘ
ッドやジャケットライナー等と激しく摺接するために、
磁性層が摩耗されやすいので、磁性層の摩耗が少なくて
耐久性に優れたものが要求される。
録媒体は、一般にポリエステルフィルムなどの基体上に
、磁性粉末、結合剤樹脂(バインダー)、有機溶剤及び
その他の必要成分からなる磁性塗料を塗着して作られる
が、中でもフロッピーディスクは記録再生時に、磁気ヘ
ッドやジャケットライナー等と激しく摺接するために、
磁性層が摩耗されやすいので、磁性層の摩耗が少なくて
耐久性に優れたものが要求される。
このため、磁性層の耐摩耗性を改善する一方策として磁
性層中に種々の潤滑剤を混入することが行われている。
性層中に種々の潤滑剤を混入することが行われている。
従来から使用されている潤滑剤としては脂肪酸、オレイ
ン酸オレイル、ステアリン酸ブトキシド、脂肪酸アミド
、流動パラフィン、ワックス等がある。しかしながら、
これらの潤滑剤は性能面では満足されるものとは言い難
いのが現状である。例えば、オレイン酸オレイル、ステ
アリン酸ブトキシド等は媒体の耐久性向上に対して不十
分であり、ステアリン酸、オレイン酸等の脂肪酸や流動
パラフィン等の炭化水素系の潤滑剤は、耐久性の向上に
は有効であるがバインダーとの相溶性が悪く、多量に用
いると磁性層表面からブリードしヘッドを汚しやすい等
の欠点がある。
ン酸オレイル、ステアリン酸ブトキシド、脂肪酸アミド
、流動パラフィン、ワックス等がある。しかしながら、
これらの潤滑剤は性能面では満足されるものとは言い難
いのが現状である。例えば、オレイン酸オレイル、ステ
アリン酸ブトキシド等は媒体の耐久性向上に対して不十
分であり、ステアリン酸、オレイン酸等の脂肪酸や流動
パラフィン等の炭化水素系の潤滑剤は、耐久性の向上に
は有効であるがバインダーとの相溶性が悪く、多量に用
いると磁性層表面からブリードしヘッドを汚しやすい等
の欠点がある。
本発明者らは、良好な潤滑性が付与されて、幅広い使用
環境下でも大幅に耐久性が改善された磁気記録媒体を得
るべく鋭意研究の結果本発明に到達した。
環境下でも大幅に耐久性が改善された磁気記録媒体を得
るべく鋭意研究の結果本発明に到達した。
即ち、本発明は、磁性粉とバインダーを主たる成分とし
てなる磁性層を有する磁気記録媒体において、前記磁性
層が、下記一般式(I)で表されるエステル化合物を含
有することを特徴とする磁気記録媒体を提供するもので
ある。
てなる磁性層を有する磁気記録媒体において、前記磁性
層が、下記一般式(I)で表されるエステル化合物を含
有することを特徴とする磁気記録媒体を提供するもので
ある。
(式中、Rは炭素数3〜10の分岐を有する脂肪族炭化
水素基、R゛は炭素数7〜21の飽和又は不飽和脂肪族
炭化水素基を表わす、) 本発明に係わる前記一般式(I)で表されるエステル化
合物は非常に限定されたものであり、アルコールに由来
する部分は、炭素数が3〜10の分岐アルコールであり
、脂肪酸に由来する部分は炭素数8〜22の一塩基性脂
肪酸、好ましくは炭素数12〜18の一塩基性脂肪酸で
ある。
水素基、R゛は炭素数7〜21の飽和又は不飽和脂肪族
炭化水素基を表わす、) 本発明に係わる前記一般式(I)で表されるエステル化
合物は非常に限定されたものであり、アルコールに由来
する部分は、炭素数が3〜10の分岐アルコールであり
、脂肪酸に由来する部分は炭素数8〜22の一塩基性脂
肪酸、好ましくは炭素数12〜18の一塩基性脂肪酸で
ある。
炭素数3〜10の分岐アルコールとしては、例えばイソ
プロピルアルコール、イソブチルアルコール、セカンダ
リ−ブチルアルコール、ターシャリ−ブチルアルコール
、イソペンチルアルコール、セカンダリ−ペンチルアル
コール、ターシャリ−ペンチルアルコール、3−ペンチ
ルアルコール、2−メチル−1−ブタノール、3−メチ
ル−2−ブタノール、セカンダリ−ヘキシルアルコール
、3−ヘキシルアルコール、2−ヘプチルアルコール、
3−ヘプチルアルコール、4−ヘプチルアルコール、タ
ーシャリ−へブチルアルコール、2−エチルヘキシルア
ルコール、2−オクタツール、3−オクタツール、4−
オクタツール、2−デカノール、3−デカノール、4−
デカノール、5−デカノール等が挙げられる。特に好ま
しいのはイソプロピルアルコール、イソブチルアルコー
ル、セカンダリ−ブチルアルコール、2−エチルヘキシ
ルアルコールである。
プロピルアルコール、イソブチルアルコール、セカンダ
リ−ブチルアルコール、ターシャリ−ブチルアルコール
、イソペンチルアルコール、セカンダリ−ペンチルアル
コール、ターシャリ−ペンチルアルコール、3−ペンチ
ルアルコール、2−メチル−1−ブタノール、3−メチ
ル−2−ブタノール、セカンダリ−ヘキシルアルコール
、3−ヘキシルアルコール、2−ヘプチルアルコール、
3−ヘプチルアルコール、4−ヘプチルアルコール、タ
ーシャリ−へブチルアルコール、2−エチルヘキシルア
ルコール、2−オクタツール、3−オクタツール、4−
オクタツール、2−デカノール、3−デカノール、4−
デカノール、5−デカノール等が挙げられる。特に好ま
しいのはイソプロピルアルコール、イソブチルアルコー
ル、セカンダリ−ブチルアルコール、2−エチルヘキシ
ルアルコールである。
また炭素数8〜22の一塩基性脂肪酸としては、バルミ
チン酸、ステアリン酸、ミリスチン酸、オレイン酸等が
挙げられる。
チン酸、ステアリン酸、ミリスチン酸、オレイン酸等が
挙げられる。
本発明に係る上記一般式(I)で表されるエステル化合
物は上記の如き炭素数が3〜10の分岐アルコールと、
炭素数8〜22の一塩基性脂肪酸とを用いたエステル化
反応によって得ることができる。
物は上記の如き炭素数が3〜10の分岐アルコールと、
炭素数8〜22の一塩基性脂肪酸とを用いたエステル化
反応によって得ることができる。
本発明のエステル化合物は、磁性塗料中に添加して用い
てもよいし、適当な溶剤に溶解させて磁性塗膜上に散布
してもよい。本発明のエステル化合物の添加量は磁性粉
100重量部に対して、0.1〜10重量部が好ましく
、更に好ましくは0.5〜7重量部である。又、本発明
のエステル化合物に更に通常の潤滑剤を加えることは差
支えない。
てもよいし、適当な溶剤に溶解させて磁性塗膜上に散布
してもよい。本発明のエステル化合物の添加量は磁性粉
100重量部に対して、0.1〜10重量部が好ましく
、更に好ましくは0.5〜7重量部である。又、本発明
のエステル化合物に更に通常の潤滑剤を加えることは差
支えない。
本発明に用いられる磁性粉としては針状形の微細なT
FezO3、Fe5Oa 、Cr0tのような金属酸
化物、またCo被着7−Fe201 、CoドープTF
e20.のような加工処理を施したγ−FezO=、鉄
メタル粉、微小板状のバリウムフェライト及びそのFe
原子の一部がTi、 Co、 Znt L Nb等の1
種又は2種以上で置換された磁性粉、Co、 FeCo
、 Fe−Ni等の金属又は合金の超微粉などが挙げ
られる。これらのうち鉄メタル粉は特に化学的安定性が
悪いからこの改良のためニッケル、コバルト、チタン、
ケイ素、アルミニウムなどを金属原子、塩及び酸化物の
形で少量加えたり表面処理されることがあるが、これら
を用いることもできる。鉄メタル粉は又その安定化のた
め弱い酸化性雰囲気の中で表面に薄い酸化皮膜を作らせ
ることがあるが、このように処理されたメタル粉を用い
ることもできる。
FezO3、Fe5Oa 、Cr0tのような金属酸
化物、またCo被着7−Fe201 、CoドープTF
e20.のような加工処理を施したγ−FezO=、鉄
メタル粉、微小板状のバリウムフェライト及びそのFe
原子の一部がTi、 Co、 Znt L Nb等の1
種又は2種以上で置換された磁性粉、Co、 FeCo
、 Fe−Ni等の金属又は合金の超微粉などが挙げ
られる。これらのうち鉄メタル粉は特に化学的安定性が
悪いからこの改良のためニッケル、コバルト、チタン、
ケイ素、アルミニウムなどを金属原子、塩及び酸化物の
形で少量加えたり表面処理されることがあるが、これら
を用いることもできる。鉄メタル粉は又その安定化のた
め弱い酸化性雰囲気の中で表面に薄い酸化皮膜を作らせ
ることがあるが、このように処理されたメタル粉を用い
ることもできる。
本発明において用いることができるバインダーの例とし
ては、ポリウレタン、ポリエステル、ポリ塩化ビニル、
塩化ビニル/酢酸ビニル共重合体、ポリアクリロニトリ
ル、ニトリルゴム、エポキシ樹脂、アルキッド樹脂、ポ
リアミド、ポリアクリル酸エステル、ポリメタクリル酸
エステル、ポリ酢酸ビニル、ポリビニルブチラール、塩
化ビニリデン、塩化ビニリデン共重合体、硝化綿、マレ
イン酸変性塩化ビニル/酢酸ビニル共重合体、エチルセ
ルロースなどが挙げられる。これらは単独で用いてもよ
いが、通常2種類以上混合して用いられる。また、樹脂
の硬さを調節するため可塑剤や硬化剤を加えて使用する
こともできる。
ては、ポリウレタン、ポリエステル、ポリ塩化ビニル、
塩化ビニル/酢酸ビニル共重合体、ポリアクリロニトリ
ル、ニトリルゴム、エポキシ樹脂、アルキッド樹脂、ポ
リアミド、ポリアクリル酸エステル、ポリメタクリル酸
エステル、ポリ酢酸ビニル、ポリビニルブチラール、塩
化ビニリデン、塩化ビニリデン共重合体、硝化綿、マレ
イン酸変性塩化ビニル/酢酸ビニル共重合体、エチルセ
ルロースなどが挙げられる。これらは単独で用いてもよ
いが、通常2種類以上混合して用いられる。また、樹脂
の硬さを調節するため可塑剤や硬化剤を加えて使用する
こともできる。
また、バインダーの配合量は一般に磁性粉100重量部
に対して15〜60重量部である。最も大きな結合力を
有するバインダーであっても15重量部より少ないとき
は磁性塗膜の強度が弱く、また基板と磁性塗膜の接着力
が不足となる。また60重量部より多いときには磁性塗
膜中の磁性粉濃度が小さくなって再生出力が低下して不
利である。また塗膜特性が低下することもある。
に対して15〜60重量部である。最も大きな結合力を
有するバインダーであっても15重量部より少ないとき
は磁性塗膜の強度が弱く、また基板と磁性塗膜の接着力
が不足となる。また60重量部より多いときには磁性塗
膜中の磁性粉濃度が小さくなって再生出力が低下して不
利である。また塗膜特性が低下することもある。
本発明の磁気記録媒体の磁性層には以上の成分の他、こ
の分野で通常使用される研磨剤、帯電防止剤等の添加剤
を加えることができる。
の分野で通常使用される研磨剤、帯電防止剤等の添加剤
を加えることができる。
〔実施例]
以下、実施例により本発明を更に詳細に説明するが、本
発明はこれらの実施例に限定されるものではない。
発明はこれらの実施例に限定されるものではない。
実施例1〜5及び比較例1〜3
Co 1 Fet03 100
重量部塩化ビニル/酢酸ビニル共重合体m′15ポリウ
レタン樹脂115 α−八へ!(h
5カーボンブラツク
5ポリイソシアネ一ト化合物133 メチルエチルケトン 100トルエン
100シクロへキサノン
100注)ml 米国U、C,C,社製
の商品名VAGH*2 日本ポリウレタン社製の商品名
N−2304本3 日本ポリウレタン社製の商品名コロ
ネートし 上記の組成からなる磁性塗料を調製後、表1に示す潤滑
剤を添加混合し、次いでこれらの塗料をポリエステルベ
ースフィルム上に塗布・乾燥して磁性塗膜を作成した。
重量部塩化ビニル/酢酸ビニル共重合体m′15ポリウ
レタン樹脂115 α−八へ!(h
5カーボンブラツク
5ポリイソシアネ一ト化合物133 メチルエチルケトン 100トルエン
100シクロへキサノン
100注)ml 米国U、C,C,社製
の商品名VAGH*2 日本ポリウレタン社製の商品名
N−2304本3 日本ポリウレタン社製の商品名コロ
ネートし 上記の組成からなる磁性塗料を調製後、表1に示す潤滑
剤を添加混合し、次いでこれらの塗料をポリエステルベ
ースフィルム上に塗布・乾燥して磁性塗膜を作成した。
これを172インチ巾にスリット後、記録再生装置に装
填し、40°C180%RHのもとでスチル状態にセッ
トし、初期の出力が3dB低下するまでの時間で耐久性
を評価した。
填し、40°C180%RHのもとでスチル状態にセッ
トし、初期の出力が3dB低下するまでの時間で耐久性
を評価した。
その結、果を表1に示す。
表
Claims (1)
- 【特許請求の範囲】 1、磁性粉とバインダーを主たる成分としてなる磁性層
を有する磁気記録媒体において、前記磁性層が、下記一
般式( I )で表されるエステル化合物を含有すること
を特徴とする磁気記録媒体。 ▲数式、化学式、表等があります▼・・・( I ) (式中、Rは炭素数3〜10の分岐を有する脂肪族炭化
水素基、R′は炭素数7〜21の飽和又は不飽和脂肪族
炭化水素基を表わす。)