JPH0363931A - 磁気記録媒体 - Google Patents
磁気記録媒体Info
- Publication number
- JPH0363931A JPH0363931A JP19998489A JP19998489A JPH0363931A JP H0363931 A JPH0363931 A JP H0363931A JP 19998489 A JP19998489 A JP 19998489A JP 19998489 A JP19998489 A JP 19998489A JP H0363931 A JPH0363931 A JP H0363931A
- Authority
- JP
- Japan
- Prior art keywords
- magnetic
- magnetic layer
- recording medium
- magnetic recording
- formula
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は磁気記録媒体に関し、詳しくは耐久性に優れた
磁気記録媒体に関するものである。
磁気記録媒体に関するものである。
〔従来の技術及び発明が解決しようとする課題〕磁気記
録媒体は、記録再生時に磁気ヘッドやパッドなどと激し
く摺動し、磁性層が摩耗されやすいため、磁性層の摩耗
が少なく耐久性に優れたものが望まれている。
録媒体は、記録再生時に磁気ヘッドやパッドなどと激し
く摺動し、磁性層が摩耗されやすいため、磁性層の摩耗
が少なく耐久性に優れたものが望まれている。
このため、磁性層の耐摩耗性を改善する方策として、磁
性層中に種々の潤滑剤を混入する内添法、あるいは磁性
層表面に潤滑層を形成するトップコート法等が行われて
いる。
性層中に種々の潤滑剤を混入する内添法、あるいは磁性
層表面に潤滑層を形成するトップコート法等が行われて
いる。
従来から使用されている潤滑剤としては、高級脂肪酸お
よびそのエステル、脂肪酸アミド、流動パラフィン、シ
リコーンオイル等がある。
よびそのエステル、脂肪酸アミド、流動パラフィン、シ
リコーンオイル等がある。
しかしながら、これらの潤滑剤は性能面では満足される
ものとは言い難いのが現状である。
ものとは言い難いのが現状である。
本発明者は、良好な潤滑性が付与され大幅に耐久性が改
善された磁気記録媒体を得るべく鋭意研究の結果本発明
に到達した。
善された磁気記録媒体を得るべく鋭意研究の結果本発明
に到達した。
即ち本発明は、非磁性支持体上に磁性層を有する磁気記
録媒体において、該磁性層が、下記一般式(1)で表さ
れるエーテル化合物を保持していることを特徴とする磁
気記録媒体を提供するものである。
録媒体において、該磁性層が、下記一般式(1)で表さ
れるエーテル化合物を保持していることを特徴とする磁
気記録媒体を提供するものである。
(式中、Rは炭素数4〜32の炭化水素基又は炭素数2
〜30のアルコキシ基を表す。)本発明に係わる前記一
般式(1)で表されるエーテル化合物(以下エーテル化
合物(1)と略記する)において、Rは炭素数4〜32
の炭化水素基又は炭素数2〜30のアルコキシ基である
が、中でも炭素数lO〜24の炭化水素基又は炭素数8
〜22のアルコキシ基が好ましい、また、Rは直鎖であ
っても分岐鎖を有していてもよく、更に飽和であっても
不飽和結合を有していてもよい。
〜30のアルコキシ基を表す。)本発明に係わる前記一
般式(1)で表されるエーテル化合物(以下エーテル化
合物(1)と略記する)において、Rは炭素数4〜32
の炭化水素基又は炭素数2〜30のアルコキシ基である
が、中でも炭素数lO〜24の炭化水素基又は炭素数8
〜22のアルコキシ基が好ましい、また、Rは直鎖であ
っても分岐鎖を有していてもよく、更に飽和であっても
不飽和結合を有していてもよい。
エーテル化合物(1)は下記一般式(2)で表される当
該アルキルオキシラン又は当該アルキルグリシジルエー
テルと、下記の式(3)で表されるテトラヒドロフルフ
リルアルコールとを適当な触媒(例えばNaOCH3,
Na0CJs+(CHi) 5cOK等のアルカリ金属
アルコラード)の存在下、公知の方法により反応させる
ことにより得られる。
該アルキルオキシラン又は当該アルキルグリシジルエー
テルと、下記の式(3)で表されるテトラヒドロフルフ
リルアルコールとを適当な触媒(例えばNaOCH3,
Na0CJs+(CHi) 5cOK等のアルカリ金属
アルコラード)の存在下、公知の方法により反応させる
ことにより得られる。
本発明におけるエーテル化合物(1)の磁気記録媒体へ
の添加量は、磁性材料100重量部あたり0.05〜1
5重量部が好ましい。また必要に応じて他の汎用潤滑剤
、例えばブチルステアレートのようなエステル、オレイ
ン酸のような脂肪酸、スクアランのような炭化水素と併
用して用いても良い。
の添加量は、磁性材料100重量部あたり0.05〜1
5重量部が好ましい。また必要に応じて他の汎用潤滑剤
、例えばブチルステアレートのようなエステル、オレイ
ン酸のような脂肪酸、スクアランのような炭化水素と併
用して用いても良い。
本発明におけるエーテル化合物(1)は、塗料中にあら
かじめ混入するか、又は磁性塗膜形成後にイソプロパノ
ール、ヘキサン等の汎用溶剤の溶液を塗布、乾燥するこ
とにより、塗膜に含浸して用いることができる。
かじめ混入するか、又は磁性塗膜形成後にイソプロパノ
ール、ヘキサン等の汎用溶剤の溶液を塗布、乾燥するこ
とにより、塗膜に含浸して用いることができる。
また、スパッタあるいは蒸着法により非磁性支持体上に
磁性層を形成して成る媒体に対しても、同様な方法で塗
布して用いることができる。
磁性層を形成して成る媒体に対しても、同様な方法で塗
布して用いることができる。
本発明の磁気記録媒体に使用される磁性粉としては針状
形の微細な1−Fez03. Fe5Oa+ Crow
のような金属酸化物、またCo被着7−Fe、0□C。
形の微細な1−Fez03. Fe5Oa+ Crow
のような金属酸化物、またCo被着7−Fe、0□C。
ドープγ−Fe、O,のような加工処理を施したTPe
t’s 、金属鉄粉末、微小板状のバリウムフェライト
及びそのFe原子の一部がTi、 Co、 Zn。
t’s 、金属鉄粉末、微小板状のバリウムフェライト
及びそのFe原子の一部がTi、 Co、 Zn。
V、 Nb等の1種又は2種以上で置換された磁性粉、
Go、 Fe−C0+ Fe−Ni等の金属又は合金の
超微粉などが挙げられる。これらのうち金属鉄粉末は特
に化学的に安定性が悪くこの改良のためニッケル、コバ
ルト、チタン、ケイ素、アルミニウムなどを金属原子、
塩及び酸化物の形で少量加えたり表面処理されることが
あるが、これらを用いることもできる。金属鉄粉末は又
その安定化のため弱い酸化性雰囲気の中で表面に薄い酸
化被膜を作らせることがあるが、このように処理された
金属粉を用いることもできる。また前述の磁性粉を2種
以上混合して用いてもよい。
Go、 Fe−C0+ Fe−Ni等の金属又は合金の
超微粉などが挙げられる。これらのうち金属鉄粉末は特
に化学的に安定性が悪くこの改良のためニッケル、コバ
ルト、チタン、ケイ素、アルミニウムなどを金属原子、
塩及び酸化物の形で少量加えたり表面処理されることが
あるが、これらを用いることもできる。金属鉄粉末は又
その安定化のため弱い酸化性雰囲気の中で表面に薄い酸
化被膜を作らせることがあるが、このように処理された
金属粉を用いることもできる。また前述の磁性粉を2種
以上混合して用いてもよい。
本発明において用いられる、磁性粉を分散させて磁性層
を形成させるための結合剤の例としては、ポリウレタン
、ポリ塩化ビニル、塩化ビニル酢酸ビニル共重合体、ポ
リアクリルニトリル、ニトリルゴム、エポキシ樹脂、ア
ルキッド樹脂、ポリアミド、ポリアクリル酸エステル、
ポリメタクリル酸エステル、ポリ酢酸ビニル、ポリビニ
ルブチラール、塩化ビニリデン、硝化綿、マレイン酸変
性塩化ビニル・酢酸ビニル共重合体、エチルセルロース
などが挙げられる。
を形成させるための結合剤の例としては、ポリウレタン
、ポリ塩化ビニル、塩化ビニル酢酸ビニル共重合体、ポ
リアクリルニトリル、ニトリルゴム、エポキシ樹脂、ア
ルキッド樹脂、ポリアミド、ポリアクリル酸エステル、
ポリメタクリル酸エステル、ポリ酢酸ビニル、ポリビニ
ルブチラール、塩化ビニリデン、硝化綿、マレイン酸変
性塩化ビニル・酢酸ビニル共重合体、エチルセルロース
などが挙げられる。
これらは単独で用いても、2種以上混合して用いてもよ
い。また樹脂の硬さを調節するため可塑剤や硬化剤を加
えて使用することもできる。
い。また樹脂の硬さを調節するため可塑剤や硬化剤を加
えて使用することもできる。
本発明の磁気記録媒体の磁性層には以上の成分の他、こ
の分野で通常、使用される研磨剤、帯電防止剤等の添加
剤を加えることができる。
の分野で通常、使用される研磨剤、帯電防止剤等の添加
剤を加えることができる。
また、本発明の磁気記録媒体を製造する際に用いられる
非磁性支持体としては、ポリエチレンテレフタレートの
ようなポリエステル;ポリエチレン、ポリプロピレン等
のポリオレフィン;セルローストリアセテート、セルロ
ースジアセテート等のセルロース誘導体;ボリカーボネ
ート;ポリ塩化ビニル;ポリイミド;芳香族ボリアくド
等のプラスチックiA1.Cu等の金属:紙等が使用さ
れる。形態はフィルム、テープ、シート、ディスク、カ
ード、ドラム等いずれでもよい。また支持体表面はコロ
ナ放電、放射線、紫外線等で処理されていても、あるい
は適当な樹脂でプレコートされていてもよい。
非磁性支持体としては、ポリエチレンテレフタレートの
ようなポリエステル;ポリエチレン、ポリプロピレン等
のポリオレフィン;セルローストリアセテート、セルロ
ースジアセテート等のセルロース誘導体;ボリカーボネ
ート;ポリ塩化ビニル;ポリイミド;芳香族ボリアくド
等のプラスチックiA1.Cu等の金属:紙等が使用さ
れる。形態はフィルム、テープ、シート、ディスク、カ
ード、ドラム等いずれでもよい。また支持体表面はコロ
ナ放電、放射線、紫外線等で処理されていても、あるい
は適当な樹脂でプレコートされていてもよい。
以下本発明を実施例により更に詳細に説明するが、本発
明がこれら実施例に限定されるものではないことは言う
までもない。
明がこれら実施例に限定されるものではないことは言う
までもない。
実施例1〜4
金属鉄粉末 100重量部塩化ビ
ニル−酢酸ビニル共重合体(I l 11 〃ポリ
ウレタン樹脂*2 11 〃カーボンブラ
ック(帯電防止剤) 2 〃CrzO3(研磨剤)
10〃 トルエン 71〃メチルエチル
ケトン 71〃シクロヘキサノン
107#注) 傘l:ユニオンカーバイド社製商品名VAGH傘2:日
本ポリウレタン社製商品名N−2301上記組成物をサ
ンドミルにて10時間混合した後、フィルタを通して取
出し、更に塗布直前に硬化剤を4.4重量部添加して撹
拌した。この塗料を32μ厚のポリエチレンテレフタレ
ートフィルム上に、乾燥後の磁性層厚みが4μになるよ
うにして両面に塗布し乾燥し巻き取った。これをカレン
ダー処理後硬化をしてから円盤状に打ち抜き、表1に示
される潤滑剤の2.0重量%イソプロパノール溶液を、
表1に示される潤滑剤の塗布量が600■/ポとなるよ
うに塗布して試料ディスクを作製した。
ニル−酢酸ビニル共重合体(I l 11 〃ポリ
ウレタン樹脂*2 11 〃カーボンブラ
ック(帯電防止剤) 2 〃CrzO3(研磨剤)
10〃 トルエン 71〃メチルエチル
ケトン 71〃シクロヘキサノン
107#注) 傘l:ユニオンカーバイド社製商品名VAGH傘2:日
本ポリウレタン社製商品名N−2301上記組成物をサ
ンドミルにて10時間混合した後、フィルタを通して取
出し、更に塗布直前に硬化剤を4.4重量部添加して撹
拌した。この塗料を32μ厚のポリエチレンテレフタレ
ートフィルム上に、乾燥後の磁性層厚みが4μになるよ
うにして両面に塗布し乾燥し巻き取った。これをカレン
ダー処理後硬化をしてから円盤状に打ち抜き、表1に示
される潤滑剤の2.0重量%イソプロパノール溶液を、
表1に示される潤滑剤の塗布量が600■/ポとなるよ
うに塗布して試料ディスクを作製した。
表
表 2
比較例1〜4
実施例1〜4で用いた潤滑剤の代わりに、表2に示す各
種潤滑剤を用いた他は、実施例1〜4と全く同様にして
試料ディスクを作製した。
種潤滑剤を用いた他は、実施例1〜4と全く同様にして
試料ディスクを作製した。
試験例
実施例1〜4及び比較例1〜4で得られた試料ディスク
について、耐久性を調べるため、各試料ディスクを不織
布を裏打ちしたシェルに収納し、記録再生装置に装填し
、同一トラック上でヘッドを連続走行させた。このとき
の周速は7閉/secである。
について、耐久性を調べるため、各試料ディスクを不織
布を裏打ちしたシェルに収納し、記録再生装置に装填し
、同一トラック上でヘッドを連続走行させた。このとき
の周速は7閉/secである。
一定バス回数後の試料ディスクの磁性層の傷つきを目視
で評価した。傷のまったく無い状態を◎とし、以下傷の
少ない順にQ、Δ、×として評価した。
で評価した。傷のまったく無い状態を◎とし、以下傷の
少ない順にQ、Δ、×として評価した。
この結果を表3に示す。
Claims (1)
- 【特許請求の範囲】 1 非磁性支持体上に磁性層を有する磁気記録媒体にお
いて、該磁性層が、下記一般式(1)で表されるエーテ
ル化合物を保持していることを特徴とする磁気記録媒体
。 ▲数式、化学式、表等があります▼(1) (式中、Rは炭素数4〜32の炭化水素基又は炭素数2
〜30のアルコキシ基を表す。)